CN111039425B - Composite scale and corrosion inhibitor suitable for natural pH operation and application thereof - Google Patents

Composite scale and corrosion inhibitor suitable for natural pH operation and application thereof Download PDF

Info

Publication number
CN111039425B
CN111039425B CN201811189684.9A CN201811189684A CN111039425B CN 111039425 B CN111039425 B CN 111039425B CN 201811189684 A CN201811189684 A CN 201811189684A CN 111039425 B CN111039425 B CN 111039425B
Authority
CN
China
Prior art keywords
corrosion inhibitor
condensation reaction
reaction product
copolymer
acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201811189684.9A
Other languages
Chinese (zh)
Other versions
CN111039425A (en
Inventor
张化冰
任志峰
魏新
冯婕
杨玉
常磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sinopec Beijing Research Institute of Chemical Industry
China Petroleum and Chemical Corp
Original Assignee
Sinopec Beijing Research Institute of Chemical Industry
China Petroleum and Chemical Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sinopec Beijing Research Institute of Chemical Industry, China Petroleum and Chemical Corp filed Critical Sinopec Beijing Research Institute of Chemical Industry
Priority to CN201811189684.9A priority Critical patent/CN111039425B/en
Publication of CN111039425A publication Critical patent/CN111039425A/en
Application granted granted Critical
Publication of CN111039425B publication Critical patent/CN111039425B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to the field of circulating cooling water treatment, and discloses a composite scale and corrosion inhibitor suitable for natural pH operation and application thereof, wherein the composite scale and corrosion inhibitor contains a condensation reaction product, 2-phosphonic acid-1, 2, 4-butane tricarboxylate, a sulfonate copolymer and zinc salt; the condensation reaction product is as follows by weight ratio: 2-phosphono-1, 2, 4-tricarboxylic acid butane: sulfonate copolymer: zinc salt is 1:0.44-1.5:0.89-5: 0.11-0.75; the condensation reaction product is a condensation reaction product of sodium gluconate and aspartic acid and/or a condensation reaction product of potassium gluconate and aspartic acid; the weight of the zinc salt is calculated as zinc ion. The composite scale and corrosion inhibitor provided by the invention has a synergistic effect among the components, has good scale and corrosion inhibition effects, and is less in component and lower in dosage.

Description

Composite scale and corrosion inhibitor suitable for natural pH operation and application thereof
Technical Field
The invention relates to the field of circulating cooling water treatment, in particular to a composite scale and corrosion inhibitor and application thereof in circulating cooling water treatment.
Background
The supply and demand conditions of the circulating cooling water have great influence on water use, drainage and water saving of the whole industrial enterprise, but the problem of scaling and candle corrosion of cooling facilities in the circulating cooling water system is brought along. In a circulating cooling water system, adding a scale and corrosion inhibitor is one of the most important methods for preventing the scale and corrosion of a circulating cooling water facility. Along with the gradual improvement of environmental protection regulations in China, in recent years, new requirements are provided for the direct discharge standard of water pollutants, wherein GB 31570 2015 'emission standard of petroleum refining industry pollutants' and GB31571-2015 'emission standard requirement of petrochemical industry pollutants' are required, from 7 months and 1 days in 2017, the total phosphorus of water discharged by enterprises is less than or equal to 1.0mg/L, the total zinc is less than or equal to 2.0mg/L, and the total phosphorus of a special discharge area is limited to 0.5 mg/L; the local standard of Beijing requires that COD is less than or equal to 30mg/L, total phosphorus is less than or equal to 0.3mg/L, and total zinc is less than or equal to 1.5 mg/L.
As the environmental protection standard is increasingly strict, the problem that the total phosphorus of the discharged sewage of most petrochemical enterprises exceeds the standard according to the new standard is solved. The circulating water which is used as a main source of phosphorus is treated by a source, the phosphorus content of the scale and corrosion inhibitor is controlled to be most economical and effective, the clean production concept is met, and the non-phosphorization or near-non-phosphorization of the scale and corrosion inhibitor is urgent. At present, the phosphorus-free corrosion inhibitor with excellent performance can be selected with small scope, and over 30 years, and the novel phosphorus-free corrosion inhibitor is always in active research and exploration.
CN107522300A discloses a non-phosphorus corrosion inhibitor and corrosion inhibitor composition, a preparation method thereof, application of the composition in inhibiting water corrosion and a treatment method of circulating water, wherein the corrosion inhibitor and zinc salt composition has good corrosion inhibition effect in specific water quality, the dosage of the corrosion inhibitor is 10-20mg/L, and the dosage is higher.
Therefore, the research of reducing the total phosphorus content in the circulating cooling water and reducing the components and the dosage of the composite scale and corrosion inhibitor while ensuring the scale and corrosion inhibition effect becomes the key point of the circulating cooling water treatment.
Disclosure of Invention
The invention aims to overcome the problems of high phosphorus content, more components and large dosage in the composite scale and corrosion inhibitor in the prior art, and provides the composite scale and corrosion inhibitor and the application thereof in circulating cooling water treatment.
