CN110407501A - A kind of permeable Concrete strength agent - Google Patents
A kind of permeable Concrete strength agent Download PDFInfo
- Publication number
- CN110407501A CN110407501A CN201910749163.2A CN201910749163A CN110407501A CN 110407501 A CN110407501 A CN 110407501A CN 201910749163 A CN201910749163 A CN 201910749163A CN 110407501 A CN110407501 A CN 110407501A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- concrete strength
- concrete
- reducing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of permeable Concrete strength agent, which is characterized in that potent dose of the raw material includes: 10~25 parts of sodium lignin sulfonate in parts by weight;1~5 part of isoamyl alcohol polyoxyethylene ether;5~10 parts of water-reducing agent;Wherein, the raw material of the water-reducing agent includes lignosulfonates, sodium alkyl sulfonate and Long carbon chain alkylol.It joined special water-reducing agent in the Concrete strength agent, while guaranteeing concreting machinery performance, so that the water-reducing rate of concrete is improved to 20% or more in the case where not adding other water-reducing agents, and give concrete good water permeability.
Description
Technical field
The invention belongs to concrete additive fields, are related to a kind of permeable Concrete strength agent.
Background technique
Concrete be most widely used in modern society, a kind of maximum construction material of usage amount, China is in the world
Using the maximum country of concrete material, as country is for the huge investment of foundation construction field and for the urgent of urbanization
The situation for growth of walking unhurriedly is presented in the usage amount short time of demand, China's concrete and associated materials, concrete passes through concrete
The hydration reaction solidification carried out between material is to have stronger compression strength, however, due to existing between concrete material
Barrier is reacted, the hydration reaction of common concrete material is only capable of completion 70~80%, moreover, the hydration reaction class of concrete material
Like the process of crystal structure, the product that common concrete material only has about 80% after hydration reaction is formd with structural strength
Concrete, there are segmental defects for remaining reaction product, and the compression strength of concrete entirety is caused not can be further improved.
In order to further increase the performance of concrete, generallys use add potent dose, potent dose thereto in the prior art
Main function it is main there are two, first is that increase concrete material dispersibility so that can between the particle of concrete material
Fully disperse, prevent it from reuniting together, and then accelerate the hydration process of cement, reduces the usage amount of cement in concrete,
Second is that increasing other concrete additives such as water-reducing agent etc. for the adsorption capacity of concrete material, enhance its using effect.
108424030 A of CN discloses a kind of collapse protection type Concrete strength agent, and in parts by weight, described potent dose includes
Following component: 6~20 parts of lignosulfonates, 6~20 parts of polyquaterniums, 1~8 part of isoamyl alcohol polyoxyethylene ether, 8~20 parts
Hydroxylamine, the technical solution can be improved the workability of concrete by introducing polyquaternium in potent dose of conventional concrete,
And the slump-loss of concrete can be effectively reduced under the premise of enhancing concrete strength.
104016617 A of CN discloses a kind of Concrete strength agent and preparation method thereof, and Concrete strength agent includes isoamyl
1~8 parts by weight of enol polyoxyethylene ether;8~20 parts by weight of triethanolamine;4~15 parts by weight of modified starch;Sodium lignin sulfonate
6~20 parts by weight;1~8 parts by weight of filler material;And 27~70 parts by weight of moisture.Preparation method includes: first by prenol
Polyoxyethylene ether, sodium lignin sulfonate, filler material are added in reactor, are stirred 1~2 hour, are obtained at a temperature of 50~80 DEG C
To mixture A;And then stir triethanolamine, modified starch in water 0.5~1 hour, obtain mixture B;Finally to mixing
Mixture B is poured into object A, after being mixed 1 hour, obtains Concrete strength agent mother liquor.The technical solution can be applied to coagulation
Soil additive technical field can be realized and be effectively improved defect present in concrete in the prior art, can be improved concrete
Comprehensive performance.
In the prior art, in potent dose of raw material usually include water-reducing agent, and in water-reducing agent polycarboxylate water-reducer performance
Preferably, but its higher cost, and preparation process is complicated.Compared to polycarboxylic acids dehydragent, ligninsulfonate water-reducing agent cost
Low, preparation process is simple, but its water-reducing rate generally only has 8~10%, and use scope is relatively narrow.
