CN110948964A - 吸水脚垫及其制造方法 - Google Patents

吸水脚垫及其制造方法 Download PDF

Info

Publication number
CN110948964A
CN110948964A CN201911096211.9A CN201911096211A CN110948964A CN 110948964 A CN110948964 A CN 110948964A CN 201911096211 A CN201911096211 A CN 201911096211A CN 110948964 A CN110948964 A CN 110948964A
Authority
CN
China
Prior art keywords
water
parts
water absorbing
foot pad
mass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911096211.9A
Other languages
English (en)
Inventor
吴富荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiaxing Kefu Printing Materials Co ltd
Original Assignee
Jiaxing Kefu Printing Materials Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiaxing Kefu Printing Materials Co ltd filed Critical Jiaxing Kefu Printing Materials Co ltd
Priority to CN201911096211.9A priority Critical patent/CN110948964A/zh
Publication of CN110948964A publication Critical patent/CN110948964A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种吸水脚垫，在使用时能迅速吸干足底水分，而且自身具有良好的干燥能力。一种吸水脚垫，包括可卷的基材层，基材层具有吸水性，在基材层的上表面设有吸水材料层，在基材层的下表面设有防滑材料层；其中，所述吸水材料层包括以下质量份的组分：白炭黑7‑15质量份、胶粘剂3‑18质量份、助剂0.3‑1质量份和色粉0.5‑1.5质量份。本发明还提供一种吸水脚垫的制造方法，包括吸水材料制备步骤、涂布吸水材料和烘干步骤、镜面冷压步骤、施胶步骤。

