CN110497664A - A kind of aluminium plastic composite packaging film and preparation method thereof - Google Patents
A kind of aluminium plastic composite packaging film and preparation method thereof Download PDFInfo
- Publication number
- CN110497664A CN110497664A CN201810479404.1A CN201810479404A CN110497664A CN 110497664 A CN110497664 A CN 110497664A CN 201810479404 A CN201810479404 A CN 201810479404A CN 110497664 A CN110497664 A CN 110497664A
- Authority
- CN
- China
- Prior art keywords
- layer
- plastic composite
- packaging film
- composite packaging
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of aluminium plastic composite packaging film and preparation method thereof, and the aluminium plastic composite packaging film successively includes: polyamide laminate film, surface layer adhesive, aluminium foil layer, internal layer adhesive and three-layer co-extruded cast polypropylene layer from surface layer to internal layer;Wherein, the three-layer co-extruded cast polypropylene layer is the three-layer co-extruded film that preparation is processed using coextrusion curtain coating mode, from outside to inside successively includes aluminium foil adhesive layer, refractory layer and hot sealing layer;The polyamide laminate film and the aluminium foil layer and the aluminium foil layer and the three-layer co-extruded cast polypropylene layer are using dry compound machine progress dry laminating.Aluminium plastic composite packaging film of the invention and preparation method thereof, the heat seal strength that aluminium plastic composite packaging film can be improved, the electrolyte resistance corrosive nature for improving aluminium plastic composite packaging film, cell package equipment and packaging technology are required it is lower, to reduce process costs and improve the battery safety that encapsulation is completed.
Description
Technical field
The invention belongs to battery packages field, it is related to a kind of aluminium plastic composite packaging film and preparation method thereof.
Background technique
Aluminium plastic composite packaging film is a kind of important manner of packing of lithium battery, opposite aluminum hull, steel shell and cylinder packaging, plastic-aluminum
Composite package film, which has, to be had a safety feature, and energy density is high, and internal resistance is small, the advantages such as flexible design.
Currently, aluminum-plastic composite membrane generallys use nylon film (PA) as surface layer, aluminium foil is as middle layer, cast polypropylene
Structure of the film (CPP) as internal layer.In aluminum-plastic composite membrane heat seal process, CPP has part thin film melt, and strand occurs
It tangles and two layers of aluminum-plastic composite membrane bonds together, if the CPP film for participating in sealing is than relatively thin, only surface layer is melted,
It is lower to may result in heat seal strength;If the CPP film for participating in heat-sealing is thicker, remaining CPP melts than relatively thin or whole
It wears, then will lead to electrolytic corrosion aluminium foil, cause battery leakage and bulging;Therefore have to lithium battery encapsulation equipment and packaging technology
Relatively high requirement, while encapsulating the lithium battery of completion there is also security risks.
Summary of the invention
In view of the foregoing deficiencies of prior art, the purpose of the present invention is to provide a kind of aluminium plastic composite packaging film and its
Preparation method, for solving, aluminum-plastic composite membrane heat seal strength is low in the prior art, electrolyte resistance corrosive nature is poor, to cell package
Equipment and packaging technology it is more demanding and encapsulation complete battery there are problems that security risk.
In order to achieve the above objects and other related objects, the present invention provides a kind of aluminium plastic composite packaging film, and the plastic-aluminum is multiple
Closing packaging film successively includes: that polyamide laminate film, surface layer adhesive, aluminium foil layer, internal layer adhesive and three layers are total from surface layer to internal layer
Squish flow prolongs polypropylene layer;Wherein, the three-layer co-extruded cast polypropylene layer is to process the three of preparation using coextrusion curtain coating mode
Layer coextruded film successively includes aluminium foil adhesive layer, refractory layer and hot sealing layer from outside to inside;The polyamide laminate film and the aluminium foil
Layer and the aluminium foil layer and the three-layer co-extruded cast polypropylene layer are using dry compound machine progress dry laminating.
Preferably, the polyamide laminate film thickness range is 10 μm~50 μm.
Preferably, the surface layer adhesive thickness range is 1 μm~10 μm.
Preferably, the aluminium foil layer thickness range is 15 μm~80 μm.
Preferably, the internal layer adhesive thickness range is 1 μm~10 μm.
Preferably, the three-layer co-extruded cast polypropylene layer thickness range is 15 μm~80 μm.