Summary of the invention
To solve the technical problems existing in the prior art, the present invention provides a kind of permeable Concrete strength agent, described
It joined special water-reducing agent in Concrete strength agent, while guaranteeing concreting machinery performance, so that subtracting not adding other
The water-reducing rate of concrete is improved to 20% or more in the case where aqua, and gives concrete good water permeability.
In order to achieve the above object, the invention adopts the following technical scheme:
The present invention provides a kind of permeable Concrete strength agent, and potent dose of the raw material includes: in parts by weight
10~25 parts of sodium lignin sulfonate;
1~5 part of isoamyl alcohol polyoxyethylene ether;
5~10 parts of water-reducing agent;
Wherein, the raw material of the water-reducing agent includes lignosulfonates, sodium alkyl sulfonate and Long carbon chain alkylol.
Wherein, the parts by weight of ligninsulfonate can be 11 parts, 12 parts, 13 parts, 14 parts, 15 parts, 16 parts, 17 parts, 18 parts,
19 parts, 20 parts, 21 parts, 22 parts, 23 or 24 parts etc., the parts by weight of water-reducing agent can be 6 parts, 6.5 parts, 7 parts, 7.5 parts, 8 parts,
8.5 parts, 9 parts or 9.5 parts etc., the parts by weight of isoamyl alcohol polyoxyethylene ether can be 1.5 parts, 2 parts, 2.5 parts, 3 parts, 3.5 parts,
4 parts or 4.5 parts etc., it is not limited to cited numerical value, other interior unlisted numerical value of above-mentioned each numberical range are equally suitable
With.
As currently preferred technical solution, according to mass parts meter, the raw material of the water-reducing agent includes:
20~30 parts of lignosulfonates;
12~20 parts of sodium alkyl sulfonate;
12~20 parts of Long carbon chain alkylol.
Wherein, the mass parts of lignosulfonates can be 21 parts, 22 parts, 23 parts, 24 parts, 25 parts, 26 parts, 27 parts, 28
Part or 29 parts etc., the mass parts of sodium alkyl sulfonate can be 13 parts, 14 parts, 15 parts, 16 parts, 17 parts, 18 parts or 19 parts etc., long carbon
The mass parts of alkyl group alcohol can be 13 parts, 14 parts, 15 parts, 16 parts, 17 parts, 18 parts or 19 parts etc., it is not limited to listed
The numerical value of act, other interior unlisted numerical value of above-mentioned each numberical range are equally applicable.
In the present invention, sodium alkyl sulfonate and lignosulfonates are used in compounding, improved solid in water-reducing agent and concrete
The binding ability of body particle, but sodium alkyl sulfonate itself has Long carbon chain, and ligninsulfonate has multiple benzene ring structures, this
It is weaker to have resulted in intermolecular force between the two, and the Long carbon chain in sodium alkyl sulfonate easily itself is twined by Van der Waals force
Around together, therefore long-chain is added in order to further increase the binding ability of solid particle in water-reducing agent and concrete in the present invention
Alkylol has sodium alkyl sulfonate to have multiple oxygen atoms, can be used as hydrogen binding sites, and long-chain alkyl alcohol itself has hydroxyl,
Hydrogen bond can be formed, Long carbon chain can be acted on by Van der Waals force and sodium alkyl sulfonate, increase sodium alkyl sulfonate and sulfomethylated lignin
The synergistic effect of hydrochlorate, so that the water reducing ability of water-reducing agent is further promoted.
In the present invention, described potent dose play enhancing concreting machinery intensity while, due to water-reducing agent and concrete
In solid particle combine after sparse water-repellent layer is formd in solid particles surface, due between solid particle accumulate after exist
Gap, when moisture flows into, since the presence of water-repellent layer makes moisture be not easy to accumulate in the gap between solid particle, enhancing
The water permeable ability of hole, improves the water permeability of concrete in concrete.
