CN110448043A - A kind of brush filament preparation method of antibacterial environment protection brush for machine - Google Patents
A kind of brush filament preparation method of antibacterial environment protection brush for machine Download PDFInfo
- Publication number
- CN110448043A CN110448043A CN201910657970.1A CN201910657970A CN110448043A CN 110448043 A CN110448043 A CN 110448043A CN 201910657970 A CN201910657970 A CN 201910657970A CN 110448043 A CN110448043 A CN 110448043A
- Authority
- CN
- China
- Prior art keywords
- brush
- brush filament
- environment protection
- cooling
- machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of brush filament preparation methods of antibacterial environment protection brush for machine, including glass fibre, epoxy resin, polyurethane resin, PBT resin part to be put into drying machine and be dried, then slicing treatment is carried out, hybrid slicing after drying is sufficiently mixed stirring with adjuvant, antibacterial agent, then melting extrusion is handled；The material of fusion plastification is extruded to shape through the mouth mold that inner cavity is multiple grooves, traction wire drawing obtains the primary brush filament that three-dimensional side is several fins；Twisting；It is impregnated in TPM9007 solution；The brush filament that the present invention obtains has excellent wear-resisting property and high resiliency, also has excellent antibacterial environment protection performance；Brush filament surface had both had three-dimensional concaveconvex structure, there is helicitic texture again, both it can preferably clean, the dirt to fall off when also can store scrub, it can be widely used for cleaning brush and polish brush, screw thread and concaveconvex structure more preferably can extract and accommodate the medium to be extracted simultaneously, effectively improve the scope of application of screw thread brush filament.
Description
Technical field
The present invention relates to brushes for machine to produce related fields, specially a kind of brush filament preparation side of antibacterial environment protection brush for machine
Method.
Background technique
Industrial hairbrush is that upgrading and improved novel product are carried out on the basis of civilian hairbrush, is mainly used for industrializing
Cleaning, dedusting, polishing in production process etc..Main material used be steel wire, copper wire, stainless steel wire, nylon yarn, plastic wire,
Abrasive filaments, horse tail hair, bristles, sisal hemp etc..
Existing brush filament has the disadvantage in that common brush filament surface is more smooth during use, cannot be clear well
The scope of application of clean body surface, common brush filament is more narrow；Performance of the existing brush for machine in terms of antibacterial environment protection simultaneously
It is poor, while its wearability is also to be improved.
Summary of the invention
The purpose of the present invention is to provide a kind of brush filament preparation methods of antibacterial environment protection brush for machine, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the invention provides the following technical scheme:
A kind of brush filament preparation method of antibacterial environment protection brush for machine, comprises the following specific steps that:
S1: by 16-20 parts of glass fibre, 18-22 parts of epoxy resin, 15-24 parts of polyurethane resin, 10-16 parts of PBT resin
It is put into drying machine and is dried, then carry out slicing treatment, by re-dry 2-3h after slice mixing；
S2: by the hybrid slicing after above-mentioned drying with 6-10 parts of adjuvant, 5-8 parts of antibacterial agent in 65-90 DEG C of condition
Under be sufficiently mixed stirring 20-30min, be then added in melt extruder progress melting extrusion processing；
S3: by the material of fusion plastification through inner cavity be multiple grooves mouth mold be extruded to shape, and by cooling-water machine into
Row cold water is cooling, then carries out traction wire drawing to material after cooling using dragger, and obtaining three-dimensional side is several fins
Primary brush filament；
S4: by primary brush filament, spiral winding is twisted two-by-two, and the bifilar brush filament of helical structure is formed after thermal finalization；
S5: by bifilar brush filament obtained above in the TPM9007 solution of 0.3-1% Initial Soak 2-3min, after drying
1-2min is impregnated again, and be then formed under the conditions of temperature is 110-125 DEG C 3-5min
S6: the said goods are obtained into brush filament finished product after cooling-water machine is cooling.
As a preferred technical solution of the present invention, adjuvant described in step S2 is fire retardant, coupling agent and solidification
Agent.