Preferably, the material of the bonding foil layer includes copolymer polypropylene and adjuvant, and melting range is 110 DEG C~
160 DEG C, thickness range is 5 μm~20 μm.
Preferably, the material of the refractory layer include poly(4-methyl-1-pentene), homopolypropylene, propylene-based elastomeric and
Adjuvant, melting range are 160 DEG C~240 DEG C, and thickness range is 5 μm~30 μm.
Preferably, the material of the hot sealing layer includes copolymer polypropylene, propylene-based elastomeric and adjuvant, hot sealing layer fusing point
Range is 110 DEG C~160 DEG C, and thickness range is 5 μm~20 μm.
Preferably, the adjuvant include PPA fluoropolymer additive, antioxidant, slipping agent, opening agent, at
One of core agent and antistatic agent or combination.
The present invention also provides a kind of methods for preparing aluminium plastic composite packaging film, comprising the following steps:
S1: polyamide laminate film, surface layer adhesive, aluminium foil layer, internal layer adhesive, bonding foil layer, refractory layer and heat are provided
Sealing;
S2: the bonding foil layer, refractory layer and hot sealing layer are prepared into three-layer co-extruded curtain coating by being coextruded curtain coating mode
Polypropylene layer;
S3: the outer surface of the aluminium foil layer and inner surface are passivated processing by inactivating treatment liquid;
S4: the surface layer adhesive carries out dry laminating by dry compound machine will be outside the polyamide laminate film and aluminium foil layer
Surface recombination;
S5: the internal layer adhesive is total by the aluminium foil layer inner surface and three layers by dry compound machine progress dry laminating
It is compound that squish flow prolongs polypropylene layer.
Preferably, further include step S3 before step S2 or step S5 is formed by one in combination before step S 4
Kind.
Preferably, the inactivating treatment liquid includes phosphoric acid, polyacrylic acid and chromic salt, and the aluminium foil layer is outer after drying
The range of the chromium adhesion amount of surface and inner surface is 15mg/m2~30mg/m2。
Preferably, the surface layer adhesive is double component polyester system adhesive, and weight proportion is polyester resin: poly- isocyanide
Acid esters: ethyl acetate=100:10:40~100:20:50, the range of coating weight is 2g/m after drying2~8g/m2。
Preferably, the internal layer adhesive is maleic anhydride modified polyolefin adhesive, and weight proportion changes for maleic anhydride
Property polyolefin: epoxy resin: butanone: cyclohexane=100:1.4:35:5~100:1.5:36:6, it is dry after coating weight range
For 2g/m2~8g/m2。
Preferably, the polyamide laminate film includes two-way stretching polyamide film, and thickness range is 10 μm~50 μm, described
Aluminium foil layer includes soft aluminium foil, and thickness range is 15 μm~80 μm, the three-layer co-extruded cast polypropylene layer, thickness range 15
μm~80 μm.
Preferably, the thickness of the bonding foil layer in the three-layer co-extruded cast polypropylene layer, refractory layer and hot sealing layer
Degree is than being 1:2:1.
Preferably, the thickness range of the bonding foil layer is 5 μm~20 μm, and raw material and weight proportion are that copolymerization is poly-
Propylene: fluoropolymer additive PPA: antioxidant: opening slipping agent=96:1:2:1.
Preferably, the thickness range of the refractory layer is 5 μm~30 μm, and raw material and weight proportion are poly- 4- methyl-
1- amylene: propylene-based elastomeric: homopolypropylene: fluoropolymer additive PPA: antioxidant: opening slipping agent=38:
38:20:1:2:1.
Preferably, the thickness range of the hot sealing layer is 5 μm~20 μm, and raw material and weight proportion are copolymerization poly- third
Alkene: propylene-based elastomeric: fluoropolymer additive PPA: antioxidant: opening slipping agent=76:20:1:2:1.
As described above, aluminium plastic composite packaging film and preparation method thereof of the invention, has the advantages that raising plastic-aluminum
The heat seal strength of composite package film, the electrolyte resistance corrosive nature for improving aluminium plastic composite packaging film, to cell package equipment and envelope
It is lower to fill technique requirement, to reduce process costs and improve the battery safety that encapsulation is completed.
Detailed description of the invention
Fig. 1 is shown as the schematic cross-sectional view of aluminium plastic composite packaging film in the embodiment of the present invention one.
