CN110964434A - Aldehyde-free green environment-friendly adhesive and preparation method thereof - Google Patents
Aldehyde-free green environment-friendly adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN110964434A CN110964434A CN201911190740.5A CN201911190740A CN110964434A CN 110964434 A CN110964434 A CN 110964434A CN 201911190740 A CN201911190740 A CN 201911190740A CN 110964434 A CN110964434 A CN 110964434A
- Authority
- CN
- China
- Prior art keywords
- aldehyde
- green environment
- friendly adhesive
- free green
- urea
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an aldehyde-free green environment-friendly adhesive and a preparation method thereof. The adhesive disclosed by the invention is strong in binding power, free of formaldehyde release and stable in color. The preparation method is simple, no other curing agent is added, the production cost is low, and the preparation conditions are mild. The adhesive prepared by the method is good in adhesive property, green and environment-friendly, and does not generate harmful gas in the using process.
Description
Technical Field
The invention relates to the technical field of chemical synthesis, and particularly relates to an aldehyde-free green environment-friendly adhesive and a preparation method thereof.
Background
China is a large wood consumption country, and the artificial board is one of the main ways of wood consumption, and the artificial board industry develops rapidly and has a huge market in China; at present, 90% of adhesives for artificial boards in the market contain substances harmful to human bodies, such as formaldehyde, benzene, toluene and the like. Currently, adhesives are widely used in life and production of people, and are widely used in furniture manufacturing industry and decoration industry. With the development of social economy and the increasing living standard of people, people have higher environmental awareness and higher requirements on living environment and living goods. Long-term inhalation of small amounts of formaldehyde also causes strong carcinogenicity. Therefore, the production of an aldehyde-free green environment-friendly adhesive is a trend of the development of adhesives in the future.
At present, a novel green, environment-friendly, formaldehyde-free, green and environment-friendly adhesive and a preparation method thereof are lacked.
Disclosure of Invention
The invention aims to provide a novel green, environment-friendly and thorough formaldehyde-free high-performance thermosetting resin adhesive and a preparation method thereof.
The technical scheme of the invention is as follows: the aldehyde-free green environment-friendly adhesive disclosed by the invention is composed of a high-branching polymer obtained by reacting urea with Polyethyleneimine (PEI).
Further, the molar ratio of the polyethyleneimine PEI to the urea is 1: 2-6.
The preparation method of the aldehyde-free green environment-friendly adhesive comprises the following steps:
(1) weighing polyethyleneimine PEI and Urea Urea according to the proportion;
(2) uniformly stirring, and placing the mixture in an oil bath kettle at the temperature of 120-135 ℃ for reaction for 4-10 h;
(3) and cooling to room temperature after reaction, weighing the mass of the product, and adding water according to 50-60% of solid content to completely dissolve the product to prepare the aldehyde-free green environment-friendly adhesive.
Further, in the step (2), the reaction temperature is 130 ℃.
Further, in the step (2), the reaction time is 6 h.
Further, in the step (3), the solid content of the adhesive is 55%.
Has the advantages that: the adhesive disclosed by the invention is strong in binding power, free of formaldehyde release and stable in color. The preparation method is simple, no other curing agent is added, the production cost is low, and the preparation conditions are mild. The adhesive prepared by the method is good in adhesive property, green and environment-friendly, and does not generate harmful gas in the using process.
Detailed Description
The invention is further illustrated by the following examples. It should be understood that these examples are illustrative and exemplary of the present invention, and are not intended to limit the scope of the present invention in any way.
Example 1
The invention relates to an aldehyde-free green environment-friendly adhesive and a preparation method thereof, which comprises the following steps: (1) adding 39.25g PEI and 10.00g Urea to a reactor; the molar ratio is as follows: polyethyleneimine PEI: urea 1: 2;
(2) stirring uniformly, and placing in an oil bath kettle at 130 ℃ for reaction for 10 h;
(3) and cooling to room temperature after reaction, and adding water according to the solid content of 55% to completely dissolve the mixture to obtain the aldehyde-free green environment-friendly adhesive.
