Abstract

The embodiment of the invention provides a manufacturing method of a Yunlong silk ornament, which comprises the following steps: s1, processing the pre-prepared alloy gold bar to form a square wire with a preset size, and polishing the square wire; s2, cutting the polished square wires according to a preset length, and winding the cut square wires into cloud-shaped cloud dragon veins; s3, welding and sealing the opening of each cloud dragon pattern; s4, manufacturing a bottom tire based on a preset modeling structure; s5, coating glue on the cloud dragon patterns according to the shape of the tread of the bottom tire and placing the cloud dragon patterns on the tread; and S6, welding and molding the cloud and dragon patterns arranged on the tire surface. The Yunlong ornamentation manufactured by the embodiment has good structural stability, and can realize jewelry inlaying.

Description

Yunlong silk ornament and manufacturing method thereof

Technical Field

The invention relates to the field of ornament manufacturing, in particular to a manufacturing method of a Yunlong silk ornament.

Background

The filament is embedded with the traditional Chinese handwork skills and is mainly used for manufacturing ornaments. The filament inlay comprises a process of forming the filament and a process of inlaying jewelry. Usually, the filament is formed by using gold and silver as raw materials, drawing the raw materials into filaments and knitting the filaments; the inlaying is to beat and shape the gold and silver sheets and embed the pearl jewel into the gold and silver sheets to manufacture the ornament.

The whole process is complicated, and firstly, the tire is manufactured so as to facilitate modeling; then, forming the filament by stacking, weaving and weaving methods, and welding; then bitten with acid (acid washing), then bluing or plating gold and silver, and then brightening. And finally, inlaying jewelry to finish a finished product.

Disclosure of Invention

The invention provides a method for manufacturing a Yunlong silk ornament, and aims to provide a novel ornament manufacturing method which is more suitable for three-dimensional presentation.

The embodiment of the invention provides a manufacturing method of a Yunlong silk ornament, which comprises the following steps:

s1, processing the pre-prepared alloy gold bar to form a square wire with a preset size, and polishing the square wire;

s2, cutting the polished square wires according to a preset length, and winding the cut square wires into cloud-shaped cloud dragon veins;

s3, welding and sealing the opening of each cloud dragon pattern;

s4, manufacturing a bottom tire based on a preset modeling structure;

s5, coating glue on the cloud dragon patterns according to the shape of the tread of the bottom tire and placing the cloud dragon patterns on the tread;

and S6, welding and molding the cloud and dragon patterns arranged on the tire surface.

Preferably, the method further comprises the following steps:

and S7, carrying out jewelry inlaying on the welded and connected formed dragon-shaped veins.

Preferably, in step S1, the processing of the alloy gold bar into a square line with a preset size includes:

s1a, pressing the prepared alloy gold bar, and drawing the alloy into a square strip shape to form a round filament with the diameter of 5 mm;

s1b, pressing the round filaments obtained in the step S1a into square threads with the width of 3mm and the height of 6mm by a wire pressing machine.

Preferably, in step S2, the cutting of the square thread at a length of 7-9cm and the winding of the square thread into the cloud dragon pattern in the shape of a cloud include:

and S2a, winding the square wires into 8-shaped clouds.

Preferably, in the step S3, the welding and sealing of the opening of each cloud dragon pattern is to seal the opening by spot welding.

Preferably, in step S5, the process of placing the dragon pattern on the tread includes:

s5a, placing the dragon veins on the tire surface at intervals of less than 3 mm.

Preferably, in step S6, the process of welding and forming the cloud dragon pattern includes:

s6a, cutting the low soldering lug into square pieces, melting the square pieces into balls, and dipping borax on the balls to align to the connection points for welding.

Preferably, in step S6a, the size of the square pieces is 1 × 1mm or approximately 1 × 1mm square pieces.

Preferably, the alloy is any one of silver, 14K, 18K gold, rhodium, platinum, and palladium, and the low pads have the same K number as that of the alloy in step S6.

Preferably, in the step S1, the polishing of the square wire is performed by manually polishing with an agate knife.

In the embodiment of the invention, the cloud-shaped structure is easier to support, is not easy to deform when being made into a three-dimensional shape, and can be applied in a large area, so that the traditional process method that the filaments only can be planar and are less used for three-dimensional is broken through, each cloud dragon line has stronger structural strength due to the adoption of square line forming, and more three-dimensional ornaments with stable shapes and structures can be manufactured based on the base tire. The glossiness of the ornament is ensured by a polishing means. The Yunlong ornamentation manufactured by the embodiment has good structural stability, and can realize jewelry inlaying.

Drawings

In order to more clearly illustrate the embodiments of the present invention or the technical solutions in the prior art, the drawings used in the description of the embodiments or the prior art will be briefly described below, it is obvious that the drawings in the following description are only some embodiments of the present invention, and for those skilled in the art, other drawings can be obtained according to the structures shown in the drawings without creative efforts.

