CN110453505A - A method of increasing down jackets heat insulation effect - Google Patents
A method of increasing down jackets heat insulation effect Download PDFInfo
- Publication number
- CN110453505A CN110453505A CN201810430074.7A CN201810430074A CN110453505A CN 110453505 A CN110453505 A CN 110453505A CN 201810430074 A CN201810430074 A CN 201810430074A CN 110453505 A CN110453505 A CN 110453505A
- Authority
- CN
- China
- Prior art keywords
- down jackets
- accumulation
- coating
- heat
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of methods for increasing down jackets heat insulation effect to dissolve accumulation of heat coating by dimethylformamide, and coating slurry is made by the padding sizing accumulation of heat coating in down jackets ontology;And coating slurry is uniformly applied to the outer cloth for being used to sew down jackets ontology, and it is immersed in the water into solidification film, since dimethylformamide can be infinitely miscible with water, dimethylformamide dissolves out in water, and accumulation of heat coating is not soluble in water, concentration increases rapidly, finally it is deposited on above base fabric, in coating process of setting, due to the effect of semi-permeable membrane, dimethylformamide is sharply oozed out from accumulation of heat coating, cause the channel micropore perpendicular to film surface, passing through Drying and cooling, obtain the cloth with heat insulation effect, a kind of method increasing down jackets heat insulation effect proposed by the present invention, by the reference of accumulation of heat coating fabric on ready-made clothes, keep ready-made clothes heat accumulation thermal effect more preferable, it is more preferable than traditional down jackets heat insulating ability.
Description
Technical field
The invention belongs to technical field of costume design more particularly to a kind of methods for increasing down jackets heat insulation effect.
Background technique
The jacket of eider down filler is filled in down jackets (down coat), shape is huge mellow and full.The general duck's down amount of down jackets accounts for one
Half or more, while some tiny feathers can be mixed, duck's down is cleaned up, through high-temperature sterilization, is filled later in the clothes
It is exactly down jackets.
A kind of method increasing down jackets heat insulation effect is now provided, is to quote accumulation of heat coating fabric on ready-made clothes, makes into
Clothing heat accumulation thermal effect is more preferable, more preferable than traditional down jackets heat insulating ability.
Summary of the invention
The present invention is to solve well-known technique and provide a kind of method for increasing down jackets heat insulation effect.
The present invention is adopted the technical scheme that solve well-known technique: a kind of increase down jackets guarantor
The method of temp effect, by the padding sizing accumulation of heat coating in down jackets ontology, the following steps are included:
Step 1: accumulation of heat coating being dissolved by dimethylformamide, and coating slurry is made;
Step 2: the coating slurry in step 1 being uniformly applied to the outer cloth for being used to sew down jackets ontology, and is soaked
Enter at solidification film in water, since dimethylformamide can be infinitely miscible with water, dimethylformamide is dissolved out in water, and accumulation of heat applies
Layer is not soluble in water, and concentration increases rapidly, and is finally deposited on above base fabric, in coating process of setting, due to the effect of semi-permeable membrane,
Dimethylformamide is sharply oozed out from accumulation of heat coating, causes the channel micropore perpendicular to film surface;
Step 3: after impregnated in step 2 in aqueous solution design on fabric surface solidification after the completion of, by cloth be put into dryer into
Row drying, drying temperature are 120-180 DEG C.Drying time is 15-30min;
Step 4: after being dried completely in step 3, being put under natural environment and carry out natural cooling, it is completely cooling to obtain cloth
Afterwards, sewing down jackets be can be used to, and the outermost layer cloth as down jackets uses.
In the present invention, in the step 2 diameter of channel micropore be 0.5~5 μm with.
In the present invention, the weight proportion of the accumulation of heat coating are as follows: 5.0g/L Teflon powder, 2.0% antibacterial agent, 1.0g/
L Disperse Leveler, 1.0g/L moisture absorbing and sweat releasing softening agent, 1.0g/L age resister, 3.0g/L restore remover, 1.0g/L antistatic
Agent, 1.6% fuel are disperse dyes.
In the present invention, the accumulation of heat coating is respectively arranged on the outer layer of down jackets ontology outer layer cloth or interior according to use demand
In layer surface.
The present invention has the advantage that as follows with good effect:
A kind of method increasing down jackets heat insulation effect proposed by the present invention, by the reference of accumulation of heat coating fabric on ready-made clothes,
Keep ready-made clothes heat accumulation thermal effect more preferable, it is more preferable than traditional down jackets heat insulating ability.
