CN110391051A - A kind of preparation method of lithium and graphene composite film - Google Patents
A kind of preparation method of lithium and graphene composite film Download PDFInfo
- Publication number
- CN110391051A CN110391051A CN201810351747.XA CN201810351747A CN110391051A CN 110391051 A CN110391051 A CN 110391051A CN 201810351747 A CN201810351747 A CN 201810351747A CN 110391051 A CN110391051 A CN 110391051A
- Authority
- CN
- China
- Prior art keywords
- lithium
- nmp
- composite film
- preparation
- graphene composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method of lithium and graphene composite film, process are as follows: (1) by the NMP(N- N-methyl-2-2-pyrrolidone N of nano oxidized graphite and electrically conductive polyaniline) slurry, nanometer lithium NMP slurry be sequentially placed into container, high-speed stirred is uniform;(2) adjuvant is added and stirs evenly;(3) mixed material is placed on silicon substrate plate, tiling is uniform, then thereon with another silicon substrate plate valve deck;(4) sandwich silicon substrate plate is placed in micro-wave oven and is heated 5 minutes, after material is cooling, product lithium and graphene composite film can be obtained.It is demonstrated experimentally that required product can be obtained in examples detailed above, obtaining product has many advantages, such as that electrochemistry is excellent, and transparency is good.
Description
Technical field
The present invention relates to the preparation methods of a kind of lithium and graphene composite film, belong to new function material field.
Background technique
The invention patent relates to the properties of lithium and graphene.
Lithium is most light alkali metal element.Masurium derives from Greek, and original meaning is " stone ".1817 by Sweden's science
Family's A Fuwei acute hearing is in analysis petalite mine Shi Faxian.Main lithium minerals is spodumene, lepidolite, petalite in nature
With peganite etc..Lithium can be found in humans and animals body, soil and mineral water, cocoa power, tobacco leaf, seaweed.Lithium metal is
A kind of argenteous light metal.Lithium metal dissolves in liquefied ammonia.Lithium is different from other alkali metal, at room temperature compared with water reaction
Slowly, but the lithium nitride crystal for generating black can be reacted with nitrogen.The salt of weak acid of lithium is all insoluble in water.In alkali metal chloride
In, only lithium chloride is soluble in organic solvent.The flame of the volatile salts of lithium is in peony, can identify lithium with this.Lithium holds very much
Easily with the chemical combination such as oxygen, nitrogen, sulphur, deoxidier can be used as in metallurgical industry.It is light that lithium can also do lead-containing alloy and beryllium, magnesium, aluminium etc.
The ingredient of matter alloy.Lithium has important use in atomic energy industry.
Graphene (Graphene) is the only one layer of atomic thickness for being stripped out from graphite material, being made of carbon atom
Two dimensional crystal.2004, Univ Manchester UK physicist An Deliegaimu and Constantine's Nuo Woxiao love,
Graphene is isolated in success from graphite, it was demonstrated that therefore it can also obtain jointly Nobel's object in 2010 with individualism, two people
Neo-Confucianism prize.Graphene is both most thin material, and most tough material, and 200 times more taller than best steel of breaking strength.
It has good elasticity again simultaneously, and stretch range can reach the 20% of own dimensions.It is that current nature is most thin, intensity highest
Material, if being made into hammock with one piece 1 square metre of area of graphene, weight itself can bear one less than 1 milligram
One kilogram of cat.Graphene most potential application at present is the substitute as silicon, ultra micro transistor npn npn is manufactured, for producing
Following supercomputer.Replace silicon with graphene, the speed of service of computer processor will be hundreds times fast.In addition, graphite
Alkene is almost fully transparent, the light of absorption 2.3%.On the other hand, it is very fine and close, even the smallest gas atom (helium
Atom) it can not also penetrate.These features make it be highly suitable as the raw material of transparent electron product, and such as transparent touch is shown
Screen, luminescent screen and solar panel.
Summary of the invention
A kind of preparation method of lithium and graphene composite film
1. the preparation method of a kind of lithium and graphene composite film, process are as follows:
(1) by the NMP(N- N-methyl-2-2-pyrrolidone N of nano oxidized graphite and electrically conductive polyaniline) slurry, nanometer lithium NMP slurry
It is sequentially placed into container, high-speed stirred is uniform;
(2) adjuvant is added and stirs evenly;
(3) mixed material is placed on silicon substrate plate, tiling is uniform, then thereon with another silicon substrate plate valve deck;
(4) sandwich silicon substrate plate is placed in micro-wave oven and is heated 5 minutes, after material is cooling, product lithium and graphene can be obtained
Composite membrane.