Example 2
The invention relates to an aldehyde-free green environment-friendly adhesive and a preparation method thereof, which comprises the following steps:
in step (1), the reactants PEI 33.00g and Urea 12.60g were added to the reactor; the molar ratio is as follows: polyethyleneimine PEI: urea 1: 3;
in the step (2), uniformly stirring, and placing in an oil bath kettle at 130 ℃ for reaction for 10 h;
in the step (3), after the reaction, cooling to room temperature, and adding water according to the solid content of 55% to completely dissolve the reaction product, thereby obtaining the aldehyde-free green environment-friendly adhesive.
Example 3
The invention relates to an aldehyde-free green environment-friendly adhesive and a preparation method thereof, which comprises the following steps:
in the step (1), 19.60g of polyethyleneimine PEI and 10.00g of Urea Urea are added into a reactor; the molar ratio is as follows: polyethyleneimine PEI: urea 1: 4;
in the step (2), uniformly stirring, and placing in an oil bath kettle at 130 ℃ for reaction for 10 h;
in the step (3), after the reaction, cooling to room temperature, and adding water according to the solid content of 55% to completely dissolve the reaction product, thereby obtaining the aldehyde-free green environment-friendly adhesive.
Example 4
The invention relates to an aldehyde-free green environment-friendly adhesive and a preparation method thereof, which comprises the following steps:
in the step (1), 15.70g of polyethyleneimine PEI and 10.00g of Urea Urea are added into a reactor; the molar ratio is as follows: polyethyleneimine PEI: urea 1: 5;
in the step (2), uniformly stirring, and placing in an oil bath kettle at 130 ℃ for reaction for 10 h;
in the step (3), after the reaction, cooling to room temperature, and adding water according to the solid content of 55% to completely dissolve the reaction product, thereby obtaining the aldehyde-free green environment-friendly adhesive.
Example 5
The invention relates to an aldehyde-free green environment-friendly adhesive and a preparation method thereof, which comprises the following steps:
in the step (1), 13.07g of polyethyleneimine PEI and 10.00g of Urea Urea are added into a reactor; the molar ratio is as follows: polyethyleneimine PEI: urea 1: 6;
in the step (2), uniformly stirring, and placing in an oil bath kettle at 130 ℃ for reaction for 10 h;
in the step (3), after the reaction, cooling to room temperature, and adding water according to the solid content of 55% to completely dissolve the reaction product, thereby obtaining the aldehyde-free green environment-friendly adhesive.
Example 6
The invention relates to an aldehyde-free green environment-friendly adhesive and a preparation method thereof, which comprises the following steps: (1) adding 39.25g of PEI and 10.00g of Urea Urea into a reactor; the molar ratio is as follows: polyethyleneimine PEI: urea 1: 2;
(2) stirring uniformly, and placing in an oil bath kettle at 120 ℃ for reaction for 10 h;
(3) and cooling to room temperature after reaction, and adding water according to the solid content of 55% to completely dissolve the mixture to obtain the aldehyde-free green environment-friendly adhesive.
Example 7
The invention relates to an aldehyde-free green environment-friendly adhesive and a preparation method thereof, which comprises the following steps:
in the step (1), 33.00g of polyethyleneimine PEI and 12.60g of Urea Urea are added into a reactor; the molar ratio is as follows: polyethyleneimine PEI: urea 1: 3;
in the step (2), uniformly stirring, and placing in an oil bath kettle at 125 ℃ for reaction for 10 h;
in the step (3), after the reaction, cooling to room temperature, and adding water according to the solid content of 55% to completely dissolve the reaction product, thereby obtaining the aldehyde-free green environment-friendly adhesive.
Example 8
The invention relates to an aldehyde-free green environment-friendly adhesive and a preparation method thereof, which comprises the following steps:
in the step (1), 19.60g of polyethyleneimine PEI and 10.00g of Urea Urea are added into a reactor; the molar ratio is as follows: polyethyleneimine PEI: urea 1: 4;
in the step (2), uniformly stirring, and placing in a 135 ℃ oil bath for reaction for 10 h;
in the step (3), after the reaction, cooling to room temperature, and adding water according to the solid content of 55% to completely dissolve the reaction product, thereby obtaining the aldehyde-free green environment-friendly adhesive.
