CN110452562A - A kind of jade mud and titanium dioxide compo and preparation method thereof - Google Patents
A kind of jade mud and titanium dioxide compo and preparation method thereof Download PDFInfo
- Publication number
- CN110452562A CN110452562A CN201910660039.9A CN201910660039A CN110452562A CN 110452562 A CN110452562 A CN 110452562A CN 201910660039 A CN201910660039 A CN 201910660039A CN 110452562 A CN110452562 A CN 110452562A
- Authority
- CN
- China
- Prior art keywords
- powder
- jade
- titanium dioxide
- weight
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of jade mud and titanium dioxide compo and preparation method thereof are related to technical field of coatings.Jade mud and titanium dioxide compo, it is made of following raw material by weight: natural jade 80-85 parts by weight, titanium dioxide powder 1-10 parts by weight, negative oxygen ion powder 10-15 parts by weight, dispersable adhesive powder 5-10 parts by weight, hydroxyl second methylcellulose 0.5-1 parts by weight.Negative oxygen ion powder can also be not added in proportion.Natural toner 0.1-0.5 parts by weight can also be added.Of the invention is critical that having used the use of titanium dioxide powder and negative oxygen ion powder, especially titanium dioxide powder is the scheme for comparing and testing repeatedly.Characteristic pure white, that adhesive force is high make jade mud using more preferable.
Description
Technical field
The present invention relates to technical field of coatings.It exactly, is a kind of jade mud and titanium dioxide compo and its system
Preparation Method.
Background technique
Currently, inner-outer wall coating decoration and protection are mainly decorated using emulsion paint, emulsion paint is a kind of water paint, uses water
Dilution, washs with water, not soluble in water in the film that building surface is formed, the fundamental property with traditional paint, deep by people
Like.However easily there is subtle slight crack in metope in emulsion paint, has been easy dust, and is easy odorous, is unfavorable for interior
Air
Purification.Occurs the diatomite paint of the more feature of environmental protection currently on the market, but its film poor plasticity cannot cover
Substrate
The defects of slight crackle.For improved technology defect, Chinese Patent Application No. CN201810503481.6 discloses one kind
The application for a patent for invention of entitled title " nano rare earth coating " is exactly a kind of better coating.Also useful jade is as raw material
Coating, close to it is of the invention be number of patent application 201510017248.3 patent of invention " a kind of jade mud compo and its
Preparation method ", in its constituent content, zeolite is composition important in the present invention.
It is known that natural jade contain more than 30 kinds of selenium, zinc, nickel, cobalt, manganese, magnesium, calcium of needed by human body etc. it is beneficial to human body
Microelement, these elements to promote blood circulation of human body, enhancing metabolism and exclude bodily waste have good effect.
But it since the caking property of natural jade is inadequate, uses natural jade as coating in the prior art, is often added in coating
Various auxiliary materials, but the addition of these auxiliary materials often will affect its performance, especially adhesion strength and purifying formaldehyde
Etc. performances.
Summary of the invention
The object of the present invention is to provide a kind of jade mud and titanium dioxide compo and preparation method thereof.It has cost
The characteristics of lower, raw material sources are easy, non-discolouring and mildew, good decorating effect.By various extensive and careful research and reality
It is testing as a result, adsorbent using titanium dioxide powder as strong adsorptivity, the appropriate negative oxygen ion powder that adds not only have preferably
Adsorptivity can also discharge a certain amount of negative oxygen ion.And purifying formaldehyde efficiency is very high.Dioxy has been used in of the invention being critical that
The use for changing titanium valve and negative oxygen ion powder, especially titanium dioxide powder is the scheme for comparing and testing repeatedly.It is pure white, stick
The high characteristic of power make jade mud using more preferable.
Technical scheme is as follows: the jade mud and titanium dioxide compo, by it is following by weight
Raw material is made: natural jade 80-85 parts by weight, negative oxygen ion powder 10-15 parts by weight, can divide at titanium dioxide powder 1-10 parts by weight
Dissipate property rubber powder 5-10 parts by weight, hydroxyl second methylcellulose 0.5-1 parts by weight.Negative oxygen ion powder can also be not added in proportion.Can also it add
Add natural 0. 1-0.5 parts by weight of toner.
The natural jade and titanium dioxide is ground that the powder greater than 800 mesh is made.Due to by natural jade and two
Titanium oxide has been ground into thinner particle, keeps the jade slime paint more uniform, makes the more smooth exquisiteness of the wall after wiping.
Wherein, the natural jade and titanium dioxide are ground into fritter through mineral breaker after strictly screening, such as diameter is l0cm
Hereinafter, use-case such as raymond mill is ground into 800 powder materials again；
The present invention also provides a kind of jade mud and titanium dioxide compo and preparation method thereof, include the following steps: by
Natural jade and titanium dioxide powder are mixed according to weight ratio, and stir 25-30min with powder stirrer；
Later according to weight ratio addition negative oxygen ion powder, dispersable adhesive powder and hydroxyethylmethylcellulose, and stirred with dry powder
Machine stirring 25-30min is mixed to get finished product.
It further include adding natural toner in finished product and stirring evenly.