In order to achieve the above objects, the present invention provides in a first aspect a composite scale and corrosion inhibitor suitable for natural pH operation, comprising a condensation reaction product, 2-phosphonobutane-1, 2, 4-tricarboxylate (PBTCA), a sulfonate copolymer, and a zinc salt; wherein, the condensation reaction product: PBTCA: sulfonate copolymer: zinc salt 1:0.44-1.5:0.89-5:0.11-0.75 (by weight); wherein the condensation reaction product is a condensation reaction product of sodium gluconate and aspartic acid and/or a condensation reaction product of potassium gluconate and aspartic acid; the weight of the zinc salt is calculated as zinc ion.
The second aspect of the invention provides an application of the composite scale and corrosion inhibitor in circulating cooling water treatment.
By adopting the technical scheme, good scale inhibition and corrosion inhibition effects can be achieved under the conditions of less components and low consumption (especially the consumption of condensation reaction products) of the water treatment agent, the current increasingly severe pollutant discharge requirements can be met, and the cost is reduced.
Detailed Description
The endpoints of the ranges and any values disclosed herein are not limited to the precise range or value, and such ranges or values should be understood to encompass values close to those ranges or values. For ranges of values, between the endpoints of each of the ranges and the individual points, and between the individual points may be combined with each other to give one or more new ranges of values, and these ranges of values should be considered as specifically disclosed herein.
The invention provides a composite scale and corrosion inhibitor suitable for natural pH operation, which comprises a condensation reaction product, PBTCA, a sulfonate copolymer and zinc salt; wherein, the condensation reaction product: PBTCA: sulfonate copolymer: zinc salt is 1:0.44-1.5:0.89-5:0.11-0.75 (weight ratio), wherein the weight of zinc salt is calculated by zinc ion.
In the invention, the condensation reaction product is a condensation reaction product of sodium gluconate and aspartic acid and/or a condensation reaction product of potassium gluconate and aspartic acid.
Preferably, the condensation reaction product: PBTCA: sulfonate copolymer: zinc salt is 1:0.44-1.3:1.08-4: 0.14-0.58.
According to the invention, the condensation reaction product can be produced by reacting sodium gluconate or potassium gluconate with aspartic acid in water by direct contact under condensation reaction conditions in the presence of a catalyst. The condensation reaction refers to dehydration condensation reaction between carboxyl in sodium gluconate or potassium gluconate and carboxyl hydroxyl in aspartic acid. Preferably, the molar ratio of the aspartic acid to the sodium gluconate or potassium gluconate is (0.5-8): 1. The catalyst is preferably an acid catalyst, more preferably the catalyst is selected from sulfuric acid and/or nitric acid, preferably the molar ratio of the catalyst to the sodium gluconate or potassium gluconate calculated on hydrogen ion is (0.4-6): 1. Preferably, the conditions of the condensation reaction include: the contacting is carried out at a temperature sufficient to distill off water, preferably the contacting is carried out in a heating bath at 100-. Preferably, the condensation reaction product has a molecular weight distribution of 300-600.
According to the present invention, the sulfonate copolymer (or sulfonic acid group-containing copolymer) is commercially available, and preferably, the sulfonate copolymer is a binary copolymer or a ternary copolymer. Preferably, the sulfonate copolymer is selected from the group consisting of a copolymer of acrylic acid ester and styrene sulfonic acid, a copolymer of acrylic acid and allyl sulfonic acid, a copolymer of acrylic acid and vinyl sulfonic acid, a copolymer of acrylic acid and 2-methyl-2 ' -acrylamidopropanesulfonic acid, a copolymer of acrylic acid, acrylamide and 2-methyl-2 ' -acrylamidopropanesulfonic acid, a copolymer of acrylic acid, acrylic acid ester and 2-methyl-2 ' -acrylamidopropanesulfonic acid, a copolymer of acrylic acid and 2-acrylamide-2-methylpropanesulfonic acid (AA/AMPS), a copolymer of acrylic acid, 2-acrylamide-2-methylpropanesulfonic acid and hydroxypropyl acrylate (AA/AMPS/HPA), an acrylic acid-sulfonate copolymer (TH-2000), and carboxylate-sulfonate-nonionic copolymer (TH-3100). More preferably, the acrylate is at least one of methyl acrylate, ethyl acrylate, and hydroxypropyl acrylate. The limiting viscosity of the sulfonate copolymer at 30 ℃ is usually from 0.065 to 0.085dL/g, or the kinetic viscosity of the sulfonate copolymer at 25 ℃ is usually 100-500 cps.
According to the present invention, both the PBTCA and the zinc salt are commercially available. Wherein, the zinc salt is an inorganic salt which can be dissolved in water and provide zinc ions. Preferably, the zinc salt is selected from zinc sulphate and/or zinc chloride.
According to the invention, in order to make the composite scale and corrosion inhibitor suitable for copper material circulating cooling water equipment, preferably, the composite scale and corrosion inhibitor also contains heterocyclic compounds; more preferably, the heterocyclic compound is at least one selected from mercaptobenzothiazole (2-mercaptobenzothiazole), benzotriazole and methylbenzotriazole.