Description

吸水脚垫及其制造方法
技术领域
本发明属于吸水脚垫的技术领域，本发明还涉及一种吸水脚垫的制造方法。
背景技术
吸水脚垫，作为浴室内的物件，使用者在沐浴后，站到吸水脚垫上，利用吸水脚垫吸干人体足底的水分。
目前，吸水脚垫有两种结构：一种是纺织吸水脚垫，还有一种是采用硅藻土材料制成的吸水脚垫。
在使用过程中纺织吸水脚垫其自身的干燥能力有限，通常在使用后需要清洗晒干。硅藻土吸水脚垫，是采用硅藻土等材料制成，其质地较硬，使用舒适度较差，并且制造成本相较高。
发明内容
本发明的目的是提供一种吸水脚垫，在使用时能迅速吸干足底水分，而且自身具有良好的干燥能力。
为解决上述技术问题，本发明采用的技术方案是：
一种吸水脚垫，包括可卷的基材层，基材层具有吸水性，在基材层的上表面设有吸水材料层，在基材层的下表面设有防滑材料层；其中，所述吸水材料层包括以下质量份的组分：白炭黑7-15质量份、胶粘剂3-18质量份、助剂0.3-1质量份和色粉0.5-1.5质量份。
在上述方案的基础上并作为上述方案的优选方案：所述基材层为棉布。
在上述方案的基础上并作为上述方案的优选方案：所述防滑材料层为可移胶。
在上述方案的基础上并作为上述方案的优选方案：所述吸水材料层包括以下质量份的组分：白炭黑10质量份、胶粘剂5-10质量份、助剂0.5质量份和色粉1质量份。
在上述方案的基础上并作为上述方案的优选方案：所述胶粘剂为PVA、VAE乳液、聚氨酯胶粘剂或PA胶水。
本发明还提供一种吸水脚垫的制造方法，包括吸水材料制备步骤；吸水材料由包括以下质量份的组分：白炭黑7-15质量份、胶粘剂3-18质量份、助剂0.3-1质量份、色粉0.5-1.5质量份和水3-8质量份；将7-15质量份的白炭黑、3-18质量份的胶粘剂、0.3-1质量份的助剂、0.5-1.5质量份的色粉和3-8质量份的水制备成可用于涂布的吸水材料；
涂布吸水材料和烘干步骤，将可涂布的吸水材料通过涂布工艺涂布在基材层的一面，并将其烘干；
镜面冷压步骤，对经烘干后的吸水材料进行镜面滚压；
施胶步骤，在基材层的另一面设置可移胶。
在上述方案的基础上并作为上述方案的优选方案：吸水材料由以下质量份的组分组成：白炭黑10质量份、胶粘剂5-10质量份、助剂0.5质量份、色粉1质量份和水4质量份。
在上述方案的基础上并作为上述方案的优选方案：所述胶粘剂为PVA，将PVA配置成浓度小于10％的水溶液，再将白炭黑、助剂、色粉和水与水溶液混合均匀。
在上述方案的基础上并作为上述方案的优选方案：所述胶粘剂为VAE乳液、聚氨酯胶粘剂或PA胶水。
本发明相比现有技术突出且有益的技术效果是：
本发明的吸水脚垫，在使用时，脚底的水分经过白炭黑的孔隙向基材层渗透，被基材层吸收，基材层形成锁水，从而对人体足底的水具有良好的吸收能力，同时，水分被基材层吸收后，吸水材料层又在人体足底和基材层之间形成隔离，以保证足底干燥。另外，白炭黑具有多孔隙，具有较大的比表面积，这样吸水材料层干燥速度较快，保证二次使用效果。另外，这种结构的吸水脚垫整体可卷，便于运输和存放。这种吸水脚垫制造成本低。
附图说明
图1是本发明的结构示意图。
具体实施方式
为使本申请的目的、技术方案和优点更加清楚，下面将结合实施例中的附图，对实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本申请一部分实施例，而不是全部实施例。基于已给出的实施例，本领域普通技术人员在未做出创造性劳动前提下所获得的所有其他实施例，都属于本申请保护的范围。
在本申请的描述中，需要理解的是，术语“上”、“下”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本申请和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本申请的限制。
本发明公开了一种吸水脚垫以及吸水脚垫的制造方法，这种吸水脚垫通常在浴室等场所使用，代替传统的地巾使、吸水硅胶垫，在沐浴后站立到该吸水脚垫上，由吸水脚垫吸附足底的水。
本发明的一种吸水脚垫，包括可卷的基材层2，在基材层2的上表面设有吸水材料层1，在基材层2的下表面设有防滑材料层；其中，所述吸水材料层1包括以下质量份的组分：白炭黑7质量份、胶粘剂3质量份、助剂0.3质量份和色粉0.5质量份。其中，所述基材层2为棉布，当然也可以采用其它具有吸水性的材料。为提高吸水脚垫的吸水能力，基材层2优选采用具有良好吸水性的棉布。由于棉布位于吸水材料层1的下方，利用白炭黑的多孔性质，使脚底的水分经过白炭黑的孔隙向棉布渗透，被棉布层吸收，棉层形成锁水，从而对人体足底的水具有良好的吸收能力，同时，水分被棉布层吸收后，吸水材料层1又在人体足底和棉布层之间形成隔离，以保证足底干燥。另外，白炭黑具有多孔隙，具有较大的比表面积，这样吸水材料层1干燥速度较快，保证二次使用效果。
作为吸水脚垫的另一种实施例，其包括可卷的基材层2，在基材层2的上表面设有吸水材料层1，在基材层2的下表面设有防滑材料层；其中，所述吸水材料层1包括以下质量份的组分：白炭黑15质量份、胶粘剂18质量份、助剂1质量份和色粉1.5质量份。
作为吸水脚垫的另一种实施例，其包括可卷的基材层2，在基材层2的上表面设有吸水材料层1，在基材层2的下表面设有防滑材料层3；所述吸水材料层1包括以下质量份的组分：白炭黑10质量份、胶粘剂5质量份、助剂0.5质量份和色粉1质量份。
作为吸水脚垫的另一种实施例，其包括可卷的基材层2，在基材层2的上表面设有吸水材料层1，在基材层2的下表面设有防滑材料层3；所述吸水材料层1包括以下质量份的组分：白炭黑10质量份、胶粘剂10质量份、助剂0.5质量份和色粉1质量份。
在上述实施例中，所述防滑材料层3为可移胶。所述胶粘剂为PVA、VAE乳液、聚氨酯胶粘剂或PA胶水。
经实验证明，采用上述技术方案的吸水脚垫，吸水脚垫能够吸附足底的水，使足底变干。另外，这种结构的吸水脚垫整体可卷，便于运输和存放。
本发明还公开了一种吸水脚垫的制造方法，包括吸水材料制备步骤；吸水材料由包括以下质量份的组分：白炭黑7质量份、胶粘剂3质量份、助剂0.3质量份、色粉0.5质量份和水3质量份；将7质量份的白炭黑、3质量份的胶粘剂、0.3质量份的助剂、0.5质量份的色粉和3质量份的水制备成可用于涂布的吸水材料。其中，所述胶粘剂为PVA，吸水材料采用如下方式配置：将PVA配置成浓度小于10％的水溶液，再将白炭黑、助剂、色粉和水与水溶液混合均匀。
涂布吸水材料和烘干步骤，将可涂布的吸水材料通过涂布工艺涂布在基材层2的一面，并将其烘干；
镜面冷压步骤，对经烘干后的吸水材料进行镜面滚压；
施胶步骤，在基材层2的另一面设置可移胶。
作为吸水脚垫的制造方法另一种实施例，包括吸水材料制备步骤；吸水材料由包括以下质量份的组分：白炭黑15质量份、胶粘剂18质量份、助剂1质量份、色粉1.5质量份和水8质量份；将15质量份的白炭黑、18质量份的胶粘剂、1质量份的助剂、1.5质量份的色粉和8质量份的水制备成可用于涂布的吸水材料。其中，所述胶粘剂为PVA，吸水材料采用如下方式配置：将PVA配置成浓度小于10％的水溶液，再将白炭黑、助剂、色粉和水与水溶液混合均匀。
涂布吸水材料和烘干步骤，将可涂布的吸水材料通过涂布工艺涂布在基材层2的一面，并将其烘干；
镜面冷压步骤，对经烘干后的吸水材料进行镜面滚压；
施胶步骤，在基材层2的另一面设置可移胶。
作为吸水脚垫的制造方法另一种实施例，包括吸水材料制备步骤；吸水材料由包括以下质量份的组分：白炭黑10质量份、胶粘剂5质量份、助剂0.5质量份、色粉1质量份和水4质量份；将10质量份的白炭黑、5质量份的胶粘剂、0.5质量份的助剂、1质量份的色粉和4质量份的水制备成可用于涂布的吸水材料。其中，所述胶粘剂为PVA，吸水材料采用如下方式配置：将PVA配置成浓度小于10％的水溶液，再将白炭黑、助剂、色粉和水与水溶液混合均匀。
涂布吸水材料和烘干步骤，将可涂布的吸水材料通过涂布工艺涂布在基材层2的一面，并将其烘干；
镜面冷压步骤，对经烘干后的吸水材料进行镜面滚压；
施胶步骤，在基材层2的另一面设置可移胶。
作为吸水脚垫的制造方法另一种实施例，包括吸水材料制备步骤；吸水材料由包括以下质量份的组分：白炭黑10质量份、胶粘剂10质量份、助剂0.5质量份、色粉1质量份和水4质量份；将10质量份的白炭黑、10质量份的胶粘剂、0.5质量份的助剂、1质量份的色粉和4质量份的水制备成可用于涂布的吸水材料。其中，所述胶粘剂为PVA，吸水材料采用如下方式配置：将PVA配置成浓度小于10％的水溶液，再将白炭黑、助剂、色粉和水与水溶液混合均匀。
涂布吸水材料和烘干步骤，将可涂布的吸水材料通过涂布工艺涂布在基材层2的一面，并将其烘干；
镜面冷压步骤，对经烘干后的吸水材料进行镜面滚压；
施胶步骤，在基材层2的另一面设置可移胶。
在上述实施例中，作为胶粘剂的PVA可用VAE乳液、聚氨酯胶粘剂或PA胶水代替。
上述实施例仅为本发明的较佳实施例，并非依此限制本发明的保护范围，故：凡依本发明的结构、形状、原理所做的等效变化，均应涵盖于本发明的保护范围之内。