As a preferred technical solution of the present invention, antibacterial agent described in step S2 is that antibacterial agent is silver, zinc or silver-colored zinc
The phosphate or glass micro mist of compound.
As a preferred technical solution of the present invention, the melting temperature of melt extruder is 200-220 DEG C in step S2.
As a preferred technical solution of the present invention, the cooling temperature of cold water is 35-45 DEG C in step S3.
As a preferred technical solution of the present invention, material after cooling is pre-processed before being drawn in step S3,
Including alkaline etching, cleaning, lubrication.
It is circular configuration, circle knot in the middle part of the section of the primary brush filament as a preferred technical solution of the present invention
Structure is a circle strip structure, and the diameter of the circular configuration is 0.2-0.3mm.
Compared with prior art, the beneficial effects of the present invention are:
1. the present invention is using glass fibre, epoxy resin, polyurethane resin, PBT resin as the main raw material(s) of brush filament, ring
Protect it is pollution-free so that brush filament not only has an excellent wear-resisting property of glass fibre, while also with the high resiliency of resin；Anti-
Under the mixing of microbial inoculum, in conjunction with the immersion of subsequent dual antibacterial agent TPM9007 solution, so that the brush filament produced is with excellent
Antibacterial environment protection performance.
2. the present invention obtains solid by carrying out shaping the material of fusion plastification using the mouth mold that inner cavity is multiple grooves
Side be the primary brush filament of several fins, and the primary brush filament of fin structure is subjected to bifilar twisting, so that brush filament surface was both
With three-dimensional concaveconvex structure, and there is helicitic texture, both can preferably clean, the dirt to fall off when also can store scrub,
Cleaning efficiency is improved, can be widely used for cleaning brush and polish brush, while screw thread and concaveconvex structure can more preferably extract and receiving is wanted
The medium of extraction can be used in paintbrush, cosmetic brush and paintbrush, can also chemical sharpening, make as sharpening brushing bristle
With effectively improving the scope of application of screw thread brush filament, preferably remove dirt by scraping, and it can have with common brush filament
Same durability, and shape more abundant is provided.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1: the present invention provides a kind of technical solution: a kind of brush filament preparation method of antibacterial environment protection brush for machine, packet
Include following specific steps:
S1: by 16-20 parts of glass fibre, 18-22 parts of epoxy resin, 15-24 parts of polyurethane resin, 10-16 parts of PBT resin
It is put into drying machine and is dried, then carry out slicing treatment, by re-dry 2-3h after slice mixing；
S2: by the hybrid slicing after above-mentioned drying with 6-10 parts of adjuvant, 5-8 parts of antibacterial agent in 65-90 DEG C of condition
Under be sufficiently mixed stirring 20-30min, be then added in melt extruder progress melting extrusion processing；
S3: by the material of fusion plastification through inner cavity be multiple grooves mouth mold be extruded to shape, and by cooling-water machine into
Row cold water is cooling, then carries out traction wire drawing to material after cooling using dragger, and obtaining three-dimensional side is several fins
Primary brush filament；
S4: by primary brush filament, spiral winding is twisted two-by-two, and the bifilar brush filament of helical structure is formed after thermal finalization；
S5: by bifilar brush filament obtained above in the TPM9007 solution of 0.3-1% Initial Soak 2-3min, after drying
1-2min is impregnated again, and be then formed under the conditions of temperature is 110-125 DEG C 3-5min
S6: the said goods are obtained into brush filament finished product after cooling-water machine is cooling.
Further, adjuvant described in step S2 is fire retardant, coupling agent and curing agent.
Further, antibacterial agent described in step S2 is the phosphate or glass that antibacterial agent is silver, zinc or silver zinc complex object
Micro mist.
Further, the melting temperature of melt extruder is 200-220 DEG C in step S2.
Further, the cooling temperature of cold water is 35-45 DEG C in step S3.
Further, material after cooling is pre-processed before being drawn in step S3, including alkaline etching, cleaning, lubrication.
