CN111138968A - Special liquid crystal ceramic paint for underwater decoration and protection and preparation method thereof - Google Patents
Special liquid crystal ceramic paint for underwater decoration and protection and preparation method thereof Download PDFInfo
- Publication number
- CN111138968A CN111138968A CN201911386386.3A CN201911386386A CN111138968A CN 111138968 A CN111138968 A CN 111138968A CN 201911386386 A CN201911386386 A CN 201911386386A CN 111138968 A CN111138968 A CN 111138968A
- Authority
- CN
- China
- Prior art keywords
- agent
- paint
- liquid crystal
- underwater
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a special liquid crystal ceramic paint for underwater decoration and protection and a preparation method thereof, wherein the special liquid crystal ceramic paint for underwater decoration and protection consists of epoxy modified resin, high-temperature resistant pigment, filler, organic modifier and auxiliary agent; the material has the characteristics of higher bonding strength, high-speed water flow impact resistance, low possibility of abrasion, and resistance to water-borne positive and negative water pressure without delamination, reaches the drinking water environmental protection standard, can meet the coating environmental protection requirements of the water world, the ocean hall and the swimming pool, and can thoroughly solve the problems of delamination, cracking and shelling of coatings of the water world, the ocean hall and the swimming pool under underwater double positive and negative underwater conditions.
Description
Technical Field
The invention relates to the technical field of coatings, in particular to a special liquid crystal ceramic paint for underwater decoration and protection.
Background
The concrete of the water world, the ocean and the swimming pool is subjected to chemical medium pool water soaking (mainly disinfectant water, copper sulfate and the like) and outdoor severe environment examination (mainly ultraviolet irradiation, solar explosion and temperature difference cold and heat cycle change); the technical requirements of environmental protection, corrosion resistance, antibiosis, water resistance and no delamination of the service life and underwater humid environment are difficult to meet without excellent material mechanical property and maintenance measures;
the chemical properties of the product obtained by the existing underwater paint preparation method and production process are not stable enough, so that the service life of the product is short; particularly, the problems of coating falling, blistering and the like caused by the double action of positive and negative water pressure in water and the phenomenon that tourists in the water world fall down carelessly in the surfing process are difficult to effectively solve in underwater coating.
Disclosure of Invention
The invention aims to provide a liquid crystal ceramic paint for underwater decoration and protection, which can be used in the water world, a marine museum and a swimming pool.
The invention also aims to provide a preparation method of the liquid crystal ceramic paint for underwater decoration and protection.
The special liquid crystal ceramic paint for underwater decoration and protection comprises the following components in parts by weight:
base material: 40-60
Auxiliary agent: 2-5
Pigment: 10-30
Filling: 15-40
Organic modified product: 90-120
The base material is epoxy modified resin;
the organic modifier is modified polyamide;
the auxiliary agent comprises a wetting agent, a dispersing agent, a flatting agent, a softening agent, anti-skid particles, an anti-settling agent and a defoaming agent which are compatible with the coating; the main function is to assist in the formulation of the paint and to provide a certain aspect of the product with properties or to improve a certain aspect of the product.
The pigment is high-temperature calcined pigment or high-temperature resistant pigment; pigments and fillers not only provide a wide variety of colors to the coating, but also enhance some of the properties of the coating itself, such as hardness, abrasion resistance, hiding power.
Further, the organic modifier is one or a mixture of more than two of modifiers selected from PA/PE, PA/PP, PA/ABS, PA/PC, PA/PBT, PA/PET, PA/PPO, PA/PPS, PA/I, PA/PA, PPO/PA6 and PPS/PA 66.
The epoxy modified resin is one or a mixture of more than two of modified substances of polysulfide rubber, polyamide resin, polyvinyl butyral, nitrile rubber, phenolic resin, polyester resin, urea-formaldehyde melamine resin, furfural resin, vinyl resin, isocyanate and silicone resin.
Further, a curing agent used for paint preparation of the coating is an M233-B curing agent, and the solid content of the M233-B curing agent is 100%.
Further, the wetting and dispersing agent is a high molecular block copolymer with pigment-philic groups or an acrylic polymer containing pigment affinity groups.