Preferably, the condensation reaction product: the heterocyclic compound is 1:0.11-0.75 (weight ratio).
More preferably, the condensation reaction product: the heterocyclic compound is 1: 0.13-0.65.
According to the preferred embodiment of the invention, the composite scale and corrosion inhibitor consists of the components. The individual ingredients may be provided in the form of a solution or suspension, but the amounts or amounts are on a dry basis (solids content).
The composite scale and corrosion inhibitor is particularly suitable for medium hard water, namely corrosion and scale inhibition of circulating cooling water with the sum of the calcium hardness and the total alkalinity of supplementing water of 100-300 mg/L.
The invention also provides the application of the composite scale and corrosion inhibitor in circulating cooling water treatment.
The circulating cooling water of the invention can continuously supplement fresh water (make-up water) in the using process, and preferably, the composite scale and corrosion inhibitor of the invention is more suitable for medium hard water with the sum of calcium hardness and total alkalinity of make-up water of 100-300 mg/L.
Preferably, Ca in the makeup of the circulating cooling water2+The content of (A) is 50-150mg/L, and the total alkalinity is 50-150 mg/L.
By combining the components, excellent scale and corrosion inhibition effects can be obtained under the condition of low consumption of the condensation reaction product, therefore, the addition amount of the composite scale and corrosion inhibitor is preferably selected to ensure that the concentration of the condensation reaction product in circulating cooling water is 2-4.5 mg/L.
Preferably, the concentration of 2-phosphonobutane-1, 2, 4-tricarboxylate in the circulating cooling water is 2-3 mg/L.
Preferably, the concentration of the sulfonate copolymer in the recirculating cooling water is from 4 to 10 mg/L.
Preferably, the concentration of zinc salt (in terms of zinc ions) in the recirculating cooling water is from 0.5 to 1.5 mg/L.
Preferably, the concentration of the heterocyclic compound in the circulating cooling water is 0.5 to 1.5 mg/L.
The total dosage of each component is not higher than 21mg/L (preferably 9-20.5 mg/L).
The composite scale and corrosion inhibitor can realize the total phosphorus content (in PO) in the circulating cooling water4 3-Calculated) is below 1 mg/L.
The present invention will be described in detail below by way of examples. The starting materials used are all commercially available unless otherwise specified.
In the following examples, test raw water was concentrated 5 times to simulate the supplement of circulating cooling water, and test water was obtained.
The quality of the raw water is shown in Table 1
TABLE 1
Ca2+ Total alkalinity Cl- SO4 2- Electrical conductivity of pH
Test raw Water 1 123 135 80 112 612 7.8
Test raw Water 2 100 100 63 96 482 7.6
Note: 1) pH is nothing, conductivity is ms/cm, the rest is mg/L, Ca2+CaCO for total alkalinity3The same applies below.
2)Ca2+This represents the calcium hardness, as follows.
In Table 1, Ca2+According to the national standard GB/T6910-; the total alkalinity is measured according to the national standard GB/T15451-2006 determination of alkalinity of industrial circulating cooling water, total alkali and phenolphthalein; cl-Measured according to the standard GB/T15453-2008; SO (SO)4 2-Determined according to standard GB/T14642-; the conductivity is determined according to the standard GB/T6908-2008; the pH value was determined according to the standard GB/T6920-1986.
The test raw water 1 and the test raw water 2 were concentrated 5 times to obtain test water 1 and test water 2, respectively.
The rotary coupon corrosion test method comprises the following steps:
will 20#Fixing the carbon steel test piece/brass on a coupon instrument, putting the test piece/brass into test water, keeping the constant temperature at 45 +/-1 ℃, keeping the rotating speed at 75r/min for 72h, recording the weight of the test piece before and after the test, and calculating the average corrosion rate.
The average corrosion rate is calculated by the formula:
F=(C×△W)/(A×T×ρ)
c: the constants were calculated, in mm/a, such that C is 8.76 × 107
Δ W: corrosion weight loss (g) of the test piece;
a: area of test piece (cm)2);
T: corrosion test time (h);
ρ: density of test piece Material (kg/m)3)。
The method for measuring the performance of the scale inhibition (calcium carbonate) comprises the following steps:
taking test raw water, adding the composite scale and corrosion inhibitor according to the embodiment, evaporating and concentrating in a constant-temperature water bath at the temperature of 80 +/-1 ℃ until the concentration multiple is 5 times, sampling and analyzing the residual Ca in the water2+And simultaneously making blank samples, and calculating the scale inhibition rate.
The scale inhibition rate calculation formula is as follows: scale inhibition rate ═ C-C0)/(nC1-C0)×100%
C: actually measured Ca2+The concentration of (c);
C0: ca of blank2+The concentration of (c);
C1: ca in raw water2+The concentration of (c);
n: concentration times.
In the following preparation examples, the molecular weight of the condensation reaction product of sodium gluconate and/or potassium gluconate and aspartic acid was measured by mass spectrometry, and the scanning method was FTMS-p ESI Full ms [100-1000 ].
