CN110510927A - A kind of energy saving and environment friendly composite floor brick and preparation method thereof - Google Patents
A kind of energy saving and environment friendly composite floor brick and preparation method thereof Download PDFInfo
- Publication number
- CN110510927A CN110510927A CN201810492793.1A CN201810492793A CN110510927A CN 110510927 A CN110510927 A CN 110510927A CN 201810492793 A CN201810492793 A CN 201810492793A CN 110510927 A CN110510927 A CN 110510927A
- Authority
- CN
- China
- Prior art keywords
- parts
- energy saving
- environment friendly
- chlorite
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of energy saving and environment friendly composite floor bricks, including coal slime: 35 parts -40 parts；Chlorite: 25 parts -30 parts；Slag powders: 20 parts -26 parts；Acetylacetonate: 5 parts -12 parts；Stearate: 3 parts -6 parts；Fire retardant: 3 parts；Attapulgite: 12 parts -20 parts；Pearl sand: 4 parts -8 parts；Wood fibre: 7 parts -12 parts；Diatomite: 5 parts -10 parts；Broken ceramics: 2 parts -5 parts；Corvic: 13 parts -16 parts；The pungent vinegar of phthalic acid two: 18 parts -24 parts；Polyethylene beads: 5 parts -10 parts；Soybean fiber: 2 parts -6 parts.Compared with prior art, the present invention has that skid resistance is good and wearability is good, energy-saving and environment-friendly beneficial effect.
Description
Technical field
The invention belongs to art work field more particularly to a kind of energy saving and environment friendly composite floor brick and its production sides
Method.
Background technique
Floor tile, also known as floor tile.A kind of floor decorative material, is fired with clay, and specification is a variety of.It is chiefly used in public
The ground and floor of building and civil buildings.In numerous floor decorative materials, floor tile becomes the first choice of consumer.Especially
The selection of building tile is more focused on, it is the association durable consumer goods tightened around house property, therefore when consumption
Take on very typical immobility consumption feature, that is to say, that the building tile consumption of common people is bought simultaneously once being formed
Paving is good, then unless it is absolutely necessary, being usually will not be light easily changeable, and changing hands even up to this house can just fill again
It repairs.So the requirement to floor tile is higher and higher, it is desirable that floor tile is with quality is solid, is convenient to clean, is heat-resisting, is wear-resisting, is acidproof
Alkali, it is impermeable the advantages that, and require now environmental protection and energy-saving effect.But traditional floor tile comprehensive performance is bad, no
Have energy saving, and has certain pollution.Therefore, new technology is needed to improve the deficiencies in the prior art.
Summary of the invention
Goal of the invention: the object of the present invention is to provide a kind of energy saving and environment friendly composite floor brick and preparation method thereof,
Be able to solve existing floor brick skid resistance difference and wear no resistance, not energy-efficient and environmental protection the problem of.
A kind of technical solution: energy saving and environment friendly composite floor brick, it is characterised in that: including coal slime, chlorite, slag
Powder, acetylacetonate, stearate, fire retardant, attapulgite, pearl sand, wood fibre, diatomite, broken ceramics, polyvinyl chloride
Resin, the pungent vinegar of phthalic acid two, polyethylene beads, soybean fiber；The coal slime, chlorite, slag powders, acetylacetonate,
Stearate, fire retardant, attapulgite, pearl sand, wood fibre, diatomite, broken ceramics, Corvic, O-phthalic
Sour two pungent vinegar, polyethylene beads, soybean fiber are made by weight and by following component: coal slime: 35 parts -40 parts；Chlorite:
25 parts -30 parts；Slag powders: 20 parts -26 parts；Acetylacetonate: 5 parts -12 parts；Stearate: 3 parts -6 parts；Fire retardant: 3
Part；Attapulgite: 12 parts -20 parts；Pearl sand: 4 parts -8 parts；Wood fibre: 7 parts -12 parts；Diatomite: 5 parts -10 parts；It is broken
Ceramics: 2 parts -5 parts；Corvic: 13 parts -16 parts；The pungent vinegar of phthalic acid two: 18 parts -24 parts；Polyethylene beads: 5
- 10 parts of part；Soybean fiber: 2 parts -6 parts.