Further, the pigment is one or a mixture of more than two of titanium dioxide, titanium nickel yellow, bismuth vanadate yellow, chrome yellow, strontium yellow, manganese iron black, copper chromium black, iron titanium black, carbon black, cobalt blue, titanium chromium brown, iron chromium brown, chromium green, cobalt green, molybdenum chromium red, iron red, pearlescent pigment, aluminum silver paste, mica powder, transparent silicon dioxide and transparent aluminum oxide.
In order to achieve the second purpose, the following technical scheme is adopted:
the preparation method of the special liquid crystal ceramic paint for underwater decoration and protection comprises the following steps:
(1) preparing paint: sequentially adding epoxy modified resin, modified polyamide, wetting agent, dispersing agent and anti-settling agent into a stirring kettle, dispersing for 5min at medium speed, wherein the rotating speed of the stirring kettle is as follows: 1000 r/min; titanium dioxide and filler are added in sequence in the dispersion, and the high-speed dispersion is carried out for 20-30 min; the rotating speed of the stirring kettle is as follows: 1500r/min, and the detection fineness is less than or equal to 35 um; and finally, sequentially adding a flatting agent and a defoaming agent in the dispersion, dispersing at an intermediate speed for 5min, wherein the rotating speed of the stirring kettle is as follows: 1000 r/min.
(2) Ceramic surface treatment: the method comprises the steps of firstly carrying out wax removal and oil removal treatment on the ceramic surface, then using a high-pressure air spray gun to spray oxides, stains and sand dust on the ceramic surface, wherein the workpiece subjected to impurity removal treatment needs to be sprayed within 1 hour, and the sand dust weather needs to be shortened as much as possible.
(3) Construction: mixing the main paint and the curing agent according to the ratio of 3.4:1, filtering the mixed paint by using a 200-300-mesh filter screen, adding the filtered paint into a spray gun, spraying under the normal air condition, adopting quick thin spraying when spraying for the first time, controlling the thickness to be 25-30um, directly spraying for the second time after naturally cooling for 5min, controlling the thickness to be 20-25 um according to the requirement, and cooling for 4 hours in the natural environment; and after spraying, the spray gun is cleaned by ethyl acetate.
The invention adopts the nano-crystal ceramic improvement technology to compositely modify the epoxy resin, and adds special additives such as a softening agent, anti-skid particles and the like to generate a solvent-free modified tough epoxy anti-skid ceramic resin composite material (namely liquid crystal ceramic for short); the material has the characteristics of higher bonding strength, high-speed water flow impact resistance, difficult abrasion, water resistance, and no delamination under positive and negative water pressure; meanwhile, the material of the invention conforms to GB/T17219-1998 safety evaluation standard of drinking water delivery and distribution equipment and protective materials for life, reaches the drinking water environmental protection standard, can adapt to the coating environmental protection requirements of the water world, the ocean hall and the swimming pool, and can thoroughly solve the problems of delamination, cracking and shelling of coatings of the water world, the ocean hall and the swimming pool under double underwater positive and negative conditions; the anti-slip particles specially added in the product can effectively prevent the risk of careless falling of tourists in the surfing process; meanwhile, the solid content of the product is up to 100 percent, and the product is not easy to dissolve in water due to the adoption of a wet curing agent; therefore, the coating can be completely and directly coated on wet surfaces, in light rain and underwater concrete, the construction efficiency is greatly improved, the coating time is saved, the construction compatibility is widened, and the problems of delamination and foaming caused by insufficient bonding strength of the conventional oily products (such as polyurea products) used for underwater coating, poor environmental protection effect, capability of resisting positive water pressure and incapability of effectively resisting negative water pressure are solved; and solves the problems of easy abrasion and difficult cleaning of the coating caused by insufficient hardness and poor stain resistance effect of the traditional waterborne products (such as waterborne polyurethane) used for underwater coating.
Detailed Description
The following examples further illustrate embodiments of the present invention. It should be noted that the description of the embodiments is provided to help understanding of the present invention, but the present invention is not limited thereto. In addition, the technical features involved in the embodiments of the present invention described below may be combined with each other as long as they do not conflict with each other.