Preparation example 1
Preparation of condensation reaction product of sodium gluconate and aspartic acid
Sodium gluconate (available from carbofuran technologies, Inc.) was added to a four-necked flask equipped with a stirrer, distillation apparatus and thermometerAstro corporation, analytical purity) 21.8g (0.1mol), aspartic acid (from Aladdin reagent (Shanghai) Co., Ltd., analytical purity) 26.6g (0.2mol) and 100mL of water were stirred to fully dissolve and mix sodium gluconate and aspartic acid, and then concentrated sulfuric acid (from Tianjin optometry chemical research institute, analytical purity, concentration 98 wt%) 15g (containing H) was added at room temperature (20 deg.C)2SO40.15 mol). The heating bath (heating medium is dimethyl silicone oil) with the flask inside is heated to 100 ℃ and reacted for 10 hours, the distilled water amount in the reaction process is 30g, and the residual liquid, namely the condensation reaction product of the sodium gluconate and the aspartic acid with the solid content of 29.5 weight percent, is measured, and the molecular weight distribution is in the range of 311-426.
Preparation example 2
Preparation of condensation reaction product of sodium gluconate and aspartic acid
10.9g (0.05mol) of sodium gluconate, 16.6g (0.125mol) of aspartic acid and 100mL of water are added into a four-neck flask provided with a stirrer, a distilling device and a thermometer, stirring is started to fully dissolve and mix the sodium gluconate and the aspartic acid, and then 7.5g (containing H) of concentrated sulfuric acid is added at room temperature (20℃)2SO40.075 mol). The heating bath (heating medium is dimethyl silicone oil) with the flask inside is heated to 140 ℃ and reacted for 6 hours, the distilled water amount in the reaction process is 45g, and the residual liquid, namely the condensation reaction product of the sodium gluconate and the aspartic acid with the solid content of 26.3 weight percent, is measured, and the molecular weight distribution is in the range of 311-426.
Preparation example 3
Preparation of condensation reaction product of potassium gluconate and aspartic acid
23.4g (0.1mol) of potassium gluconate (purchased from carbofuran technologies, Ltd., analytical purity), 13.3g (0.1mol) of aspartic acid and 100mL of water were placed in a four-necked flask equipped with a stirrer, a distillation apparatus and a thermometer, stirring was started to sufficiently dissolve and mix the potassium gluconate and the aspartic acid, and then 3.7g (containing HNO) of concentrated nitric acid (purchased from Yili fine chemical research institute, Beijing, analytical purity, 68 wt%) was added at room temperature (20 ℃ C.) to the flask30.04 mol). A heating bath (heating medium) containing the flaskDimethyl silicone oil) is heated to 180 ℃ and reacted for 6 hours, the distilled water amount in the reaction process is 55g, and the residual liquid, namely the condensation reaction product of potassium gluconate with the solid content of 41.7 weight percent and aspartic acid, is measured, and the molecular weight distribution is in the range of 311-426.
Preparation example 4
Preparation of condensation reaction product of trisodium citrate and alanine
A four-necked flask equipped with a stirrer, a distillation apparatus and a thermometer was charged with 29.4g (0.1mol) of trisodium citrate (available from national pharmaceutical group chemical Co., Ltd., analytical grade), 8.9g (0.1mol) of alanine (available from Alantin reagent Co., Ltd., analytical grade), and 100mL of water, and stirred to sufficiently dissolve and mix the trisodium citrate and alanine, and then 8.0g (containing H) of concentrated sulfuric acid was charged at room temperature (20 ℃ C.) to the mixture2SO40.08 mol). The heating bath (heating medium is dimethyl silicone oil) with the flask inside is heated to 150 ℃ and reacted for 4 hours, the distilled water amount in the reaction process is 50g, and the residual liquid, namely the condensation reaction product of trisodium citrate and alanine with the solid content of 31.8 weight percent, is measured, and the molecular weight distribution is in the range of 263-358.
Example 1
8.8g of the condensation reaction product of sodium gluconate and aspartic acid obtained in preparation example 1, 5g of PBTCA (purchased from Shandongtai and Water treatment science and technology Co., Ltd., the same below) having a solid content of 50 wt%, 21.3g of a copolymer of acrylic acid and styrenesulfonic acid (having a solid content of 47 wt%, (the weight ratio of the two monomers was 70/30, the limiting viscosity at 30 ℃ was 0.080dL/g, purchased from Luoyangqiang industries Co., Ltd.), and 6.6g of ZnSO4·7H2O, adding water and shaking up to obtain 100g of the composite scale and corrosion inhibitor, wherein the condensation reaction product of the sodium gluconate and the aspartic acid comprises PBTCA, copolymer of acrylic acid and styrene sulfonic acid and Zn2+1:0.96:3.84:0.57 (by weight).
