CN110510962A - A kind of light heat-insulation wall material and preparation method thereof that soundproof effect is good - Google Patents
A kind of light heat-insulation wall material and preparation method thereof that soundproof effect is good Download PDFInfo
- Publication number
- CN110510962A CN110510962A CN201910946270.4A CN201910946270A CN110510962A CN 110510962 A CN110510962 A CN 110510962A CN 201910946270 A CN201910946270 A CN 201910946270A CN 110510962 A CN110510962 A CN 110510962A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulation wall
- light heat
- soundproof effect
- wall material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of good light heat-insulation wall materials and preparation method thereof of soundproof effect, are made by following raw material weight number proportion: 20-40 parts of portland cement, 5-10 parts of paraffin, 15-35 parts of ore foamed material, 10-30 parts of gangue, 1-4 parts of methyl hyetellose, 20-40 parts of flyash, 5-25 parts of mountain flour, 30-60 parts of water, 5-15 parts of wood fibre, 10-30 parts of expanded perlite, 4-12 parts of sodium carbonate, 25-55 parts of borax, 20-50 parts of quartz.By facts have proved, light solid composite wall plate can effectively improve the construction quality of building in construction projects, the use value of building is fully played, its economic results in society is improved, and the application better meets the social high request to construction material thermal insulation property, quality now.
Description
Technical field
The present invention relates to materials for wall more particularly to a kind of soundproof effect good light heat-insulation wall materials and its preparation side
Method.
Background technique
With the continuous social and economic development, living standards of the people have also obtained certain raising, in such society's back
Under scape, we also have higher requirement architectural engineering.In recent years, people increasingly focus on environmental protection, energy conservation in life,
Also gradually energy-saving and environment-friendly theory is dissolved into architectural engineering, construction material as environment protection architecture engineering important content it
One, people are even more to require its performance.Various energy-saving materials are had already appeared in current market, this indicates China
Energy saving building is more and more, improves the development level of building trade.Light solid composite wall plate is a kind of novel energy-saving ring
Protect material.
Novel energy-saving environment-friendly material, it is therefore intended that the luminous energy in nature, thermal energy is made full use of to reach saving with these materials
Fossil energy reduces pollution and garbage emission.These material some come into the application stage.According to some data, following room
Room wall can at least save energy using natural heat energy using air entrained concrete or micropore concrete composite block or multi-functional composite wall material
Source 30%.Following door and window uses vacuum LOW-E glass, energy conservation 30%, and has good soundproof effect；Vacuum Low emissivity glass
Glass, can save energy 30-40%, and 10 years saving petroleum 1400kg/m2 economize on electricity 5000 degree every square metre for 30 years.SUN-E glass can subtract
Few solar radiation, is suitable for south, reduces the usage amount of air-conditioning.The following cladding will extensively use glass, can economize on resources 30
Times, and due to using natural lighting, can save lighting electricity consumption.And door and window industry will save 630,000 tons of standard coal every year.Not
The roof come will use greening roof, i.e., drought-enduring grass seeds is planted on roof, and top layer heat preservation may be implemented, and reduce building top layer empty
Calling amount, using electricity wisely.In addition also capable of purifying air, reduce tropical island effect.New material can be following building conservation in a word
The energy about 75%.
With the continuous social and economic development, living standards of the people have also obtained certain raising, in such society's back
Under scape, we also have higher requirement architectural engineering.In recent years, people increasingly focus on environmental protection, energy conservation in life,
Also gradually energy-saving and environment-friendly theory is dissolved into architectural engineering, construction material as environment protection architecture engineering important content it
One, people are even more to require its performance.Various energy-saving materials are had already appeared in current market, this indicates China
Energy saving building is more and more, improves the development level of building trade.Light solid composite wall plate is a kind of novel energy-saving ring
Material is protected, hereafter this is furtherd investigate.After measured, the weight of each unit area light solid composite wall plate is too late
The weight of two-sided plastering masonry after 120mm.So we can effectively reduce this material application in building structure
The weight of wall, and the bearing capacity of beam column can be reduced, interval can be played the role of in the construction process.Relative to common
Masonry structure for, it have biggish superiority.
