CN110862735A - Universal electric vehicle water-based plastic paint and preparation method thereof - Google Patents
Universal electric vehicle water-based plastic paint and preparation method thereof Download PDFInfo
- Publication number
- CN110862735A CN110862735A CN201911245999.5A CN201911245999A CN110862735A CN 110862735 A CN110862735 A CN 110862735A CN 201911245999 A CN201911245999 A CN 201911245999A CN 110862735 A CN110862735 A CN 110862735A
- Authority
- CN
- China
- Prior art keywords
- percent
- agent
- rotating speed
- electric vehicle
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a universal electric vehicle water-based plastic paint which comprises the following materials in percentage by weight: water-based silicone-acrylic emulsion: 35% -45%; aqueous polyurethane dispersion: 10% -20%; propylene glycol butyl ether: 2% -10%; 0.1 to 0.5 percent of defoaming agent; 0.2 to 0.5 percent of dispersant; 5 to 15 percent of titanate coupling agent; 0.1 to 0.5 percent of flatting agent; pigment and filler: 5% -10%; deionized water: 15% -35%; 0.3 to 0.8 percent of thickening agent; wetting agent: 0.1 to 0.3 percent. The technical scheme of the invention has the technical effects of ultralow VOC content, strong hardness, good adhesive force, excellent weather resistance, and bright, fine and flexible formed paint film.
Description
Technical Field
The invention relates to a universal electric vehicle water-based plastic paint and a preparation method thereof.
Background
The plastic paint is a standard type plastic paint prepared by using thermoplastic acrylic resin as a matrix and adding high-grade applicable auxiliary agents and pigments. The paint has the characteristics of high hardness, high gloss, high degree of fullness, good interlayer adhesion, easy construction and the like, and is widely applied to the coating of products of plastic substrates. Such as plastic toys, plastic daily necessities, electrical products, plastic artware and the like. The existing plastic paint has the defects of high voc content, poor weather resistance and environmental protection pressure and weather resistance, and the common water-based plastic paint can not meet the market demand.
Disclosure of Invention
Based on the problems, the invention provides the high-strength water-based automobile chassis protective paint which has the advantages of ultralow VOC content, strong hardness, good adhesive force, excellent weather resistance, bright and fine paint film and good flexibility.
In order to achieve the purpose, the invention provides the following technical scheme: the universal electric vehicle water-based plastic paint comprises the following materials in percentage by weight:
water-based silicone-acrylic emulsion: 35% -45%;
aqueous polyurethane dispersion: 10% -20%;
propylene glycol butyl ether: 2% -10%;
0.1 to 0.5 percent of defoaming agent;
0.2 to 0.5 percent of dispersant;
5 to 15 percent of titanate coupling agent;
0.1 to 0.5 percent of flatting agent;
pigment and filler: 5% -10%;
deionized water: 15% -35%;
0.3 to 0.8 percent of thickening agent;
wetting agent: 0.1 to 0.3 percent.
The invention further provides that: the material comprises the following materials in percentage by weight:
water-based silicone-acrylic emulsion: 40 percent;
aqueous polyurethane dispersion: 15 percent;
propylene glycol butyl ether: 6 percent;
0.2 percent of defoaming agent;
0.3 percent of dispersant;
10 percent of titanate coupling agent;
0.3 percent of flatting agent;
pigment and filler: 7.5 percent;
deionized water: 20 percent;
0.5 percent of thickening agent;
wetting agent: 0.2 percent.
The invention further provides that: the defoaming agent is a long-chain alkyl silicone oil defoaming agent in the modified silicone oil defoaming agent.
The invention further provides that: the dispersant is glyceryl tristearate.
The invention further provides that: the leveling agent is one of BYK346, BYK381, or modesty 435.
The invention further provides that: the thickening agent is hydroxypropyl methyl cellulose or polyvinylpyrrolidone.
The invention further provides that: the wetting agent is one of EFKA3500, EFKA3034 or TEGO 270.
The invention also aims to provide a preparation method of the universal electric vehicle water-based plastic paint, which is characterized by comprising the following steps: the method comprises the following steps:
s1, sequentially adding the aqueous silicone-acrylic emulsion and the aqueous polyurethane dispersoid into a dispersion cylinder, dispersing at the rotating speed of 800r/min in 700-;
s2, adding propylene glycol butyl ether and titanate coupling agent at the rotating speed of 800r/min of 700-;
s3, adding a wetting agent, a thickening agent and a defoaming agent at the rotating speed of 800r/min of 700-;
s4: adding the pigment and the filler at the rotating speed of 800r/min of 700 plus materials, and dispersing for 5-10 minutes at the rotating speed of 1000r/min of 800 plus materials until the mixture is uniformly stirred;
s5: adding the flatting agent and the dispersing agent at the rotating speed of 800r/min of 700 plus materials, and dispersing for 10-15 minutes at the rotating speed of 1000r/min of 800 plus materials until the materials are uniformly stirred.
