CN110421656A - A kind of production technology of Environmental protection floor - Google Patents
A kind of production technology of Environmental protection floor Download PDFInfo
- Publication number
- CN110421656A CN110421656A CN201910742713.8A CN201910742713A CN110421656A CN 110421656 A CN110421656 A CN 110421656A CN 201910742713 A CN201910742713 A CN 201910742713A CN 110421656 A CN110421656 A CN 110421656A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- bamboo chip
- chip
- environmental protection
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production technologies of Environmental protection floor, including following preparation step: step 1: choosing suitable bamboo material, after pretreatment, bamboo chip is placed on slicer and carries out hacking, the bamboo chip after hacking is pressed into fragmentation but the not broken broken bamboo chip of bamboo filament fibre again, obtained bamboo chip is bamboo silk；Step 2: the bamboo silk that step 1 obtains is put into thermophilic digestion pot, and Vermins-proof mildew-proof agent is added, boiling 30-50min, then carbonization treatment is carried out to bamboo chip, bamboo chip is placed in the environment of high temperature, high humidity and high pressure, so that the organic compound in bamboo wood is decomposed denaturation, so that moth and mould is lost source of nutrition, while the worm's ovum being attached in bamboo wood and fungi being killed.For the present invention using bamboo wood as raw material, stock utilization is high, and product has the function of absorbing and sound absorption etc., wearable environment protection, and production easy to process, is appropriate for promoting.
Description
Technical field
The present invention relates to Environmental protection floor technical field, in particular to a kind of production technology of Environmental protection floor.
Background technique
Floor has a wide range of applications in current house decoration, and existing floor is mostly wooden, to expend very much
Timber, and the flooring product being made does not have absorbing and sound absorption function, and hygroscopic, it is easily-deformable.
Therefore, it is necessary to solve the above problems to invent a kind of production technology of Environmental protection floor.
Summary of the invention
The purpose of the present invention is to provide a kind of production technologies of Environmental protection floor, by connecting cork in bamboo base plate bottom
Plate can promote the elasticity on the floor, and absorbing, thin sound, and waterproof and dampproof, by being carried out with compound flame retardant aqueous solution to bamboo wood
Immersion treatment promotes the fire-retardant fireproof ability on the floor so that bamboo wood has good flame retardant property, by substituting wood with bamboo wood
Material can promote raw material availability, sustainable production, and more environmentally-friendly, Environmental protection floor density and hardness height, with very high anti-
Impact flexibility, while water absorption resistance, are unlikely to deform, to solve the problems mentioned in the above background technology.
To achieve the above object, the invention provides the following technical scheme:
A kind of production technology of Environmental protection floor, including following preparation step:
Step 1: choosing suitable bamboo material, after pretreatment, bamboo chip is placed on slicer and carries out hacking, then by the bamboo chip after hacking
It is pressed into fragmentation but the not broken broken bamboo chip of bamboo filament fibre, obtained bamboo chip is bamboo silk；
Step 2: the bamboo silk that step 1 obtains being put into thermophilic digestion pot, and Vermins-proof mildew-proof agent is added, boiling 30-50min,
Then carbonization treatment is carried out to bamboo chip, i.e., bamboo chip is placed in the environment of high temperature, high humidity and high pressure, makes the organic compound in bamboo wood
Object decomposes denaturation, so that moth and mould is lost source of nutrition, while the worm's ovum being attached in bamboo wood and fungi being killed；
Step 3: being dried the bamboo chip after boiling and carbonization treatment, and bamboo chip is then put into configured compounding and is hindered
It fires in agent aqueous solution, then impregnation 100-120min is dried；
Step 4: bamboo chip is placed in iron cage, is then placed in the glue pond for modulating glue, mentions iron cage after impregnating 15-25min
It rises and drains extra glue, then bamboo chip is put into the hopper of press, by bamboo chip cold moudling, further take out and be put into mold, and
Mold is put into solidification room and is solidified, taking-up, which is put into hot press, after 2-3h carries out hot pressing, and taking-up obtains bamboo substrate；
Step 5: shape and surface quality required for bamboo substrate is worked into, including saw head, open the light, sanding, fixed-length cut-off and
Vertically and horizontally fluting etc.；
Step 6: choose cork sheet be cut to it is suitably sized, then by step 5 obtain bamboo substrate take out, utilize hot press will
Cork sheet is hot-pressed onto bamboo base plate bottom, then carries out edge sealing using conductive adhesive tape in periphery, finally coats in bamboo flooring outer surface
The road 5-7 priming paint and 2 finishing coats decoration, obtain Environmental protection floor finished product.