Wherein, which includes 35 parts of coal slime, and 25 parts of chlorite, 20 parts of slag powders, 5 parts of acetylacetonate, stearic acid
3 parts of salt, 3 parts of fire retardant, 12 parts of attapulgite, 4 parts of pearl sand, 7 parts of wood fibre, 5 parts of diatomite, broken ceramic 2 parts, polychlorostyrene second
13 parts of olefine resin, two 18 parts of pungent vinegar of phthalic acid, 5 parts of polyethylene beads, 2 parts of soybean fiber.
Wherein, which includes 40 parts of coal slime, and 30 parts of chlorite, 26 parts of slag powders, 12 parts of acetylacetonate, stearic acid
6 parts of salt, 3 parts of fire retardant, 20 parts of attapulgite, 8 parts of pearl sand, 12 parts of wood fibre, 10 parts of diatomite, broken ceramic 5 parts, polychlorostyrene
16 parts of vinyl, two 24 parts of pungent vinegar of phthalic acid, 10 parts of polyethylene beads, 6 parts of soybean fiber.
Wherein, which includes 37 parts of coal slime, and 28 parts of chlorite, 23 parts of slag powders, 8 parts of acetylacetonate, stearic acid
5 parts of salt, 3 parts of fire retardant, 16 parts of attapulgite, 6 parts of pearl sand, 9 parts of wood fibre, 8 parts of diatomite, broken ceramic 3.5 parts, polychlorostyrene
14.5 parts of vinyl, two 21 parts of pungent vinegar of phthalic acid, 7.5 parts of polyethylene beads, 4 parts of soybean fiber.
A kind of production method of energy saving and environment friendly composite floor brick, it is characterised in that: the following steps are included:
(1) according to raw material proportioning, by coal slime, chlorite, slag powders, acetylacetonate, stearate, fire retardant, bumps
It is stick soil, pearl sand, wood fibre, diatomite, broken ceramics, Corvic, the pungent vinegar of phthalic acid two, polyethylene beads, big
Stirrer for mixing is added in beans fiber, and revolving speed is 1300 revs/min, and the time is 22-32 minutes, and temperature is 100 DEG C, is mixed
Object is spare；
(2) mixture obtained in step (1) is added at a temperature of 128 DEG C of pelletizer and is granulated, the grain that will be obtained
After material is cooling, a kind of energy saving and environment friendly composite floor brick is obtained；
(3) granular composite material floor brick obtained in step (2) is passed through into extruding production line, extrusion temperature control
Between 210 DEG C -225 DEG C, squeeze out blank after, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain a kind of energy conservation and environmental protection
Type composite floor brick.
The utility model has the advantages that compared with prior art, the present invention provides a kind of energy saving and environment friendly composite floor brick and its production
Method, be able to solve existing floor brick skid resistance difference and wear no resistance, not energy-efficient and environmental protection the problem of.
Specific embodiment
Technical scheme is described further below.
A kind of energy saving and environment friendly composite floor brick, it is characterised in that: including coal slime, chlorite, slag powders, levulinic
Ketone salt, stearate, fire retardant, attapulgite, pearl sand, wood fibre, diatomite, broken ceramics, Corvic, adjacent benzene
The pungent vinegar of dioctyl phthalate two, polyethylene beads, soybean fiber；The coal slime, chlorite, slag powders, acetylacetonate, stearate,
Fire retardant, attapulgite, pearl sand, wood fibre, diatomite, broken ceramics, Corvic, the pungent vinegar of phthalic acid two,
Polyethylene beads, soybean fiber are made by weight and by following component: coal slime: 35 parts -40 parts；Chlorite: 25 parts -30
Part；Slag powders: 20 parts -26 parts；Acetylacetonate: 5 parts -12 parts；Stearate: 3 parts -6 parts；Fire retardant: 3 parts；Concave convex rod
Soil: 12 parts -20 parts；Pearl sand: 4 parts -8 parts；Wood fibre: 7 parts -12 parts；Diatomite: 5 parts -10 parts；Broken ceramics: 2
- 5 parts of part；Corvic: 13 parts -16 parts；The pungent vinegar of phthalic acid two: 18 parts -24 parts；Polyethylene beads: 5 parts -10
Part；Soybean fiber: 2 parts -6 parts.