Component label instructions
100 polyamide laminate films
200 surface layer adhesives
300 aluminium foil layers
400 internal layer adhesives
500 three-layer co-extruded cast polypropylene layers
501 aluminium foil adhesive layers
502 refractory layers
503 hot sealing layers
S1~S5 step
Specific embodiment
Embodiments of the present invention are illustrated by particular specific embodiment below, those skilled in the art can be by this explanation
Content disclosed by book is understood other advantages and efficacy of the present invention easily.
Please refer to Fig. 1.It should be clear that this specification structure depicted in this specification institute accompanying drawings, ratio, size etc., only to cooperate
The revealed content of specification is not intended to limit the invention enforceable so that those skilled in the art understands and reads
Qualifications, therefore do not have technical essential meaning, the modification of any structure, the change of proportionate relationship or the adjustment of size, In
It does not influence still fall in disclosed technology contents under the effect of present invention can be generated and the purpose that can reach
It obtains in the range of capable of covering.Meanwhile cited such as "upper", "lower", "left", "right", " centre " and " one " in this specification
Term, be merely convenient to being illustrated for narration, rather than to limit the scope of the invention, the change of relativeness or
Adjustment, under the content of no substantial changes in technology, when being also considered as the enforceable scope of the present invention.
Embodiment one
As shown in Figure 1, the present invention provides a kind of aluminium plastic composite packaging film, polyamide laminate film is followed successively by internal layer by surface layer
100, surface layer adhesive 200, aluminium foil layer 300, internal layer adhesive 400 and three-layer co-extruded cast polypropylene layer 500.Wherein, described
Three-layer co-extruded cast polypropylene layer 500 is to process the three-layer co-extruded film of preparation using coextrusion curtain coating mode, from outside to inside according to
Secondary includes aluminium foil adhesive layer 501, refractory layer 502 and hot sealing layer 503.
As an example, the thickness range of the polyamide laminate film 100 is 10 μm~50 μm;The surface layer adhesive 200
Thickness range is 1 μm~10 μm;The thickness range of the aluminium foil layer 300 is 15 μm~80 μm;The thickness of the internal layer adhesive 400
Spending range is 1 μm~10 μm;The thickness range of the three-layer co-extruded cast polypropylene layer 500 is 15 μm~80 μm, wherein described
The thickness range of bonding foil layer 501 is 5 μm~20 μm;The thickness range of the refractory layer 502 is 5 μm~30 μm;The heat
The thickness range of sealing 503 is 5 μm~20 μm.
As an example, the material of the bonding foil layer 501 includes copolymer polypropylene and adjuvant, melting range 110
DEG C~160 DEG C;The material of the refractory layer 502 includes poly(4-methyl-1-pentene), homopolypropylene, propylene-based elastomeric and institute
Adjuvant is stated, melting range is 160 DEG C~240 DEG C;The material of the hot sealing layer 503 includes copolymer polypropylene, Propylene-based elastomers
Body and the adjuvant, melting range are 110 DEG C~160 DEG C.The adjuvant includes fluoropolymer additive PPA, resists
One of oxidant, slipping agent, opening agent, nucleating agent and antistatic agent or combination.The aluminium plastic composite packaging film is applicable
In lithium ion battery.
Embodiment two
The present invention also provides a kind of methods for preparing aluminium plastic composite packaging film, comprising the following steps:
S1: polyamide laminate film, surface layer adhesive, aluminium foil layer, internal layer adhesive, bonding foil layer, refractory layer and heat are provided
Sealing;
S2: the bonding foil layer, refractory layer and hot sealing layer are prepared into three-layer co-extruded curtain coating by being coextruded curtain coating mode
Polypropylene layer;
S3: the outer surface of the aluminium foil layer and inner surface are passivated processing by inactivating treatment liquid;
S4: the surface layer adhesive carries out dry laminating by dry compound machine will be outside the polyamide laminate film and aluminium foil layer
Surface recombination;
S5: the internal layer adhesive is total by the aluminium foil layer inner surface and three layers by dry compound machine progress dry laminating
It is compound that squish flow prolongs polypropylene layer.
As an example, the aluminium plastic composite packaging film is applicable to lithium ion battery.