The composite scale and corrosion inhibitor is respectively added into test water 1 and test water 2 according to the concentration of 100mg/L, so that the concentration of the condensation reaction product of the sodium gluconate and the aspartic acid in the test water 1 and the test water 2 is 2.6mg/L, and the condensation reaction product is respectively added in the test water 1 and the test water 2The test water 1 and the test water 2 were spun into a coupon (20)#Carbon steel) corrosion test, and measuring the scale inhibition performance thereof.
Example 2
13.3g of the condensation product of sodium gluconate and aspartic acid from preparation 2, 4.6g of PBTCA having a solids content of 50% by weight, 17g of a copolymer of acrylic acid, hydroxypropyl acrylate and 2-methyl-2' -acrylamidopropanesulfonic acid having a solids content of 33% by weight (weight ratio of the three monomers 70/15/15, limiting viscosity at 30 ℃ of 0.078dL/g, from Luoyangstromen, Co., Ltd.), 1g of ZnCl2Adding water and shaking up to obtain 100g of composite scale and corrosion inhibitor, wherein the condensation reaction product of sodium gluconate and aspartic acid comprises PBTCA, acrylic acid, hydroxypropyl acrylate and copolymer of 2-methyl-2' -acrylamidopropanesulfonic acid, and Zn2+1:0.66:1.6:0.15 (weight ratio).
The composite scale and corrosion inhibitor is respectively added into test water 1 and test water 2 according to the concentration of 100mg/L, so that the concentration of a condensation reaction product of sodium gluconate and aspartic acid in the test water 1 and the test water 2 is 3.5mg/L, and the composite scale and corrosion inhibitor is respectively subjected to rotary hanging in the test water 1 and the test water 2 (20)#Carbon steel) corrosion test, and measuring the scale inhibition performance thereof.
Example 3
14.2g of the condensation reaction product of sodium gluconate and aspartic acid obtained in preparation example 1, 4.4g of PBTCA having a solids content of 50% by weight, 20.9g of a copolymer of methyl acrylate and styrenesulfonic acid having a solids content of 35% by weight (the weight ratio of the two monomers is 70/30, the limiting viscosity at 30 ℃ is 0.078dL/g, available from Luoyangong industries, Ltd.), 2.5g of ZnCl2Adding water and shaking up to obtain 100g of composite scale and corrosion inhibitor, wherein the condensation reaction product of sodium gluconate and aspartic acid comprises PBTCA, a copolymer of methyl acrylate and styrene sulfonic acid, and Zn2+1:0.52:1.74:0.29 (weight ratio).
The composite scale and corrosion inhibitor is respectively added into test water 1 and test water 2 according to the concentration of 100mg/L, so that the concentration of the condensation reaction product of the sodium gluconate and the aspartic acid in the test water 1 and the test water 2At 4.2mg/L, spin-hang chips (20) were added to test water 1 and test water 2, respectively#Carbon steel) corrosion test, and measuring the scale inhibition performance thereof.
Example 4
4.8g of the condensation reaction product of potassium gluconate and aspartic acid obtained in preparation 3, 5.2g of PBTCA having a solids content of 50% by weight, 9.1g of AA/AMPS having a solids content of 33% by weight (70/30 parts by weight of the monomers, 0.075dL/g of limiting viscosity at 30 ℃ C. ex Loxolone industries, Ltd.), 13.5g of a copolymer of acrylic acid and allylsulfonic acid having a solids content of 37% by weight (80/20 parts by weight of the monomers, 0.078dL/g of limiting viscosity at 30 ℃ C. ex Loxolone industries, Ltd.), and 3.5g of ZnSO4·7H2O, adding water and shaking up to obtain 100g of composite scale and corrosion inhibitor, wherein the condensation reaction product of potassium gluconate and aspartic acid comprises PBTCA, AA/AMPS, copolymer of acrylic acid and allylsulfonic acid and Zn2+1:1.3:1.5:2.5:0.4 (weight ratio).
The composite scale and corrosion inhibitor is respectively added into test water 1 and test water 2 according to the concentration of 100mg/L, so that the concentration of a condensation reaction product of potassium gluconate and aspartic acid in the test water 1 and the test water 2 is 2mg/L, and rotary hanging pieces (20) are respectively carried out in the test water 1 and the test water 2#Carbon steel) corrosion test, and measuring the scale inhibition performance thereof.
Example 5
15.3g of the condensation reaction product of sodium gluconate and aspartic acid obtained in preparation example 1, 4g of PBTCA having a solids content of 50% by weight, 14.5g of a copolymer of acrylic acid and styrenesulfonic acid having a solids content of 47% by weight (the weight ratio of the two monomers is 70/30, the limiting viscosity at 30 ℃ is 0.080dL/g, available from Luoyangong industries, Ltd.), 6.6g of ZnSO4·7H2O, adding water and shaking up to obtain 100g of the composite scale and corrosion and scale inhibitor, wherein the condensation reaction product of sodium gluconate and aspartic acid comprises PBTCA, copolymer of acrylic acid and styrene sulfonic acid and Zn2+1:0.45:1.51:0.33 (weight ratio).