Embodiment 1: the energy saving and environment friendly composite floor brick includes 35 parts of coal slime, and 25 parts of chlorite, 20 parts of slag powders,
5 parts of acetylacetonate, 3 parts of stearate, 3 parts of fire retardant, 12 parts of attapulgite, 4 parts of pearl sand, 7 parts of wood fibre, diatomite
5 parts, broken ceramic 2 parts, 13 parts of Corvic, two 18 parts of pungent vinegar of phthalic acid, 5 parts of polyethylene beads, 2 parts of soybean fiber.
When preparation, according to raw material proportioning, by coal slime, chlorite, slag powders, acetylacetonate, stearate, fire retardant, attapulgite,
Pearl sand, wood fibre, diatomite, broken ceramics, Corvic, the pungent vinegar of phthalic acid two, polyethylene beads, soybean fiber
Stirrer for mixing is added, revolving speed is 1300 revs/min, and the time is 22-32 minutes, and temperature is 100 DEG C, and it is standby to obtain mixture
With；Obtained mixture is added at a temperature of 128 DEG C of pelletizer and is granulated, after the cooling of obtained pellet, obtains one kind
Energy saving and environment friendly composite floor brick；By obtained granular composite material floor brick by extruding production line, squeeze
Out temperature control between 210 DEG C -225 DEG C, squeeze out blank after, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain one
The energy saving and environment friendly composite floor brick of kind.
Embodiment 2: the energy saving and environment friendly composite floor brick includes 40 parts of coal slime, and 30 parts of chlorite, 26 parts of slag powders,
12 parts of acetylacetonate, 6 parts of stearate, 3 parts of fire retardant, 20 parts of attapulgite, 8 parts of pearl sand, 12 parts of wood fibre, diatom
10 parts of soil, broken ceramic 5 parts, 16 parts of Corvic, two 24 parts of pungent vinegar of phthalic acid, 10 parts of polyethylene beads, soybean fiber 6
Part.When preparation, according to raw material proportioning, by coal slime, chlorite, slag powders, acetylacetonate, stearate, fire retardant, concave convex rod
Soil, pearl sand, wood fibre, diatomite, broken ceramics, Corvic, the pungent vinegar of phthalic acid two, polyethylene beads, soybean
Stirrer for mixing is added in fiber, and revolving speed is 1300 revs/min, and the time is 22-32 minutes, and temperature is 100 DEG C, obtains mixture
It is spare；Obtained mixture is added at a temperature of 128 DEG C of pelletizer and is granulated, after the cooling of obtained pellet, obtains one
The energy saving and environment friendly composite floor brick of kind；Obtained granular composite material floor brick is passed through into extruding production line,
Extrusion temperature control between 210 DEG C -225 DEG C, squeeze out blank after, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain
A kind of energy saving and environment friendly composite floor brick.
Embodiment 3: the energy saving and environment friendly composite floor brick includes 37 parts of coal slime, and 28 parts of chlorite, 23 parts of slag powders,
8 parts of acetylacetonate, 5 parts of stearate, 3 parts of fire retardant, 16 parts of attapulgite, 6 parts of pearl sand, 9 parts of wood fibre, diatomite
8 parts, broken ceramic 3.5 parts, 14.5 parts of Corvic, two 21 parts of pungent vinegar of phthalic acid, 7.5 parts of polyethylene beads, soybean is fine
4 parts of dimension.When preparation, according to raw material proportioning, by coal slime, chlorite, slag powders, acetylacetonate, stearate, fire retardant, recessed
Convex stick soil, pearl sand, wood fibre, diatomite, broken ceramics, Corvic, the pungent vinegar of phthalic acid two, polyethylene beads,
Stirrer for mixing is added in soybean fiber, and revolving speed is 1300 revs/min, and the time is 22-32 minutes, and temperature is 100 DEG C, is mixed
It is spare to close object；Obtained mixture is added at a temperature of 128 DEG C of pelletizer and is granulated, after the cooling of obtained pellet, is obtained
To a kind of energy saving and environment friendly composite floor brick；Obtained granular composite material floor brick is passed through into extrusion
Line, extrusion temperature control between 210 DEG C -225 DEG C, squeeze out blank after, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain
To a kind of energy saving and environment friendly composite floor brick.
