CN110387056A - A kind of friction generator and preparation method thereof based on vegetable protein - Google Patents
A kind of friction generator and preparation method thereof based on vegetable protein Download PDFInfo
- Publication number
- CN110387056A CN110387056A CN201910575038.4A CN201910575038A CN110387056A CN 110387056 A CN110387056 A CN 110387056A CN 201910575038 A CN201910575038 A CN 201910575038A CN 110387056 A CN110387056 A CN 110387056A
- Authority
- CN
- China
- Prior art keywords
- protein
- friction
- film
- preparation
- friction generator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The friction generator and preparation method thereof based on vegetable protein that the invention discloses a kind of.Friction generator includes rub electric negative layer and protein film, and protein film stacks face-to-face with the electric negative layer that rubs, respective back surface adherency or plating top electrode, or only protein film back surface or the electrode of electric negative layer back surface setting ground connection;Protein powder is dissolved in water or ethanol water, plasticizer is then added, makes protein denaturation through Overheating Treatment, obtains the required structure more extended that forms a film;Finally evaporation solvent seasoning obtain it is homogeneous, have transparency and flexible protein film.The present invention, using friction nanometer power generator as biodegradable mulch, creates space electric field promotion system innovatively using vegetable protein as friction electric material for agricultural, and be further used for the growth of crops.
Description
Technical field
The present invention relates to a kind of friction nanometer power generators, send out more particularly, to a kind of friction nanometer based on vegetable protein
Motor and preparation method thereof.
Background technique
With flexible and portable electronic product fast development, effectively various forms of mechanical energy can be converted to
The friction nanometer power generator of electric energy will be used as the mainstream of future world energy supply.So far, friction nanometer power generator
Most of research work are all emphasizing structure design or material innovation.
Widely used material includes polyamide (nylon) -11 and poly terephthalic acid in friction nanometer power generator at present
Glycol ester (PET) etc..It is worth noting that these materials can not be degradable and be easy to discharge dangerous chemical substance,
As the quick upgrading of electronic product will become electronic waste, this undoubtedly brings huge burden to environment.Therefore, with biology
The flexible apparatus of degradable and non-toxic material manufacture receives more and more attention.
In recent years, a variety of biomaterials such as starch, chitosan, silk nanofiber, gelatin and Nano bacteria cellulose system
Standby friction generator is widely used in implanted equipment, in the fields such as health care and environmental monitoring.However, cumbersome adds
Work step will make it be difficult to practical application suddenly.So far, the application or one about vegetable protein in friction nanometer power generator
Piece blank, triboelectrification property and mechanism also need to be probed into.
Summary of the invention
In order to solve the problems, such as background technique and to plug a gap, it is an object of the invention to using vegetable protein as
A kind of new friction electric material is introduced into friction generator field, and innovatively makees the friction generator based on vegetable protein
It is applied in space electric field growth-promoting system for biodegradable mulch.This friction nanometer power generator can be used for collecting in environment
Mechanical energy, and can be used as biodegradable mulch for space electric field growth-promoting system.
Technical solution of the present invention:
One, a kind of friction generator based on vegetable protein:
The friction generator includes rub electric negative layer and Plant Protein Films, using Plant Protein Films as friction electron
Layer, Plant Protein Films stack face-to-face with the electric negative layer that rubs, respective back surface adherency or plating top electrode, or only protein film is carried on the back
The electrode of surface or electric negative layer back surface setting ground connection of rubbing.
Present invention firstly provides the applications that Plant Protein Films are used for triboelectricity, and are also put forward for the first time and have this
The friction generator of Plant Protein Films is used to act on the growth of biological tissue.
The protein film is prepared in the following ways: insoluble protein powder is dissolved in water (when being dissolved in water
Keep protein dispersibility uniform far from isoelectric point by adjusting pH) or ethanol water in, then add plasticizer (can subtract in this way
So that film stretching performance improves, flexible reinforced is not easy dry and cracked for interaction between few protein molecule), by being more than glass
Change the heat treatment of transition temperature so that protein denaturation, obtains the required structure more extended that forms a film, protein chain is in this process
In by forming hydrogen bond, ionic bond, covalent bond and hydrophobic effect enhance the network structure intensity of albuminous membranae, including rush
Enhance the network strength of albuminous membranae at disulfide bond into sulfhydryl oxidase;Finally evaporation solvent seasoning obtains homogeneous, has
Transparency and flexible protein film.