FIG. 1 is a flow chart of a method for manufacturing a Yunlong silk ornament according to an embodiment of the present invention;

fig. 2 is a schematic view of a cloud dragon pattern structure provided by an embodiment of the present invention;

FIG. 3 is a schematic view of a Yunlong silk ornament according to an embodiment of the present invention;

fig. 4 is a schematic view of another perspective view of the yunlong silk ornament provided by the embodiment of the present invention.

Detailed Description

The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are some, not all, embodiments of the present invention. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

Reference herein to "an embodiment" means that a particular feature, structure, or characteristic described in connection with the embodiment can be included in at least one embodiment of the application. The appearances of the phrase in various places in the specification are not necessarily all referring to the same embodiment, nor are separate or alternative embodiments mutually exclusive of other embodiments. It is explicitly and implicitly understood by one skilled in the art that the embodiments described herein can be combined with other embodiments.

As shown in fig. 1, an embodiment of the present invention provides a method for manufacturing a yunlong silk ornament, including the following steps:

s3, welding and sealing the opening of each cloud dragon pattern;

s4, manufacturing a bottom tire based on a preset modeling structure;

The cloud dragon pattern structure manufactured by the embodiment is stable in structure, and can realize jewelry inlaying, so that the method further comprises the following steps:

In this embodiment, in step S1, the processing of the alloy gold bar into a square line with a preset size includes:

Specifically, the Yunlong silk is completely different from the silk in the existing silk process, although before the silk is pulled, the prepared alloy or noble metal strip is placed on a strip rolling machine to be repeatedly pressed until the silk becomes a square strip with proper thickness, and then the formal silk pulling is started. In the same way, the thread is manually pulled by using a thread pulling plate, then forty to fifty eyelets with different diameters are used for gradually thinning the thick thread to finally reach the required diameter, in the embodiment, the thread of the Yunlong silk is mostly the thread diameter of 3.5 to 10 millimeters, and the thread of the flower silk is mostly round thread with the specification of 2 to 2.6 millimeters at present. Of course, the thread diameter may also be adjusted appropriately based on the requirements of different ornaments, but is generally larger than the thread diameter of the filament.

Specifically, in step S1b, the mechanical principle is utilized, for example, when the diameter of the round thread is 5mm, the round thread of 5mm is pressed into a rectangular square thread with a width of 3mm and a height of 6mm by a thread press, and this process can be called a binding process, so that when the cloud of the yunlong silk is made, the force of the cloud is easier to support, and when the cloud is made into a three-dimensional shape, the cloud is not easy to deform and can be applied in a large area, which breaks through the fact that the flower silk can only be planar, and is less used for a new three-dimensional process (the flower silk process does not have a binding process because the thread of the round thread).

In this embodiment, in the step S1, the polishing of the square wire is performed by manually polishing the square wire with an agate knife. Specifically, the bundled thread is polished manually by an agate knife, so that the thread is smooth at 360 degrees, the appearance of the thread is ensured, and the whole thread is smooth and has no dead angle (different from a filament process, the filament does not use light, and the thread of the filament is a round thread and is repeatedly pulled by a wire pulling plate to become smooth).

In this embodiment, in the step S2, the cutting of the square thread at a length of 7 to 9cm and the winding of the square thread into the cloud dragon pattern in the shape of a cloud include:

and S2a, winding the square wires into 8-shaped clouds.

In this embodiment, in the step S3, the welding and sealing of the opening of each cloud dragon pattern is to seal the opening by spot welding.

Specifically, the manufacturing pattern of the cloud dragon veins of the yunlong silk in the embodiment is different from the patterns formed by the stacking, weaving and weaving method in the filaments, each of the cloud dragon veins of the yunlong silk in the embodiment is welded to increase the strength of the cloud, and meanwhile, the shape of the cause and effect number 8 of the book of changes is integrated, so that the shape supporting force is stronger from the mechanical angle, and meanwhile, the patterns are firmer and more Chinese by combining Chinese culture symbols. As shown in fig. 2, in order to wind the cut square lines 11 into the 8-shaped moire pattern 10, spot welding is performed at the opening 12 after winding, so that the opening is bonded (the spot welding surface can be placed on the back surface in the process of forming the swing tire, so that the spot welding position cannot be seen).

In this embodiment, in step S4, the bottom base is made of a material selected from any one of silver base, copper base, stainless steel base, and gypsum base, which is different from the filament process, in this embodiment, the "yunlong silk" decoration article is made by making the base, and only the large ornament is inlaid with the filament, and the base is made of small jewelry without making the base, and the filament is mostly planar, and the yunlong silk is mostly three-dimensional, and the bottom base can be used to realize the pendulum moulding of the yunlong pattern.

In this embodiment, the step S5 of placing the dragon pattern on the tread includes:

s5a, indirectly placing the Yunlong patterns on the tire surface according to the size of less than 3 mm.

Specifically, the process of the pendulum tire forming is to coat glue on Yunlong patterns according to the distance less than 3mm and place the Yunlong patterns on the tire surface and place the Yunlong patterns according to the tire shapes, the pendulum tire forming is the most careful and time-consuming process in the Yunlong silk process, the attractiveness of pattern placement can be affected by fine breathing, the pendulum tire forming of the Yunlong silk completely overturns and innovates the filling of the silk, and the difference from the filling of the silk is that the filling is carried out according to a plane in a frame, while the pendulum tire forming in the Yunlong silk process is not provided with a frame, is arranged on the tire surface along the tire surface structure, most of products are in a three-dimensional structure, more accords with the artistic aesthetic sense of the modern process on jewelry, and has more international effect than the silk process.