The present invention is to provide the application method of the jade slime paint, comprising the following steps:
(1) Site is stirred evenly the raw material in the ratio of material-water ratio 1:0.4 or so；
(2) it wipes:
A, first wall putty bottoming is smoothed out, keeps its smooth flawless；
B, it is wiped on wall in the ratio of every square metre of materials 1200g, then carrying out press polish makes the smooth exquisiteness of wall.
Silk screen printing pattern, wall spraying can also be carried out after wiping press polish and scribed or painted by hand.
Jade slime paint of the present invention at least has the advantages that
Formaldehyde and harmful substance are eliminated, jade slime paint of the present invention has extremely strong absorption and ion exchanging function, can incite somebody to action
The harmful substances such as formaldehyde, the benzene to dissociate in air and the peculiar smell such as cigarette, raw meat, smelly are decomposed by absorbing, and are converted to harmless object
Matter, through national building materials, test center is examined: purifying formaldehyde efficiency is up to 95% purifying formaldehyde persistence and is up to 91%.The present invention
Raw material is easy to get, non-discolouring after smearing and mildew, good decorating effect, and negative oxygen ion powder discharges a certain amount of negative oxygen ion, is beneficial to
Human health.
Jade contains more than 30 kinds of selenium, zinc, nickel, cobalt, manganese, magnesium, calcium of needed by human body etc. the microelements beneficial to human body, this
The starting wave of starting wave and human body cell that a little elements distribute is same fluctuation status, and human body cell gives out with from jade
Fluctuation empathize and resonate, be that human body cell is more vigourous and promote blood circulation, enhance metabolism and exclude internal
Waste.Medical stone contains the microelements such as potassium, sodium, calcium, magnesium, there is as many as 58 kinds, by absorbing, can be divided by the ingredient of itself
The method of solution ionizes noxious material, released mineral matter and the quantity for balancing minerals.The jade slime paint also has antibacterial suppression
Bacterium effect, is rich in negative oxygen ion group, effectively kills various germs in air, inhibits the breeding of bacterium and microorganism.
It service life 20 years or more, does not fall off, colour-fast, resistance to oxidation is never degenerated, always as new.Through national building materials
Test center
Detection: no blistering, is peeled off without fading slight crack, and caking ability reaches 0.92Mpa under standard state, and adhesion strength is high after inundation.
The jade mud just has preferable gas permeability and suction in the film that building surface is formed with titanium dioxide compo
It is aqueous；Can wetness in automatic constant-temperature regulation room, can spray water at any time in surface of wall, play water and support jade, Yu Yangren keeps wall
Body is cool in summer and warm in winter.
Absorbing sound and lowering noise, the jade mud and titanium dioxide compo, after adding water to wipe metope, will form on metope
Countless micropores, these micropores can be absorbed barrier volume, substantially reduce noise transmission.
Fire protection flame retarding, the jade mud and titanium dioxide compo use natural minerals raw material, and 1300 DEG C of high temperature resistant,
It meets open fire never to burn, will not more generate any toxic smog.
Color is soft, and jade mud and titanium dioxide compo absorptance are very strong, and the light of reflection is naturally soft, is not easy to produce
Raw visual fatigue, can protect eyesight.
Metope is self-cleaning, smooth exquisiteness is pure white.Because the characteristic of jade itself, and the natural jade is ground to 800
Mesh, so the very smooth exquisiteness of wall.
After tested center examine, jade slime paint of the present invention be free of any harmful heavy metal, because without generation electrostatic,
Floating dust is not easy to adhere to, and metope is permanently pure and fresh.
Specific embodiment
The present invention will be further described in detail below with reference to the embodiments.
Embodiment l
Jade mud of the present invention and titanium dioxide compo are formulated l:
Xiuyan is selected to produce natural jade powder 850kg
10 kg of titanium dioxide powder
Negative oxygen ion powder 100kg
Dispersable adhesive powder 50kg
Hydroxyethylmethylcellulose 5kg
The jade slime paint the preparation method is as follows:
Step 1: Xiuyan production natural jade and titanium dioxide powder are ground into fritter through mineral breaker respectively after strictly screening
Example
If diameter is less than l0cm hereinafter, use-case such as raymond mill is ground into 800 powder materials again；
Step 2: titanium dioxide powder wears into 100 mesh graininess；
Step 3: according to by natural jade powder 800kg and titanium dioxide powder 100kg mixing, and stirred with powder stirrer
Mix 30min；It is fine that negative oxygen ion powder 150kg, dispersable adhesive powder 100kg and hydroxyethyl methyl are proportionally added later
Element 10kg is tieed up,
And with powder stirrer stirring 30min to get finished product.