The composite scale and corrosion inhibitor is respectively added into test water 1 and a test according to the concentration of 100mg/LThe condensation reaction product of sodium gluconate and aspartic acid was allowed to have a concentration of 4.5mg/L in test water 1 and test water 2 in water 2, and the spun-sheets (20) were applied to test water 1 and test water 2, respectively#Carbon steel) corrosion test, and measuring the scale inhibition performance thereof.
Example 6
9.5g of the condensation reaction product of sodium gluconate and aspartic acid obtained in preparation example 1, 6g of PBTCA having a solid content of 50% by weight, 9.3g of TH-2000 having a solid content of 43% by weight (density (20 ℃) of not less than 1.15g cm)-3100-500cps dynamic viscosity (25 ℃), obtained from Shandongtai and Water treatment science and technology Co., Ltd., the same below), 16.7g of a copolymer of acrylic acid, acrylamide and 2-methyl-2' -acrylamidopropanesulfonic acid having a solid content of 30% (the weight ratio of the three monomers is 70/15/15, the limiting viscosity at 30 ℃ is 0.068dL/g, obtained from Luoyangqianglong practical Co., Ltd., the same below), 1.3g of ZnCl2Adding water and shaking up to obtain 100.0g of composite scale and corrosion inhibitor, wherein the condensation reaction product of sodium gluconate and aspartic acid comprises PBTCA, TH-2000, acrylic acid, acrylamide and 2-methyl-2' -acrylamide propane sulfonic acid copolymer, Zn2+1:1.07:1.43:1.79:0.21 (weight ratio).
The composite scale and corrosion inhibitor is respectively added into test water 1 and test water 2 according to the concentration of 100mg/L, so that the concentration of a condensation reaction product of sodium gluconate and aspartic acid in the test water 1 and the test water 2 is 2.8mg/L, and the composite scale and corrosion inhibitor is respectively subjected to rotary hanging in the test water 1 and the test water 2 (20)#Carbon steel) corrosion test, and measuring the scale inhibition performance thereof.
Example 7
12.5g of the condensation reaction product of sodium gluconate and aspartic acid obtained in preparation example 1, 5.6g of PBTCA having a solid content of 50% by weight, and 8.9g of TH-3100 having a solid content of 45% by weight (density (20 ℃ C.)) of not less than 1.15g cm-3Dynamic viscosity (25 ℃) of 100-300cps, purchased from Shandongtai and Water treatment science and technology Co., Ltd, the same below) and 3.1g of ZnSO4·7H2O, adding water and shaking up to obtain 100g of the composite scale and corrosion inhibitor, wherein the condensation reaction product of the sodium gluconate and the aspartic acid is PBTCA:TH-3100:Zn2+1:0.76:1.09:0.19 (weight ratio).
The composite scale and corrosion inhibitor is respectively added into test water 1 and test water 2 according to the concentration of 100mg/L, so that the concentration of a condensation reaction product of sodium gluconate and aspartic acid in the test water 1 and the test water 2 is 3.7mg/L, and the composite scale and corrosion inhibitor is respectively subjected to rotary hanging in the test water 1 and the test water 2 (20)#Carbon steel) corrosion test, and measuring the scale inhibition performance thereof.
Example 8
10.2g of the condensation product of sodium gluconate and aspartic acid obtained in preparation 1, 5.4g of PBTCA having a solids content of 50% by weight, 15.0g of AA/AMPS/HPA having a solids content of 30% by weight (the weight ratio of the monomers is 60/20/20, the limiting viscosity at 30 ℃ is 0.075dL/g, from Rockwell industries, Ltd.), and 4.2g of ZnCl are weighed out2Adding water and shaking up to obtain 100g of composite scale and corrosion inhibitor, wherein the condensation reaction product of sodium gluconate and aspartic acid comprises PBTCA, AA/AMPS/HPA and Zn2+1:0.9:1.5:0.33 (weight ratio).
The composite scale and corrosion inhibitor is respectively added into test water 1 and test water 2 according to the concentration of 100mg/L, so that the concentration of a condensation reaction product of sodium gluconate and aspartic acid in the test water 1 and the test water 2 is 3mg/L, and rotary hanging pieces (20) are respectively carried out in the test water 1 and the test water 2#Carbon steel) corrosion test, and measuring the scale inhibition performance thereof.
Example 9
A test was conducted in accordance with the procedure of example 7, except that 0.5g of mercaptobenzothiazole (available from Shandongtai and Water treatment science, Ltd.) was further used to prepare the composite scale and corrosion inhibitor, and the material used in the spin-on sheet corrosion test was brass, and the scale inhibition performance thereof was measured.
Comparative example 1
The experiment was performed according to the method of example 4, except that PBTCA was not added in the process of preparing the composite scale and corrosion inhibitor.
Comparative example 2
The experiment was performed according to the method of example 6, except that TH-2000 and acrylic acid, acrylamide and 2-methyl-2' -acrylamidopropanesulfonic acid copolymer were not added during the preparation of the composite scale and corrosion inhibitor.