As currently preferred technical solution, the matter of lignosulfonates and the sodium alkyl sulfonate in the water-reducing agent
Amount is than being (1.2~1.5): 1, such as 1.25:1,1.3:1,1.35:1,1.4:1 or 1.45:1, it is not limited to cited
Numerical value, other interior unlisted numerical value of the numberical range are equally applicable.
As currently preferred technical solution, the ligninsulfonate is wooden sodium sulfonate.
Preferably, the Long carbon chain alkylol includes the sodium alkyl sulfonate of C12~C18, such as C13, C14, C15, C16 or
The Long carbon chain alkylol of C17.
Preferably, the sodium alkyl sulfonate is the sodium alkyl sulfonate of C12~C18, such as C13, C14, C15, C16 or C17
Sodium alkyl sulfonate.
As currently preferred technical solution, in parts by weight, the water-reducing agent includes 1~5 part of air entraining agent, such as
1.5 parts, 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts or 4.5 parts etc., it is not limited to cited numerical value, in the numberical range
Other unlisted numerical value are equally applicable.
Preferably, the air entraining agent includes rosin tree lipid air entraining agent and/or benzene sulfonamide acids air entraining agent.
Preferably, in parts by weight, described potent dose includes 40~60 parts of water, such as 42 parts, 45 parts, 48 parts, 50 parts, 52
Part, 55 parts or 58 parts etc., it is not limited to cited numerical value, other unlisted numerical value are equally suitable in the numberical range
With.
As currently preferred technical solution, in parts by weight, described potent dose includes 30~50 parts of water, and such as 32
Part, 35 parts, 38 parts, 40 parts, 42 parts, 45 parts or 48 parts etc., it is not limited to cited numerical value, in the numberical range other
Unlisted numerical value is equally applicable.
As currently preferred technical solution, the preparation method of the water-reducing agent includes:
The lignosulfonates and the sodium alkyl sulfonate are mixed, the Long carbon chain alkylol mixing is added,
It heats and stands after mixing, cooling obtains the water-reducing agent.
As currently preferred technical solution, the lignosulfonates and sodium alkyl sulfonate mix under stiring.
Preferably, the rate of the overtime work is 200~500rpm, such as 250rpm, 300rpm, 350rpm, 400rpm or
450rpm etc., it is not limited to cited numerical value, other interior unlisted numerical value of the numberical range are equally applicable.
Preferably, the time of the stirring be 30~90min, as 35min, 40min, 45min, 50min, 55min,
60min, 65min, 70min, 75min, 80min or 85min etc., it is not limited to cited numerical value, in the numberical range
Other unlisted numerical value are equally applicable.
As currently preferred technical solution, mixed under stiring after the Long carbon chain alkylol is added.
Preferably, the rate of the overtime work is 200~500rpm, such as 250rpm, 300rpm, 350rpm, 400rpm or
450rpm etc., it is not limited to cited numerical value, other interior unlisted numerical value of the numberical range are equally applicable.
Preferably, the time of the stirring be 30~90min, as 35min, 40min, 45min, 50min, 55min,
60min, 65min, 70min, 75min, 80min or 85min etc., it is not limited to cited numerical value, in the numberical range
Other unlisted numerical value are equally applicable.
Preferably, the temperature of the heating is 40~60 DEG C, such as 42 DEG C, 45 DEG C, 48 DEG C, 50 DEG C, 52 DEG C, 55 DEG C or 58 DEG C
Deng it is not limited to cited numerical value, other unlisted numerical value are equally applicable in the numberical range.
Preferably, the time that the heating is stood is 120~180min, such as 130min, 140min, 150min, 160min
Or 170min etc., it is not limited to cited numerical value, other interior unlisted numerical value of the numberical range are equally applicable.
As currently preferred technical solution, the lignosulfonates and the sodium alkyl sulfonate mix jointly with water
It closes.
Preferably, air entraining agent is added when the Long carbon chain alkylol is added.
