CN110876951B - Composite material containing metal oxide, preparation method and application thereof - Google Patents
Composite material containing metal oxide, preparation method and application thereof Download PDFInfo
- Publication number
- CN110876951B CN110876951B CN201811039766.5A CN201811039766A CN110876951B CN 110876951 B CN110876951 B CN 110876951B CN 201811039766 A CN201811039766 A CN 201811039766A CN 110876951 B CN110876951 B CN 110876951B
- Authority
- CN
- China
- Prior art keywords
- composite material
- metal oxide
- metal
- carbon nitride
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a composite material and a preparation method and application thereof. Wherein the composite material comprises: a carbon nitride matrix having a sheet structure; the auxiliary agent is loaded on the carbon nitride matrix and comprises metal oxide particles and elemental metal particles, wherein the metal oxide particles are suitable for attracting holes, and the elemental metal particles are suitable for attracting electrons. The inventor finds that the composite material is simple in structure and easy to realize, has high reducing capacity under the excitation of sunlight, can effectively reduce water to obtain hydrogen under the illumination condition, and can also isomerize norbornadiene with high efficiency to obtain tetracyclic heptane, so that novel fuel hydrogen energy and tetracyclic heptane can be prepared by utilizing renewable energy, and the composite material is suitable for large-scale production.
Description
Technical Field
The invention relates to the technical field of photocatalysis, in particular to a composite material, a preparation method and application thereof, and more particularly relates to a composite material, a preparation method of the composite material and application of the composite material in photocatalytic hydrogen production and preparation of tetracycloheptane by photochemical isomerization of norbornadiene.
Background
At present, the development and utilization of renewable energy sources are more urgent. Renewable energy mainly includes solar energy, wind energy, water energy, etc., wherein solar energy is considered as one of the most promising alternative energy sources, and efficient utilization and conversion of solar energy are the current research hotspots. At present, the use of solar energy to synthesize new fuels is receiving increasing attention.
The synthesis of the novel fuel has important significance in the fields of machinery, war industry, aerospace and the like. The hydrogen energy has the advantages of high heat value, cleanness, environmental protection and the like, and is one of the green energy sources with the greatest prospect. The double-component low-temperature liquid propellant consisting of liquid hydrogen and liquid oxygen has important application in communication satellites, space shuttles and other carrier rockets. Besides liquid hydrogen, tetracycloheptane is also a high-energy aerospace hydrocarbon fuel with excellent performance. Tetracycloheptane is a typical high-tension cage-like liquid hydrocarbon with a density of up to 0.98g cm -3 The freezing point is lower than-40 ℃, the stability is good, the catalyst can be safely stored and transported, and the catalyst can be prepared by photocatalysis isomerization of norbornadiene. The development of a novel and efficient synthesis method of hydrogen and tetracycloheptane is a research focus from the past.
Disclosure of Invention
The present invention is directed to solving, at least in part, one of the technical problems in the related art. Therefore, the invention aims to provide a composite material which can effectively generate electrons and holes under the excitation of sunlight, has low recombination rate of the electrons and the holes and strong reduction capability, and is suitable for photocatalytic hydrogen production or preparation of tetracycloheptane by photochemical isomerization of norbornadiene.
In one aspect of the invention, the invention provides a composite material. According to an embodiment of the invention, the composite material comprises: a carbon nitride matrix having a sheet structure; the auxiliary agent is loaded on the carbon nitride matrix and comprises metal oxide particles and elemental metal particles, wherein the metal oxide particles are suitable for attracting holes, and the elemental metal particles are suitable for attracting electrons. The inventor finds that the composite material is simple in structure and easy to realize, under the excitation action of sunlight, the carbon nitride can generate electrons and holes, the metal oxide attracts the holes, the metal simple substance attracts electrons, the utilization rate of the electrons and the holes is improved, the utilization rate of light energy can be improved, the electrons and the holes can be effectively separated under the combined action of the metal oxide and the metal simple substance, the recombination rate of the electrons and the holes is reduced, the composite material has high reduction capacity, water can be effectively reduced under the illumination condition to obtain hydrogen, norbornadiene can be efficiently isomerized to obtain tetracycloheptane, and therefore novel fuel hydrogen energy and tetracycloheptane can be prepared by utilizing renewable energy sources, and the composite material is suitable for large-scale production.
According to an embodiment of the present invention, the elemental metal particles are formed on the surfaces of the carbon nitride substrate and the metal oxide particles. Therefore, the position relation between the metal simple substance and the metal oxide is more favorable for separating electrons and holes, so that the composite material has stronger reducing capability, and the capability of preparing hydrogen by photocatalysis and preparing tetracycloheptane by photocatalysis and isomerization of norbornadiene is stronger.
According to an embodiment of the present invention, the metal oxide particles have a particle size of 10 nm to 20 nm. Therefore, the specific surface area of the metal oxide particles is appropriate, the capacity of capturing holes is strong, and the holes can be effectively separated from electrons.
According to the embodiment of the invention, the particle size of the metal simple substance particles is 3 nm-8 nm. Therefore, the specific surface area of the metal simple substance is appropriate, the capability of capturing electrons is strong, and the electrons and the holes can be effectively separated.