Compared with the prior art, the invention has the following effects:
(1) the waterborne plastic paint for the electric vehicle disclosed by the invention is ultralow in VOC content, strong in hardness, good in adhesive force and excellent in weather resistance, and the formed paint film is bright, fine and smooth and good in flexibility.
(2) The aqueous polyurethane dispersion is selected, has excellent mechanical properties, is added into a system, improves the compatibility of film forming substances, enables the performances of the film forming substances to be cooperated, improves the bonding strength, the water resistance, the moisture resistance and the weather resistance of the coating, and is reacted with the aqueous silicone-acrylate emulsion to endow the coating with excellent bonding strength, good chemical resistance and high film hardness.
(3) The titanate coupling agent can increase the amount of pigment filler, improve the dispersion performance, have the anti-settling effect, prevent the blooming, improve the strength of a paint film, and have bright color and other properties.
(4) The long-chain alkyl silicone oil defoaming agent can effectively eliminate bubbles brought by paint preparation, has good affinity, does not influence the post-processing performance of products, can reduce the surface tension of water-based paint, ensures long-short wave leveling in the drying process of a paint film, obtains the paint film with excellent surface leveling, fine hand feeling and excellent surface decoration effect.
(5) The universal electric vehicle water-based plastic paint disclosed by the invention is simple in preparation process and construction, can obtain an ideal coating film by one-time construction, and is widely suitable for surface coating and decoration protection of various products such as toys, electric appliances, household appliances, articles for daily use, automobile accessories and the like.
Detailed Description
The present embodiment is only for explaining the present invention, and it is not limited to the present invention, and those skilled in the art can make modifications of the present embodiment without inventive contribution as needed after reading the present specification, but all of them are protected by patent law within the scope of the claims of the present invention.
Example 1
1) The formula of the universal electric vehicle water-based plastic paint comprises the following components in percentage by weight:
water-based silicone-acrylic emulsion: 40 percent;
aqueous polyurethane dispersion: 15 percent;
propylene glycol butyl ether: 6 percent;
0.2 percent of long-chain alkyl silicone oil defoaming agent;
0.3 percent of tristearin;
10 percent of titanate coupling agent;
BYK346 (assistant selected from Bike assistant Germany) 0.3%;
pigment and filler: 7.5 percent;
deionized water: 20 percent;
0.5 percent of hydroxypropyl methyl cellulose;
EFKA3500 (adjuvant selected from EFKA adjuvants corporation): 0.2 percent.
2) The preparation process of the universal electric vehicle water-based plastic paint comprises the following steps:
preparation: sequentially adding the aqueous silicone-acrylic emulsion and the aqueous polyurethane dispersoid into a dispersion cylinder, dispersing at the rotating speed of 800r/min, adding deionized water during stirring, and dispersing at the rotating speed of 1000r/min for 20 minutes until the mixture is uniformly stirred; adding propylene glycol butyl ether and titanate coupling agent at the rotating speed of 800r/min, and then dispersing for 15 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred; adding a wetting agent, a thickening agent and a defoaming agent at the rotating speed of 800r/min, and dispersing for 15 minutes at the rotating speed of 1500r/min until the mixture is uniformly stirred; adding pigment and filler at the rotating speed of 800r/min, and dispersing for 10 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred; adding a flatting agent and a dispersing agent at the rotating speed of 800r/min, and dispersing for 15 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred for later use;
paint mixing: according to the field construction conditions, adding a proper amount of deionized water into the plastic paint and stirring uniformly.
Example 2
1) The formula of the universal electric vehicle water-based plastic paint comprises the following components in percentage by weight:
water-based silicone-acrylic emulsion: 35 percent;
aqueous polyurethane dispersion: 20 percent;
propylene glycol butyl ether: 4 percent;
0.1 percent of long-chain alkyl silicone oil defoaming agent;
0.2 percent of tristearin;
10 percent of titanate coupling agent;
BYK346 (adjuvant selected from Bike adjuvant Germany) 0.1%;
pigment and filler: 10 percent;
deionized water: 20 percent;
0.5 percent of hydroxypropyl methyl cellulose;
EFKA3500 (adjuvant selected from EFKA adjuvants corporation): 0.1 percent.