Further, the pretreatment of described step one kind is first to rush open thick bamboo tube with colliding, and it is of substantially equal to obtain width
Then bamboo chip carries out force plane to bamboo chip with rough planing machine, remove bamboo blueness and the tabasheer of inner layer on surface layer, obtain substantially flat bamboo
Piece, and bamboo blueness will all be removed, the residual quantity of tabasheer is no more than 30%.
Further, certain oxidative bleaching agent can be also added in the step 2 in thermophilic digestion pot, since oxidation is floated
White dose of effect makes the bamboo wood color of all ages and classes and different parts reach unanimity, increases the aesthetics on floor.
Further, the compound flame retardant aqueous solution is after solid phosphoric acid hydrogen diammonium is dissolved into boric acid, then with it is water-soluble
Liquid compounds, and fire retardant mass fraction is 25-35%.
Further, the drying process of the step 3 is that bamboo chip is put into drying kiln, is heated using steam, is made
Moisture drops to 10% or less in bamboo chip.
Further, the cork sheet in the step 6 is using cork as raw material, through crushing, screening, glue mixing, membrane pressure, heat
Cork shavings made of the processes such as solidification, anatomy and sanding.
Technical effect and advantage of the invention:
1, by carrying out thermophilic digestion to bamboo chip material using Vermins-proof mildew-proof agent and oxidative bleaching agent, can by bamboo chip material can
Soluble organism is precipitated, and kills the worm's ovum in bamboo wood and mould, to achieve the purpose that Vermins-proof mildew-proof, then is carbonized to bamboo wood
Processing, makes the organic compound in bamboo wood, and such as sugar, starch and breaks down proteins denaturation make moth and mould lose source of nutrition,
Floor is avoided to damage by worms and go mouldy in use.
2, by installing conductive adhesive tape in floor periphery, during installation can by conductive adhesive tape casing wired earth, so as to
Electrostatic is guided, by connecting cork sheet in bamboo base plate bottom, the elasticity on the floor, and absorbing, thin sound can be promoted, and waterproof is anti-
Tide, by carrying out immersion treatment to bamboo wood with compound flame retardant aqueous solution, so that bamboo wood has good flame retardant property, being promoted should
The fire-retardant fireproof ability on floor.
3, by substituting timber with bamboo wood, raw material availability, sustainable production, and more environmentally-friendly, environmental protection ground can be promoted
Plate density and hardness is high, has very high toughness, while water absorption resistance, is unlikely to deform.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
Embodiment 1
A kind of production technology of Environmental protection floor, including following preparation step:
Step 1: choosing suitable bamboo material, after pretreatment, bamboo chip is placed on slicer and carries out hacking, then by the bamboo chip after hacking
It is pressed into fragmentation but the not broken broken bamboo chip of bamboo filament fibre, obtained bamboo chip is bamboo silk；
Step 2: the bamboo silk that step 1 obtains being put into thermophilic digestion pot, and Vermins-proof mildew-proof agent is added, boiling 30-50min,
Then carbonization treatment is carried out to bamboo chip, i.e., bamboo chip is placed in the environment of high temperature, high humidity and high pressure, makes the organic compound in bamboo wood
Object decomposes denaturation, so that moth and mould is lost source of nutrition, while the worm's ovum being attached in bamboo wood and fungi being killed；
Step 3: being dried the bamboo chip after boiling and carbonization treatment, and bamboo chip is then put into configured compounding and is hindered
It fires in agent aqueous solution, then impregnation 100-120min is dried；
Step 4: bamboo chip is placed in iron cage, is then placed in the glue pond for modulating glue, mentions iron cage after impregnating 15-25min
It rises and drains extra glue, then bamboo chip is put into the hopper of press, by bamboo chip cold moudling, further take out and be put into mold, and
Mold is put into solidification room and is solidified, taking-up, which is put into hot press, after 2-3h carries out hot pressing, and taking-up obtains bamboo substrate；
Step 5: shape and surface quality required for bamboo substrate is worked into, including saw head, open the light, sanding, fixed-length cut-off and
Vertically and horizontally fluting etc.；
Step 6: choose cork sheet be cut to it is suitably sized, then by step 5 obtain bamboo substrate take out, utilize hot press will
Cork sheet is hot-pressed onto bamboo base plate bottom, then carries out edge sealing using conductive adhesive tape in periphery, finally coats in bamboo flooring outer surface
The road 5-7 priming paint and 2 finishing coats decoration, obtain Environmental protection floor finished product.
