CN110714271A - Method for preparing PDMS-PMMA (polydimethylsiloxane-polymethyl methacrylate) super-hydrophobic membrane based on electrostatic spinning - Google Patents
Method for preparing PDMS-PMMA (polydimethylsiloxane-polymethyl methacrylate) super-hydrophobic membrane based on electrostatic spinning Download PDFInfo
- Publication number
- CN110714271A CN110714271A CN201911134889.1A CN201911134889A CN110714271A CN 110714271 A CN110714271 A CN 110714271A CN 201911134889 A CN201911134889 A CN 201911134889A CN 110714271 A CN110714271 A CN 110714271A
- Authority
- CN
- China
- Prior art keywords
- electrostatic spinning
- polymethyl methacrylate
- dimethyl siloxane
- preparing
- pmma
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing a PDMS-PMMA (polydimethylsiloxane-polymethyl methacrylate) superhydrophobic film based on electrostatic spinning, which comprises the steps of preparing an electrospinning solution by combining polymethyl methacrylate (PDMS) and dimethyl siloxane (PMMA), and then treating the electrospinning solution by using an electrostatic spinning technology to finally prepare the PDMS-PMMA superhydrophobic film; the super-hydrophobic membrane has good hydrophobic property and salt ion interception effect, and is convenient for subsequent treatment and degradation after use; thereby preventing the secondary pollution to the environment.
Description
Technical Field
The invention relates to a method for preparing a PDMS-PMMA (polydimethylsiloxane-polymethyl methacrylate) super-hydrophobic film based on electrostatic spinning, belonging to the technical field of hydrophobic film preparation.
Background
With the continuous advance of industrialization in various countries, the problem of water pollution caused by the progress of industrialization is more serious. The oily wastewater discharged into water bodies such as rivers, oceans and the like can cause great threat to the survival of aquatic organisms, and a series of diseases can be caused after people eat fishes in polluted areas by mistake. Therefore, how to properly treat the oily wastewater becomes a problem to be solved urgently. At present, the oily wastewater mainly comprises the following treatment methods: gravity separation, centrifugal separation, flotation, coagulation, combustion, photocatalytic oxidation, adsorption, and the like. However, most of the methods have complex operation flow and complex process, and are easy to generate toxic substances to cause secondary pollution to the environment. Membrane separation methods which have been developed in recent years have been increasingly used for separation of oil-containing wastewater due to the characteristics of simple devices, wide application range, high separation efficiency and the like; wherein the key to the process is the performance of the superhydrophobic film.
At present, polymer materials such as polyvinylidene fluoride (PVDF), Polystyrene (PS) and Polyurethane (PU) are commonly used for preparing the oil-water separation membrane. However, the materials are difficult to degrade, wherein PVDF and PS are toxic, and the subsequent treatment is easy to cause secondary pollution to the environment. The existing super-hydrophobic membrane has poor hydrophobicity and poor retention effect on salt ions in wastewater; therefore, how to prepare the super-hydrophobic membrane which has good hydrophobic property and good salt ion interception effect and is convenient for subsequent treatment and degradation is the research direction of the industry.
Disclosure of Invention
Aiming at the problems in the prior art, the invention provides a method for preparing a PDMS-PMMA (polydimethylsiloxane-polymethyl methacrylate) super-hydrophobic film based on electrostatic spinning, and the prepared super-hydrophobic film has good hydrophobic property and salt ion interception effect, and is convenient for subsequent treatment and degradation after use; thereby preventing the secondary pollution to the environment.