The friction electricity negative layer uses polytetrafluoroethylene (PTFE) (Teflon), dimethyl silicone polymer (PDMS), polyvinyl chloride
(PVC), polyimides (Kapton), silicon rubber (Ecoflex), polylactic acid (PLA) etc., can be used as rubbing for friction generator
Wipe electric negative layer material.
Two, a kind of preparation method of the friction generator based on vegetable protein:
It is friction electron layer --- the preparation of protein film first: insoluble protein powder is dissolved in water and (is dissolved in water
When by adjusting pH keep protein dispersibility uniform far from isoelectric point) or ethanol water in, then add plasticizer (such energy
The interaction between protein molecule is reduced so that film stretching performance improves, flexible reinforced is not easy dry and cracked), by being more than glass
The heat treatment of glass transition temperature obtains the required structure more extended that forms a film so that protein denaturation, protein chain mistake herein
Enhance the network structure intensity of albuminous membranae by forming hydrogen bond, ionic bond, covalent bond and hydrophobic effect in journey, including
Sulfhydryl oxidase is promoted to enhance the network strength of albuminous membranae at disulfide bond;Finally evaporation solvent seasoning obtains homogeneous, tool
There are transparency and flexible protein film;Protein film and the electric negative layer that rubs are stacked face-to-face, respective back surface adherency or plating
Top electrode or only protein film back surface or the electrode for electric negative layer back surface setting ground connection of rubbing.
The protein powder is rice protein, peanut protein isolate, soybean protein isolate, wheat gluten, corn
The powder of alcohol soluble protein.
The plasticizer is polyalcohol (glycerol, propylene glycol, ethylene glycol, sorbierite, polyethylene glycol etc.).
The friction electricity negative layer uses polytetrafluoroethylene (PTFE) (Teflon), dimethyl silicone polymer (PDMS), polyvinyl chloride
(PVC), polyimides (Kapton), silicon rubber (Ecoflex), polylactic acid (PLA) etc., can be used as rubbing for friction generator
Wipe electric negative layer material.
The step 1) specifically: protein dispersibility is water-soluble for the ethyl alcohol of 70%-90% in aqueous solution or concentration
Protein solution is prepared into (mass fraction of protein is 1-10%, w/w) in liquid;Then quality is added in protein solution is
The plasticizer (such as glycerol) of protein 10-60% (w/w), after 60-95 DEG C of heating water bath denaturation is stirred 30-60min,
It deaerates 10 minutes under vacuum, is poured into mold later and be put into baking oven evaporation drying under the conditions of 30-70 DEG C.
The friction electricity negative layer uses polytetrafluoroethylene (PTFE) (Teflon), dimethyl silicone polymer (PDMS), polyvinyl chloride
(PVC), polyimides (Kapton), silicon rubber (Ecoflex), polylactic acid (PLA) etc., can be used as rubbing for friction generator
Wipe electric negative layer material.
The protein is rice protein, peanut protein isolate, soybean protein isolate and wheat gluten, specifically will
Protein mixes in deionized water solution with glycerol, after magnetic agitation, then also adjusts egg using 1M sodium hydroxide solution
White matter precursor solution pH adjusts protein solution pH value to 12;Again by protein solution at 65 DEG C heating stirring 30 minutes,
Degasification process 10 minutes under vacuum to remove bubble.
The protein is zeins, is specifically 70% in mass concentration by zeins and glycerol
Ethanol water in dissolve after, directly by protein solution at 65 DEG C heating stirring 30 minutes, then take off under vacuum
Gas process 10 minutes.
Friction generator of the invention is used for the growth application of crops, has facilitation to the growth of crops.It will
Friction generator is placed on soil, and protein film makes friction electricity in the side of contact soil, and to the friction generator applied force
It approaches, leave or Relative sliding between negative layer and protein film, that is, be applied with mechanical energy, and then life is produced to crops
The long electric field promoted.