Specifically, step S3 can also be before step S2 or step S5 can also be before step S 4 in above-mentioned steps
One of combination is formed by by it.Those skilled in the art can select according to actual needs, herein with no restrictions.Step
It is using dry compound machine that the polyamide laminate film and aluminium foil layer outer surface is compound or by the aluminium foil layer in rapid S4 and step S5
Inner surface and three-layer co-extruded cast polypropylene layer carry out the mode of dry laminating, and heat-sealing can be improved and melt Cheng Kuandu, it is strong to improve heat-sealing
Degree and electrolyte resistance performance.
As an example, the inactivating treatment liquid includes phosphoric acid, polyacrylic acid and chromic salt, the aluminium foil layer after drying
The range of the chromium adhesion amount of outer surface and inner surface is 15mg/m2~30mg/m2, preferably 20mg/m2。
As an example, the surface layer adhesive is double component polyester system adhesive, weight proportion range is polyester resin:
Polyisocyanate: ethyl acetate=100:10:40~100:20:50, the range of coating weight is 2g/m after drying2~8g/m2.Institute
Stating internal layer adhesive is maleic anhydride modified polyolefin adhesive, and weight proportion is maleic anhydride modified polyolefin: epoxy resin:
Butanone: cyclohexane=100:1.4:35:5~100:1.5:36:6, the range of coating weight is 2g/m after drying2~8g/m2.This reality
It applies in example, the weight proportion of double component polyester system adhesive is polyester resin: polyisocyanate: ethyl acetate=100:14:
48, coating weight is 4g/m after drying2;The weight proportion of maleic anhydride modified polyolefin adhesive is maleic anhydride modified polyene
Hydrocarbon: epoxy resin: butanone: cyclohexane=100:1.43:35.4:5.7, coating weight is 4g/m after drying2。
As an example, the polyamide laminate film includes two-way stretching polyamide film, thickness range is 10 μm~50 μm, institute
Stating aluminium foil layer includes soft aluminium foil, and thickness range is 15 μm~80 μm, the three-layer co-extruded cast polypropylene layer, and thickness range is
15 μm~80 μm.In the present embodiment, the two-way stretching polyamide film is with a thickness of 25 μm;The aluminium foil layer is soft aluminium foil,
With a thickness of 40 μm;The three-layer co-extruded cast polypropylene layer, with a thickness of 40 μm, wherein the three-layer co-extruded cast polypropylene layer
In the bonding foil layer, refractory layer and hot sealing layer thickness ratio be 1:2:1.
Specifically, the thickness range of the bonding foil layer is 5 μm~20 μm, the thickness range of the refractory layer is 5 μm
~30 μm, the thickness range of the hot sealing layer is 5 μm~20 μm.In the present embodiment, the bonding foil layer with a thickness of 10 μm,
Its raw material and weight proportion are copolymer polypropylene: fluoropolymer additive PPA: antioxidant: opening slipping agent=96:
1:2:1;The refractory layer with a thickness of 20 μm, raw material and weight proportion are poly(4-methyl-1-pentene): Propylene-based elastomers
Body: homopolypropylene: fluoropolymer additive PPA: antioxidant: opening slipping agent=38:38:20:1:2:1;It is described
Hot sealing layer with a thickness of 10 μm, raw material and weight proportion are copolymer polypropylene: propylene-based elastomeric: fluoropolymer processing
Auxiliary agent PPA: antioxidant: opening slipping agent=76:20:1:2:1.
Illustrate embodiments of the present invention to further strengthen, so that those skilled in the art can be taken off by this specification
The content of dew is understood other advantages and efficacy of the present invention more easily, is exemplified below comparative example and is further illustrated.
Comparative example
This comparative example is only that from the distinctive points in embodiment with different three-layer co-extruded cast polypropylene layers, Qi Tabu
The rapid and same embodiment of condition, details are not described herein again.
Specifically, in this comparative example three-layer co-extruded cast polypropylene layer with a thickness of 40um, including bonding foil layer, sandwich layer
And hot sealing layer, thickness ratio are 1:2:1.Wherein, the thickness of the bonding foil layer, raw material and the same embodiment of weight proportion
Two, i.e., the described bonding foil layer is with a thickness of 10um, and raw material and weight proportion are copolymer polypropylene: fluoropolymer processing helps
Agent PPA: antioxidant: opening slipping agent=96:1:2:1.The sandwich layer is with a thickness of 20um, raw material and weight proportion
Copolymer polypropylene: propylene-based elastomeric: PPA: antioxidant: opening slipping agent=58:38:1:2:1.The thickness of the hot sealing layer
For 10um, raw material and weight proportion are copolymer polypropylene: propylene-based elastomeric: PPA: antioxidant: opening slipping agent=
86:10:1:2:1.
