CN1109726C - 水溶性涂料 - Google Patents
水溶性涂料 Download PDFInfo
- Publication number
- CN1109726C CN1109726C CN 99117039 CN99117039A CN1109726C CN 1109726 C CN1109726 C CN 1109726C CN 99117039 CN99117039 CN 99117039 CN 99117039 A CN99117039 A CN 99117039A CN 1109726 C CN1109726 C CN 1109726C
- Authority
- CN
- China
- Prior art keywords
- water
- soluble paint
- pigment
- solid content
- water soluble
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种由丙烯酸酯树脂为:12~22%、丁醚化三聚氰胺树脂为:3~9%、多元醇聚合物为:6~11%、流平剂为:0~3%、催干剂为:0.3~1.5%、颜料为:27~33%、浓度28%的氨水为:2~6%、水为:30~44%组成的水溶性涂料,该水溶性涂料对包括铝质材料、铅锡合金、铝合金等在内的金属柔性材料表面涂装具有强附着力,优良柔韧性和光泽,且不易燃毒性小的效果。
Description
本发明涉及一种水溶性涂料。
众所周和,涂料中有机溶剂释放对环境造成的污染越来越被人们所重视,开发水性涂料产品替代溶剂型涂料,这不仅仅是环境保护提出的要求,同时也是我国政府提出的可持续发展战略的迫切需要。溶剂型涂料目前在金属及非金属材料涂装中被广泛地使用。通常其溶剂约占涂料总量的30%左右。据文献报导,全球涂料使用中所排放的有机溶剂量已达到1.5×107吨/年,这不仅给大气环境带来了严重的污染,而且造成了有机溶剂的极大浪费。许多国家,特别是发达国家,已经对溶剂型涂料的使用采取了严格的控制。用水性涂料替代溶剂型涂料已成为涂料工业发展的必然趋势。水性涂料可分为水溶性涂料和乳液型涂料。目前,国内水溶液性涂料正处于起步阶段,其应用范围,更有待于进一步拓展。从其质量指标可知,文献报导了水性铝质油墨属乳液型涂料,其对铝质附着力(2级)及柔韧性还不能满足广泛的金属柔性材料涂装要求。
本发明的目的在于提供一种能适用于金属柔性材料涂装要求的水溶性涂料。
为实现上述目的,本发明的水溶性涂料由丙烯酸酯树脂、丁醚化三聚氰胺树脂、多元醇聚合物、流平剂、催干剂、颜料、氨水、水组成,各成份重量比为:
丙烯酸酯树脂(固含量100%) 12~22%
丁醚化三聚氰胺树脂(固含量100%) 3~9%
多元醇聚合物 6~11%
流平剂 0~3%
催干剂 0.3~1.5%
颜料 27~33%
浓度28%的氨水 2~6%
水 30~44%
采用本发明的配方生产出来的水溶性涂料具有对包括铝质材料、铝锡合金、铝合金等在内的金属柔性材料表面涂装具有强附着力,优良柔韧性和光泽,本发明的产品涂装可采用滚涂、喷涂等机械施工,烘干温度150~200℃,烘干时间1~3分钟,本发明的产品涂料具有毒性小、不易燃,对环境无有机物污染,消除了产品贮运,施工过程中的易燃、易爆危险。
本发明的几种具体实施方案为:
1 | 2 | 3 | |||
名称 | 重量百分比 | 名称 | 重量百分比 | 名称 | 重量百分比 |
丙烯酸酯树脂(固含量100%) | 13.2 | 丙烯酸酯树脂(固含量100%) | 16 | 丙烯酸酯树脂(固含量100%) | 20 |
丁醚化三聚氰胺树脂(固含量100%) | 3 | 丁醚化三聚氰胺树脂(固含量100%) | 3.5 | 丁醚化三聚氰胺树脂(固含量100%) | 4 |
多元醇聚合物 | 11 | 多元醇聚合物 | 9 | 多元醇聚合物 | 7 |
流平剂 | 0 | 流平剂 | 2 | 流平剂 | 1 |
催干剂 | 0.3 | 催干剂 | 0.5 | 催干剂 | 1 |
颜料(钛白粉) | 30 | 颜料(钛白粉) | 29 | 颜料(钛白粉) | 27 |
浓度28%的氨水 | 2.64 | 浓度28%的氨水 | 3.2 | 浓度28%的氨水 | 4 |
水 | 39.86 | 水 | 36.8 | 水 | 37 |
本发明的生产过程是:将一部分去离子水、浓度28%的氨水,加入反应釜,加热至70~80℃搅拌并缓慢加入丙烯酸酯树脂(固含量100%),使其进行成盐反应和溶解至透明琥珀色粘稠液,制得固含量为40%的树脂液再与其它原料混合,经分散、研磨制得水溶性金属柔性材料涂料。三种配方产品测试结果为:
指标名称产品序号 | 涂料性能 | 施工性能 | 涂膜性能 | |||||||
粘度(秒) | 细度(微米) | 流平性(分钟) | 干燥时间(分钟) | 附着力(级) | 柔韧性(mm) | 光泽(%) | 耐水性 | |||
检则方法 | GB1273-79 | GB1724-79(88) | GB1750-79(88) | 150~200(℃) | GB1720-79(88) | GB1731-79 | GB1743-79(88) | GB1733-79 | ||
企业标准 | 80~130 | ≤10 | <2 | <3 | 1~2 | 1~3 | >90 | >120小时无裂纹 | ||
123 | 95105120 | <10 | 111.5 | 21.51 | 111 | 111 | 989695 | >120 |
Claims (1)
1、一种水溶性涂料,由丙烯酸酯树脂、丁醚化三聚氰胺树脂、多元醇聚合物、流平剂、催干剂、颜料、氨水、水组成,其特征在于各成份重量比为:
丙烯酸酯树脂(固含量100%) 12~22%
丁醚化三聚氰胺树脂(固含量100%) 3~9%
多元醇聚合物 6~11%
流平剂 0~3%
催干剂 0.3~1.5%
颜料 27~33%
浓度28%的氨水 2~6%
水 30~44%