CN110450442A - A kind of production method of novel Variable-temperature cup - Google Patents
A kind of production method of novel Variable-temperature cup Download PDFInfo
- Publication number
- CN110450442A CN110450442A CN201910540624.5A CN201910540624A CN110450442A CN 110450442 A CN110450442 A CN 110450442A CN 201910540624 A CN201910540624 A CN 201910540624A CN 110450442 A CN110450442 A CN 110450442A
- Authority
- CN
- China
- Prior art keywords
- cup
- temperature
- variable
- resin
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of living goods, and disclose a kind of production method of novel Variable-temperature cup, the following steps are included: 1) resin and mill base is taken to be put into stirred tank, stirred tank starting in stirred tank resin and mill base heating after be sufficiently mixed and above-mentioned material is stayed do it is spare.The production method of the novel Variable-temperature cup, by adding luminescent powder, impart the completely new decorative form of cup appearance, in cup appearance, coat the luminescent powder for varying with temperature and changing, make the appearance color of cup, pattern changes with the variation of cup body temperature, and the shape of luminescent powder spraying and the color of the luminescent powder sprayed can change, to pleasantly surprised to people's one kind, surprised and reverie feeling, give people a kind of completely new visual effect changeable, people are made to generate strong interest to this phenomenon, to greatly cause the desire that people buy cup, achieve the purpose that cup promotes, be conducive to improve the competitiveness of enterprise.
Description
Technical field
The present invention relates to technical field of living goods, specially a kind of production method of novel Variable-temperature cup.
Background technique
Cup is a kind of vessel being specially filled with water, its major function is all for drinking or drinking tea, in ancient times from ancient times to the present
The cup having tea is referred to as teabowl with a cover, and basic type is straight mouth or opening mostly, and opening's edge diameter and cup are high almost equal, have it is flat,
Ring foot or high foot, archaeological materials show earliest cup first appeared in the Neolithic Age, either Yangshao culture, the Longshan culture still
The presence for having ceramic cup is all seen in the Hemudu Culture ruins, this period cup type multiplicity the most peculiar: having monaural or double with ear
Ear cup, mostly taper, tripodia cup, wine vessel shape cup and cup with high handle etc. with foot can be divided into glass according to making material difference
Cup, plastic cup, ceramic cup and wooden cup etc..
For example common teacup of existing cup, vacuum cup and health-care cup etc., their appearance all has certain decoration, has plenty of
The enamel of barbecue is drawn, and has plenty of glazing picture, is mostly the character pattern that coating is drawn, these decorations are to the promotion of product and to people
Bring and served in terms of aesthetic feeling certain, still, decorative form so is almost unchanged for many years, so that outside cup
Table decorative form seems outmoded, and old stuff does not have vigor, and the effect in terms of promotion is smaller and smaller, can not promote the purchase of consumer
Desire, enterprise competitiveness is low, so a kind of production method of novel Variable-temperature cup is proposed to solve the problems, such as above-mentioned propose.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides a kind of production method of novel Variable-temperature cup, having can change colour
The advantages of, the decorative form for solving cup for many years is almost unchanged, so that cup appearance decorative form seems outmoded, always
No vigor is covered, the effect in terms of promotion is smaller and smaller, can not promote the desire to purchase of consumer, and enterprise competitiveness is low to ask
Topic.
(2) technical solution
To realize the above-mentioned purpose that can change colour, the invention provides the following technical scheme: a kind of production of novel Variable-temperature cup
Method, comprising the following steps:
1) resin and mill base is taken to be put into stirred tank, stirred tank starting in stirred tank resin and mill base heating after carry out
Be sufficiently mixed and above-mentioned material is stayed do it is spare；
2) material will be made in step 1) and is poured into injection moulding machine obtained cup body；
3) from taking out the cup body prepared in injection moulding machine and being fixed on processing platform, then luminescent powder is taken to set
Enter in spray gun, spray gun uniformly sprays luminescent powder in cup body, obtains Variable-temperature cup cup body；
4) continue to take resin and repeat the operation in step 2, can be prepared by Variable-temperature cup cup lid, Variable-temperature cup cup lid and Variable-temperature cup
Cup body cooperation can be prepared by above-mentioned Variable-temperature cup.