The three-layer co-extruded cast polypropylene layer then prepared to embodiment and comparative example carries out heat-sealing test.Seal work
Skill setting are as follows: 180 DEG C of temperature, pressure 0.35MPA, the time is respectively 2 seconds, 3 seconds, 4 seconds, 5 seconds, 6 seconds, 7 seconds.
The test result of above-described embodiment and comparative example is compared and is assessed, wherein comparison project has:
Initial heat seal strength situation: initial heat seal strength whether >=50N/15mm
Three-layer co-extruded cast polypropylene layer thickness variation is than situation: thickness change than whether≤30%
The result is as follows:
It can be seen that embodiment compared with comparative example by upper table, using different three-layer co-extruded cast polypropylenes
Layer, the three-layer co-extruded cast polypropylene layer in embodiment has preferably initially by the way that the refractory layer is arranged compared with comparative example
Heat seal strength and lower thickness change ratio, to improve the heat seal strength and electrolyte resistance corrosivity of aluminium plastic composite packaging film
Energy;The hot sealing process section for improving aluminium plastic composite packaging film, it is lower to cell package equipment and packaging technology requirement, to reduce
Process costs and the battery safety for improving encapsulation completion.
In conclusion aluminium plastic composite packaging film and preparation method thereof of the invention, can be improved the heat of aluminium plastic composite packaging film
Sealing strength, the electrolyte resistance corrosive nature for improving aluminium plastic composite packaging film, cell package equipment and packaging technology are required it is lower,
To reduce process costs and improve the battery safety of encapsulation completion.So the present invention effectively overcomes in the prior art
Various shortcoming and have high industrial utilization value.
The above-described embodiments merely illustrate the principles and effects of the present invention, and is not intended to limit the present invention.It is any ripe
The personage for knowing this technology all without departing from the spirit and scope of the present invention, carries out modifications and changes to above-described embodiment.Cause
This, institute is complete without departing from the spirit and technical ideas disclosed in the present invention by those of ordinary skill in the art such as
At all equivalent modifications or change, should be covered by the claims of the present invention.
Claims (20)
1. a kind of aluminium plastic composite packaging film, which is characterized in that the aluminium plastic composite packaging film successively includes: from surface layer to internal layer
Polyamide laminate film, surface layer adhesive, aluminium foil layer, internal layer adhesive and three-layer co-extruded cast polypropylene layer;Wherein, described three
Layer coextrusion casting polypropylene layer is the three-layer co-extruded film that preparation is processed using coextrusion curtain coating mode, successively includes from outside to inside
Aluminium foil adhesive layer, refractory layer and hot sealing layer;The polyamide laminate film and the aluminium foil layer and the aluminium foil layer and described three layers are total
Squish flow prolongs polypropylene layer and carries out dry laminating using dry compound machine.
2. aluminium plastic composite packaging film according to claim 1, it is characterised in that: the polyamide laminate film thickness range is 10
μm~50 μm.
3. aluminium plastic composite packaging film according to claim 1, it is characterised in that: the surface layer adhesive thickness range is 1 μ
M~10 μm.
4. aluminium plastic composite packaging film according to claim 1, it is characterised in that: the aluminium foil layer thickness range be 15 μm~
80μm。
5. aluminium plastic composite packaging film according to claim 1, it is characterised in that: the internal layer adhesive thickness range is 1 μ
M~10 μm.
6. aluminium plastic composite packaging film according to claim 1, it is characterised in that: the three-layer co-extruded cast polypropylene thickness
Spending range is 15 μm~80 μm.
7. aluminium plastic composite packaging film according to claim 1, it is characterised in that: the material of the bonding foil layer includes altogether
Poly- polypropylene and adjuvant, melting range are 110 DEG C~160 DEG C, and thickness range is 5 μm~20 μm.
8. aluminium plastic composite packaging film according to claim 1, it is characterised in that: the material of the refractory layer includes poly- 4- first
Base -1- amylene, homopolypropylene, propylene-based elastomeric and adjuvant, melting range are 160 DEG C~240 DEG C, and thickness range is 5 μ
M~30 μm.
