CN110551463A - Special glue for medical instrument production and preparation method thereof - Google Patents
Special glue for medical instrument production and preparation method thereof Download PDFInfo
- Publication number
- CN110551463A CN110551463A CN201910741337.0A CN201910741337A CN110551463A CN 110551463 A CN110551463 A CN 110551463A CN 201910741337 A CN201910741337 A CN 201910741337A CN 110551463 A CN110551463 A CN 110551463A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- glue
- water
- aqueous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
the invention discloses special glue for producing medical instruments, which comprises the following components in parts by weight: 40-50 parts of modified polyolefin aqueous resin liquid, 10-20 parts of polyester aqueous resin emulsion, 30-50 parts of anion tourmaline, 25-30 parts of formaldehyde, 4-7 parts of oxidant, 5-7 parts of chain-adjusting agent, 0-1 part of aqueous wetting and leveling agent, 0-1 part of aqueous defoaming agent, 0-1 part of pH regulator and 10-30 parts of deionized water. By adopting the technical scheme, the chain-adjusting agent is added, so that the storage stability is excellent, and the storage can be carried out for more than 12 months at normal temperature.
Description
Technical Field
the invention relates to the technical field of medical instruments, in particular to special glue for medical instrument production and a preparation method thereof.
background
Medical instruments are closely related to human health, and are a rapidly developing industry, and glue is essential in the production process of the medical instruments, such as manufacturing, packaging and the like. However, the glue used in the field of medical devices has high demand, so that no glue with ideal performance exists in the glue for producing the medical devices at present, which is always difficult for enterprises in the industry and brings troubles and losses to the enterprises in the industry.
Therefore, at present, water-based hot melt adhesives are generally used to replace solid hot melt adhesives, but the adhesives currently used for medical devices still have some problems.
The water-based hot glue has poor antibacterial effect, and the antibacterial effect is particularly important for medical instruments in the using process. In addition, the storage stability is poor, and the shelf life is only 3-6 months generally.
disclosure of Invention
According to the defects of the prior art, the invention provides the special glue for producing the medical instrument and the preparation method thereof, which have wide adaptability to the base material, small influence on the air permeability of the dialyzing paper, stable storage and good antibacterial effect.
In order to solve the technical problems, the technical scheme of the invention is as follows:
The glue special for producing the medical instruments comprises the following components in parts by weight: 40-50 parts of modified polyolefin aqueous resin liquid, 10-20 parts of polyester aqueous resin emulsion, 30-50 parts of anion tourmaline, 25-30 parts of formaldehyde, 4-7 parts of oxidant, 5-7 parts of chain-regulating agent, 0-1 part of aqueous wetting and leveling agent, 0-1 part of aqueous defoaming agent, 0-1 part of pH regulator and 10-30 parts of deionized water.
Preferably, the anion tourmaline is 400-mesh anion tourmaline powder.
Preferably, the oxidizing agent is a 15% strength sodium bicarbonate solution.
The invention provides a special glue for producing medical instruments, which comprises the following steps:
Step one, uniformly mixing the weighed modified polyolefin water-based resin liquid and the polyester water-based resin emulsion, and standing for 15 minutes;
Step two, dripping formaldehyde for condensation reaction;
Adding a water-based wetting leveling agent, a water-based defoaming agent and a pH regulator, further adding deionized water, keeping stirring at a high speed for 30 minutes, and standing for 1 hour;
Adding an oxidant and a chain agent, and keeping the temperature for 1 hour at the temperature of 45 ℃;
And step five, adding the anion tourmaline, and fully stirring for 30 minutes to prepare the glue containing the anion powder.
The invention has the following characteristics and beneficial effects:
By adopting the technical scheme, the whole-chain agent is added, so that the storage stability is excellent, the storage period can be more than 12 months at the normal temperature, and in addition, the anion tourmaline is added, so that the antibacterial agent has a good antibacterial effect, and the antibacterial effect on the production of medical instruments is particularly obvious.
Detailed Description
It should be noted that the embodiments and features of the embodiments may be combined with each other without conflict.
In the description of the present invention, it is to be understood that the terms "central," "longitudinal," "lateral," "upper," "lower," "front," "rear," "left," "right," "vertical," "horizontal," "top," "bottom," "inner," "outer," and the like are used in an orientation or positional relationship that is indicative of but not limiting of the present invention, merely for convenience in describing and simplifying the description, and do not indicate or imply that the device or element being referred to must have a particular orientation, be constructed and operated in a particular orientation. Furthermore, the terms "first," "second," and the like are used for descriptive purposes only and are not to be construed as indicating or implying relative importance or implicitly indicating the number of technical features indicated. Thus, a feature defined as "first," "second," etc. may explicitly or implicitly include one or more of that feature. In the description of the present invention, "a plurality" means two or more unless otherwise specified.
In the description of the present invention, it should be noted that unless otherwise explicitly stated or limited, the terms "mounted," "connected," and "connected" are to be construed broadly, e.g., as meaning either a fixed connection, a removable connection, or an integral connection; can be mechanically or electrically connected; they may be connected directly or indirectly through intervening media, or they may be interconnected between two elements. The specific meanings of the above terms in the present invention can be understood by those skilled in the art through specific situations.