Wherein, the pretreatment of described step one kind is first to rush open thick bamboo tube with colliding, and obtains the of substantially equal bamboo chip of width,
Then force plane is carried out to bamboo chip with rough planing machine, removes bamboo blueness and the tabasheer of inner layer on surface layer, obtains substantially flat bamboo chip, and bamboo
Blueness will all be removed, and the residual quantity of tabasheer is no more than 30%.
Wherein, certain oxidative bleaching agent can be also added in the step 2 in thermophilic digestion pot, due to oxidative bleaching agent
Effect, so that the bamboo wood color of all ages and classes and different parts is reached unanimity, increase the aesthetics on floor.
Wherein, after the compound flame retardant aqueous solution is dissolved into boric acid for solid phosphoric acid hydrogen diammonium, then it is multiple with aqueous solution
With forming, and fire retardant mass fraction is 25-35%.
Wherein, the drying process of the step 3 is that bamboo chip is put into drying kiln, is heated using steam, and bamboo chip is made
Interior moisture drops to 10% or less.
Wherein, the cork sheet in the step 6 be using cork as raw material, through crushing, screening, glue mixing, membrane pressure, heat cure,
It dissects and cork shavings made of the processes such as sanding.
Embodiment 2
Including following preparation step:
Step 1: choosing suitable bamboo material, after pretreatment, bamboo chip is placed on slicer and carries out hacking, then by the bamboo chip after hacking
It is pressed into fragmentation but the not broken broken bamboo chip of bamboo filament fibre, obtained bamboo chip is bamboo silk；
Step 2: the bamboo silk that step 1 obtains being put into thermophilic digestion pot, and Vermins-proof mildew-proof agent is added, boiling 30-50min,
Then carbonization treatment is carried out to bamboo chip, i.e., bamboo chip is placed in the environment of high temperature, high humidity and high pressure, makes the organic compound in bamboo wood
Object decomposes denaturation, so that moth and mould is lost source of nutrition, while the worm's ovum being attached in bamboo wood and fungi being killed；
Step 3: being dried the bamboo chip after boiling and carbonization treatment, and bamboo chip is then put into configured compounding and is hindered
It fires in agent aqueous solution, then impregnation 100-120min is dried；
Step 4: bamboo chip is placed in iron cage, is then placed in the glue pond for modulating glue, mentions iron cage after impregnating 15-25min
It rises and drains extra glue, then bamboo chip is put into the hopper of press, by bamboo chip cold moudling, further take out and be put into mold, and
Mold is put into solidification room and is solidified, taking-up, which is put into hot press, after 2-3h carries out hot pressing, and taking-up obtains bamboo substrate；
Step 5: shape and surface quality required for bamboo substrate is worked into, including saw head, open the light, sanding, fixed-length cut-off and
Vertically and horizontally fluting etc.；
Step 6: choose cork sheet be cut to it is suitably sized, then by step 5 obtain bamboo substrate take out, utilize hot press will
Cork sheet is hot-pressed onto bamboo base plate bottom, then carries out edge sealing using conductive adhesive tape in periphery, finally coats in bamboo flooring outer surface
The road 5-7 priming paint and 2 finishing coats decoration, obtain Environmental protection floor finished product.
Wherein, the pretreatment of described step one kind is first to rush open thick bamboo tube with colliding, and obtains the of substantially equal bamboo chip of width,
Then force plane is carried out to bamboo chip with rough planing machine, removes bamboo blueness and the tabasheer of inner layer on surface layer, obtains substantially flat bamboo chip, and bamboo
Blueness will all be removed, and the residual quantity of tabasheer is no more than 30%.
Wherein, certain oxidative bleaching agent can be also added in the step 2 in thermophilic digestion pot, due to oxidative bleaching agent
Effect, so that the bamboo wood color of all ages and classes and different parts is reached unanimity, increase the aesthetics on floor.
Wherein, after the compound flame retardant aqueous solution is dissolved into boric acid for solid phosphoric acid hydrogen diammonium, then it is multiple with aqueous solution
With forming, and fire retardant mass fraction is 30%, when fire retardant mass fraction is 30%, be can achieve after bamboo wood is soaking best
Flame retardant property.
Wherein, the drying process of the step 3 is that bamboo chip is put into drying kiln, is heated using steam, and bamboo chip is made
Interior moisture drops to 10% or less.
Wherein, the cork sheet in the step 6 be using cork as raw material, through crushing, screening, glue mixing, membrane pressure, heat cure,
It dissects and cork shavings made of the processes such as sanding.