As shown in figure 4, friction generator of the invention can there are four types of operating mode, perpendicular contacts-clastotype, level
Sliding-modes, single electrode mode and independent layer model.
Perpendicular contact-clastotype: in this structure, protein film stacks face-to-face with the electric negative layer that rubs, each
Back side adherency or be coated with electrode.The electric negative layer that rubs contacts with each other with protein film, and it is opposite to form symbol in two contact surfaces
Surface charge.When the two surfaces are separated due to external force, centre will form a small the air gap, and
Induced electricity potential difference is formed between two electrodes.When two electrodes are linked together by load, electrons are by loading from one
A electrode flows to another electrode, forms a reversed potential difference and comes equilibrium electrostatic field.When in rub electric negative layer and protein film
Between the air gap closure when, the potential difference disappearance formed by triboelectric charge, electrons flow back.It constantly recycles in this way, with
The electric field of time change will drive electrode of the electronics at the electrode of albumen back of the membrane and the electric negative layer back side that rubs to flow back and forth, thus
Generate alternating current.
Horizontal sliding-modes: the initial identical and protein film of structure vertical contact-clastotype of this mode with rub
It wipes electric negative layer to stack face-to-face, their own back side adheres to or is coated with electrode, and mutually interconnects between two electrodes by external circuit
It connects.When protein film and the electric negative layer that rubs contact, the phase of the horizontal direction parallel with surface can be taken place along between two kinds of materials
To sliding, triboelectric charge can also be generated on both surfaces in this way.In this way, just will form polarization in the horizontal direction, can drive
Dynamic electronics flows between the electrode of albumen back of the membrane and the electrode at the electric negative layer back side that rubs, to balance the quiet of triboelectric charge generation
Electric field.It can produce one with closure by periodically sliding separation and exchange output.Here it is slidingtype friction nanometer generatings
The basic principle of machine, and this sliding can exist in a variety of forms, including planar slide, cylindrical slid you and disk sliding
Deng.
Single electrode operating mode: above-mentioned protein film and the electric negative layer that rubs are combined, and in the back of protein film
Surface or the electric negative layer back surface that rubs arrange one layer of electrode again, and electrode is grounded, and thus constitutes friction generator.When upper
The electric negative layer of friction in portion closer to or farther from lower part protein film when or top the electric negative layer opposing lower portions of friction protein film
When frictional movement, local field distribution will change, and electron exchange can be occurred in this way by descending between electrode and the earth, to balance electricity
Potential change on extremely.
Independent layer model: albumen back of the membrane adhere to or plate two disjunct symmetry electrodes, the size of electrode and its
Spacing can suitable control, and two electrodes are connected by external circuit.When the electric negative layer that rubs is in two electrodes of albumen film surface
Between when moving reciprocatingly, the variation of potential difference can be generated between two electrodes, and then electronics is driven to be supported on by external circuit
It is flowed back and forth between two electrodes, with the variation of equilibrium potential difference.
Compared with the prior art, the present invention has the following beneficial effects:
First on material, this biomaterial of vegetable protein from being not introduced into friction generator field, vegetable protein due to
There are the groups such as many hydroxy aminos on surface, has stronger electron donation, is a kind of candidate that friction nanometer power generator is natural
Material;
Secondly, Plant Protein Films preparation process is simple compared with other biological material, and it is from a wealth of sources, and its price is low
It is honest and clean, often it is disposed of as scrap;
Finally, using the space for being applied to agricultural for the first time as mulch based on the friction nanometer power generator of vegetable protein of preparation
In electric field growth-promoting system, using bean seedlings as test object, good technical effect has been obtained as a result, therefore with very big before
Scape.
The present invention innovatively using vegetable protein as friction electric material, various vegetable proteins is used to be charged by friction row
For, including rice protein, peanut protein isolate, soybean protein isolate, wheat gluten and zeins, innovatively utilize
Friction nanometer power generator creates space electric field promotion system as biodegradable mulch, for agricultural, and achieves considerable
Significant technological achievement.