In this embodiment, in step S6, the process of welding and forming the cloud dragon pattern includes:

In step S6a, the square pieces have a size of 1 × 1mm or approximately 1 × 1 mm.

In this embodiment, the alloy is any one of silver, 14K, 18K gold, rhodium, platinum, and palladium, and in step S6, the low pads are low pads having the same K number as the alloy.

Specifically, the welding and forming process of the steps S6 and S6a is an important process of Yunlong silk forming, the Yunlong lines formed by the swinging of the tire are connected by spot welding to be the most precise place when the Yunlong silk is used for manufacturing ornaments and works, the welding process is extremely severe, the ornament and the works can be abandoned by carelessness, firstly, low welding pieces with the same number K are used, square pieces with the diameter of 1mm are cut by a pair of scissors, then, the square pieces are melted into balls, borax is stained on the connection points, welding is carried out, an operator is required to keep the fire tip of blue fire of a welding gun close to the low welding balls in the welding process, the whole welding process is stable and cannot shake at the moment, the welding balls are melted in the welding positions, the welding marks cannot be seen, the welding is completed, the area of each centimeter needs 3-4 welding positions, the whole work is absolutely exquisite, and no spot welding is left. The welding forming of "yunlong silk" is different with the welding of filament, the filament majority is the plane, so at the in-process that welds, directly with the undersize sieve with the welding flux powder sieve evenly sprinkle on the filament surface, reuse fire heats the process that just welds on the powder, and the welding forming of "yunlong silk", the contrast filament can be more firm, do not have under the condition of a strong point in the work even, the molding is also firm, it is stiff, it deposits and wears to change, owing to not supporting, the goods is more graceful, the jewelry of same volume size, its weight is half of ordinary jewelry works only.

In this embodiment, step S7 is to inlay the jewelry in the yunlong silk inlay work, and the inlaying skill of the gem is determined according to the design style, and the yunlong silk inlay is mostly cold inlay, that is, the gem is inlaid at the end of the work, and the inlaying skill can be applied to any skill, such as all inlaying techniques of bag inlay, wall inlay, claw inlay, borderless inlay, and the like, which fully embodies the accuracy and delicacy of the modern industrial development, and is more inclusive, wider, and more elegant than the silk inlay which is limited to several kinds of inlays.

Based on the above method, as shown in fig. 3 and 4, the invention can also provide a Yunlong silk ornament manufactured based on the above method. Which comprises a yunlong silk made of yunlong patterns and a jade piece embedded in the yunlong silk. The yunlong silk shown in fig. 3 and 4 has a three-dimensional structure, and jewelry can be directly inlaid by a cold inlaying method, so that the structural strength is high, the content is high, and the application is wide.

The above disclosure is only for the purpose of illustrating the preferred embodiments of the present invention, and it is therefore to be understood that the invention is not limited by the scope of the appended claims.

Claims

1. The manufacturing method of the Yunlong silk ornament is characterized by comprising the following steps:

s3, welding and sealing the opening of each cloud dragon pattern;

s4, manufacturing a bottom tire based on a preset modeling structure;

2. The method for manufacturing the Yunlong silk ornament as claimed in claim 1, further comprising the steps of:

3. The method for manufacturing the Yunlong silk ornament as claimed in claim 1, wherein in step S1, the step of processing the alloy gold bar into the square wire with the preset size includes:

4. The method for manufacturing the Yunlong silk ornament as claimed in claim 1, wherein in step S2, the process of cutting the square thread to a length of 7-9cm and winding the square thread into Yunlong lines in the shape of clouds includes:

and S2a, winding the square wires into 8-shaped clouds.

5. The method for manufacturing a Yunlong silk ornament as claimed in claim 1, wherein in step S3, the welding and sealing of the opening of each Yunlong vein is performed by spot welding.

6. The method for manufacturing the Yunlong silk ornament as claimed in claim 1, wherein in the step S5, the process of placing Yunlong patterns on the tread comprises:

7. The method for manufacturing the Yunlong silk ornament as claimed in claim 1, wherein in step S6, the process of welding and forming the Yunlong patterns includes:

8. The method for manufacturing the Yunlong silk ornament as claimed in claim 7, wherein in the step S6a, the size of the square pieces is 1 x 1mm or approximately 1 x 1 mm.

9. The method for manufacturing the Yunlong silk ornament as claimed in claim 7, wherein the alloy is any one of silver, 14K, 18K gold, rhodium, platinum and palladium, and in the step S6, the low solder pieces are low solder pieces with the same K number as the alloy.

10. The method for manufacturing the Yunlong silk ornament as claimed in claim 1, wherein in the step S1, the square threads are polished by hand with an agate knife.

11. A yunlong silk ornament, characterized in that it is manufactured by the method as claimed in any one of claims 1 to 10.