9. aluminium plastic composite packaging film according to claim 1, it is characterised in that: the material of the hot sealing layer includes that copolymerization is poly-
Propylene, propylene-based elastomeric and adjuvant, hot sealing layer melting range are 110 DEG C~160 DEG C, and thickness range is 5 μm~20 μm.
10. according to the aluminium plastic composite packaging film any in claim 7~9, it is characterised in that: the adjuvant includes containing
One of fluoropolymer process aid PPA, antioxidant, slipping agent, opening agent, nucleating agent and antistatic agent or combination.
11. a kind of method for preparing aluminium plastic composite packaging film, which comprises the following steps:
S1: polyamide laminate film, surface layer adhesive, aluminium foil layer, internal layer adhesive, bonding foil layer, refractory layer and hot sealing layer are provided;
S2: the bonding foil layer, refractory layer and hot sealing layer are prepared into three-layer co-extruded curtain coating poly- third by being coextruded curtain coating mode
Alkene layer;
S3: the outer surface of the aluminium foil layer and inner surface are passivated processing by inactivating treatment liquid;
S4: the surface layer adhesive carries out dry laminating for the polyamide laminate film and aluminium foil layer outer surface by dry compound machine
It is compound;
S5: the internal layer adhesive carries out dry laminating for the aluminium foil layer inner surface and three-layer co-extruded stream by dry compound machine
It is compound to prolong polypropylene layer.
12. the method according to claim 11 for preparing aluminium plastic composite packaging film, it is characterised in that: further include that step S3 exists
Before step S2 or step S5 is formed by one of combination before step S 4.
13. the method according to claim 11 for preparing aluminium plastic composite packaging film, it is characterised in that: the inactivating treatment liquid
Comprising phosphoric acid, polyacrylic acid and chromic salt, the range of the chromium adhesion amount of the outer surface and inner surface of the aluminium foil layer after drying
For 15mg/m2~30mg/m2。
14. the method according to claim 11 for preparing aluminium plastic composite packaging film, it is characterised in that: the surface layer adhesive
For double component polyester system adhesive, weight proportion range is polyester resin: polyisocyanate: ethyl acetate=100:10:40
~100:20:50, the range of coating weight is 2g/m after drying2~8g/m2。
15. the method according to claim 11 for preparing aluminium plastic composite packaging film, it is characterised in that: the internal layer adhesive
For maleic anhydride modified polyolefin adhesive, weight proportion is maleic anhydride modified polyolefin: epoxy resin: butanone: cyclohexane
=100:1.4:35:5~100:1.5:36:6, the range of coating weight is 2g/m after drying2~8g/m2。
16. the method according to claim 11 for preparing aluminium plastic composite packaging film, it is characterised in that: the polyamide laminate film
Including two-way stretching polyamide film, thickness range is 10 μm~50 μm, and the aluminium foil layer includes soft aluminium foil, and thickness range is
15 μm~80 μm, the three-layer co-extruded cast polypropylene layer, thickness range is 15 μm~80 μm.
17. the method according to claim 16 for preparing aluminium plastic composite packaging film, it is characterised in that: the three-layer co-extruded stream
The thickness ratio for prolonging the bonding foil layer in polypropylene layer, refractory layer and hot sealing layer is 1:2:1.
18. the method according to claim 17 for preparing aluminium plastic composite packaging film, it is characterised in that: the bonding foil layer
Thickness range be 5 μm~20 μm, raw material and weight proportion are copolymer polypropylene: fluoropolymer additive PPA: anti-
Oxidant: opening slipping agent=96:1:2:1.
19. the method according to claim 17 for preparing aluminium plastic composite packaging film, it is characterised in that: the thickness of the refractory layer
Spending range is 5 μm~30 μm, and raw material and weight proportion are poly(4-methyl-1-pentene): propylene-based elastomeric: homopolymerization poly- third
Alkene: fluoropolymer additive PPA: antioxidant: opening slipping agent=38:38:20:1:2:1.
20. the method according to claim 17 for preparing aluminium plastic composite packaging film, it is characterised in that: the thickness of the hot sealing layer
Spending range is 5 μm~20 μm, and raw material and weight proportion are copolymer polypropylene: propylene-based elastomeric: fluoropolymer processing
Auxiliary agent PPA: antioxidant: opening slipping agent=76:20:1:2:1.