In order to achieve the purpose, the invention adopts the technical scheme that: a method for preparing PDMS-PMMA super-hydrophobic film based on electrostatic spinning comprises the following specific steps:
A. selecting raw materials: selecting polymethyl methacrylate (PDMS) and dimethyl siloxane (PMMA) as raw materials;
B. preparing an electrospinning solution: adding polymethyl methacrylate and dimethyl siloxane into a mixing container, wherein the mass ratio of the polymethyl methacrylate to the dimethyl siloxane is (1-3) to (1-2), then enabling the temperature of the mixing container to reach 50-70 ℃, stirring the mixed solution by using a magnetic stirrer under the temperature condition, continuing for 2-3 hours, placing the mixed solution in an environment with the temperature of 20-25 ℃ after the mixed solution is finished, and completing the preparation of an electrospinning solution after the mixed solution is cooled to the ambient temperature;
C. preparing a polymethyl methacrylate/dimethyl siloxane super-hydrophobic film: injecting the electrospinning solution into an injector of an electrostatic spinning device, installing the injector on a propulsion pump, determining parameters of electrostatic spinning, starting the electrostatic spinning device to carry out electrostatic spinning on the electrospinning solution, and preparing a dimethyl siloxane/dimethyl siloxane super-hydrophobic membrane after completing the electrostatic spinning; wherein the parameters of electrospinning include: the applied voltage is 8-13 kV, the receiving distance is 8-16 cm, and the propelling speed is 0.6-1.5 mL h-1。
Further, the mass ratio of the polymethyl methacrylate to the dimethyl siloxane is 1:1.
Furthermore, among the parameters of the electrostatic spinning, the applied voltage is 10.5kV, the receiving distance is 13cm, and the advancing speed is 1.0mL h-1。
Compared with the prior art, the invention adopts polymethyl methacrylate (PDMS) and dimethyl siloxane (PMMA) to prepare the electrospinning solution, then the electrospinning solution is processed by adopting the electrostatic spinning technology, and finally the PDMS-PMMA superhydrophobic film is prepared; the super-hydrophobic membrane has good hydrophobic property and salt ion interception effect, and is convenient for subsequent treatment and degradation after use; thereby preventing the secondary pollution to the environment.
Drawings
FIG. 1 is a graph of variation of static contact angle of Water (WCA) on the surface of the super-hydrophobic membrane prepared by different mass ratios of PDMS to PMMA according to the example of the present invention, as a function of Viscosity of the spinning solution (Viscosity).
Detailed Description
The present invention will be further explained below.
Example 1:
a method for preparing PDMS-PMMA super-hydrophobic film based on electrostatic spinning comprises the following specific steps:
A. selecting raw materials: selecting polymethyl methacrylate (PDMS) and dimethyl siloxane (PMMA) as raw materials;
B. preparing an electrospinning solution: adding polymethyl methacrylate and dimethyl siloxane into a mixing container, wherein the mass ratio of the polymethyl methacrylate to the dimethyl siloxane is 1:2, then enabling the temperature of the mixing container to reach 65 ℃, stirring the mixed solution by adopting a magnetic stirrer under the temperature condition, continuing for 2.5 hours, placing the mixed solution in an environment with the temperature of 24 ℃ after the mixed solution is finished, and finishing the preparation of an electrospinning solution after the mixed solution is cooled to the ambient temperature;
C. preparing a polymethyl methacrylate/dimethyl siloxane super-hydrophobic film: injecting the electrospinning solution into an injector of an electrostatic spinning device, installing the injector on a propulsion pump, determining parameters of electrostatic spinning, starting the electrostatic spinning device to carry out electrostatic spinning on the electrospinning solution, and preparing a dimethyl siloxane/dimethyl siloxane super-hydrophobic membrane after completing the electrostatic spinning; wherein the parameters of electrospinning include: the applied voltage is 12kV, the receiving distance is 14cm, and the advancing speed is 1.3mL h-1。
Example 2:
a method for preparing PDMS-PMMA super-hydrophobic film based on electrostatic spinning comprises the following specific steps:
