CN110373935A - A kind of preparation method of ferronickel slag inorganic fiber paper pulp - Google Patents
A kind of preparation method of ferronickel slag inorganic fiber paper pulp Download PDFInfo
- Publication number
- CN110373935A CN110373935A CN201910607717.5A CN201910607717A CN110373935A CN 110373935 A CN110373935 A CN 110373935A CN 201910607717 A CN201910607717 A CN 201910607717A CN 110373935 A CN110373935 A CN 110373935A
- Authority
- CN
- China
- Prior art keywords
- ferronickel slag
- paper pulp
- ferronickel
- preparation
- inorganic fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of preparation method of ferronickel slag inorganic fiber paper pulp, and this method step includes: 1, mixes ferronickel clinker slurry with lime, lead oxide and zinc oxide by transmission device;2, slurries are made in the calcining of high temperature electric smelter high temperature in uniformly mixed raw material;3, alumina silicate is added to slurry made of calcining, is pulled out in time when slurry being made to become cotton-shaped cotton, and ferronickel slag inorfil is collected by cotton collecting machine;4, ferronickel slag inorfil obtained is shredded, is removed the gred through desilting tank, then added softening agent, paper pulp fiber, thickener, modifying agent, modified thickener, binder, water and carry out slurrying;5, the above solution is increased into temperature and continues to stir, then further removed the gred by desander, arrive uniform ferronickel slag inorganic fiber paper pulp after being cooled to room temperature.The ferronickel slag inorganic fiber paper pulp that the method for the present invention obtains has the advantages that ultra-fine, ultra-soft and flexible.
Description
Technical field
The present invention relates to paper pulp and its method field of manufacturing, specifically, being a kind of system of ferronickel slag inorganic fiber paper pulp
Make method.
Background technique
In recent years, China's ferronickel slag annual emissions surpass 30,000,000 tons, it has also become China is after scum, steel slag, red mud
Four big metallurgical slags.A large amount of ferronickel slags can only be handled as waste, pile up processing or deep-sea landfill, not only land occupation, pollution ring
Border, the sustainable development for returning nickel-iron smelting bring severe challenge.
It is counted according to Chinese papermaking association, 79,490,000 tons of China's pulp production amount in 2017 increases by 0.30% on a year-on-year basis.It is wherein wooden
10,500,000 tons are starched, increases by 4.48% on a year-on-year basis;63,020,000 tons of secondary stock, 0.43% is reduced on year-on-year basis;5,970,000 tons of non-wood pulp increases on year-on-year basis
Long 1.02%.It goes into operation although the country has part to increase wood pulp production capacity newly, compares huge market demand, China's wood pulp production capacity is still
It is unable to satisfy demand, relies primarily on import.
The country ferronickel slag overwhelming majority is technical process of the laterite in electric furnace reduction melting ferronickel of humic soil type at present
Middle generation, main component is FeO, MgO and SiO2, submember is Al2O3、Cr2O3, CaO etc., belong to FeO-MgO-SiO
Ternary slag system.
China's paper product demand is huge, and raw material of wood pulp supply is much insufficient, oneself production chemical pulp wastes a large amount of water moneys
Source, and cause the pollution of serious environment.Because of a kind of ferronickel slag inorganic fiber paper pulp of the invention, as ferronickel slag must be comprehensively utilized
New way is had found, and reduces paper product cost, save timber, the wasting of resources is reduced, protects environment.
Summary of the invention
The present invention provides a kind of using ferronickel slag inorganic fiber paper pulp as the papermaking process of raw material, former to solve traditional papermaking
Material shortage problem.
To achieve the goals above, the technical solution of the present invention is as follows:
The preparation of S1, ferronickel slag inorfil, preparation process include:
S11, ferronickel clinker slurry is mixed with lime, lead oxide and zinc oxide;
S12, slurries are made in the slurry high-temperature calcination that completion is mixed in S11;
S13, alumina silicate is added to slurry made of the calcining, pull-out when slurry being made to become cotton-shaped cotton, and collect nickel
Scum inorfil;
The preparation of S2, ferronickel slag inorganic fiber paper pulp, preparation process include:
Ferronickel slag inorfil made from S1 is shredded, then adds softening agent, paper pulp fiber, thickener, modifying agent, modification
Thickener, binder, water carry out slurrying;
S3, the made slurries of S2 are increased into temperature and continue to stir, further removed the gred, arrive nickel after being cooled to room temperature
Scum inorganic fiber paper pulp.