According to an embodiment of the invention, the composite material comprises, based on the total mass of the composite material: 0.5 to 10wt% of said metal oxide; 0.1-5wt% of the elemental metal; and the balance of the carbon nitride matrix. Therefore, the composite material has stronger capability of separating and transmitting electrons and holes and stronger reduction capability, and is more favorable for preparing hydrogen by photocatalysis and preparing tetracycloheptane by norbornadiene by photocatalysis and isomerization.
According to an embodiment of the present invention, the metal oxide includes manganese oxide, and the elemental metal includes at least one of platinum, gold, and silver. Therefore, the metal oxide has low price, strong capacity of attracting and transmitting holes and strong capacity of attracting and transmitting electrons by the metal, can efficiently utilize light energy, improves the utilization rate of photo-generated electrons and holes, has high separation efficiency of the electrons and the holes, and ensures that the composite material has strong reduction capacity.
In another aspect of the invention, the invention provides a method of making a composite material as hereinbefore described. According to an embodiment of the invention, the method comprises: providing a carbon nitride substrate; metal oxide particles and elemental metal particles are formed on the surface of the carbon nitride substrate. The inventor finds that the method is simple and convenient to operate and easy to implement, and the composite material with the characteristics and the advantages can be prepared.
According to an embodiment of the present invention, forming the metal oxide particles and the elemental metal particles on the surface of the carbon nitride substrate includes: mixing the carbon nitride substrate, the metal salt and the sodium hydroxide solution and then carrying out a first reaction so as to load the metal oxide particles on the carbon nitride substrate; and mixing the carbon nitride matrix loaded with the metal oxide particles with a metal precursor, and carrying out a second reaction under the illumination condition so as to obtain the composite material. Therefore, the metal oxide particles form rich active sites for adsorption and deposition of the metal simple substance particles, so that part of the metal simple substance particles are formed on the surfaces of the metal oxide particles, and stronger interaction between the metal oxide and the metal simple substance is formed, so that the separation of electrons and holes is more efficient, the photocatalytic performance of the composite material is improved, and the photocatalytic hydrogen production and the isomerization of norbornadiene to generate tetracycloheptane are facilitated.
According to an embodiment of the invention, the temperature of the first reaction is 40-80 ℃ and the time is 2-4h. Therefore, the effect of forming the metal oxide particles is better, and further, the separation of the photo-generated electrons and the holes is facilitated.
According to an embodiment of the invention, the concentration of the sodium hydroxide solution is 4-12g/L. The size of the metal oxide particles can thereby be optimized to enhance the catalytic activity of the composite material.
According to an embodiment of the invention, the time of the second reaction is 2-4h. Therefore, the effect of forming the metal simple substance particles is better, even partial metal simple substance particles can be effectively formed on the surfaces of the metal oxide particles, the interaction between the metal simple substance and the metal oxide is favorably improved, and the separation efficiency of electrons and holes is favorably improved.
According to an embodiment of the invention, the metal salt is selected from at least one of manganese chloride, manganese nitrate and manganese sulfate. Thus, the metal salt is widely available and inexpensive, and the metal oxide particles obtained from the metal salt have a strong ability to attract electrons.
According to an embodiment of the present invention, the metal precursor includes at least one of chloroplatinic acid, chloroauric acid, and silver nitrate. Therefore, the metal precursor is suitable for being reduced into metal simple substance particles under the illumination condition, the reduction efficiency is high, the obtained metal simple substance particles have high electron attracting capacity, and the separation efficiency of photo-generated electrons and holes is improved.
In another aspect of the invention, the invention provides the use of the composite material in photocatalytic hydrogen production and photochemical isomerization of norbornadiene to produce tetracycloheptane. The inventor finds that the composite material has high efficiency in preparing hydrogen and tetracycloheptane by photocatalysis, is favorable for obtaining novel fuel, and is suitable for large-scale application.
The invention can at least obtain the following beneficial effects:
1. by simple means (e.g. atmospheric oil bath) 2 Closely grown at g-C 3 N 4 The electronic transmission between the two is facilitated; pt is grown on g-C by means of photo-deposition without any chemical reducing agent and organic solvent 3 N 4 C, removing;
2. in g-C 3 N 4 Adding MnO simultaneously 2 And Pt are used for promoting the generation of hydrogen and the occurrence of norbornadiene isomerization reaction;
3. the norbornadiene photocatalytic isomerization reaction is carried out under the condition of no solvent, so that the separation of products and the recovery of a catalyst are facilitated.
4. The catalyst has the advantages of simple preparation method, low price of raw materials, rich sources, simple and convenient operation of the preparation process and low preparation cost.
5. The activity of the composite material photocatalytic hydrogen production and norbornadiene isomerization is respectively improved by 4-39 times and 5-10 times compared with that of pure carbon nitride.
Drawings
FIG. 1 is a schematic flow diagram of a method for preparing a composite material according to one embodiment of the present invention.
Fig. 2 is a schematic flow chart of a method for forming metal oxide particles and elemental metal particles on the surface of a carbon nitride substrate according to an embodiment of the present invention.