A. selecting raw materials: selecting polymethyl methacrylate (PDMS) and dimethyl siloxane (PMMA) as raw materials;
B. preparing an electrospinning solution: adding polymethyl methacrylate and dimethyl siloxane into a mixing container, wherein the mass ratio of the polymethyl methacrylate to the dimethyl siloxane is 1:1.5, then enabling the temperature of the mixing container to reach 55 ℃, stirring the mixed solution by using a magnetic stirrer under the temperature condition, continuing for 2 hours, placing the mixed solution in an environment with the temperature of 21 ℃ after the mixed solution is finished, and finishing the preparation of an electrospinning solution after the mixed solution is cooled to the ambient temperature;
C. preparing a polymethyl methacrylate/dimethyl siloxane super-hydrophobic film: injecting the electrospinning solution into an injector of an electrostatic spinning device, installing the injector on a propulsion pump, determining parameters of electrostatic spinning, starting the electrostatic spinning device to carry out electrostatic spinning on the electrospinning solution, and preparing a dimethyl siloxane/dimethyl siloxane super-hydrophobic membrane after completing the electrostatic spinning; wherein the parameters of electrospinning include: the applied voltage is 9kV, the receiving distance is 14cm, and the advancing speed is 0.7mL h-1。
Example 3:
a method for preparing PDMS-PMMA super-hydrophobic film based on electrostatic spinning comprises the following specific steps:
A. selecting raw materials: selecting polymethyl methacrylate (PDMS) and dimethyl siloxane (PMMA) as raw materials;
B. preparing an electrospinning solution: adding polymethyl methacrylate and dimethyl siloxane into a mixing container, wherein the mass ratio of the polymethyl methacrylate to the dimethyl siloxane is 1:1, then enabling the temperature of the mixing container to reach 60 ℃, stirring the mixed solution by adopting a magnetic stirrer under the temperature condition, continuing for 3 hours, placing the mixed solution in an environment with the temperature of 23 ℃ after the mixed solution is finished, and finishing the preparation of an electrospinning solution after the mixed solution is cooled to the ambient temperature;
C. preparing a polymethyl methacrylate/dimethyl siloxane super-hydrophobic film: injecting the electrospinning solution into an injector of an electrostatic spinning device, installing the injector on a propulsion pump, determining parameters of electrostatic spinning, starting the electrostatic spinning device to carry out electrostatic spinning on the electrospinning solution, and preparing a dimethyl siloxane/dimethyl siloxane super-hydrophobic membrane after completing the electrostatic spinning; wherein the parameters of electrospinning include: applied voltage 10.5kV, receiving distance 12cm, advancing speed 1.0mL h-1。
Example 4:
a method for preparing PDMS-PMMA super-hydrophobic film based on electrostatic spinning comprises the following specific steps:
A. selecting raw materials: selecting polymethyl methacrylate (PDMS) and dimethyl siloxane (PMMA) as raw materials;
B. preparing an electrospinning solution: adding polymethyl methacrylate and dimethyl siloxane into a mixing container, wherein the mass ratio of the polymethyl methacrylate to the dimethyl siloxane is 3:2, then enabling the temperature of the mixing container to reach 50 ℃, stirring the mixed solution by adopting a magnetic stirrer under the temperature condition, continuing for 2.8 hours, placing the mixed solution in an environment with the temperature of 25 ℃ after the mixed solution is finished, and finishing the preparation of an electrospinning solution after the mixed solution is cooled to the ambient temperature;
C. preparing a polymethyl methacrylate/dimethyl siloxane super-hydrophobic film: injecting the electrospinning solution into an injector of an electrostatic spinning device, installing the injector on a propulsion pump, determining parameters of electrostatic spinning, starting the electrostatic spinning device to carry out electrostatic spinning on the electrospinning solution, and preparing a dimethyl siloxane/dimethyl siloxane super-hydrophobic membrane after completing the electrostatic spinning; wherein the parameters of electrospinning include: the applied voltage is 13kV, the receiving distance is 15cm, and the advancing speed is 1.4mL h-1。
Example 5:
a method for preparing PDMS-PMMA super-hydrophobic film based on electrostatic spinning comprises the following specific steps:
A. selecting raw materials: selecting polymethyl methacrylate (PDMS) and dimethyl siloxane (PMMA) as raw materials;
B. preparing an electrospinning solution: adding polymethyl methacrylate and dimethyl siloxane into a mixing container, wherein the mass ratio of the polymethyl methacrylate to the dimethyl siloxane is 2:1, then enabling the temperature of the mixing container to reach 68 ℃, stirring the mixed solution by adopting a magnetic stirrer under the temperature condition, continuing for 2.4 hours, placing the mixed solution in an environment with the temperature of 20 ℃ after the mixed solution is finished, and finishing the preparation of an electrospinning solution after the mixed solution is cooled to the ambient temperature;
C. preparing a polymethyl methacrylate/dimethyl siloxane super-hydrophobic film: injecting the electrospinning solution into an injector of an electrostatic spinning device, installing the injector on a propulsion pump, determining parameters of electrostatic spinning, starting the electrostatic spinning device to carry out electrostatic spinning on the electrospinning solution, and preparing a dimethyl siloxane/dimethyl siloxane super-hydrophobic membrane after completing the electrostatic spinning; wherein the parameters of electrospinning include: applying voltage of 9kV, receiving distance of 9cm, and advancing speed of 0.7mL h-1。
The test proves that: as can be seen from fig. 1, the superhydrophobic films prepared under different mass ratios of PDMS-PMMA have the highest mass ratio of the static contact angle of Water (WCA) on the surface of the film at 1:1, the minimum fluctuation range (i.e. the most stable), and the highest concentration at the mass ratio of the Viscosity of the spinning solution (viscocity) at 2: 1; the larger the contact angle is, the larger the viscosity concentration of the spinning solution is, the better the performance of the super-hydrophobic membrane can be ensured, wherein the specific gravity of the contact angle on the performance is larger, so that the prepared super-hydrophobic membrane has the best performance when the mass ratio is 1:1. The performance of the superhydrophobic films prepared in the respective examples was also examined, and it was found that the superhydrophobic film prepared in example 3 had the best performance.
Claims (3)
1. A method for preparing PDMS-PMMA super-hydrophobic film based on electrostatic spinning is characterized by comprising the following specific steps:
A. selecting raw materials: selecting polymethyl methacrylate and dimethyl siloxane as raw materials;
B. preparing an electrospinning solution: adding polymethyl methacrylate and dimethyl siloxane into a mixing container, wherein the mass ratio of the polymethyl methacrylate to the dimethyl siloxane is (1-3) to (1-2), then enabling the temperature of the mixing container to reach 50-70 ℃, stirring the mixed solution by using a magnetic stirrer under the temperature condition, continuing for 2-3 hours, placing the mixed solution in an environment with the temperature of 20-25 ℃ after the mixed solution is finished, and completing the preparation of an electrospinning solution after the mixed solution is cooled to the ambient temperature;
C. preparing a polymethyl methacrylate/dimethyl siloxane super-hydrophobic film: spinning the electric spinningInjecting the silk solution into an injector of an electrostatic spinning device, mounting the injector on a propulsion pump, determining electrostatic spinning parameters, starting the electrostatic spinning device to carry out electrostatic spinning on the electrostatic spinning solution, and preparing a dimethyl siloxane/dimethyl siloxane super-hydrophobic membrane after completing the electrostatic spinning; wherein the parameters of electrospinning include: the applied voltage is 8-13 kV, the receiving distance is 8-16 cm, and the propelling speed is 0.6-1.5 mLh-1。
2. The method for preparing PDMS-PMMA superhydrophobic film based on electrostatic spinning according to claim 1, wherein the mass ratio of the polymethyl methacrylate to the dimethyl siloxane is 1:1.
3. The method for preparing PDMS-PMMA superhydrophobic film based on electrostatic spinning according to claim 1, wherein the electrostatic spinning parameters are that the applied voltage is 10.5kV, the receiving distance is 13cm, and the advancing speed is 1.0mL h-1。