It further, is circular configuration in the middle part of the section of the primary brush filament, circular configuration is a circle strip structure, described
The diameter of circular configuration is 0.2-0.3mm.
The present invention is using glass fibre, epoxy resin, polyurethane resin, PBT resin as the main raw material(s) of brush filament, environmental protection
It is pollution-free, so that brush filament not only has the excellent wear-resisting property of glass fibre, while also with the high resiliency of resin；In antibacterial
Under the mixing of agent, in conjunction with the immersion of subsequent dual antibacterial agent TPM9007 solution, so that the brush filament produced is with excellent
Antibacterial environment protection performance.The present invention is obtained by being carried out shaping the material of fusion plastification using the mouth mold that inner cavity is multiple grooves
Three-dimensional side is the primary brush filament of several fins, and the primary brush filament of fin structure is carried out bifilar twisting, so that brush filament table
Face had not only had three-dimensional concaveconvex structure, but also had helicitic texture, both can preferably clean, the dirt to fall off when also can store scrub
Dirt improves cleaning efficiency, can be widely used for cleaning brush and polish brush, while screw thread and concaveconvex structure more preferably can be extracted and be accommodated
The medium to be extracted can be used in paintbrush, cosmetic brush and paintbrush, can also chemical sharpening, as sharpening brushing bristle
It uses, effectively improves the scope of application of screw thread brush filament, dirt is preferably removed by scraping, and it can have with common brush filament
There is same durability, and shape more abundant is provided.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of brush filament preparation method of antibacterial environment protection brush for machine, which is characterized in that comprise the following specific steps that:
S1: 16-20 parts of glass fibre, 18-22 parts of epoxy resin, 15-24 parts of polyurethane resin, 10-16 parts of PBT resin are put into
It is dried in drying machine, then carries out slicing treatment, by re-dry 2-3h after slice mixing；
S2: the hybrid slicing after above-mentioned drying is filled under the conditions of 65-90 DEG C with 6-10 parts of adjuvant, 5-8 parts of antibacterial agent
Divide and 20-30min is mixed, is then added to progress melting extrusion processing in melt extruder；
S3: the material of fusion plastification is extruded to shape through the mouth mold that inner cavity is multiple grooves, and is carried out by cooling-water machine cold
Water is cooling, then carries out traction wire drawing to material after cooling using dragger, and obtaining three-dimensional side is the first of several fins
Grade brush filament；
S4: by primary brush filament, spiral winding is twisted two-by-two, and the bifilar brush filament of helical structure is formed after thermal finalization；
S5: by bifilar brush filament obtained above in the TPM9007 solution of 0.3-1% Initial Soak 2-3min, after drying again
1-2min is impregnated, be then formed under the conditions of temperature is 110-125 DEG C 3-5min
S6: the said goods are obtained into brush filament finished product after cooling-water machine is cooling.
2. a kind of brush filament preparation method of antibacterial environment protection brush for machine according to claim 1, which is characterized in that step S2
Described in adjuvant be fire retardant, coupling agent and curing agent.
3. a kind of brush filament preparation method of antibacterial environment protection brush for machine according to claim 1, which is characterized in that step S2
Described in antibacterial agent be phosphate or glass micro mist that antibacterial agent is silver, zinc or silver zinc complex object.
4. a kind of brush filament preparation method of antibacterial environment protection brush for machine according to claim 1, which is characterized in that step S2
The melting temperature of middle melt extruder is 200-220 DEG C.
5. a kind of brush filament preparation method of antibacterial environment protection brush for machine according to claim 1, which is characterized in that step S3
The cooling temperature of middle cold water is 35-45 DEG C.
6. a kind of brush filament preparation method of antibacterial environment protection brush for machine according to claim 1, which is characterized in that step S3
Material after cooling is pre-processed before middle traction, including alkaline etching, cleaning, lubrication.
7. a kind of brush filament preparation method of antibacterial environment protection brush for machine according to claim 1, which is characterized in that described first
It is circular configuration in the middle part of the section of grade brush filament, circular configuration is a circle strip structure, and the diameter of the circular configuration is 0.2-
0.3mm。