Summary of the invention
The technical issues of solution:
The application provides a kind of sound insulation to the high request of construction material thermal insulation property, quality to meet society now
The good light heat-insulation wall material and preparation method thereof of effect.
A kind of light heat-insulation wall material that soundproof effect is good is made: silicate cement by following raw material weight number proportion
20-40 parts of mud, 5-10 parts of paraffin, 15-35 parts of ore foamed material, 10-30 parts of gangue, 1-4 parts of methyl hyetellose, powder
20-40 parts of coal ash, 5-25 parts of mountain flour, 30-60 parts of water, 5-15 parts of wood fibre, 10-30 parts of expanded perlite, sodium carbonate 4-12
Part, 25-55 parts of borax, 20-50 parts of quartz.
Further, the good light heat-insulation wall material of a kind of soundproof effect is matched by following raw material weight number
Than being made: 30 parts of portland cement, 8 parts of paraffin, 25 parts of ore foamed material, 20 parts of gangue, 3 parts of methyl hyetellose,
30 parts of flyash, 15 parts of mountain flour, 45 parts of water, 10 parts of wood fibre, 20 parts of expanded perlite, 8 parts of sodium carbonate, 40 parts of borax, stone
40 parts of diamond stone.
Further, the preparation method of the good light heat-insulation wall material of a kind of soundproof effect, first by silicate
Cement, paraffin, ore foamed material, gangue, flyash, borax, mountain flour, quartz are put into roller and blend, and filter out grain
Diameter is less than 1.The mineral dust of 5mm；Then methyl hyetellose, water, wood fibre, expanded perlite, quartz sand, carbon is added
Sour sodium powder end, is heated while stirring；Two stages high-temperature process is carried out respectively, and the first stage raises the temperature to 500 DEG C, and maintains
28-40 minutes, second stage raised the temperature to 1400 DEG C, and maintained 30-45 minutes；It is finally down to room temperature naturally, to obtain
Obtain light heat-insulation wall material.
Beneficial effect
Good light heat-insulation wall material of a kind of soundproof effect of the present invention and preparation method thereof uses the above technical side
Case, light solid composite material because have many advantages, such as high-performance, high quality, energy conservation and environmental protection and by people in the industry's extensive concern,
And more and more it is used in construction projects, by it was verified that light solid composite wall plate in construction projects may be used
With the effective construction quality for improving building, the use value of building is fully played, and improves its economic results in society,
The application better meets the social high request to construction material thermal insulation property, quality now.
Specific embodiment
Embodiment 1:
A kind of light heat-insulation wall material that soundproof effect is good is made: silicate cement by following raw material weight number proportion
20 parts of mud, 5 parts of paraffin, 15 parts of ore foamed material, 10 parts of gangue, 1 part of methyl hyetellose, 20 parts of flyash, mountain flour 5
Part, 30 parts of water, 5 parts of wood fibre, 10 parts of expanded perlite, 4 parts of sodium carbonate, 25 parts of borax, 20 parts of quartz.
A kind of preparation method of the good light heat-insulation wall material of the soundproof effect, first by portland cement, paraffin,
Ore foamed material, gangue, flyash, borax, mountain flour, quartz are put into roller and blend, and filter out partial size less than 1.5mm
Mineral dust；Then methyl hyetellose, water, wood fibre, expanded perlite, quartz sand, powdered sodium carbonate, side is added
Stir side heating；Two stages high-temperature process is carried out respectively, the first stage raises the temperature to 500 DEG C, and maintains 28 minutes, and second
Stage raises the temperature to 1400 DEG C, and maintains 30 minutes；It is finally down to room temperature naturally, to obtain light insulating wall material
Material.