Example 9
The invention relates to an aldehyde-free green environment-friendly adhesive and a preparation method thereof, which comprises the following steps:
in the step (1), 15.70g of polyethyleneimine PEI and 10.00g of Urea Urea are added into a reactor; the molar ratio is as follows: polyethyleneimine PEI: urea 1: 5;
in the step (2), uniformly stirring, and placing in an oil bath kettle at 120 ℃ for reaction for 8 h;
in the step (3), after the reaction, cooling to room temperature, and adding water according to the solid content of 55% to completely dissolve the reaction product, thereby obtaining the aldehyde-free green environment-friendly adhesive.
Example 10
The invention relates to an aldehyde-free green environment-friendly adhesive and a preparation method thereof, which comprises the following steps:
in the step (1), 13.07g of polyethyleneimine PEI and 10.00g of Urea Urea are added into a reactor; the molar ratio is as follows: polyethyleneimine PEI: urea 1: 6;
in the step (2), uniformly stirring, and placing in an oil bath kettle at 120 ℃ for reaction for 6 h;
in the step (3), after the reaction, cooling to room temperature, and adding water according to the solid content of 55% to completely dissolve the reaction product, thereby obtaining the aldehyde-free green environment-friendly adhesive.
Test example 1
In order to verify the performance characteristics of the synthesized aldehyde-free green environment-friendly adhesive, the following tests were carried out:
the aldehyde-free green environment-friendly adhesive prepared in the embodiment is taken, poplar veneers with the thickness of 2mm are used for pressing three layers of plywood, the physical and mechanical properties of the board are tested according to the requirements of national standard GB/T17657 plus 2013 physicochemical property test method for artificial boards and decorative artificial boards, and the water resistance of the board is mainly tested. The method comprises the following specific steps: the synthesized aldehyde-free green environment-friendly adhesive is 160g/m according to the adhesive application amount2The test paper is coated on a single-layer poplar board, the hot pressing temperature is 200 ℃, the hot pressing is carried out for 6 minutes, then the board is cut into 36 test pieces, the dry strength, the wet strength (the test pieces are soaked in 63 ℃ water for 3 hours), the water resistance (the test pieces are soaked in boiling water for 3 hours) and the like of the 36 test pieces are respectively tested by dividing the test pieces into 3 parts on average, and the test results are shown in table 1:
TABLE 1
According to the measured intensity of each example, the following results are obtained by screening: when the molar ratio of each reactant is: PEI: 1: and 3, the corresponding aldehyde-free green environment-friendly adhesive has the best performance.
According to the water resistance requirement of GB/T9846-.
The specific embodiments described herein are merely illustrative of the spirit of the invention. Various modifications or additions may be made to the described embodiments or alternatives may be employed by those skilled in the art without departing from the spirit or ambit of the invention as defined in the appended claims.
Claims (6)
1. The aldehyde-free green environment-friendly adhesive is characterized by comprising the following components in parts by weight: the aldehyde-free green environment-friendly adhesive is composed of a hyperbranched polymer obtained by reacting urea and Polyethyleneimine (PEI).
2. The aldehyde-free green environment-friendly adhesive as claimed in claim 1, wherein: the molar ratio of the polyethyleneimine PEI to the urea is 1: (2-6).
3. The preparation method of the aldehyde-free green environment-friendly adhesive as claimed in claim 2 is characterized by comprising the following steps:
(1) weighing PEI and urea in the proportions recited in claim 2;
(2) uniformly stirring, and placing the mixture in an oil bath kettle at the temperature of 120-135 ℃ for reaction for 4-10 h;
(3) and cooling to room temperature after reaction, weighing the mass of the product, and adding water according to 50-60% of solid content to completely dissolve the product to prepare the aldehyde-free green environment-friendly adhesive.
4. The aldehyde-free green environment-friendly adhesive as claimed in claim 3, wherein: in step (2), the reaction temperature is 130 ℃.
5. The aldehyde-free green environment-friendly adhesive as claimed in claim 3, wherein: in the step (2), the reaction time is 6 h.
6. The aldehyde-free green environment-friendly adhesive as claimed in claim 3, wherein: in the step (3), the solid content of the adhesive is 55%.