The working principle of the invention and process for using: bamboo chip material is carried out using Vermins-proof mildew-proof agent and oxidative bleaching agent high
Dissolved organic matter in bamboo chip material can be precipitated, and kill the worm's ovum in bamboo wood and mould by warm boiling, anti-to reach insect prevention
Mould purpose, then carbonization treatment is carried out to bamboo wood, make the organic compound in bamboo wood, such as sugar, starch and breaks down proteins denaturation,
So that moth and mould is lost source of nutrition, floor is avoided to damage by worms and go mouldy in use, conducting resinl is installed in floor periphery
Item can connect cork sheet in bamboo base plate bottom by conductive adhesive tape casing wired earth, so as to guide electrostatic during installation,
The elasticity on the floor, and absorbing, thin sound can be promoted, and waterproof and dampproof, bamboo wood is carried out at immersion with compound flame retardant aqueous solution
Reason promotes the fire-retardant fireproof ability on the floor so that bamboo wood has good flame retardant property, substitutes timber with bamboo wood, can be promoted
Raw material availability, sustainable production, and it is more environmentally-friendly, the Environmental protection floor density and hardness is high, there is very high toughness,
Water absorption resistance simultaneously, is unlikely to deform.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (6)
1. a kind of production technology of Environmental protection floor, which is characterized in that including following preparation step:
Step 1: choosing suitable bamboo material, after pretreatment, bamboo chip is placed on slicer and carries out hacking, then by the bamboo chip after hacking
It is pressed into fragmentation but the not broken broken bamboo chip of bamboo filament fibre, obtained bamboo chip is bamboo silk；
Step 2: the bamboo silk that step 1 obtains being put into thermophilic digestion pot, and Vermins-proof mildew-proof agent is added, boiling 30-50min,
Then carbonization treatment is carried out to bamboo chip, i.e., bamboo chip is placed in the environment of high temperature, high humidity and high pressure, makes the organic compound in bamboo wood
Object decomposes denaturation, so that moth and mould is lost source of nutrition, while the worm's ovum being attached in bamboo wood and fungi being killed；
Step 3: being dried the bamboo chip after boiling and carbonization treatment, and bamboo chip is then put into configured compounding and is hindered
It fires in agent aqueous solution, then impregnation 100-120min is dried；
Step 4: bamboo chip is placed in iron cage, is then placed in the glue pond for modulating glue, mentions iron cage after impregnating 15-25min
It rises and drains extra glue, then bamboo chip is put into the hopper of press, by bamboo chip cold moudling, further take out and be put into mold, and
Mold is put into solidification room and is solidified, taking-up, which is put into hot press, after 2-3h carries out hot pressing, and taking-up obtains bamboo substrate；
Step 5: shape and surface quality required for bamboo substrate is worked into, including saw head, open the light, sanding, fixed-length cut-off and
Vertically and horizontally fluting etc.；
Step 6: choose cork sheet be cut to it is suitably sized, then by step 5 obtain bamboo substrate take out, utilize hot press will
Cork sheet is hot-pressed onto bamboo base plate bottom, then carries out edge sealing using conductive adhesive tape in periphery, finally coats in bamboo flooring outer surface
The road 5-7 priming paint and 2 finishing coats decoration, obtain Environmental protection floor finished product.
2. a kind of production technology of Environmental protection floor according to claim 1, it is characterised in that: the pre- place of described step one kind
Reason obtains the of substantially equal bamboo chip of width, then carries out force plane to bamboo chip with rough planing machine, remove first to rush open thick bamboo tube with colliding
The bamboo blueness on surface layer and the tabasheer of inner layer obtain substantially flat bamboo chip, and bamboo blueness will all be removed, and the residual quantity of tabasheer cannot surpass
Cross 30%.
3. a kind of production technology of Environmental protection floor according to claim 1, it is characterised in that: the step 2 is steamed in high temperature
Certain oxidative bleaching agent can also be added in saucepan, due to the effect of oxidative bleaching agent, make the bamboo of all ages and classes and different parts
Material color reaches unanimity, and increases the aesthetics on floor.
4. a kind of production technology of Environmental protection floor according to claim 1, it is characterised in that: the compound flame retardant is water-soluble
Liquid is after solid phosphoric acid hydrogen diammonium is dissolved into boric acid, then compounds with aqueous solution, and fire retardant mass fraction is 25-
35%.
5. a kind of production technology of Environmental protection floor according to claim 1, it is characterised in that: at the drying of the step 3
Reason is that bamboo chip is put into drying kiln, is heated using steam, and moisture in bamboo chip is made to drop to 10% or less.
6. a kind of production technology of Environmental protection floor according to claim 1, it is characterised in that: the cork in the step 6
Plate is using cork as raw material, through cork shavings made of the processes such as crushing, screening, glue mixing, membrane pressure, heat cure, anatomy and sanding.