Comparative example 3
The experiment was conducted as in example 7, except that ZnSO was not added in the process of preparing the composite scale and corrosion inhibitor4·7H2O。
Comparative example 4
The experiment was performed according to the method of example 7, except that the condensation reaction product of sodium gluconate and aspartic acid was not added in the preparation of the composite scale and corrosion inhibitor.
Comparative example 5
A test was conducted in accordance with the procedure of example 7 except that 0.56g of PBTCA having a solid content of 50% by weight was added to obtain a composite scale and corrosion inhibitor, and the condensation reaction product of sodium gluconate and aspartic acid PBTCA: TH-3100: Zn2+1:0.08:1.08:0.19 (weight ratio).
Comparative example 6
A test was conducted in accordance with the procedure of example 7 except that 0.88g of TH-3100 having a solid content of 45% by weight was added to obtain a composite scale and corrosion inhibitor containing a condensation reaction product of sodium gluconate and aspartic acid PBTCA, TH-3100 and Zn2+1:0.76:0.11:0.19 (weight ratio).
Comparative example 7
The experiment was carried out as in example 7, except that PBTCA was replaced with 7.0g of polyaminopolyether methylene phosphonic acid PAPEMP (available from Shandong Tai and Water treatment science Co., Ltd.) having a solid content of 40% by weight.
Comparative example 8
The experiment was carried out in the same manner as in example 7 except that 11.6g of the condensation reaction product of trisodium citrate and alanine obtained in preparation example 4 was used in place of the condensation reaction product of sodium gluconate and aspartic acid.
Comparative example 9
50.8g of the condensation reaction product of sodium gluconate obtained in preparation example 1 and aspartic acid, 8.8g of ZnSO4·7H2Adding water and shaking up to obtain 100g of the phosphorus-free composite corrosion inhibitor, wherein,condensation reaction product of sodium gluconate and aspartic acid Zn2+1:0.13 (weight ratio).
The phosphorus-free composite corrosion inhibitor is respectively added into test water 1 and test water 2 according to the concentration of 100mg/L, and condensation reaction products of sodium gluconate and aspartic acid and Zn are added into the water2+Respectively has an effective concentration of 15mg/L and 2mg/L, and is subjected to spin coating in test water 1 and test water 2 (20)#Carbon steel) corrosion test.
Comparative example 10
67.8g of the condensation reaction product of sodium gluconate obtained in preparation example 1 and aspartic acid, 8.8g of ZnSO were weighed out4·7H2O, adding water and shaking up to obtain 100g of the phosphorus-free composite corrosion inhibitor, wherein the condensation reaction product of the sodium gluconate and the aspartic acid is Zn2+1:0.1 (weight ratio).
The phosphorus-free composite corrosion inhibitor is respectively added into test water 1 and test water 2 according to the concentration of 100mg/L, and condensation reaction products of sodium gluconate and aspartic acid and Zn are added into the water2+Respectively has an effective concentration of 20mg/L and 2mg/L, and is subjected to spin coating in test water 1 and test water 2 (20)#Carbon steel) corrosion test.
The results of the spin corrosion tests of the above examples and comparative examples are shown in table 2.
TABLE 2
Figure GDA0001881217380000151
Figure GDA0001881217380000161
The results in table 2 show that the composite scale and corrosion inhibitor provided by the invention contains a condensation reaction product, 2-phosphonobutane-1, 2, 4-tricarboxylate, a sulfonate copolymer and a zinc salt, is limited to be 1:0.44-1.5:0.89-5:0.11-0.75 by weight ratio, can play a synergistic effect, reduces the dosage of the condensation reaction product, and has good scale inhibition and corrosion inhibition effects. The composite scale and corrosion inhibitor provided by the invention has few components and low dosage, and is particularly suitable for medium-hard circulating cooling water treatment with the sum of the hardness of water supplementing calcium and the total alkalinity of 100-300 mg/L.
Example 10
To simulate the field, dynamic simulation tests were performed. The dynamic simulation test method is carried out according to the chemical industry standard HG/T2160-2008 of the people's republic of China, and the control parameters are as follows.
Concentration multiple:
tower A: 5 times of
Tower B: 5 times of
Flow rate: 1.0m/s
Medicament:
tower A: example 7 composite Scale and Corrosion inhibitor
Tower B: comparative example 3 composite scale and corrosion inhibitor
Inlet temperature: temperature difference of 32. + -. 1 ℃: 10 deg.C
The water quality of the test raw water is shown in the test raw water 1 of table 1.
The results of the dynamic simulation test strips and tubes are shown in Table 3.
TABLE 3
Figure GDA0001881217380000171
The corrosion speed of the carbon steel pipe wall of the open system is less than or equal to 0.075mm/a as specified in national standard GB 50050-2007 design Specification for Industrial circulating Cooling Water treatment 3.1.6; in the cooling water analysis and test method compiled by the production department and the development department of the general company of petrochemical industry, the laboratory small simulation test method stipulates that the corrosion speed of carbon steel is in a good grade between 0 and 0.028mm/a, in a good grade between 0.028 and 0.056mm/a and in an allowable grade between 0.056 and 0.070 mm/a; the adhesion speed is of the order of "good" at 0-6mcm, of "good" at 6-15mcm and of "permissible" at 15-20 mcm.