2) The preparation process of the universal electric vehicle water-based plastic paint comprises the following steps:
preparation: sequentially adding the aqueous silicone-acrylic emulsion and the aqueous polyurethane dispersoid into a dispersion cylinder, dispersing at the rotating speed of 800r/min, adding deionized water during stirring, and dispersing at the rotating speed of 1000r/min for 20 minutes until the mixture is uniformly stirred; adding propylene glycol butyl ether and titanate coupling agent at the rotating speed of 800r/min, and then dispersing for 15 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred; adding a wetting agent, a thickening agent and a defoaming agent at the rotating speed of 800r/min, and dispersing for 15 minutes at the rotating speed of 1500r/min until the mixture is uniformly stirred; adding pigment and filler at the rotating speed of 800r/min, and dispersing for 10 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred; adding a flatting agent and a dispersing agent at the rotating speed of 800r/min, and dispersing for 15 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred for later use;
paint mixing: the paint is added with deionized water with the same amount as that in the example 1 and stirred evenly.
Example 3
1) The formula of the universal electric vehicle water-based plastic paint comprises the following components in percentage by weight:
water-based silicone-acrylic emulsion: 45 percent;
aqueous polyurethane dispersion: 10 percent;
propylene glycol butyl ether: 5 percent;
0.5 percent of long-chain alkyl silicone oil defoaming agent;
0.4 percent of tristearin;
15 percent of titanate coupling agent;
BYK346 (adjuvant selected from Bike adjuvant Germany) 0.5%;
pigment and filler: 5 percent;
deionized water: 17.5 percent;
0.8 percent of hydroxypropyl methyl cellulose;
EFKA3500 (adjuvant selected from EFKA adjuvants corporation): 0.3 percent.
2) The preparation process of the universal electric vehicle water-based plastic paint comprises the following steps:
preparation: sequentially adding the aqueous silicone-acrylic emulsion and the aqueous polyurethane dispersoid into a dispersion cylinder, dispersing at the rotating speed of 800r/min, adding deionized water during stirring, and dispersing at the rotating speed of 1000r/min for 20 minutes until the mixture is uniformly stirred; adding propylene glycol butyl ether and titanate coupling agent at the rotating speed of 800r/min, and then dispersing for 15 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred; adding a wetting agent, a thickening agent and a defoaming agent at the rotating speed of 800r/min, and dispersing for 15 minutes at the rotating speed of 1500r/min until the mixture is uniformly stirred; adding pigment and filler at the rotating speed of 800r/min, and dispersing for 10 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred; adding a flatting agent and a dispersing agent at the rotating speed of 800r/min, and dispersing for 15 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred for later use;
paint mixing: the paint is added with deionized water with the same amount as that in the example 1 and stirred evenly.
Example 4
1) The formula of the universal electric vehicle water-based plastic paint comprises the following components in percentage by weight:
water-based silicone-acrylic emulsion: 37.5 percent;
aqueous polyurethane dispersion: 17.5 percent;
propylene glycol butyl ether: 5 percent;
0.15 percent of long-chain alkyl silicone oil defoaming agent;
0.25 percent of tristearin;
13.5 percent of titanate coupling agent;
BYK346 (adjuvant selected from Bike adjuvant Germany) 0.15%;
pigment and filler: 7 percent;
deionized water: 18.4 percent;
0.4 percent of hydroxypropyl methyl cellulose;
EFKA3500 (adjuvant selected from EFKA adjuvants corporation): 0.15 percent.
2) The preparation process of the universal electric vehicle water-based plastic paint comprises the following steps:
preparation: sequentially adding the aqueous silicone-acrylic emulsion and the aqueous polyurethane dispersoid into a dispersion cylinder, dispersing at the rotating speed of 800r/min, adding deionized water during stirring, and dispersing at the rotating speed of 1000r/min for 20 minutes until the mixture is uniformly stirred; adding propylene glycol butyl ether and titanate coupling agent at the rotating speed of 800r/min, and then dispersing for 15 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred; adding a wetting agent, a thickening agent and a defoaming agent at the rotating speed of 800r/min, and dispersing for 15 minutes at the rotating speed of 1500r/min until the mixture is uniformly stirred; adding pigment and filler at the rotating speed of 800r/min, and dispersing for 10 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred; adding a flatting agent and a dispersing agent at the rotating speed of 800r/min, and dispersing for 15 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred for later use;
paint mixing: the paint is added with deionized water with the same amount as that in the example 1 and stirred evenly.
Example 5
1) The formula of the universal electric vehicle water-based plastic paint comprises the following components in percentage by weight:
water-based silicone-acrylic emulsion: 42.5 percent;
aqueous polyurethane dispersion: 12.5 percent;
propylene glycol butyl ether: 5 percent;
0.3 percent of long-chain alkyl silicone oil defoaming agent;
0.35 percent of tristearin;
12 percent of titanate coupling agent;
BYK346 (adjuvant selected from Bike adjuvant Germany) 0.4%;
pigment and filler: 8.6 percent;
deionized water: 17.5 percent;
0.6 percent of hydroxypropyl methyl cellulose;
EFKA3500 (adjuvant selected from EFKA adjuvants corporation): 0.25 percent.