Detailed description of the invention
Fig. 1 is the A rice protein determined in the embodiment of the present invention according to the direction of output current signal, B peanut separation egg
The arrangement position figure of white, C soybean protein isolate, D wheat gluten, E zeins in common materials triboelectric series;
Fig. 2 is the output performance figure of the friction nanometer power generator based on five kinds of albumen in the embodiment of the present invention, and A is defeated in figure
Voltage out, B are output electric current;
Fig. 3 is the testing fatigue result figure of the friction nanometer power generator in the embodiment of the present invention based on rice protein, continuously
Work 40000 times still with good reliability;
Fig. 4 is four kinds of operating mode schematic diagrames of the invention.
Specific embodiment
Present invention will be further explained below with reference to the attached drawings and examples.
It is implemented in implementing below the present invention are as follows:
1) be first protein film preparation: by protein dispersibility in the ethanol water that aqueous solution or concentration are 70%-90%
Protein solution is prepared into (1-10%, w/w) in solution;Then it is protein 10-60% (w/ that quality is added in protein solution
W) plasticizer (such as glycerol) deaerates 10 points under vacuum after 60-95 DEG C of heating water bath denaturation is stirred 30-60min
Clock pours into mold later and is put into baking oven evaporation drying under the conditions of 30-70 DEG C.
In specific implementation, finally by dry albumen film stripping, specific implementation also by protein film be placed in stationary temperature and
It is placed under damp condition, so that its equilibrium water conten under certain temperature and damp condition, for electrical testing later.
2) rub electric negative layer: the friction electricity negative layer of specific implementation uses polytetrafluoroethylene (PTFE) (Teflon), polydimethylsiloxanes
Alkane (PDMS), polyvinyl chloride (PVC), polyimides (Kapton), silicon rubber (Ecoflex), polylactic acid (PLA) etc., can make
For the friction electricity negative layer material of friction generator.
The present invention implement first by protein film and common test material (nylon-11, the wool of braiding, braiding silk,
Aluminium, paper, acetate fiber, PET, PDMS, PTFE) composition friction electricity is to testing electron donation size, concrete operation method
Are as follows: above, protein film is placed below for test material, and places electrode in protein film bottom, and electrode is grounded, test material is worked as
When separateing with protein film, the current signal generated with multimeter test, positive and negative according to current signal judges electric current
Direction to obtain the flow direction of electronics, and then judges the charge polarity of test material Yu albumen film surface band, releases test
The power of material and protein film electron donation.
Such as Fig. 1, by five kinds of Plant Protein Films (rice protein, peanut protein isolate, soybean protein isolate, wheat gluten,
Zeins) test is compared with the triboelectric series of common test material respectively, judge that five kinds of vegetable proteins exist
Position in triboelectric series.It can be seen from the figure that the electron donation of protein film is stronger, the friction electricity of common materials is come
Sequence leans on front position.
Embodiment
Embodiment 1
1) be first protein film preparation, by by rice protein, peanut protein isolate, soybean protein isolate, wheat paddy
Albumen is dispersed in distilled water (5%, w/w) and prepares film forming solution, and it is 70% that in addition zeins, which is dispersed in concentration,
In ethanol water (5%, w/w).Then the glycerol for 30% (w/w) that quality is protein is added in five kinds of protein solutions.
2) in this embodiment example, for rice protein, peanut protein isolate, soybean protein isolate, wheat gluten, with
Under specifically: 5g phytoprotein is mixed in 100mL deionized water solution with 1.5g glycerol, at magnetic agitation 10 minutes
Afterwards, then regulatory protein matter precursor solution pH.Protein solution pH value is adjusted to 12 using 1M sodium hydroxide solution;Then will
Protein solution heating stirring 30 minutes at 65 DEG C, degasification process 10 minutes under vacuum to remove bubble.
It is special for zeins in this embodiment example, be in detail below by 5g zeins with
After 1.5g glycerol dissolves in the ethanol water that 100mL concentration is 70%, directly protein solution is heated at 65 DEG C
Stirring 30 minutes, then degasification process 10 minutes under vacuum.