Claims (5)
1. a kind of energy saving and environment friendly composite floor brick, it is characterised in that: including coal slime, chlorite, slag powders, acetylacetone,2,4-pentanedione
Salt, stearate, fire retardant, attapulgite, pearl sand, wood fibre, diatomite, broken ceramics, Corvic, adjacent benzene two
The pungent vinegar of formic acid two, polyethylene beads, soybean fiber；The coal slime, chlorite, slag powders, acetylacetonate, stearate, resistance
It fires agent, attapulgite, pearl sand, wood fibre, diatomite, broken ceramics, Corvic, the pungent vinegar of phthalic acid two, gather
Ethylene pearl, soybean fiber are made by weight and by following component: coal slime: 35 parts -40 parts；Chlorite: 25 parts -30 parts；
Slag powders: 20 parts -26 parts；Acetylacetonate: 5 parts -12 parts；Stearate: 3 parts -6 parts；Fire retardant: 3 parts；Attapulgite:
12 parts -20 parts；Pearl sand: 4 parts -8 parts；Wood fibre: 7 parts -12 parts；Diatomite: 5 parts -10 parts；Broken ceramics: 2 parts -5
Part；Corvic: 13 parts -16 parts；The pungent vinegar of phthalic acid two: 18 parts -24 parts；Polyethylene beads: 5 parts -10 parts；Greatly
Beans fiber: 2 parts -6 parts.
2. a kind of energy saving and environment friendly composite floor brick according to claim 1, it is characterised in that: the floor tile includes
35 parts of coal slime, 25 parts of chlorite, 20 parts of slag powders, 5 parts of acetylacetonate, 3 parts of stearate, 3 parts of fire retardant, attapulgite 12
Part, 4 parts of pearl sand, 7 parts of wood fibre, 5 parts of diatomite, broken ceramic 2 parts, 13 parts of Corvic, phthalic acid two is pungent
18 parts of vinegar, 5 parts of polyethylene beads, 2 parts of soybean fiber.
3. a kind of energy saving and environment friendly composite floor brick according to claim 1, it is characterised in that: the floor tile includes
40 parts of coal slime, 30 parts of chlorite, 26 parts of slag powders, 12 parts of acetylacetonate, 6 parts of stearate, 3 parts of fire retardant, attapulgite
20 parts, 8 parts of pearl sand, 12 parts of wood fibre, 10 parts of diatomite, broken ceramic 5 parts, 16 parts of Corvic, phthalic acid
Two 24 parts of pungent vinegar, 10 parts of polyethylene beads, 6 parts of soybean fiber.
4. a kind of energy saving and environment friendly composite floor brick according to claim 1, it is characterised in that: the floor tile includes
37 parts of coal slime, 28 parts of chlorite, 23 parts of slag powders, 8 parts of acetylacetonate, 5 parts of stearate, 3 parts of fire retardant, attapulgite 16
Part, 6 parts of pearl sand, 9 parts of wood fibre, 8 parts of diatomite, broken ceramic 3.5 parts, 14.5 parts of Corvic, phthalic acid
Two 21 parts of pungent vinegar, 7.5 parts of polyethylene beads, 4 parts of soybean fiber.
5. a kind of production method of energy saving and environment friendly composite floor brick, it is characterised in that: the following steps are included:
(1) according to raw material proportioning, by coal slime, chlorite, slag powders, acetylacetonate, stearate, fire retardant, attapulgite,
Pearl sand, wood fibre, diatomite, broken ceramics, Corvic, the pungent vinegar of phthalic acid two, polyethylene beads, soybean fiber
Stirrer for mixing is added, revolving speed is 1300 revs/min, and the time is 22-32 minutes, and temperature is 100 DEG C, and it is standby to obtain mixture
With；
(2) mixture obtained in step (1) is added at a temperature of 128 DEG C of pelletizer and is granulated, obtained pellet is cold
But after, a kind of energy saving and environment friendly composite floor brick is obtained；
(3) by granular composite material floor brick obtained in step (2) by extruding production line, extrusion temperature control exists
Between 210 DEG C -225 DEG C, after squeezing out blank, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain a kind of energy saving and environment friendly
Composite floor brick.