Compared with prior art, the present invention at least has the advantages that
The present invention provides a kind of permeable Concrete strength agent, joined special diminishing in the Concrete strength agent
Agent, while guaranteeing concreting machinery performance, so that the water-reducing rate of concrete improves in the case where not adding other water-reducing agents
To 20% or more, and give concrete good water permeability.
Specific embodiment
Of the invention for ease of understanding, it is as follows that the present invention enumerates embodiment.Those skilled in the art are it will be clearly understood that the implementation
Example is only to aid in the understanding present invention, should not be regarded as a specific limitation of the invention.
Embodiment 1
The present embodiment provides a kind of permeable Concrete strength agent, potent dose of the raw material includes: in parts by weight
10 parts of sodium lignin sulfonate, 1 part of isoamyl alcohol polyoxyethylene ether TPEG-2400,5 parts of water-reducing agent, 30 parts of water.
The water-reducing agent the preparation method comprises the following steps:
20 parts of sodium lignin sulfonates, 40 parts of water and 15 parts of dodecyl sodium sulfates are stirred at 200 rpm
90min adds 12 parts of octadecyl alcolol continuation and is stirred 90min at 200 rpm, stands 180min at 40 DEG C after mixing, cold
But the water-reducing agent is obtained to room temperature.
Embodiment 2
The present embodiment provides a kind of permeable Concrete strength agent, potent dose of the raw material includes: in parts by weight
25 parts of sodium lignin sulfonate, 5 parts of isoamyl alcohol polyoxyethylene ether TPEG-2400,10 parts of water-reducing agent, 50 parts of water.
The water-reducing agent the preparation method comprises the following steps:
30 parts of sodium lignin sulfonates, 60 parts of water and 20 parts of dodecyl sodium sulfates are stirred at 500 rpm
30min adds 20 parts of hexadecanol continuation and is stirred 30min at 500 rpm, stands 120min at 60 DEG C after mixing, cold
But the water-reducing agent is obtained to room temperature.
Embodiment 3
The present embodiment provides a kind of permeable Concrete strength agent, potent dose of the raw material includes: in parts by weight
20 parts of sodium lignin sulfonate, 3 parts of isoamyl alcohol polyoxyethylene ether TPEG-2400,8 parts of water-reducing agent, 40 parts of water.
The water-reducing agent the preparation method comprises the following steps:
22 parts of sodium lignin sulfonates, 50 parts of water and 16 parts of dodecyl sodium sulfates are stirred at 300 rpm
60min adds 20 parts of lauryl alcohol continuation and is stirred 60min at 300 rpm, stands 150min at 50 DEG C after mixing, cold
But the water-reducing agent is obtained to room temperature.
Embodiment 4
The present embodiment provides a kind of permeable Concrete strength agent, potent dose of the raw material includes: in parts by weight
20 parts of sodium lignin sulfonate, 3 parts of isoamyl alcohol polyoxyethylene ether TPEG-2400,8 parts of water-reducing agent, 40 parts of water.
The water-reducing agent the preparation method comprises the following steps:
22 parts of sodium lignin sulfonates, 50 parts of water and 16 parts of dodecyl sodium sulfates are stirred at 300 rpm
60min, adds 20 parts of lauryl alcohols and 1 part of neopelex continuation is stirred 60min at 300 rpm, mixes
150min is stood at 50 DEG C afterwards, is cooled to room temperature to obtain the water-reducing agent.
Embodiment 5
The present embodiment provides a kind of permeable Concrete strength agent, potent dose of the raw material includes: in parts by weight
20 parts of sodium lignin sulfonate, 3 parts of isoamyl alcohol polyoxyethylene ether TPEG-2400,8 parts of water-reducing agent, 40 parts of water.
The water-reducing agent the preparation method comprises the following steps:
22 parts of sodium lignin sulfonates, 50 parts of water and 16 parts of dodecyl sodium sulfates are stirred at 300 rpm
60min, adds 20 parts of lauryl alcohols and 5 parts of neopelex continuation are stirred 60min at 300 rpm, mixes
150min is stood at 50 DEG C afterwards, is cooled to room temperature to obtain the water-reducing agent.