3) finally final film forming solution is poured into round Teflon mold (diameter 3cm), and in 60 DEG C of baking oven
It is dry.Then it is placed 24 hours by dry film removing and in the constant temperature and humidity incubator of 25 DEG C and 40% relative humidity,
Then it is tested as friction electron layer.
Dimethyl silicone polymer (PDMS) film is used in this experiment of the electric negative layer that rubs.The preparation of PDMS film is by will be elastic
Agent and curing agent, for 10:1 vacuum outgas after mixing, are placed in baking oven with mass ratio and solidify 20- under the conditions of 65-95 DEG C
60min。
It is right that protein film is combined into the electricity that rubs with PDMS film, and places aluminium foil as electrode in PDMS film bottom, passes through albumen
The contact separation of film and PDMS film, generates the flowing of electronics in external circuit, and carries out electricity survey with electrometer and oscillograph
Examination, such as Fig. 2, five kinds of protein films have different size of output voltage and electric current, and the sequence of output signal size is big with electron donation
It is small consistent, the conclusion before further demonstrating: electron donation is descending be respectively rice protein, peanut protein isolate,
Soybean protein isolate, wheat gluten, zeins.
Embodiment 2
By taking rice protein as an example, 5g rice protein is mixed in 100mL deionized water solution with 1.5g glycerol, in magnetic force
Stirring after ten minutes, using 1M sodium hydroxide solution is adjusted protein solution pH value to 12.Then by protein solution 65
Heating stirring 30 minutes at DEG C, degasification process 10 minutes under vacuum to remove bubble.Finally final film forming solution is poured into
In round Teflon mold (diameter 3cm), and it is dry in 60 DEG C of baking oven.Finally by dry film removing and at 25 DEG C and
It places in the constant temperature and humidity incubator of 40% relative humidity 24 hours and is tested as friction electron layer.
The preparation for the electric negative layer that rubs: polylactic acid film is cut into the circle that diameter is 3cm.
The preparation of friction nanometer power generator: it is right to be combined into friction electricity for above-mentioned rice protein film and polylactic acid film, and
Polylactic acid membrane side places aluminium foil as electrode and constitutes friction nanometer power generator, with its voltage signal of oscilloscope measurement.Such as Fig. 3,
It is recycled by 40,000 times, signal still keeps very stable.
Embodiment 3
After 5g zeins and 1.5g glycerol are dissolved in the ethanol water that 100mL concentration is 70%, directly
Heating stirring 30 minutes at 65 DEG C are connect protein solution, then degasification process 10 minutes under vacuum.It finally will be final
Film forming solution pours into round Teflon mold (diameter 3cm), and dry in 60 DEG C of baking oven.Finally dry film is shelled
It places 24 hours from and 25 DEG C and in the constant temperature and humidity incubator of 40% relative humidity, is surveyed as friction electron layer
Examination.
The preparation for the electric negative layer that rubs: polylactic acid film is cut into the circle that diameter is 3cm, then in polylactic acid film one
Side is coated with poly- (3,4- ethene dioxythiophene)-polystyrolsulfon acid (PEDOT:PSS) as electrode at 1000rpm.
Protein film and polylactic acid film are combined into mulch, have been coated with conductive PEDOT: the polylactic acid membrane of PSS above, egg
Tunica albuginea applies the mechanical energy in a certain size power simulated environment to the friction generator in the side of contact soil.With beans
Seedling is subjects, after bean or pea are impregnated 4 hours, is put into the constant temperature and humidity incubator of 25 DEG C and 40% relative humidity and cultivates three
It selects the much the same bean seedlings of growing way and is divided into two groups, respectively test group and control group after long budding.Test group, which is placed in, rubs
It wipes in the electric field that generator generates and (places 4 hours daily), bean seedlings elongation and rate of body weight gain are measured after 48 hours to characterize bean seedlings
Growing state.
Table 1
Using bean seedlings as research object in 1 present invention of table, the friction nanometer power generator based on vegetable protein is used to receive as mulch
Collect the mechanical energy in environment and generates electric field in growth-promoting system.The electric field pair that friction generator generates it can be seen from upper table 1
Bean seedlings growth has apparent facilitation, illustrates that the friction nanometer power generator based on vegetable protein can be applied to agriculture as mulch
In the space electric field growth-promoting system of industry.