Claims (9)

1.一种吸水脚垫，其特征在于：包括可卷的基材层，基材层具有吸水性，在基材层的上表面设有吸水材料层，在基材层的下表面设有防滑材料层；其中，所述吸水材料层包括以下质量份的组分：白炭黑7-15质量份、胶粘剂3-18质量份、助剂0.3-1质量份和色粉0.5-1.5质量份。
2.根据权利要求1所述的吸水脚垫，其特征在于：所述基材层为棉布。
3.根据权利要求1所述的吸水脚垫，其特征在于：所述防滑材料层为可移胶。
4.根据权利要求1所述的吸水脚垫，其特征在于：所述吸水材料层包括以下质量份的组分：白炭黑10质量份、胶粘剂5-10质量份、助剂0.5质量份和色粉1质量份。
5.根据权利要求4所述的吸水脚垫，其特征在于：所述胶粘剂为PVA、VAE乳液、聚氨酯胶粘剂或PA胶水。
6.一种吸水脚垫的制造方法，其特征在于：包括吸水材料制备步骤；吸水材料由包括以下质量份的组分：白炭黑7-15质量份、胶粘剂3-18质量份、助剂0.3-1质量份、色粉0.5-1.5质量份和水3-8质量份；将7-15质量份的白炭黑、3-18质量份的胶粘剂、0.3-1质量份的助剂、0.5-1.5质量份的色粉和3-8质量份的水制备成可用于涂布的吸水材料；
涂布吸水材料和烘干步骤，将可涂布的吸水材料通过涂布工艺涂布在基材层的一面，并将其烘干；
镜面冷压步骤，对经烘干后的吸水材料进行镜面滚压；
施胶步骤，在基材层的另一面设置可移胶。
7.根据权利要求6所述的吸水脚垫的制造方法，其特征在于：吸水材料由以下质量份的组分组成：白炭黑10质量份、胶粘剂5-10质量份、助剂0.5质量份、色粉1质量份和水4质量份。
8.根据权利要求7所述的吸水脚垫的制造方法，其特征在于：所述胶粘剂为PVA，将PVA配置成浓度小于10％的水溶液，再将白炭黑、助剂、色粉和水与水溶液混合均匀。
9.根据权利要求6所述的吸水脚垫的制造方法，其特征在于：所述胶粘剂为VAE乳液、聚氨酯胶粘剂或PA胶水。
CN201911096211.9A 2019-11-11 2019-11-11 吸水脚垫及其制造方法 Pending CN110948964A (zh)