Preferably, between 50-90 degree, the injection pressure of injection moulding machine exists the forming temperature of the injection moulding machine
Between 191-271 (Mpa).
Preferably, the content accounting of the resin, mill base and luminescent powder is respectively 80%, 10% and 10%, the mill base
For using resin paint vehicle as the resin mill base of adhesive, and a small amount of zinc naphthenate surfactant is added in mill base.
Preferably, the resin can be any in polypropylene, polyethylene, polystyrene, polytetrafluoroethylene (PTFE) and polycarbonate
One kind.
Preferably, the spraying method of the spray gun can be corona electrostatic spraying or friction electrostatic painting, and the spray gun can
To spray out different shapes in cup body, such as whole body spraying or locally sprayed, also such as rectangle, circle, symbol and animal
Shape.
Preferably, the luminescent powder can be in red noctilucent powder, blue noctilucent powder, purple noctilucent powder and green noctilucent powder
Any one.
(3) beneficial effect
Compared with prior art, the present invention provides a kind of production method of novel Variable-temperature cup, have it is following the utility model has the advantages that
1, the production method of the novel Variable-temperature cup imparts the completely new decorative form of cup appearance by addition luminescent powder,
It makes full use of cup to change this feature pouring into cold water-cup temperature, in cup appearance, coat vary with temperature and
The luminescent powder of variation changes the appearance color of cup, pattern with the variation of cup body temperature, and luminescent powder spraying shape and
The color of the luminescent powder sprayed can change, so that feeling pleasantly surprised to people's one kind, surprised and reverie, a kind of to people
Completely new visual effect changeable, makes people generate strong interest to this phenomenon, to greatly cause people's purchase
The desire for buying cup achievees the purpose that cup promotes, and is conducive to the competitiveness for improving enterprise.
2, the production method of the novel Variable-temperature cup, through the forming temperature of control injection moulding machine between 50-90 degree, when
When the mold of injection moulding machine is lower than 50 degree, the plastic produced is rough, is also easy to produce that welding is bad and current mark, works as injection molding
Buckling deformation easily occurs more than when the mold of machine is higher than 90 degree, controls what its temperature can guarantee to be molded by between 50-90 degree
Cup body is smooth, and Forming Quality is high, by being added with a small amount of zinc naphthenate surfactant in mill base, can make in mill base
Pigment be better dispersed in resin, it is ensured that cup body color after molding is uniform, further improves the quality of Variable-temperature cup, mentions
The competitiveness of high enterprise.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
The invention provides the following technical scheme: a kind of production method of novel Variable-temperature cup, comprising the following steps:
1) resin and mill base is taken to be put into stirred tank, stirred tank starting in stirred tank resin and mill base heating after carry out
Be sufficiently mixed and above-mentioned material is stayed do it is spare；
2) material will be made in step 1) and is poured into injection moulding machine obtained cup body, the forming temperature of injection moulding machine exists
Between 50-90 degree, the injection pressure of injection moulding machine is between 191-271 (Mpa)；
3) from taking out the cup body prepared in injection moulding machine and being fixed on processing platform, then luminescent powder is taken to set
Enter in spray gun, luminescent powder can be any one in red noctilucent powder, blue noctilucent powder, purple noctilucent powder and green noctilucent powder
Kind, spray gun uniformly sprays luminescent powder in cup body, obtains Variable-temperature cup cup body, the spraying method of spray gun can be quiet for corona
Electrospray or friction electrostatic painting, spray gun can spray out different shapes, such as whole body spraying or locally sprayed in cup body,
Also such as rectangle, circle, symbol and animals shaped can form different patterns after cup discoloration, significantly increase cup
The interest of son；
4) continue to take resin and repeat the operation in step 2, can be prepared by Variable-temperature cup cup lid, Variable-temperature cup cup lid and Variable-temperature cup
Cup body cooperation can be prepared by above-mentioned Variable-temperature cup, and the content accounting of resin, mill base and luminescent powder is respectively 80%, 10% and 10%,
Mill base be using resin paint vehicle as the resin mill base of adhesive, and in mill base be added with a small amount of zinc naphthenate surfactant, resin
It can be arbitrary a kind of in polypropylene, polyethylene, polystyrene, polytetrafluoroethylene (PTFE) and polycarbonate.
