CN110724233A - Synthesis method of MBS resin - Google Patents
Synthesis method of MBS resin Download PDFInfo
- Publication number
- CN110724233A CN110724233A CN201810780729.3A CN201810780729A CN110724233A CN 110724233 A CN110724233 A CN 110724233A CN 201810780729 A CN201810780729 A CN 201810780729A CN 110724233 A CN110724233 A CN 110724233A
- Authority
- CN
- China
- Prior art keywords
- styrene
- initiator
- linking agent
- cross
- mbs resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of high molecular compounds, and relates to a synthesis method of MBS resin, which comprises the following raw materials of methyl methacrylate, styrene-butadiene latex, an initiator, a cross-linking agent, sodium p-styrene sulfonate and soft water, wherein the raw materials are mixed according to the weight ratio of 15:10:5:55:2: 13: 300, adding soft water, styrene-butadiene latex, styrene, an initiator, methyl methacrylate, a cross-linking agent and sodium styrene sulfonate into a reactor in sequence for reaction in a feeding link.
Description
Technical Field
The invention belongs to the field of high molecular compounds, and relates to a synthetic method of MBS resin.
Background
The MBS resin is a terpolymer prepared by emulsion graft polymerization, is a novel high molecular material synthesized under the concept of particle design, and has a typical core-shell structure on a submicroscopic structure. The core of the material is a rubber phase spherical core with the diameter of 50-300 nm, and the rubber phase spherical core can change the shape and absorb and disperse impact energy when being impacted by external force; the shell grafted by styrene and MMA is arranged outside, and because the solubility parameters are similar, the shell part plays a role of an interface adhesive between PVC and rubber phase particles, a homogeneous phase can be formed in the processing and mixing process, and the rubber phase is dispersed in a PVC continuous medium in a particle state. Therefore, the toughness of the PVC can be improved by more than several times by adding a small amount of MBS into the PVC.
In the prior art, only methyl methacrylate, styrene-butadiene latex and other raw materials are added when MBS resin is synthesized, so that the chromaticity, haze and impact strength of PVC have obvious defects.
Disclosure of Invention
In view of the above-mentioned drawbacks of the prior art, the present invention aims to provide a method for synthesizing an MBS resin for improving the chromaticity, haze and impact strength of PVC.
In order to achieve the purpose, the invention provides a synthesis method of MBS resin, wherein raw materials for synthesizing the MBS resin comprise methyl methacrylate, styrene-butadiene latex, an initiator, a cross-linking agent and sodium p-styrene sulfonate, and in the material preparation link, the raw materials of the methyl methacrylate, the styrene-butadiene latex, the initiator, the cross-linking agent, the sodium p-styrene sulfonate and soft water are mixed according to the weight ratio of 15:10:5:55:2: 13: 300, adding soft water with the temperature of 50 ℃ into a reactor in a feeding link, and then sequentially adding styrene-butadiene latex, styrene, an initiator, methyl methacrylate, a cross-linking agent and sodium styrene sulfonate into the reactor according to the proportion to react.
Preferably, the initiator is dibenzoyl peroxide or potassium persulfate salts.
Preferably, the crosslinking agent is divinylbenzene.
The invention has the beneficial effects that:
the method mainly comprises the steps of preparing raw materials of methyl methacrylate, styrene-butadiene latex, an initiator, a cross-linking agent, sodium styrene sulfonate and soft water according to a specific preparation proportion in a grafting reaction, and synthesizing the MBS resin according to a certain feeding sequence.
Detailed Description
The invention provides a synthesis method of MBS resin, which comprises the steps of material preparation, feeding, reaction, condensation, dehydration, drying and finished product packaging, wherein in the material preparation process, prepared raw materials comprise methyl methacrylate, styrene-butadiene latex, an initiator, a cross-linking agent and sodium p-styrenesulfonate, wherein the initiator is dibenzoyl peroxide or potassium persulfate salt, the cross-linking agent is divinylbenzene, in addition, soft water is also required to be prepared, and the material preparation ratio of the methyl methacrylate, the styrene-butadiene latex, the initiator, the cross-linking agent, the sodium p-styrenesulfonate and the soft water is 15:10:5:55:2: 13: 300.
in the feeding process, soft water with the temperature of 50 ℃ is added into a reactor, and then styrene-butadiene latex, styrene, an initiator, methyl methacrylate, a cross-linking agent and sodium styrene sulfonate are sequentially added into the reactor according to the proportion to react.
Claims (3)
1. A synthesis method of MBS resin is characterized in that:
the raw materials for synthesizing the MBS resin comprise methyl methacrylate, styrene-butadiene latex, an initiator, a cross-linking agent and sodium p-styrene sulfonate, in addition, soft water is also required to be prepared, and in the material preparation link, the raw materials of the methyl methacrylate, the styrene-butadiene latex, the initiator, the cross-linking agent, the sodium p-styrene sulfonate and the soft water are mixed according to the weight ratio of 15:10:5:55:2: 13: 300 are prepared.
In the feeding step, soft water at 50 ℃ is added into a reactor, and then styrene-butadiene latex, styrene, an initiator, methyl methacrylate, a cross-linking agent and sodium styrene sulfonate are sequentially added into the reactor according to the proportion to react.
2. The method of claim 1, wherein the MBS resin is synthesized by the steps of:
the initiator is dibenzoyl peroxide or potassium persulfate salts.
3. The method of claim 1, wherein the MBS resin is synthesized by the steps of:
the cross-linking agent is divinylbenzene.