Embodiment 2:
A kind of light heat-insulation wall material that soundproof effect is good is made: silicate cement by following raw material weight number proportion
30 parts of mud, 8 parts of paraffin, 25 parts of ore foamed material, 20 parts of gangue, 3 parts of methyl hyetellose, 30 parts of flyash, mountain flour
15 parts, 45 parts of water, 10 parts of wood fibre, 20 parts of expanded perlite, 8 parts of sodium carbonate, 40 parts of borax, 40 parts of quartz.
A kind of preparation method of the good light heat-insulation wall material of the soundproof effect, first by portland cement, paraffin,
Ore foamed material, gangue, flyash, borax, mountain flour, quartz are put into roller and blend, and filter out partial size less than 1.5mm
Mineral dust；Then methyl hyetellose, water, wood fibre, expanded perlite, quartz sand, powdered sodium carbonate, side is added
Stir side heating；Two stages high-temperature process is carried out respectively, the first stage raises the temperature to 500 DEG C, and maintains 35 minutes, and second
Stage raises the temperature to 1400 DEG C, and maintains 40 minutes；It is finally down to room temperature naturally, to obtain light insulating wall material
Material.
Embodiment 3:
A kind of light heat-insulation wall material that soundproof effect is good is made: silicate cement by following raw material weight number proportion
40 parts of mud, 10 parts of paraffin, 35 parts of ore foamed material, 30 parts of gangue, 4 parts of methyl hyetellose, 40 parts of flyash, mountain flour
25 parts, 60 parts of water, 15 parts of wood fibre, 30 parts of expanded perlite, 12 parts of sodium carbonate, 55 parts of borax, 50 parts of quartz.
A kind of preparation method of the good light heat-insulation wall material of the soundproof effect, first by portland cement, paraffin,
Ore foamed material, gangue, flyash, borax, mountain flour, quartz are put into roller and blend, and filter out partial size less than 1.5mm
Mineral dust；Then methyl hyetellose, water, wood fibre, expanded perlite, quartz sand, powdered sodium carbonate, side is added
Stir side heating；Two stages high-temperature process is carried out respectively, the first stage raises the temperature to 500 DEG C, and maintains 40 minutes, and second
Stage raises the temperature to 1400 DEG C, and maintains 45 minutes；It is finally down to room temperature naturally, to obtain light insulating wall material
Material.
Claims (3)
1. a kind of good light heat-insulation wall material of soundproof effect, which is characterized in that be made by following raw material weight number proportion:
20-40 parts of portland cement, 5-10 parts of paraffin, 15-35 parts of ore foamed material, 10-30 parts of gangue, methyl hyetellose
1-4 parts, 20-40 parts of flyash, 5-25 parts of mountain flour, 30-60 parts of water, 5-15 parts of wood fibre, 10-30 parts of expanded perlite, carbon
Sour sodium 4-12 parts, 25-55 parts of borax, 20-50 parts of quartz.
2. a kind of good light heat-insulation wall material of soundproof effect according to claim 1, which is characterized in that press following original
Material parts by weight proportion is made: 30 parts of portland cement, 8 parts of paraffin, 25 parts of ore foamed material, 20 parts of gangue, methyl hydroxyl
3 parts of second cellulose, 30 parts of flyash, 15 parts of mountain flour, 45 parts of water, 10 parts of wood fibre, 20 parts of expanded perlite, 8 parts of sodium carbonate,
40 parts of borax, 40 parts of quartz.
3. a kind of preparation method of the good light heat-insulation wall material of soundproof effect according to claim 1, feature exist
In first portland cement, paraffin, ore foamed material, gangue, flyash, borax, mountain flour, quartz are put into roller
It blends, filters out partial size less than 1.The mineral dust of 5mm；Then methyl hyetellose, water, wood fibre, expansion treasure is added
Zhu Yan, quartz sand, powdered sodium carbonate, are heated while stirring；Two stages high-temperature process is carried out respectively, and the first stage increases temperature
It to 500 DEG C, and maintains 28-40 minutes, second stage raises the temperature to 1400 DEG C, and maintains 30-45 minutes；Finally drop naturally
To room temperature, to obtain light heat-insulation wall material.