Wherein, ferronickel clinker slurry 80-85wt% described in step S11, the lime 10-15wt%, the lead oxide
0.5-3.5wt%, the zinc oxide 4-7wt%;
1800-2200 DEG C of calcination temperature of high temperature electric smelter described in S12, time 30-60min;
It is 0.03-0.1wt% that alumina silicate described in S13, which accounts for its ratio for mixing slurry,;
Each composition quality proportion is the softening agent 1-6%, the paper pulp fiber 0.1-10%, the thickener in S2
0.05-0.5%, the modifying agent 0.05-0.2%, the modified thickener 0.3-1.2%, the binder 1-4%, more than water
Amount;
It is 80 ± 5 DEG C that solution described in S3, which increases temperature, mixing time 1-2h.
Wherein, described in step S1 in 1-3 μm of diameter, length 3-10cm, step S2 of ferronickel slag inorfil by the ferronickel
Slag inorfil is cut into the section of 3-6mm, and the slagging-off is to remove the ferronickel solid impurity particle not melted in the ferronickel slag inorfil,
And melt down the ferronickel solid impurity particle, melt wire drawing again.
Wherein, softening agent described in step S2 is waterborne polyurethane resin, polyvinyl acetate, aqueous epoxy resins, three
The mixture of one or more of poly cyanamid liquid, polyacrylic acid substance.
Wherein, paper pulp fiber described in step S2 is the mixture of plant fiber and ferronickel slag inorfil, two kinds of mixing
Object mixing quality ratio is 3-7: 7-3.
Wherein, binder described in step S2 is one in polyvinyl alcohol, epoxy resin, methacrylate binder etc.
The mixture of kind or several substances.
Wherein, thickener described in step S2 is cellulose thickener, polyacrylate, association type polyurethane thickener
One of.
Wherein, modifying agent described in step S2 is one or more of sodium hydroxide, calcium hydroxide, calcium carbonate substance
Mixture.
Wherein, modified thickener described in step S2 be oxidized starch, cationic starch, anionic starch, dialdehyde starch,
The mixture of one or more of phosphate ester starch.
Wherein, plant fiber described in step S2 is lumber fibre, leaf fibre, waste paper.
The present invention has the advantage that laterite ferronickel slag prepared by this method, carries out complete analysis it is found that its primary chemical
Ingredient is SiO2: 52.15%, Al2O3: 4.77%, Fe2O3: 5.5%, CaO:32.71%, MgO:4.42% etc., due to the high magnesium of calcium
Low feature, fiber have the advantages that ultra-fine, ultra-soft and flexible, can prepare a variety of paper such as white board, printing paper, copy paper
Product, indices can reach corresponding national standard well.
Naked eyes evaluation fiber flexibility method: the pliability of fiber includes many indexs, and resultant effect touches evaluation:
Each fiber sample is repeated to touch 5 times, average value is the pliability of sample.As a result with 1,2,3,4 totally four grades
It indicates, pliability is incremented by successively, and the "+" and "-" number of numeric suffix indicate slightly strong and slightly weak.
General fibre | Ferronickel slag fiber | |
Feel grade | 1+ | 3 |
There are no the technologies for using ferronickel slag fiber papermaking currently on the market, by the paper product of the method for the present invention preparation and market
Paper made from the upper prior art is detected, and show that resistance to broken, tensile strength, the tearability of present invention paper product produced mention
It rises.
Plain paper | Ferronickel slag fibrous paper | |
Bursting strength (KPa) | 182.7 | 196.5 |
Tensile strength (N/M) | 2167.8 | 2985.9 |
4 paper tearabilities (mN) | 2494.4 | 2576.0 |
The present invention produces ferronickel inorfil using electric smelter, compared with prior art without burning coal, both saves energy
Source, and the problem of effective solution environmental pollution.And this method is suitable for industrial mass production, manufactures full mistake in slurries
Journey non-pollutant discharge, and papermaking cost is reduced, it is significant to the meaning that protects forest resources.