Claims (10)
1. a kind of friction generator based on vegetable protein, it is characterised in that: the friction generator includes the electric negative layer that rubs
And protein film, protein film stack face-to-face with the electric negative layer that rubs, respective back surface adherency or plating top electrode, or only protein film
Back surface or the electrode of electric negative layer back surface setting ground connection.
2. a kind of friction generator based on vegetable protein according to claim 1, it is characterised in that: the friction electricity
Negative layer uses polytetrafluoroethylene (PTFE) (Teflon), dimethyl silicone polymer (PDMS), polyvinyl chloride (PVC), polyimides
(Kapton), silicon rubber (Ecoflex), polylactic acid (PLA) etc..
3. a kind of preparation method of the friction generator based on vegetable protein, it is characterised in that: be friction electron first
Layer --- the preparation of protein film: protein powder is dissolved in water or ethanol water, plasticizer is then added, at overheat
Reason is so that protein denaturation, obtains the required structure more extended that forms a film;Finally evaporation solvent seasoning obtains homogeneous, has
Transparency and flexible protein film;Protein film and the electric negative layer that rubs are stacked face-to-face, respective back surface is adhered to or plated
Electrode or only protein film back surface or the electrode of electric negative layer back surface setting ground connection.
4. a kind of preparation method of friction generator based on vegetable protein according to claim 3, it is characterised in that: institute
The protein powder stated is rice protein, peanut protein isolate, soybean protein isolate, wheat gluten, zeins
Powder.
5. a kind of preparation method of friction generator based on vegetable protein according to claim 3, it is characterised in that: institute
The plasticizer stated is polyalcohol (glycerol, propylene glycol, ethylene glycol, sorbierite, polyethylene glycol etc.).
6. a kind of preparation method of friction generator based on vegetable protein according to claim 3, it is characterised in that: institute
The friction electricity negative layer stated uses polytetrafluoroethylene (PTFE) (Teflon), dimethyl silicone polymer (PDMS), polyvinyl chloride (PVC), polyamides
Imines (Kapton), silicon rubber (Ecoflex), polylactic acid (PLA) etc..
7. a kind of preparation method of friction generator based on vegetable protein according to claim 3, it is characterised in that: institute
The step 1) stated specifically: by protein dispersibility in the ethanol water that aqueous solution or concentration are 70%-90% (protein
Mass fraction be 1-10%, w/w) in be prepared into protein solution;Then it is protein 10- that quality is added in protein solution
The plasticizer of 60% (w/w) deaerates 10 points under vacuum after 60-95 DEG C of heating water bath denaturation is stirred 30-60min
Clock pours into mold later and is put into baking oven evaporation drying under the conditions of 30-70 DEG C.
8. a kind of preparation method of friction generator based on vegetable protein according to claim 3, it is characterised in that: institute
The friction electricity negative layer stated uses polytetrafluoroethylene (PTFE) (Teflon), dimethyl silicone polymer (PDMS), polyvinyl chloride (PVC), polyamides
Imines (Kapton), silicon rubber (Ecoflex), polylactic acid (PLA) etc..
9. a kind of preparation method of friction generator based on vegetable protein according to claim 3, it is characterised in that: institute
The protein stated be rice protein, peanut protein isolate, soybean protein isolate and wheat gluten, specifically by protein with it is sweet
Oil mixes in deionized water solution, then also molten using 1M sodium hydroxide solution regulatory protein matter precursor after magnetic agitation
Liquid pH adjusts protein solution pH value to 12;Again by protein solution at 65 DEG C heating stirring 30 minutes, take off under vacuum
Gas process 10 minutes to remove bubble.
10. a kind of preparation method of friction generator based on vegetable protein according to claim 3, it is characterised in that:
The protein is zeins, the ethanol water for being specifically 70% in mass concentration by zeins and glycerol
After being dissolved in solution, directly by protein solution at 65 DEG C heating stirring 30 minutes, then degasification process 10 under vacuum
Minute.