Embodiment 2
Jade mud of the present invention and titanium dioxide compo formula 2:
Xiuyan produces natural jade powder 800kg
Titanium dioxide powder l00kg
Negative oxygen ion powder 150kg
Import dispersable adhesive powder 100kg
1 kg of hydroxyethylmethylcellulose
The jade mud and titanium dioxide compo the preparation method is as follows:
Step 1: Xiuyan production natural jade and titanium dioxide powder are ground into fritter example through mineral breaker after strictly screening
If diameter is l0cm hereinafter, use-case such as raymond mill is ground into 800 powder materials again；
Step 2: negative oxygen ion powder is ground into 400 mesh graininess；
Step 3: according to by natural jade powder 800kg and titanium dioxide powder particles l00kg mixing, and use powder stirrer
Stir 25min；It is fine that negative oxygen ion powder l50kg, dispersable adhesive powder 100kg, hydroxyethyl methyl are proportionally added later
Element 1kg is tieed up, and with powder stirrer stirring 25min to get finished product.
Embodiment 3
The formula 3 of jade mud of the present invention and titanium dioxide compo:
In order to make coating have different colors, different natural toners can be added.
Xiuyan produces natural jade powder 820kg
8 kilograms of titanium dioxide powder
12 kilograms of negative oxygen ion powder
7 kilograms of dispersable adhesive powder
Hydroxyethylmethylcellulose 0.8kg
Natural toner 2.0kg
The jade mud and titanium dioxide compo the preparation method is as follows:
Step 1: Xiuyan, which is produced natural jade and titanium dioxide, is ground into fritter example through mineral breaker after strictly screening respectively
If diameter is l0cm hereinafter, being ground into 800 powder materials with raymond mill again；
Step 2: negative oxygen ion powder is ground into 400 mesh graininess；
Step 3 is mixed according to by natural jade powder 800kg and titanium dioxide powder particles l00kg, and is stirred with powder stirrer
Mix 25min；Negative oxygen ion powder l50kg, dispersable adhesive powder 100kg, hydroxyethylmethylcellulose are proportionally added later
1kg, and with powder stirrer stirring 25min to get finished product.
Above-described embodiment 1-3 all has following application methods.It is close with the application method of current coating.
The application method of the jade slime paint is as follows:
Step 1: the jade mud and titanium dioxide compo are stirred evenly in the ratio of material-water ratio 1:0.3-0.6 can go up wall
It wipes.
Step 2: wiping method:
(1) first wall putty bottoming is smoothed out, keeps its smooth flawless.
(2) tradition can be taken to wipe, is wiped on wall in the ratio of every square metre of materials 1200g, then carry out press polish
Make the smooth exquisiteness of wall.
(3) silk screen printing after wiping press polish using tradition, then carries out silk screen printing pattern.
(4) it sprays, after wiping press polish using tradition, then carries out wall spraying.
(5) it manufactures by hand, takes and the modes such as scribe, paint by hand and manufacture.
In order to illustrate effect of the invention, it is as follows that inventor provides comparative experiments:
Jade slime paint of the present invention is examined according to JC/T2177-2013 " diatom ooze decorative wall material " test stone
It surveys.And it is compared with the diatom ooze coating now sold in the market.
Experimental method:
L, sample is smeared with sealed compartment, detects the projects such as its purifying formaldehyde efficiency, application property, wherein experiment examination
Sample ruler cun lll12；Sealed compartment volume lll13.
2, lll12 brushing sample qualities: 1200g.
3, experiment condition: temperature (202) DEG C, relative humidity 50+10%.
4, sample is detected according to non-catalysis material, and the clarification time is for 24 hours.
Its testing result is as shown in table l:
[table 1]
From upper table l, it can be seen that effect is aobvious due to using natural jade powder and titanium dioxide powder as main material in example
It writes and is higher than comparative example.Wherein, purifying formaldehyde efficiency is up to 95% purifying formaldehyde persistence and is up to 91%；
Caking ability reaches 0.92Mpa under standard state, and adhesion strength reaches 0.74Mpa after inundation, significantly larger than national standard
Even comparative example.
Claims (7)
1. a kind of jade mud and titanium dioxide powder compo, which is characterized in that be made of following raw material by weight: day
Right jade 80-85 parts by weight, titanium dioxide powder 1-10 parts by weight, dispersable adhesive powder 5-10 parts by weight, hydroxyl second methylcellulose
0.5-1 parts by weight.
2. jade mud as claimed in claim l and titanium dioxide powder compo, it is characterised in that: be added in above-mentioned coating negative
Oxonium ion powder 10-15 parts by weight.
3. jade slime paint as described in claim 1, which is characterized in that the natural jade and the ground system of titanium dioxide
At the powder for being greater than 800 mesh.
4. jade slime paint as claimed in claim 2, which is characterized in that the negative oxygen ion powder is ground at greater than 400 mesh
Powder.
5. jade slime paint as described in claim 1, which is characterized in that raw material further includes natural toner 0.1-0.5 parts by weight.
6. a kind of jade mud according to any one of claims 1-4 and titanium dioxide powder compo, it is characterised in that: including
Following steps: natural jade and titanium dioxide powder will be mixed according to weight ratio, and stirs 25- with powder stirrer
30min；Later according to weight ratio addition negative oxygen ion powder, dispersable adhesive powder and hydroxyethylmethylcellulose, it is used in combination
Powder stirrer stirs 25-30min to get finished product.
7. the preparation method of jade slime paint as described in claim 6, which is characterized in that further include adding right color in finished product
Powder simultaneously stirs evenly.