Example one
Special liquid crystal ceramic paint formula for underwater decoration protection
The preparation method of the special liquid crystal ceramic paint for underwater decoration and protection comprises the following steps:
the method comprises the following steps: sequentially adding epoxy modified resin, modified polyamide, wetting agent, dispersing agent and anti-settling agent, dispersing for 5min at medium speed, wherein the rotating speed of a stirring kettle is as follows: 1000 r/min; titanium dioxide and filler are added in sequence in the dispersion, and the high-speed dispersion is carried out for 20-30 min; the rotating speed of the stirring kettle is as follows: 1500r/min, and the detection fineness is less than or equal to 35 um; and finally, sequentially adding a flatting agent and a defoaming agent in the dispersion, dispersing at an intermediate speed for 5min, wherein the rotating speed of the stirring kettle is as follows: 1000 r/min.
Step two: and (3) mixing the main paint and the curing agent according to the ratio of 3.4:1, filtering the mixed paint by using a 200-300-mesh filter screen, and adding the filtered paint into a spray gun.
Step three: the method comprises the steps of carrying out wax and oil removal treatment on the surface of the liquid crystal ceramic for underwater decoration protection in the water world, adopting quick thin spraying when spraying for the first time, controlling the thickness to be 25-30 mu m, directly carrying out spraying for the second time after naturally cooling for 5min, controlling the thickness to be 20-25 mu m according to requirements, and cooling for 4 hours in a natural environment.
The paint film performance was tested and the data is as follows:
example two
Special liquid crystal ceramic paint formula for underwater decoration protection
| Raw materials | Proportioning |
| Epoxy modified resin | 55 |
| Wetting agent | 0.3 |
| Dispersing agent | 0.3 |
| Anti-settling agent | 1 |
| Titanium white powder | 25 |
| Filler material | 22 |
| Leveling agent | 0.4 |
| Defoaming agent | 1 |
| Modified polyamide | 95 |
The preparation method of the special liquid crystal ceramic paint for underwater decoration and protection comprises the following steps:
the method comprises the following steps: sequentially adding epoxy modified resin, modified polyamide, wetting agent, dispersing agent and anti-settling agent, dispersing for 5min at medium speed, wherein the rotating speed of a stirring kettle is as follows: 1000 r/min; titanium dioxide and filler are added in sequence in the dispersion, and the high-speed dispersion is carried out for 20-30 min; the rotating speed of the stirring kettle is as follows: 1500r/min, and the detection fineness is less than or equal to 35 um; and finally, sequentially adding a flatting agent and a defoaming agent in the dispersion, dispersing at an intermediate speed for 5min, wherein the rotating speed of the stirring kettle is as follows: 1000 r/min.
Step two: and (3) mixing the main paint and the curing agent according to the ratio of 3.4:1, filtering the mixed paint by using a 200-300-mesh filter screen, and adding the filtered paint into a spray gun.
Step three: the method comprises the steps of carrying out wax and oil removal treatment on the surface of the liquid crystal ceramic for underwater decoration and protection of a marine museum, carrying out quick thin spraying when the spraying is carried out for the first time, controlling the thickness to be 25-30 microns, carrying out natural cooling for 5min, then directly carrying out spraying for the second time, controlling the thickness to be 20-25 microns according to requirements, and cooling for 4 hours in a natural environment.
The paint film performance was tested and the data is as follows:
EXAMPLE III
| Raw materials | Proportioning |
| Epoxy modified resin | 52 |
| Wetting agent | 0.3 |
| Dispersing agent | 0.3 |
| Anti-settling agent | 1 |
| Titanium white powder | 25 |
| Filler material | 20 |
| Leveling agent | 0.4 |
| Defoaming agent | 1 |
| Modified polyamide | 110 |
The preparation method of the special liquid crystal ceramic paint for underwater decoration and protection comprises the following steps:
the method comprises the following steps: sequentially adding epoxy modified resin, modified polyamide, wetting agent, dispersing agent and anti-settling agent, dispersing for 5min at medium speed, wherein the rotating speed of a stirring kettle is as follows: 1000 r/min; titanium dioxide and filler are added in sequence in the dispersion, and the high-speed dispersion is carried out for 20-30 min; the rotating speed of the stirring kettle is as follows: 1500r/min, and the detection fineness is less than or equal to 35 um; and finally, sequentially adding a flatting agent and a defoaming agent in the dispersion, dispersing at an intermediate speed for 5min, wherein the rotating speed of the stirring kettle is as follows: 1000 r/min.