2) The preparation process of the universal electric vehicle water-based plastic paint comprises the following steps:
preparation: sequentially adding the aqueous silicone-acrylic emulsion and the aqueous polyurethane dispersoid into a dispersion cylinder, dispersing at the rotating speed of 800r/min, adding deionized water during stirring, and dispersing at the rotating speed of 1000r/min for 20 minutes until the mixture is uniformly stirred; adding propylene glycol butyl ether and titanate coupling agent at the rotating speed of 800r/min, and then dispersing for 15 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred; adding a wetting agent, a thickening agent and a defoaming agent at the rotating speed of 800r/min, and dispersing for 15 minutes at the rotating speed of 1500r/min until the mixture is uniformly stirred; adding pigment and filler at the rotating speed of 800r/min, and dispersing for 10 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred; adding a flatting agent and a dispersing agent at the rotating speed of 800r/min, and dispersing for 15 minutes at the rotating speed of 1000r/min until the mixture is uniformly stirred for later use;
paint mixing: the paint is added with deionized water with the same amount as that in the example 1 and stirred evenly.
Comparative example 1
The plastic paint is common water-based plastic paint on the market.
Performance test and experimental results
The above description is only a preferred embodiment of the present invention, and it should be noted that, for those skilled in the art, several modifications and variations can be made without departing from the technical principle of the present invention, and those modifications and variations assumed in the above are also considered to be within the protective scope of the present invention.
Claims (8)
1. The utility model provides a commonality electric motor car water-based plastic paint which characterized in that: the material comprises the following materials in percentage by weight:
water-based silicone-acrylic emulsion: 35% -45%;
aqueous polyurethane dispersion: 10% -20%;
propylene glycol butyl ether: 2% -10%;
0.1 to 0.5 percent of defoaming agent;
0.2 to 0.5 percent of dispersant;
5 to 15 percent of titanate coupling agent;
0.1 to 0.5 percent of flatting agent;
pigment and filler: 5% -10%;
deionized water: 15% -25%;
0.3 to 0.8 percent of thickening agent;
wetting agent: 0.1 to 0.3 percent.
2. The universal electric vehicle water-based plastic paint as claimed in claim 1, wherein: the material comprises the following materials in percentage by weight:
water-based silicone-acrylic emulsion: 40 percent;
aqueous polyurethane dispersion: 15 percent;
propylene glycol butyl ether: 6 percent;
0.2 percent of defoaming agent;
0.3 percent of dispersant;
10 percent of titanate coupling agent;
0.3 percent of flatting agent;
pigment and filler: 7.5 percent;
deionized water: 20 percent;
0.5 percent of thickening agent;
wetting agent: 0.2 percent.
3. The universal electric vehicle water-based plastic paint as claimed in claim 1, wherein: the defoaming agent is a long-chain alkyl silicone oil defoaming agent in the modified silicone oil defoaming agent.
4. The universal electric vehicle water-based plastic paint as claimed in claim 1, wherein: the dispersant is glyceryl tristearate.
5. The universal electric vehicle water-based plastic paint as claimed in claim 1, wherein: the leveling agent is one of BYK346, BYK381, or modesty 435.
6. The universal electric vehicle water-based plastic paint as claimed in claim 1, wherein: the thickening agent is hydroxypropyl methyl cellulose or polyvinylpyrrolidone.
7. The universal electric vehicle water-based plastic paint as claimed in claim 1, wherein: the wetting agent is one of EFKA3500, EFKA3034 or TEGO 270.
8. A preparation method of a universal electric vehicle water-based plastic paint is characterized by comprising the following steps: the method comprises the following steps:
s1, sequentially adding the aqueous silicone-acrylic emulsion and the aqueous polyurethane dispersoid into a dispersion cylinder, dispersing at the rotating speed of 800r/min in 700-;
s2, adding propylene glycol butyl ether and titanate coupling agent at the rotating speed of 800r/min of 700-;
s3, adding a wetting agent, a thickening agent and a defoaming agent at the rotating speed of 800r/min of 700-;
s4: adding the pigment and the filler at the rotating speed of 800r/min of 700 plus materials, and dispersing for 5-10 minutes at the rotating speed of 1000r/min of 800 plus materials until the mixture is uniformly stirred;
s5: adding the flatting agent and the dispersing agent at the rotating speed of 800r/min of 700 plus materials, and dispersing for 10-15 minutes at the rotating speed of 1000r/min of 800 plus materials until the materials are uniformly stirred.