Comparative example 1
This comparative example is only added outside 38 parts of sodium lignin sulfonates in addition to being added without 16 parts of dodecyl sodium sulfates,
His condition is same as Example 3.
Comparative example 2
This comparative example is added outside 70 parts of water in addition to being added without 20 parts of lauryl alcohols, other conditions with 3 phase of embodiment
Together.
Comparative example 3
This comparative example is 26 parts in addition to wooden sodium sulfonate, dodecyl sodium sulfate be 12 especially, other conditions with implementation
Example 3 is identical.
Comparative example 4
This comparative example is 20 parts in addition to wooden sodium sulfonate, dodecyl sodium sulfate be 18 especially, other conditions with implementation
Example 3 is identical.
According to voluntarily concrete batching material is formulated, concrete component is in parts by weight are as follows: 461 parts of cement (autogamy,
Ingredient is portland cement clinker 78%, gypsum 4.5%, lime stone 7.5% and flyash 10% in percentage by weight), fine coal
Grey 90 parts, 50 parts of miberal powder, 512 parts of sand, 1252 parts of stone, also the Guangdong Built to Last energy conservation and environmental protection added with 0.01% is real in cement
The QZ-99B type grinding aid of industry Co., Ltd production.
Respectively by embodiment 1-5 and comparative example the 1-4 Concrete strength agent being prepared and water according to weight ratio 1:19
Proportional arrangement at solution, above-mentioned solution, water and concrete material mix to (ratio of water and concrete material is respectively
0.079:1), solid by 28d at room temperature so that the weight of the Concrete strength agent in solution accounts for the 0.5% of mixture total weight
Change, obtains concrete, water intaking and concrete material (water-reducing agent replaces all with sodium lignin sulfonate in potent dose) are according to identical
Ratio mixing, solidifies by 28d at room temperature, and obtained concrete is as blank example 1, and water intaking and concrete material are (in potent dose
It is added without water-reducing agent) it is mixed according to same ratio, solidify at room temperature by 28d, obtained concrete is as blank example 2.
It is tested by performance of the following test method to each coagulation obtained above, test result is listed in table 1.
(1) concrete workability is tested
According to standard GB/T/T 50080-2002 " Standard for test methods of properties of ordinary concrete mixture standard "
Method tests the workability and working performance of concrete.
(2) concrete crushing strength is tested
According to side described in standard GB/T/T 50081-2002 " standard for test methods of mechanical properties of ordinary concrete "
Method tests the compression strength of concrete.
(3) permeability rate is tested
It is measured according to method described in standard CJJ/T135-2009 " water-permeable cement concrete pavement technique regulation " above-mentioned
The permeability rate of regeneration concrete 1~21.
Table 1
According to the ratio of above-mentioned concrete material and water, the dosage 5%, 15% and 25% of water is successively reduced, other
Part is constant, carries out the test of workability and compression strength again, as a result as shown in Table 2-4.
Table 2
Table 3
Workability | Compression strength/MPa | Permeability rate/mm/s | |
Embodiment 1 | It is good | 35.8 | 24.7 |
Embodiment 2 | It is good | 35.6 | 26.1 |
Embodiment 3 | It is good | 35.2 | 24.8 |
Embodiment 4 | It is good | 35.3 | 25.1 |
Embodiment 5 | It is good | 35.7 | 25.2 |
Comparative example 1 | Well | 33.7 | 16.5 |
Comparative example 2 | Well | 33.5 | 16.3 |
Comparative example 3 | Well | 33.1 | 16.5 |
Comparative example 4 | Well | 33.2 | 16.2 |
Blank example 1 | Well | 32.6 | 13.7 |
Blank example 2 | Generally | 30.3 | 11.9 |
Table 4
It can be seen that from the test result of table 1-4 compared to blank example 2, after potent dose of addition water-reducing agent, the sum of concrete
Yi Xing, compression strength and water penetration increase.When water consumption it is less 5% when, embodiment 1-5 and comparative example 1-4 are mentioned
Less, blank example 1 is only with wooden sodium sulfonate for easy property, compression strength and the water penetration variation for the concrete that the water-reducing agent of confession is added
As the water-reducing agent in potent dose, change still little.When water consumption reduces 15%, comparative example 1-4 and blank example 1
Yi Xing, compression strength and water penetration, which produce, to be decreased obviously, and the workability of embodiment 1-5, compression strength and permeable
Property slightly declines.When water consumption reduces 25%, the easy property of comparative example 1-4 and blank example 1, compression strength and water penetration are equal
It produces and is decreased obviously, and easy property, compression strength and the water penetration of embodiment 1-5 slightly decline.As it can be seen that provided by the invention
Potent dose of permeable concrete substantially increases concrete permeable ability and water reducing ability, while other components being added are honest and clean
Valence chemicals, so that water-reducing agent provided by the invention has very strong economic benefit.