FIG. 3 is a transmission electron micrograph of the composite material of example 1.
Fig. 4 is an X-ray diffraction pattern (XRD pattern) of the carbon nitride matrix and the composite material in example 1.
FIG. 5 is an infrared spectrum of the composite material of example 1.
Detailed Description
The following describes embodiments of the present invention in detail. The following examples are illustrative only and are not to be construed as limiting the invention. The examples, where specific techniques or conditions are not indicated, are to be construed according to the techniques or conditions described in the literature in the art or according to the product specifications. The reagents or instruments used are not indicated by the manufacturer, and are all conventional products commercially available.
In one aspect of the invention, a composite material is provided. According to an embodiment of the invention, the composite material comprises: a carbon nitride matrix having a sheet structure; the auxiliary agent is loaded on the carbon nitride matrix and comprises metal oxide particles and elemental metal particles, wherein the metal oxide particles are suitable for attracting holes, and the elemental metal particles are suitable for attracting electrons. The inventor finds that the composite material is simple in structure and easy to realize, has high reducing capacity under the irradiation of sunlight, can effectively reduce water to obtain hydrogen under the illumination condition, and can also efficiently isomerize norbornadiene to obtain tetracyclic heptane, so that novel fuel hydrogen energy and tetracyclic heptane can be prepared by utilizing renewable energy photocatalysis, and the composite material is suitable for large-scale production.
According to the embodiment of the invention, under the excitation of sunlight, carbon nitride (g-C) 3 N 4 ) The matrix can generate electrons and holes, the metal oxide loaded on the surface of the carbon nitride matrix attracts the holes, the metal simple substance attracts the electrons, the electrons and the holes can be effectively separated, the recombination rate of the electrons and the holes is reduced, the number of the electrons in the composite material is large, the composite material has high reduction capability, the utilization rate of the electrons and the holes can be improved under the combined action of the metal oxide and the metal simple substance, the utilization rate of light energy can be further improved, water can be effectively reduced under the illumination condition to obtain hydrogen, and norbornadiene can be efficiently isomerized to obtain tetracycloheptane; when the composite material is used for preparing hydrogen or tetracycloheptane under the excitation of sunlight, the effect of preparing novel fuel hydrogen energy and tetracycloheptane by using renewable energy sources can be realized, the preparation cost is low, and the preparation method is suitable for large-scale production. According to the embodiment of the invention, if the catalyst only contains the carbon nitride substrate, electrons and holes generated under the illumination condition are easy to recombine, so that the reduction capability of the catalyst is weak, and hydrogen and tetracycloheptane can hardly be produced by photocatalysis; if the composite material only contains the carbon nitride matrix and the metal oxide particles or metal simple substance particles loaded on the carbon nitride matrix, the separation effect of electrons and holes generated by the carbon nitride matrix under the illumination condition is poor, so that the quantity of available photogenerated electrons in the composite material is less, and further the reduction capability of the composite material is weaker, the quantity of photocatalytic hydrogen production is less, the yield of tetracyclic heptane is lower, the catalytic activity is lower, and the requirement for synthesizing a novel fuel cannot be met.
According to the embodiment of the invention, in order to enable the composite material to have high catalytic activity, the metal oxide and the metal simple substance are in a granular shape. Therefore, the specific surface area of the metal oxide and the metal simple substance is proper, the capability of attracting electrons and holes is strong, the capability of separating photo-generated electrons and holes is excellent, and the composite material has more available photo-generated electrons under the illumination condition, so that the composite material has strong reducibility, and the photocatalytic activity of the composite material can be obviously improved.
In some embodiments of the present invention, in order to make the catalytic activity of the composite material higher, the elemental metal particles are formed on the surfaces of the carbon nitride matrix and the metal oxide particles. Therefore, the structure between the metal simple substance particles and the metal oxide particles is tighter, the separation efficiency of electrons and holes is more favorably improved, the available electron quantity in the composite material is higher, the reduction capability is stronger, and the capability of preparing hydrogen by photocatalysis and preparing tetracycloheptane by photocatalysis and isomerization of norbornadiene is stronger.
According to embodiments of the present invention, the metal oxide particles have a particle size of 10 nm to 20 nm (e.g., 10 nm, 10.5 nm, 11 nm, 11.5 nm, 12 nm, 12.5 nm, 13 nm, 13.5 nm, 14 nm, 14.5 nm, 15 nm, 15.5 nm, 16 nm, 16.5 nm, 17 nm, 17.5 nm, 18 nm, 18.5 nm, 19 nm, 19.5 nm, 20 nm, etc.). Therefore, the specific surface area of the metal oxide particles is appropriate, the capacity of capturing holes is strong, and the holes can be effectively separated. With respect to the above diameter range, when the particle diameter of the metal oxide particles is too small, the ability of the metal oxide to capture holes and transport holes is relatively weak, resulting in relatively poor photo-generated charge separation effect; when the particle size of the metal oxide particles is too large, the specific surface area of the metal oxide particles is small, and the ability to attract holes is relatively weak, resulting in relatively poor photo-generated charge separation effect. The particle diameter of the metal oxide particle refers to the maximum value of the distance between any two points in the metal oxide particle.