Therefore, when the composite scale and corrosion inhibitor provided by the invention is applied, under the condition that the sum of the calcium hardness and the total alkalinity of the supplementing water is 100-300mg/L, the corrosion rate of the test tube is 0.025mm/a, the good standard of the medium petrochemical industry is achieved, the adhesion rate is 2.2 mm, the good standard is achieved, and the corrosion and scale inhibition effects are better than those of the formula of the comparative example.
The preferred embodiments of the present invention have been described above in detail, but the present invention is not limited thereto. Within the scope of the technical idea of the invention, many simple modifications can be made to the technical solution of the invention, including combinations of various technical features in any other suitable way, and these simple modifications and combinations should also be regarded as the disclosure of the invention, and all fall within the scope of the invention.

Claims (14)

1. The composite scale and corrosion inhibitor suitable for natural pH operation is characterized by comprising a condensation reaction product, 2-phosphonic acid-1, 2, 4-butane tricarboxylate, a sulfonate copolymer and zinc salt, wherein the condensation reaction product comprises the following components in percentage by weight: 2-phosphono-1, 2, 4-tricarboxylic acid butane: sulfonate copolymer: zinc salt is 1:0.44-1.5:0.89-5: 0.11-0.75; wherein the condensation reaction product is a condensation reaction product of sodium gluconate and aspartic acid and/or a condensation reaction product of potassium gluconate and aspartic acid, and the weight of the zinc salt is calculated by zinc ions.
2. The composite scale and corrosion inhibitor of claim 1, wherein the condensation reaction product: 2-phosphono-1, 2, 4-tricarboxylic acid butane: sulfonate copolymer: zinc salt is 1:0.44-1.3:1.08-4: 0.14-0.58.
3. The composite scale and corrosion inhibitor according to claim 1 or 2, wherein the molecular weight distribution of the condensation reaction product is 300-600.
4. The composite scale and corrosion inhibitor according to claim 1 or 2, wherein the sulfonate copolymer is selected from the group consisting of a copolymer of acrylic acid ester and styrene sulfonic acid, a copolymer of acrylic acid and allyl sulfonic acid, a copolymer of acrylic acid and vinyl sulfonic acid, a copolymer of acrylic acid and 2-methyl-2 ' -acrylamidopropanesulfonic acid, a copolymer of acrylic acid, acrylic acid ester and 2-methyl-2 ' -acrylamidopropanesulfonic acid, a copolymer of acrylic acid, acrylamide and 2-methyl-2 ' -acrylamidopropanesulfonic acid, a copolymer of acrylic acid and 2-acrylamide-2-methylpropanesulfonic acid, a copolymer of acrylic acid, 2-acrylamide-2-methylpropanesulfonic acid and hydroxypropyl acrylate, an acrylic acid-sulfonate copolymer, and carboxylate-sulfonate-nonionic copolymer.
5. The composite scale and corrosion inhibitor of claim 4, wherein the acrylate is at least one of methyl acrylate, ethyl acrylate and hydroxypropyl acrylate.
6. The composite scale and corrosion inhibitor according to claim 1 or 2, wherein the zinc salt is selected from zinc sulfate and/or zinc chloride.
7. The composite scale and corrosion inhibitor according to claim 1 or 2, wherein the composite scale and corrosion inhibitor further comprises a heterocyclic compound.
8. The composite scale and corrosion inhibitor according to claim 7, wherein the heterocyclic compound is at least one selected from mercaptobenzothiazole, benzotriazole and methylbenzotriazole.
9. The composite scale and corrosion inhibitor according to claim 7, wherein the condensation reaction product comprises, in weight ratio: the heterocyclic compound is 1: 0.11-0.75.
10. The composite scale and corrosion inhibitor according to claim 7, wherein the condensation reaction product comprises, in weight ratio: heterocyclic compound ═ 1: 0.13-0.65.
11. The use of the composite scale and corrosion inhibitor of any one of claims 1-10 in the treatment of circulating cooling water.
12. The use of claim 11, wherein the recirculated cooling water is medium hard water having a make-up water calcium hardness and total alkalinity of 100-300 mg/L.
13. The use according to claim 11, wherein the concentration of the condensation reaction product, 2-phosphonobutane-1, 2, 4-tricarboxylate, sulfonate copolymer, zinc salt, and heterocyclic compound in the circulating cooling water is 2-4.5mg/L, 2-3mg/L, 4-10mg/L, 0.5-1.5mg/L, and 0.5-1.5mg/L, respectively, wherein the concentration of zinc salt is based on zinc ion.
14. The use of any one of claims 11 to 13, wherein the composite scale and corrosion inhibitor has a total phosphorus content of 1mg/L or less in circulating water, wherein the total phosphorus content is PO4 3-And (6) counting.
CN201811189684.9A 2018-10-12 2018-10-12 Composite scale and corrosion inhibitor suitable for natural pH operation and application thereof Active CN111039425B (en)