Example 1
The invention provides special glue for producing medical instruments, which comprises the following components in parts by weight: 40 parts of modified polyolefin aqueous resin liquid, 10 parts of polyester aqueous resin emulsion, 30 parts of anion tourmaline, 25 parts of formaldehyde, 4 parts of oxidant, 5 parts of chain-regulating agent and 10 parts of deionized water.
Specifically, the anion tourmaline is 400-mesh anion tourmaline powder.
Specifically, the oxidizing agent is a sodium bicarbonate solution with the concentration of 15%.
Example 2
the invention provides special glue for producing medical instruments, which comprises the following components in parts by weight: 45 parts of modified polyolefin aqueous resin liquid, 15 parts of polyester aqueous resin emulsion, 40 parts of anion tourmaline, 27 parts of formaldehyde, 6 parts of oxidant, 5 parts of chain-regulating agent, 0.5 part of aqueous wetting and leveling agent, 0.5 part of aqueous defoaming agent, 0.5 part of pH regulator and 20 parts of deionized water.
Example 3
The invention provides special glue for producing medical instruments, which comprises the following components in parts by weight: 50 parts of modified polyolefin aqueous resin liquid, 20 parts of polyester aqueous resin emulsion, 50 parts of anion tourmaline, 30 parts of formaldehyde, 7 parts of oxidant, 7 parts of chain-regulating agent, 1 part of aqueous wetting and leveling agent, 1 part of aqueous defoaming agent, 1 part of pH regulator and 30 parts of deionized water.
The invention provides a special glue for producing medical instruments, which comprises the following steps:
Step one, uniformly mixing the weighed modified polyolefin water-based resin liquid and the polyester water-based resin emulsion, and standing for 15 minutes;
Step two, dripping formaldehyde for condensation reaction;
Adding a water-based wetting leveling agent, a water-based defoaming agent and a pH regulator, further adding deionized water, keeping stirring at a high speed for 30 minutes, and standing for 1 hour;
adding an oxidant and a chain agent, and keeping the temperature for 1 hour at the temperature of 45 ℃;
And step five, adding the anion tourmaline, and fully stirring for 30 minutes to prepare the glue containing the anion powder.
Specifically, the condensation reaction in the second step is to keep the temperature until the solution becomes half milk white after the formaldehyde is dripped, namely the condensation end point.
according to researches, the hydrogen bond is the source of the influence of the glue on the stability, so that the acting force of the hydrogen bond needs to be reduced to solve the stability problem, namely the number of hydroxyl groups is reduced, the number of-OH is reduced under the condition of adopting a certain temperature, meanwhile, a six-membered ring is formed to the maximum extent, the steric hindrance is increased, and meanwhile, a chain-regulating agent is added to reduce the branched chain degree.
in addition, formaldehyde is harmful to human body and must be disposed of, so that an oxidant is required to be added to oxidize formaldehyde into carbon dioxide and water.
The prepared glue contains the anion tourmaline, so that the glue has a good antibacterial effect, and the antibacterial effect on the production of medical instruments is particularly obvious.
the embodiments of the present invention have been described in detail, but the present invention is not limited to the described embodiments. It will be apparent to those skilled in the art that various changes, modifications, substitutions and alterations can be made in the embodiments, including the components, without departing from the principles and spirit of the invention, and still fall within the scope of the invention.
Claims (4)
1. the glue special for producing the medical instruments is characterized by comprising the following components in parts by weight: 40-50 parts of modified polyolefin aqueous resin liquid, 10-20 parts of polyester aqueous resin emulsion, 30-50 parts of anion tourmaline, 25-30 parts of formaldehyde, 4-7 parts of oxidant, 5-7 parts of chain-adjusting agent, 0-1 part of aqueous wetting and leveling agent, 0-1 part of aqueous defoaming agent, 0-1 part of pH regulator and 10-30 parts of deionized water.
2. the glue special for producing the medical instruments according to claim 1, wherein the anion tourmaline is 400-mesh anion tourmaline powder.
3. The glue specially used for medical equipment production according to claim 1, wherein the oxidizing agent is sodium bicarbonate solution with a concentration of 15%.
4. The preparation method of the glue special for the medical instrument production, which is described in any one of claims 1 to 3, is characterized by comprising the following steps:
step one, uniformly mixing the weighed modified polyolefin water-based resin liquid and the polyester water-based resin emulsion, and standing for 15 minutes;
Step two, dripping formaldehyde for condensation reaction;
Adding a water-based wetting and leveling agent, a water-based defoaming agent and a pH regulator, further adding deionized water, keeping stirring at a high speed for 30 minutes, and standing for 1 hour;
adding an oxidant and a chain agent, and keeping the temperature for 1 hour at the temperature of 45 ℃;
And step five, adding the anion tourmaline, and fully stirring for 30 minutes to prepare the glue containing the anion powder.