According to the embodiment of the invention, the particle size of the elemental metal particles is 3 nm to 8 nm (e.g., 3 nm, 3.5 nm, 4 nm, 4.5 nm, 5 nm, 5.5 nm, 6 nm, 6.5 nm, 7 nm, 7.5 nm, 8 nm, etc.). Therefore, the specific surface area of the metal simple substance particles is appropriate, the capability of capturing electrons is strong, and the electrons can be effectively separated. Compared with the diameter range, when the particle size of the metal simple substance particles is too small, the electron capturing capability and the electron transferring capability of the metal simple substance are relatively weak, so that the photo-generated charge separation effect is relatively poor; when the particle size of the metal simple substance particles is too large, the specific surface area of the metal simple substance is small, and the ability of attracting electrons is relatively weak, so that the effect of separating photo-generated charges is relatively poor. The particle size of the metal simple substance particles refers to the maximum value of the distance between any two points in the metal simple substance particles.
According to an embodiment of the present invention, the metal oxide includes manganese oxide, and the elemental metal includes at least one of platinum, gold, and silver. Therefore, the metal oxide has low price, strong capacity of attracting and transmitting holes, strong capacity of attracting and transmitting electrons by the metal simple substance, effective utilization of light energy, improvement of the utilization rate of photo-generated electrons and holes, high separation efficiency of the electrons and the holes and strong reduction capacity of the composite material.
According to an embodiment of the invention, the composite material comprises, based on the total mass of the composite material: 0.5 to 10wt% (e.g., 0.5wt%, 1wt%, 2wt%, 3wt%, 4wt%, 5wt%, 6wt%, 7wt%, 8wt%, 9wt%, 10wt%, etc.) of the metal oxide; 0.1-5wt% (e.g., 0.1wt%, 0.5wt%, 1wt%, 1.5wt%, 2wt%, 2.5wt%, 3wt%, 3.5wt%, 4wt%, 4.5wt%, 5wt%, etc.) of the elemental metal; and the balance of the carbon nitride matrix. Therefore, the content of the metal oxide and the metal simple substance is proper, the metal oxide particles or the metal simple substance particles can be prevented from becoming charge recombination centers, the composite material has stronger capability of separating and transmitting electrons and holes and stronger reduction capability, and is more favorable for preparing hydrogen by photocatalysis and preparing tetracycloheptane by photocatalysis and isomerization of norbornadiene. Relative to the content range, when the content of the metal oxide particles is too high or the content of the metal simple substance particles is too high, the light absorption active sites on the surface of the carbon nitride can be covered, so that the quantity of photo-generated electrons is relatively less, and the catalytic reaction efficiency is reduced; when the content of the metal oxide particles is too low or the content of the metal simple substance particles is too low, sufficient charge separation and reactive sites are not provided enough to improve the catalytic activity of the composite material and further promote the reaction.
In another aspect of the invention, the invention provides a method of making a composite material as hereinbefore described. According to an embodiment of the present invention, referring to fig. 1, the method includes:
s100: a carbon nitride substrate is provided.
According to an embodiment of the present invention, the carbon nitride matrix is obtained by calcining a nitrogen-containing precursor. Therefore, the operation is simple and convenient, and the carbon nitride matrix with good service performance can be obtained. According to an embodiment of the invention, the nitrogen-containing precursor comprises at least one of melamine, dicyandiamide and urea. Therefore, the material has wide sources and low price, and the carbon nitride matrix obtained by roasting has good service performance.
According to an embodiment of the present invention, the specific steps of preparing the carbon nitride matrix may be: the nitrogen-containing precursor is roasted for 2-4h (for example, 2h, 2.5h, 3h, 3.5h, 4h, etc.) under the condition of 520-550 ℃ (for example, 520 ℃, 530 ℃, 540 ℃, 550 ℃, etc.) in the air atmosphere. Therefore, the operation is simple and convenient, the realization is easy, and the prepared carbon nitride matrix can effectively generate electrons and holes under the illumination condition so as to be beneficial to separating the electrons and the holes by the metal oxide and the metal simple substance.
S200: metal oxide particles and elemental metal particles are formed on the surface of the carbon nitride substrate.
According to an embodiment of the present invention, referring to fig. 2, forming metal oxide particles and elemental metal particles on a surface of the carbon nitride substrate includes:
s210: the carbon nitride substrate, the metal salt, and the sodium hydroxide solution are mixed and then subjected to a first reaction to support the metal oxide particles on the carbon nitride substrate.
According to an embodiment of the present invention, before the first reaction is performed, the carbon nitride matrix may be ultrasonically dispersed in water, and then the mixed solution may be placed in a constant temperature water bath for dispersion, so as to facilitate the subsequent steps.
According to an embodiment of the invention, the metal salt is selected from at least one of manganese chloride, manganese nitrate and manganese sulphate. Therefore, the metal salt has wide sources and low price, the metal oxide particles obtained by using the above metal salt have a strong ability to attract electrons.