Specific embodiment
In order to further understand the content, features and effects of the present invention, hereby enumerating following embodiment, it is described in detail such as
Under.
A kind of method of increase down jackets heat insulation effect of the invention is formed by the padding in down jackets ontology and is stored
Hot coating, the following steps are included:
Step 1: accumulation of heat coating being dissolved by dimethylformamide, and coating slurry is made;
Step 2: the coating slurry in step 1 being uniformly applied to the outer cloth for being used to sew down jackets ontology, and is soaked
Enter at solidification film in water, since dimethylformamide can be infinitely miscible with water, dimethylformamide is dissolved out in water, and accumulation of heat applies
Layer is not soluble in water, and concentration increases rapidly, and is finally deposited on above base fabric, in coating process of setting, due to the effect of semi-permeable membrane,
Dimethylformamide is sharply oozed out from accumulation of heat coating, causes the channel micropore perpendicular to film surface;
Step 3: after impregnated in step 2 in aqueous solution design on fabric surface solidification after the completion of, by cloth be put into dryer into
Row drying, drying temperature are 120-180 DEG C.Drying time is 15-30min;
Step 4: after being dried completely in step 3, being put under natural environment and carry out natural cooling, it is completely cooling to obtain cloth
Afterwards, sewing down jackets be can be used to, and the outermost layer cloth as down jackets uses.
In the present invention, in the step 2 diameter of channel micropore be 0.5~5 μm with.The weight of the accumulation of heat coating is matched
Than are as follows: 5.0g/L Teflon powder, 2.0% antibacterial agent, 1.0g/L Disperse Leveler, 1.0g/L moisture absorbing and sweat releasing softening agent,
1.0g/L age resister, 3.0g/L reduction remover, 1.0g/L antistatic agent, 1.6% fuel are disperse dyes.The accumulation of heat applies
Layer is respectively arranged in outer layer or the internal layer surface of down jackets ontology outer layer cloth according to use demand.
The above is only the preferred embodiments of the present invention, and is not intended to limit the present invention in any form,
Any simple modification made to the above embodiment according to the technical essence of the invention, equivalent variations and modification, belong to
In the range of technical solution of the present invention.
Claims (4)
1. it is a kind of increase down jackets heat insulation effect method, by down jackets ontology padding be formed accumulation of heat coating,
It is characterized in that, comprising the following steps:
Step 1: accumulation of heat coating being dissolved by dimethylformamide, and coating slurry is made;
Step 2: the coating slurry in step 1 being uniformly applied to the outer cloth for being used to sew down jackets ontology, and immerses water
It is middle at solidification film, due to dimethylformamide can and water it is infinitely miscible, dimethylformamide dissolves out in water, and accumulation of heat coating is not
It is dissolved in water, concentration increases rapidly, and is finally deposited on above base fabric, in coating process of setting, due to the effect of semi-permeable membrane, diformazan
Base formamide is sharply oozed out from accumulation of heat coating, causes the channel micropore perpendicular to film surface;
Step 3: after the completion of impregnating design on fabric surface solidification in aqueous solution in step 2, cloth being put into dryer and is dried
Dry, drying temperature is 120-180 DEG C.Drying time is 15-30min;
Step 4: after being dried completely in step 3, be put under natural environment and carry out natural cooling, obtain cloth it is completely cooling after,
It can be used to sewing down jackets, and the outermost layer cloth as down jackets uses.
2. a kind of method for increasing down jackets heat insulation effect according to claim 1, which is characterized in that in the step 2
The diameter of channel micropore be 0.5~5 μm with.
3. a kind of method for increasing down jackets heat insulation effect according to claim 1, which is characterized in that the accumulation of heat coating
Weight proportion are as follows: 5.0g/L Teflon powder, 2.0% antibacterial agent, 1.0g/L Disperse Leveler, 1.0g/L moisture absorbing and sweat releasing are soft
Agent, 1.0g/L age resister, 3.0g/L reduction remover, 1.0g/L antistatic agent, 1.6% fuel are disperse dyes.
4. a kind of method for increasing down jackets heat insulation effect according to claim 1, which is characterized in that the accumulation of heat coating
It is respectively arranged in outer layer or the internal layer surface of down jackets ontology outer layer cloth according to use demand.