2. the preparation method of a kind of zinc oxide and graphene composite film, it is characterized in that, the nanometer lithium NMP slurry of addition with
The mass ratio of the NMP slurry of nano oxidized graphite and electrically conductive polyaniline is 30:2-15;Wherein oxygen zinc MP slurry composition in lithium: NMP
Mass ratio be 1:5 ~ 6;Graphene oxide in the polyaniline NMP slurry composition of nano oxidized graphite: polyaniline: NMP mass ratio
For 1:20-40:10-20.
3. the preparation method of a kind of lithium and graphene composite film, it is characterized in that, reduction mode is that microwave heating temperature is
100-200℃。
4. the preparation method of a kind of lithium and graphene composite film, it is characterized in that reducing agent can be hydroiodic acid, hydrobromic acid and
Hydrazine hydrate.
5. the preparation method of a kind of lithium and graphene composite film, it is characterized in that, silicon substrate plate is quartz material.
Application example:
Embodiment 1:
By the graphene powder of 10.0g, 100g nanometers of lithium NMP slurries, the NMP slurry of 200g electrically conductive polyaniline is added to the container,
Stir 2h, then be added hydroiodic acid 2ml stir 2h, reaction product is taken out, is laid on glass plate, 30 degree desiccation 5 hours, use
Another glass plate is pressed on coating, is put into micro-wave oven after 1min, is taken out cooling, is obtained product lithium and graphene composite film.
Embodiment 2:
By the graphene powder of 10.0g, 150g nanometers of lithium NMP slurries, the NMP slurry of 250g electrically conductive polyaniline is added to the container,
Stir 2.5h, then be added hydrobromic acid 3ml stir 3h, reaction product is taken out, is laid on glass plate, 30 degree desiccation 5 hours,
It is pressed on coating, is put into micro-wave oven after 2min with another glass plate, taken out cooling, obtain product lithium and graphene composite film.
Embodiment 3:
By the graphene powder of 10.0g, 200g nanometers of lithium NMP slurries, the NMP slurry agitation 3h of 300g electrically conductive polyaniline, then
Be added hydrazine hydrate 2.5ml stir 2.5h, reaction product is taken out, is laid on glass plate, 30 degree desiccation 5 hours, with another glass
Glass plate is pressed on coating, is put into micro-wave oven after 3min, is taken out cooling, is obtained product lithium and graphene composite film.
It is demonstrated experimentally that required product can be obtained in examples detailed above, obtain that product is excellent with electrochemistry, it is excellent that transparency is good etc.
Point.
Claims (5)
1. the preparation method of a kind of lithium and graphene composite film, process are as follows:
(1) by the NMP(N- N-methyl-2-2-pyrrolidone N of nano oxidized graphite and electrically conductive polyaniline) slurry, nanometer lithium NMP slurry
It is sequentially placed into container, high-speed stirred is uniform;
(2) adjuvant is added and stirs evenly;
(3) mixed material is placed on silicon substrate plate, tiling is uniform, then thereon with another silicon substrate plate valve deck;
(4) sandwich silicon substrate plate is placed in micro-wave oven and is heated 5 minutes, after material is cooling, product lithium and graphene can be obtained
Composite membrane.
2. the preparation method of a kind of zinc oxide and graphene composite film, it is characterized in that, the nanometer lithium NMP slurry and nano oxygen of addition
The mass ratio of the NMP slurry of graphite and electrically conductive polyaniline is 30:2-15;Wherein oxygen zinc MP slurry composition in lithium: the quality of NMP
Than for 1:5 ~ 6;Graphene oxide in the polyaniline NMP slurry composition of nano oxidized graphite: polyaniline: NMP mass ratio is 1:20-
40:10-20。
3. the preparation method of a kind of lithium and graphene composite film, it is characterized in that, reduction mode is that microwave heating temperature is 100-200
℃。
4. the preparation method of a kind of lithium and graphene composite film, it is characterized in that reducing agent can be hydroiodic acid, hydrobromic acid and hydration
Hydrazine.
5. the preparation method of a kind of lithium and graphene composite film, it is characterized in that, silicon substrate plate is quartz material.