According to an embodiment of the invention, the concentration of the sodium hydroxide solution is 4-12g/L (e.g., 4g/L, 5g/L, 6g/L, 7g/L, 8g/L, 9g/L, 10g/L, 11g/L, 12g/L, etc.). The particle size of the manganese dioxide can be optimized to improve the catalytic activity of the composite material and thus improve the reaction efficiency. When the concentration of the sodium hydroxide solution is too low, the metal salt precursor cannot be completely precipitated, and the effect of forming the metal oxide is relatively poor; when the concentration of the sodium hydroxide solution is too high, the particle size of the metal oxide particles is relatively too large and the particles are easily agglomerated.
According to an embodiment of the present invention, the temperature of the first reaction is 40-80 ℃ (e.g., 40 ℃, 45 ℃, 50 ℃, 55 ℃, 60 ℃, 65 ℃, 70 ℃, 75 ℃, 80 ℃, etc.) and the time is 2-4h (e.g., 2h, 2.5h, 3h, 3.5h, 4h, etc.). Therefore, the metal oxide particles can be grown on the surface of the carbon nitride substrate in situ, the effect of forming the metal oxide particles is better, and the separation of photo-generated electrons and holes is further facilitated. When the temperature of the first reaction is too high or the time is too long with respect to the above reaction temperature and time ranges, the resulting metal oxide particles may be agglomerated; when the temperature of the first reaction is too low or the time is too short, the precipitation of the metal oxide is incomplete, and the effect of forming metal oxide particles is relatively poor. According to the embodiment of the invention, the first reaction can be carried out under the condition of a normal-pressure oil bath, and the operation is simple and convenient.
The metal salt and sodium hydroxide can form a metal oxide under the conditions of the first reaction.
S220: and mixing the carbon nitride matrix loaded with the metal oxide particles with a metal precursor, and carrying out a second reaction under the illumination condition so as to obtain the composite material.
According to the embodiment of the invention, the metal oxide particles loaded on the carbon nitride substrate provide abundant active sites for the adsorption and deposition of the metal simple substance particles, so that part of the metal simple substance particles can be formed on the surfaces of the metal oxide particles, the structures of the metal oxide particles and the metal simple substance particles are tighter, and stronger interaction between the metal oxide and the metal simple substance is formed, so that the separation of electrons and holes is more efficient, the photocatalysis performance of the composite material is improved, the process of synthesizing the metal simple substance particles is green and pollution-free, and no chemical oxidant or reducing agent is needed.
According to an embodiment of the present invention, the metal precursor includes at least one of chloroplatinic acid, chloroauric acid, and silver nitrate. Therefore, the metal precursor is suitable for being reduced into a metal simple substance under the illumination condition, the metal simple substance can be synthesized in situ, the reduction efficiency is high, the obtained metal simple substance has high capability of attracting electrons, and the separation efficiency of photo-generated electrons and holes is improved.
According to an embodiment of the present invention, the above-mentioned lighting condition may be as follows: using a 300W xenon lamp at constant power (60-120 Mw/cm) 2 ) The second reaction is carried out for 2-4h (such as 2h, 2.5h, 3h, 3.5h, 4h, etc.) under the condition of illumination. Therefore, the metal simple substance particles can be deposited on the surfaces of the carbon nitride matrix or the metal oxide particles in situ, the effect of forming the metal simple substance particles is good, the interaction between the metal simple substance and the metal oxide is favorably improved, and the separation efficiency of electrons and holes is favorably improved. Compared with the above reaction time, when the second reaction time is too short, the effect of photo-reduction of the metal precursor is relatively poor, and the effect of forming a metal simple substance is relatively poor, resulting in relatively poor photocatalytic activity of the composite material; when the time of the second reaction is too long, energy is wasted.
According to an embodiment of the invention, the second reaction is carried out under stirring. Therefore, the shape of the metal simple substance is favorably regulated and controlled, the shape of the metal simple substance is metal simple substance particles, and the photocatalytic activity of the composite material is higher.
According to an embodiment of the present invention, the specific steps of preparing the composite material may be as follows:
(1) Preparation of carbon nitride matrix: weighing a certain mass of nitrogen-containing precursor, and roasting at 520-550 ℃ for 2-4h in air atmosphere.
(2) Forming metal oxide particles on a carbon nitride substrate: weighing 0.1-3 g of carbon nitride matrix, ultrasonically dispersing the carbon nitride matrix in a round-bottom flask containing 100mL of water, placing the flask in an oil bath at 60 ℃ for 30min, adding 0.01-0.3 g of anhydrous manganese chloride into the system, stirring to fully dissolve the anhydrous manganese chloride, adding 2-48ml of 4g/L NaOH solution, reacting for 3h, centrifugally separating the solid in the system, washing, and drying to obtain MnO 2 /g-C 3 N 4 。
(3) Forming elemental metal particles on the carbon nitride substrate on which the metal oxide particles are formed: weighing 0.1-3 g MnO 2 /g-C 3 N 4 In a photocatalytic reactor containing 100-150 mL of water and triethanolamine, adding a metal precursor after uniformly dispersing the water and the triethanolamine by ultrasound, stirring the mixture, and illuminating the mixture for 2-4h under the constant current of a 300W xenon lamp (60-120 mW/cm < 2 >). And recovering the obtained solid, and drying the solid overnight in vacuum at the temperature of 60 ℃ to obtain the required composite material.