Step two: and (3) mixing the main paint and the curing agent according to the ratio of 3.4:1, filtering the mixed paint by using a 200-300-mesh filter screen, and adding the filtered paint into a spray gun.
Step three: the liquid crystal ceramic surface of the underwater decoration protection of the swimming pool is subjected to wax and oil removal treatment, the quick thin spraying is adopted when the spraying is carried out for the first time, the thickness is controlled to be 25-30 mu m, the spraying is directly carried out for the second time after the natural cooling is carried out for 5min, the thickness is controlled to be 20-25 mu m according to the requirement, and the liquid crystal ceramic surface is cooled for 4 hours in the natural environment.
The paint film performance was tested and the data is as follows:
example four
The preparation method of the special liquid crystal ceramic paint for underwater decoration and protection comprises the following steps:
the method comprises the following steps: sequentially adding epoxy modified resin, modified polyamide, wetting agent, dispersing agent and anti-settling agent, dispersing for 5min at medium speed, wherein the rotating speed of a stirring kettle is as follows: 1000 r/min; titanium dioxide and filler are added in sequence in the dispersion, and the high-speed dispersion is carried out for 20-30 min; the rotating speed of the stirring kettle is as follows: 1500r/min, and the detection fineness is less than or equal to 35 um; and finally, sequentially adding a flatting agent and a defoaming agent in the dispersion, dispersing at an intermediate speed for 5min, wherein the rotating speed of the stirring kettle is as follows: 1000 r/min.
Step two: and (3) mixing the main paint and the curing agent according to the ratio of 3.4:1, filtering the mixed paint by using a 200-300-mesh filter screen, and adding the filtered paint into a spray gun.
Step three: and (3) carrying out wax and oil removal treatment on the surface of the liquid crystal ceramic for underwater decoration protection of the reservoir, carrying out quick thin spraying when the spraying is carried out for the first time, controlling the thickness to be 25-30 mu m, carrying out natural cooling for 5min, then directly carrying out spraying for the second time, controlling the thickness to be 20-25 mu m according to the requirement, and cooling for 4h in the natural environment.
The paint film performance was tested and the data is as follows:
the invention adopts the nano-crystal ceramic improvement technology to compositely modify the epoxy resin, and adds special additives such as a softening agent, anti-skid particles and the like to generate a solvent-free modified tough epoxy anti-skid ceramic resin composite material (namely liquid crystal ceramic for short); the material has the characteristics of higher bonding strength, high-speed water flow impact resistance, difficult abrasion, water resistance, and no delamination under positive and negative water pressure; meanwhile, the material of the invention conforms to GB/T17219-1998 safety evaluation standard of drinking water delivery and distribution equipment and protective materials for life, reaches the drinking water environmental protection standard, can adapt to the coating environmental protection requirements of the water world, the ocean hall and the swimming pool, and can thoroughly solve the problems of delamination, cracking and shelling of coatings of the water world, the ocean hall and the swimming pool under double underwater positive and negative conditions; the anti-slip particles specially added in the product can effectively prevent the risk of careless falling of tourists in the surfing process; meanwhile, the solid content of the product is up to 100 percent, and the product is not easy to dissolve in water due to the adoption of a wet curing agent; therefore, the coating can be directly coated on wet surfaces, light rain and underwater concrete, the construction efficiency is greatly improved, the coating time is saved, the construction compatibility is high, the coating is particularly suitable for construction of outdoor water world and swimming pool, the client can be ensured to drive 6.1 to open the garden, and the requirement of driving workers in the water world, the marine museum and the swimming pool is greatly met.
The embodiments of the present invention have been described in detail with reference to the examples, but the present invention is not limited to the described embodiments. It will be apparent to those skilled in the art that various changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, and the scope of protection is still within the scope of the invention.