The Applicant declares that the present invention is explained by the above embodiments detailed process equipment and process flow of the invention,
But the present invention is not limited to the above detailed process equipment and process flow, that is, it is above-mentioned detailed not mean that the present invention must rely on
Process equipment and process flow could be implemented.It should be clear to those skilled in the art, any improvement in the present invention,
Addition, selection of concrete mode of equivalence replacement and auxiliary element to each raw material of product of the present invention etc., all fall within of the invention
Within protection scope and the open scope.
Claims (10)
1. a kind of permeable Concrete strength agent, which is characterized in that potent dose of the raw material includes: in parts by weight
10~25 parts of sodium lignin sulfonate;
1~5 part of isoamyl alcohol polyoxyethylene ether;
5~10 parts of water-reducing agent;
Wherein, the raw material of the water-reducing agent includes lignosulfonates, sodium alkyl sulfonate and Long carbon chain alkylol.
2. Concrete strength agent according to claim 1, which is characterized in that according to mass parts meter, the original of the water-reducing agent
Material includes:
20~30 parts of lignosulfonates;
12~20 parts of sodium alkyl sulfonate;
12~20 parts of Long carbon chain alkylol.
3. Concrete strength agent according to claim 1 or 2, which is characterized in that lignosulfonates in the water-reducing agent
Mass ratio with the sodium alkyl sulfonate is (1.2~1.5): 1.
4. Concrete strength agent according to claim 1-3, which is characterized in that the ligninsulfonate is wooden
Sodium sulfonate;
Preferably, the sodium alkyl sulfonate includes the sodium alkyl sulfonate of C12~C18;
Preferably, the Long carbon chain alkylol is the Long carbon chain alkylol of C12~C18.
5. Concrete strength agent according to claim 1-4, which is characterized in that in parts by weight, described to subtract
Aqua includes 1~5 part of air entraining agent;
Preferably, the air entraining agent includes rosin tree lipid air entraining agent and/or benzene sulfonamide acids air entraining agent;
Preferably, in parts by weight, the water-reducing agent includes 40~60 parts of water.
6. Concrete strength agent according to claim 1-5, which is characterized in that in parts by weight, described strong
Imitating agent includes 30~50 parts of water.
7. Concrete strength agent according to claim 1-6, which is characterized in that the water-reducing agent preparation method packet
It includes:
The lignosulfonates and the sodium alkyl sulfonate are mixed, the Long carbon chain alkylol mixing, mixing are added
Heating is stood afterwards, and cooling obtains the water-reducing agent.
8. Concrete strength agent according to claim 7, which is characterized in that the lignosulfonates and alkyl sulfonic acid
Sodium mixes under stiring;
Preferably, the rate of the overtime work is 200~500rpm;
Preferably, the time of the stirring is 30~90min.
9. Concrete strength agent according to claim 7, which is characterized in that stirred after the Long carbon chain alkylol is added
Lower mixing;
Preferably, the rate of the overtime work is 200~500rpm;
Preferably, the time of the stirring is 30~90min;
Preferably, the temperature of the heating is 40~60 DEG C;
Preferably, the time that the heating is stood is 120~180min.
10. Concrete strength agent according to claim 7, which is characterized in that the lignosulfonates and the alkane
Base sodium sulfonate mixes jointly with water;
Preferably, air entraining agent is added when the Long carbon chain alkylol is added.