In another aspect of the invention, the invention provides the use of the composite material in photocatalytic hydrogen production and photochemical isomerization of norbornadiene to produce tetracycloheptane. The inventor finds that the composite material has high efficiency in preparing hydrogen and tetracyclic heptane by photocatalysis, is beneficial to obtaining novel fuels, and is suitable for large-scale application.
According to the embodiment of the invention, the hydrogen production by utilizing the composite material photocatalysis is to put the composite material into water and carry out the hydrogen production by photocatalysis under the illumination condition, and the hydrogen production principle is as follows: under the condition of illumination, a large number of photo-generated electrons and photo-generated holes are generated in the composite material, the holes are consumed by utilizing a hole sacrificial agent (such as triethanolamine), and the large number of photo-generated electrons in the composite material can reduce water to generate hydrogen when meeting water. In some embodiments of the present invention, the photocatalytic hydrogen production is performed by: A300W xenon lamp is used as a light source (the current is controlled to be 15A), the reaction temperature of photocatalytic hydrogen production is 0 ℃, 0.05g of composite material is dispersed into an aqueous solution containing 10% volume fraction of cavity sacrificial agent triethanolamine during reaction, argon is introduced to purge a mixed solution for 30min, the lamp is turned on for reaction, samples are taken every half an hour during the reaction, and the gas product is subjected to chromatographic quantitative analysis. Therefore, the operation is simple and convenient, and the realization is easy.
According to the embodiment of the invention, the specific operation steps for isomerizing norbornadiene photochemical valence bond by using the composite material to prepare the tetracycloheptane can be as follows: the preparation method is characterized in that the composite material is dispersed into a norbornadiene solution containing a photosensitizer (such as tetraethyl mikrone) to obtain a mixed solution, and the mixed solution is irradiated by light to obtain tetracycloheptane.
Embodiments of the present application are described below.
Examples
1. Photocatalytic hydrogen production
The photocatalytic hydrogen production reaction adopts an external illumination type quartz reactor, a light source is a 300W xenon lamp (light emitted by the xenon lamp is used for simulating sunlight), the current is controlled to be 15A, and the reaction temperature is 0 ℃. And (3) dispersing 0.05g of the composite material into a water solution containing 10% of triethanolamine by volume fraction during reaction, introducing argon to purge for 30min, then turning on a lamp to perform reaction, sampling every half an hour during the reaction process, and performing chromatographic quantitative analysis on a gas product.
2. Tetracycloheptane synthesis
The tetracycloheptane synthesis reaction adopts an internal illumination type quartz reactor, a 400W high-pressure mercury lamp as a light source, and the reaction temperature is room temperature. Mixing 150mL of norbornadiene and 3g of tetraethyl michael ketone, adding 1.5g of composite catalyst, fully stirring and mixing, transferring the mixture into a reactor, turning on a lamp, continuously stirring in the reaction process, transferring the product into a rotary evaporator after reacting for 20 hours, and distilling at the temperature of 60-70 ℃ under normal pressure to obtain the tetracycloheptane product.
Example 1
Preparing a composite material:
weighing 15g of melamine, roasting for 4h at 550 ℃ in a tubular atmosphere furnace in the air atmosphere at the heating rate of 2 ℃/min, grinding the obtained yellowish white solid, centrifuging, washing with water and ethanol for several times to obtain carbon nitride (g-C) 3 N 4 ) And (5) standby. Weighing 3g of carbon nitride in a round bottom flask, adding 100mL of ultrapure water, performing ultrasonic treatment for 1h to uniformly disperse the carbon nitride, performing oil bath at 60 ℃ for 30min, adding 0.15g of anhydrous manganese chloride into the system, stirring to fully dissolve the anhydrous manganese chloride, dropwise adding 10mL of 12g/L NaOH solution, continuously stirring in the reaction process, performing centrifugal separation on the reaction solution after 3h, washing, and drying to obtain a solid, namely MnO 2 /g-C 3 N 4 . Weighing 2g MnO 2 /g-C 3 N 4 Adding 90mL of ultrapure water and 10mL of triethanolamine as a cavity sacrificial agent into a photocatalytic reactor, performing ultrasonic treatment to uniformly disperse the ultrapure water and the triethanolamine as the cavity sacrificial agent, adding 0.04g of chloroplatinic acid, stirring, and performing illumination for 3 hours under the constant current (15A) of a 300W xenon lamp. Centrifuging the obtained solid, washing, and vacuum drying at 60 deg.C overnight to obtain the desired catalyst (MnO) 2 -Pt/g-C 3 N 4 )。
The transmission electron microscope test result of the composite material is shown in figure 3, and the XRD characterization result and the infrared spectrogram of the composite material are respectively referred to figure 4 and figure 5.