The beneficial effects of the present invention are: the production method of the novel Variable-temperature cup is imparted outside cup by adding luminescent powder
The completely new decorative form of table, it makes full use of cup to change this feature pouring into cold water-cup temperature, in cup appearance,
The luminescent powder for varying with temperature and changing is coated, changes the appearance color of cup, pattern with the variation of cup body temperature, and night
The shape of light powder spraying and the color of the luminescent powder sprayed can change, thus, surprised and reverie pleasantly surprised to people's one kind
Feeling, give a kind of completely new visual effect changeable of people, people made to generate strong interest to this phenomenon, thus
Greatly cause the desire that people buy cup, achievees the purpose that cup promotes, be conducive to the competitiveness for improving enterprise, pass through control
The forming temperature of injection moulding machine processed is between 50-90 degree, when the mold of injection moulding machine is lower than 50 degree, the plastic produced
It is rough, be also easy to produce that welding is bad and current mark, when the mold of injection moulding machine is higher than 90 degree more than buckling deformation easily occurs, control
Making its temperature can guarantee that the cup body being molded by is smooth between 50-90 degree, and Forming Quality is high, by adding in mill base
There is a small amount of zinc naphthenate surfactant, the pigment in mill base can be made to be better dispersed in resin, it is ensured that cup after molding
Body color is uniform, further improves the quality of Variable-temperature cup, improves the competitiveness of enterprise, solves the decoration shape of cup for many years
Formula is almost unchanged, so that cup appearance decorative form seems outmoded, old stuff does not have vigor, and the effect in terms of promotion is more next
It is smaller, the desire to purchase of consumer, the low problem of enterprise competitiveness can not be promoted.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of production method of novel Variable-temperature cup, which comprises the following steps:
1) resin and mill base is taken to be put into stirred tank, stirred tank starting in stirred tank resin and mill base heating after carry out it is abundant
Mix and above-mentioned material is stayed do it is spare；
2) material will be made in step 1) and is poured into injection moulding machine obtained cup body；
3) from taking out the cup body prepared in injection moulding machine and being fixed on processing platform, luminescent powder merging spray is then taken
In rifle, spray gun uniformly sprays luminescent powder in cup body, obtains Variable-temperature cup cup body；
4) continue to take resin and repeat the operation in step 2, can be prepared by Variable-temperature cup cup lid, Variable-temperature cup cup lid and Variable-temperature cup cup body
Cooperation can be prepared by above-mentioned Variable-temperature cup.
2. a kind of production method of novel Variable-temperature cup according to claim 1, which is characterized in that the injection moulding machine
Forming temperature is between 50-90 degree, and the injection pressure of injection moulding machine is between 191-271 (Mpa).
3. a kind of production method of novel Variable-temperature cup according to claim 1, which is characterized in that the resin, mill base and
The content accounting of luminescent powder is respectively 80%, 10% and 10%, the mill base be using resin paint vehicle as the resin mill base of adhesive,
And a small amount of zinc naphthenate surfactant is added in mill base.
4. a kind of production method of novel Variable-temperature cup according to claim 1, which is characterized in that the resin can be poly- third
It is arbitrary a kind of in alkene, polyethylene, polystyrene, polytetrafluoroethylene (PTFE) and polycarbonate.
5. a kind of production method of novel Variable-temperature cup according to claim 1, which is characterized in that the spraying side of the spray gun
Formula can spray out different shapes for corona electrostatic spraying or friction electrostatic painting, the spray gun in cup body, such as
Whole body spraying or locally sprayed, also such as rectangle, circle, symbol and animals shaped.
6. a kind of production method of novel Variable-temperature cup according to claim 1, which is characterized in that the luminescent powder can be
Any one in red noctilucent powder, blue noctilucent powder, purple noctilucent powder and green noctilucent powder.