Claims (7)
1. The special liquid crystal ceramic paint for underwater decoration and protection is characterized in that: the coating is a single component and comprises the following components in parts by weight:
base material: 40-60
Auxiliary agent: 2-5
Pigment: 10-30
Filling: 15-40
Organic modified product: 90-120
The base material is epoxy modified resin;
the organic modifier is modified polyamide;
the auxiliary agent comprises a wetting agent, a dispersing agent, a flatting agent, a softening agent, anti-skid particles, an anti-settling agent and a defoaming agent which are compatible with the coating;
the pigment is a high-temperature calcined pigment or a high-temperature resistant pigment.
2. The special liquid crystal ceramic paint for underwater decorative protection as claimed in claim 1, wherein: the organic modifier is one or a mixture of more than two of modifiers selected from PA/PE, PA/PP, PA/ABS, PA/PC, PA/PBT, PA/PET, PA/PPO, PA/PPS, PA/I, PA/PA, PPO/PA6 and PPS/PA 66.
3. The special liquid crystal ceramic paint for underwater decorative protection as claimed in claim 1, wherein: the epoxy modified resin is one or a mixture of more than two of modified substances of polysulfide rubber, polyamide resin, polyvinyl butyral, nitrile rubber, phenolic resin, polyester resin, urea-formaldehyde melamine resin, furfural resin, vinyl resin, isocyanate and silicon resin.
4. The special liquid crystal ceramic paint for underwater decorative protection as claimed in claim 1, wherein: the curing agent used for paint preparation of the coating is an M233-B curing agent, and the solid content of the M233-B curing agent is 100%.
5. The special liquid crystal ceramic paint for underwater decorative protection as claimed in claim 1, wherein: the wetting dispersant is a high-molecular block copolymer with pigment-philic groups or an acrylic polymer containing pigment affinity groups.
6. The special liquid crystal ceramic paint for underwater decorative protection as claimed in claim 1, wherein: the pigment is one or a mixture of more than two of titanium dioxide, titanium nickel yellow, bismuth vanadate yellow, chrome yellow, strontium yellow, manganese iron black, copper chromium black, iron titanium black, carbon black, cobalt blue, titanium chromium brown, iron chromium brown, chromium green, cobalt green, molybdenum chromium red, iron red, pearlescent pigment, aluminum silver paste, mica powder, transparent silicon dioxide and transparent aluminum oxide.
7. The method for preparing the ceramic crystal coating for the metal surface according to any one of claims 1 to 6, which is characterized by comprising the following steps:
(1) preparing paint: sequentially adding epoxy modified resin, modified polyamide, wetting agent, dispersing agent and anti-settling agent into a stirring kettle, dispersing for 5min at medium speed, wherein the rotating speed of the stirring kettle is as follows: 1000 r/min; titanium dioxide and filler are added in sequence in the dispersion, and the high-speed dispersion is carried out for 20-30 min; the rotating speed of the stirring kettle is as follows: 1500r/min, and the detection fineness is less than or equal to 35 um; and finally, sequentially adding a flatting agent and a defoaming agent in the dispersion, dispersing at an intermediate speed for 5min, wherein the rotating speed of the stirring kettle is as follows: 1000 r/min.
(2) Ceramic surface treatment: the method comprises the steps of firstly carrying out wax removal and oil removal treatment on the ceramic surface, then using a high-pressure air spray gun to spray oxides, stains and sand dust on the ceramic surface, wherein the workpiece subjected to impurity removal treatment needs to be sprayed within 1 hour, and the sand dust weather needs to be shortened as much as possible.
(3) Construction: mixing the main paint and the curing agent according to the ratio of 3.4:1, filtering the mixed paint by using a 200-300-mesh filter screen, adding the filtered paint into a spray gun, spraying under the normal air condition, adopting quick thin spraying when spraying for the first time, controlling the thickness to be 25-30um, directly spraying for the second time after naturally cooling for 5min, controlling the thickness to be 20-25 um according to the requirement, and cooling for 4 hours in the natural environment; and after spraying, the spray gun is cleaned by ethyl acetate.