Example 2:
weighing 15g of melamine, roasting the melamine in a tubular atmosphere furnace at 550 ℃ for 4h in the air atmosphere at the heating rate of 2 ℃/min, grinding the obtained yellow-white solid, centrifuging, and washing with water and ethanol for several times to obtain carbon nitride for later use. Weighing 3g of carbon nitride in a round-bottom flask, adding 100mL of ultrapure water, performing ultrasonic treatment for 1h to uniformly disperse the carbon nitride, performing oil bath at 60 ℃ for 30min, adding 0.06g of anhydrous manganese chloride into the system, and stirring to fully fill the anhydrous manganese chlorideDissolving, dropwise adding 4mL 12g/L NaOH solution, continuously stirring in the reaction process, centrifugally separating the reaction liquid after 3h, washing, and drying to obtain solid, namely MnO 2 /g-C 3 N 4 . Weighing 2g MnO 2 /g-C 3 N 4 Adding 90mL of ultrapure water and 10mL of triethanolamine into a photocatalytic reactor, performing ultrasonic treatment to uniformly disperse the ultrapure water and the triethanolamine, adding 0.04g of chloroauric acid, stirring, and illuminating for 3 hours under a 300W xenon lamp constant current (15A). Centrifuging the obtained solid, washing, and vacuum drying at 60 deg.C overnight to obtain the desired catalyst (MnO) 2 -Au/g-C 3 N 4 )。
Examples 3 to 14
Examples 3-14 composites were prepared as in example 1, except as indicated in the following table:
comparative example 1
Preparing a composite material:
weighing 15g of melamine, roasting for 4h at 550 ℃ in a tubular atmosphere furnace in the air atmosphere at the heating rate of 2 ℃/min, grinding the obtained yellowish white solid, centrifuging, washing with water and ethanol for several times to obtain carbon nitride (g-C) 3 N 4 ) And (5) standby. Weighing 3g of carbon nitride in a round bottom flask, adding 100mL of ultrapure water, performing ultrasonic treatment for 1h to uniformly disperse the carbon nitride, performing oil bath at 60 ℃ for 30min, adding 0.15g of anhydrous manganese chloride into the system, stirring to fully dissolve the anhydrous manganese chloride, dropwise adding 10mL 12g/L NaOH solution, continuously stirring in the reaction process, after 3h, performing centrifugal separation on the reaction solution, washing, and drying to obtain a solid, namely MnO 2 /g-C 3 N 4 。
Comparative example 2
Preparing a composite material:
weighing 2g g-C 3 N 4 In the light-catalyzed reactor, the light-catalyzed reactor is filled with a light-catalyzed gas,and 90mL of ultrapure water and 10mL of triethanolamine were added, ultrasonically dispersed uniformly, and then 0.04g of chloroplatinic acid was added and stirred, followed by illumination for 3 hours under a 300W xenon lamp constant current (15A). Centrifuging the obtained solid, washing, and vacuum drying at 60 deg.C overnight to obtain the desired catalyst (Pt/g-C) 3 N 4 )。
Comparative example 3
The preparation of the composite material is the same as that of comparative example 2, except that the metal precursor in the comparative example is chloroauric acid, and the obtained composite material is Au/g-C 3 N 4 。
Comparative example 4
The preparation of the composite material is the same as that of comparative example 2, except that in the comparative example, the metal precursor is silver nitrate, and the obtained composite material is Ag/g-C 3 N 4 。
Comparative example 5
The preparation method of the composite material comprises the following steps:
weighing 15g of melamine, roasting the melamine in a tubular atmosphere furnace at 550 ℃ for 4h in the air atmosphere at the heating rate of 2 ℃/min, grinding the obtained yellow-white solid, centrifuging, washing with water and ethanol for a plurality of times to obtain carbon nitride (g-C) 3 N 4 ) And (5) standby. Weighing 3g of carbon nitride in a round bottom flask, adding 100mL of ultrapure water, performing ultrasonic treatment for 1h to uniformly disperse the carbon nitride, performing oil bath at 60 ℃ for 30min, adding 0.15g of anhydrous manganese chloride into the system, stirring to fully dissolve the anhydrous manganese chloride, dropwise adding 10mL of 5g/L NaOH solution, continuously stirring in the reaction process, performing centrifugal separation on the reaction liquid after 3h, washing, and drying to obtain a solid, namely MnO 2 /g-C 3 N 4 . Weighing 2g MnO 2 /g-C 3 N 4 Adding 90mL of ultrapure water and 10mL of triethanolamine as a cavity sacrificial agent into a photocatalytic reactor, performing ultrasonic treatment to uniformly disperse the ultrapure water and the triethanolamine as the cavity sacrificial agent, adding 0.02g of chloroauric acid, stirring, and performing illumination for 3 hours under the constant current (12A) of a 300W xenon lamp. Centrifuging the obtained solid, washing, and vacuum drying at 60 deg.C overnight to obtain the desired composite material (MnO) 2 -Au/g-C 3 N 4 )。
Comparative example 6
The preparation method of the composite material comprises the following steps:
15g of melamine are weighed into a tubeCalcining at 550 deg.C for 4h in air atmosphere at 2 deg.C/min in a furnace with a formula atmosphere, grinding the obtained yellow-white solid, centrifuging, washing with water and ethanol for several times to obtain carbon nitride (g-C) 3 N 4 ) And (5) standby. Weighing 3g of carbon nitride in a round bottom flask, adding 100mL of ultrapure water, performing ultrasonic treatment for 1h to uniformly disperse the carbon nitride, performing oil bath at 60 ℃ for 30min, adding 0.15g of anhydrous manganese chloride into the system, stirring to fully dissolve the anhydrous manganese chloride, dropwise adding 1 mL of 24g/L NaOH solution, continuously stirring in the reaction process, centrifugally separating the reaction liquid after 3h, washing, and drying to obtain a solid, namely MnO 2 /g-C 3 N 4 . Weighing 2g MnO 2 /g-C 3 N 4 Adding 90mL of ultrapure water and 10mL of triethanolamine as a cavity sacrificial agent into a photocatalytic reactor, ultrasonically dispersing the ultrapure water and the triethanolamine uniformly, adding 0.04g of chloroauric acid, stirring the mixture, and illuminating the mixture for 3 hours under the constant current (20A) of a 300W xenon lamp. Centrifuging the obtained solid, washing, and vacuum drying at 60 deg.C overnight to obtain the desired composite material (MnO) 2 -Au/g-C 3 N 4 )。
Comparative example 7
The composite material was prepared in the same manner as in example 1, except that the content of the metal oxide particles was 20wt% and the content of the metal particles was 8wt% in this comparative example.
Comparative example 8
The composite material was prepared in the same manner as in example 1, except that the content of the metal oxide particles was 0.2wt% and the content of the metal particles was 0.05wt% in this comparative example.
The experimental data for examples 1-14 and comparative examples 1-8 are shown in the following table.
Furthermore, the terms "first", "second" and "first" are used for descriptive purposes only and are not to be construed as indicating or implying relative importance or implicitly indicating the number of technical features indicated. Thus, a feature defined as "first" or "second" may explicitly or implicitly include one or more of that feature. In the description of the present invention, "a plurality" means two or more unless specifically defined otherwise.
In the description herein, references to the description of the term "one embodiment," "some embodiments," "an example," "a specific example," or "some examples," etc., mean that a particular feature, structure, material, or characteristic described in connection with the embodiment or example is included in at least one embodiment or example of the invention. In this specification, the schematic representations of the terms used above are not necessarily intended to refer to the same embodiment or example. Furthermore, the particular features, structures, materials, or characteristics described may be combined in any suitable manner in any one or more embodiments or examples. Furthermore, various embodiments or examples and features of different embodiments or examples described in this specification can be combined and combined by one skilled in the art without contradiction.
Although embodiments of the present invention have been shown and described above, it will be understood that the above embodiments are exemplary and not to be construed as limiting the present invention, and that changes, modifications, substitutions and alterations can be made to the above embodiments by those of ordinary skill in the art within the scope of the present invention.
Claims (9)
1. The application of a composite material in preparing tetracycloheptane by photochemical isomerization of norbornadiene is characterized in that the composite material comprises:
a carbon nitride matrix having a sheet structure;
an auxiliary agent supported on the carbon nitride substrate, the auxiliary agent including metal oxide particles and elemental metal particles, the metal oxide particles being adapted to attract holes, the elemental metal particles being adapted to attract electrons,
the elemental metal particles are formed on the surfaces of the carbon nitride matrix and the metal oxide particles,
the metal oxide comprises manganese oxide, the metal simple substance comprises at least one of platinum, gold and silver,
in the composite material, the content of the metal oxide is 0.5-10wt%; the content of the metal simple substance is 0.1-5wt%.
2. Use according to claim 1, wherein the metal oxide particles have a particle size of 10 nm to 20 nm.
3. The use according to claim 2, wherein the elemental metal particles have a particle size of 3 nm to 8 nm.
4. Use according to claim 1, characterized in that the preparation of the composite material comprises the following steps:
providing a carbon nitride substrate;
forming metal oxide particles and metal simple substance particles on the surface of the carbon nitride substrate,
the method for forming metal oxide particles and elemental metal particles on the surface of the carbon nitride substrate includes:
performing a first reaction after mixing the carbon nitride substrate, the metal salt and the sodium hydroxide solution to support the metal oxide particles on the carbon nitride substrate;
and mixing the carbon nitride matrix loaded with the metal oxide particles with a metal precursor, and carrying out a second reaction under the illumination condition so as to obtain the composite material.
5. Use according to claim 4, wherein the first reaction is carried out at a temperature of 40-80 ℃ for a time of 2-4h.
6. The use according to claim 4, wherein the concentration of the sodium hydroxide solution is 4-12g/L.
7. Use according to claim 4, wherein the second reaction time is 2-4h.
8. Use according to any one of claims 4 to 7, wherein the metal salt is selected from at least one of manganese chloride, nitrate and sulphate.
9. Use according to any one of claims 4 to 7, wherein the metal precursor comprises at least one of chloroplatinic acid, chloroauric acid and silver nitrate.