Specific embodiment
Embodiment 1
1. the preparation of ferronickel slag inorfil
Ferronickel slag 80wt% and lime 10wt%, lead oxide 1.5wt% and zinc oxide 6wt% etc. are mixed in proportion
Afterwards, it is transported in high temperature electric smelter and is heated to 1800 DEG C, slurries are made in high-temperature calcination 60min.Calcined slurries pass through electric smelting
The bottom of furnace flows to frequency-conversion high-speed centrifugal wire drawing machine, by adding the alumina silicate of 0.05wt%, when slurry being made to become cotton-shaped cotton
It pulls out in time, and ferronickel slag inorfil is collected by cotton collecting machine.
2, the preparation of ferronickel slag inorganic fiber paper pulp
Ferronickel slag inorfil is chopped into the section of 3mm, is removed the gred through desilting tank, is removed in ferronickel slag inorfil not
The ferronickel solid impurity particle is directly melted down, melts wire drawing again by the ferronickel solid impurity particle of thawing.And it is made according to following quality proportioning
Slurries:
Waterborne polyurethane resin 2%, waste paper 3%, ferronickel slag inorfil 7%, hydroxyethyl cellulose 0.2%, hydroxide
Sodium 0.05%, cationic starch 0.5%, epoxy resin 3%, water surplus.Above-mentioned solution is persistently stirred under conditions of 80 ± 5 DEG C
2h is mixed, then is further removed the gred by desander, after being cooled to room temperature, to obtain uniform ferronickel slag inorganic fiber paper pulp.
Ferronickel slag fibre diameter obtained is 2~3 μm, and length 3-10cm belongs to fine fibre.
3, the preparation of paper product
Above-mentioned ferronickel slag inorganic fiber paper pulp is delivered in paper machine, manufactured semi-finished product drying processing system after copy paper
At paper product.
Embodiment 2
1. the preparation of ferronickel slag inorfil
Ferronickel slag 80wt% and lime 12wt%, lead oxide 1wt% and zinc oxide 5wt% etc. are mixed in proportion
Afterwards, it is transported in high temperature electric smelter and is heated to 2000 DEG C, slurries are made in high-temperature calcination 50min.Calcined slurries pass through electric smelting
The bottom of furnace flows to frequency-conversion high-speed centrifugal wire drawing machine, by adding the alumina silicate of 0.05wt%, when slurry being made to become cotton-shaped cotton
It pulls out in time, and ferronickel slag inorfil is collected by cotton collecting machine.
2, the preparation of ferronickel slag inorganic fiber paper pulp
Ferronickel slag inorfil is chopped into the section of 3mm, is removed the gred through desilting tank, is removed in ferronickel slag inorfil not
The ferronickel solid impurity particle is directly melted down, melts wire drawing again by the ferronickel solid impurity particle of thawing.And it is made according to following quality proportioning
Slurries:
Polyvinyl acetate 4%, lumber fibre 5%, ferronickel slag inorfil 5%, polyacrylate 0.2%, hydroxide
Calcium 0.05%, oxidized starch 0.5%, polyvinyl alcohol 2%, water surplus.Above-mentioned solution is persistently stirred under conditions of 80 ± 5 DEG C
1.5h, then further removed the gred by desander, after being cooled to room temperature, to obtain uniform ferronickel slag inorganic fiber paper pulp.
Ferronickel slag fibre diameter obtained is 2~3 μm, and length 3-10cm belongs to fine fibre.
3, the preparation of paper product
Above-mentioned ferronickel slag inorganic fiber paper pulp is delivered in paper machine, manufactured semi-finished product drying processing system after copy paper
At paper product.
Embodiment 3
1. the preparation of ferronickel slag inorfil
Ferronickel slag 80wt% and lime 12wt%, lead oxide 0.5wt% and zinc oxide 7wt% etc. are mixed in proportion
Afterwards, it is transported in high temperature electric smelter and is heated to 2200 DEG C, slurries are made in high-temperature calcination 30min.Calcined slurries pass through electric smelting
The bottom of furnace flows to frequency-conversion high-speed centrifugal wire drawing machine, by adding the alumina silicate of 0.05wt%, when slurry being made to become cotton-shaped cotton
It pulls out in time, and ferronickel slag inorfil is collected by cotton collecting machine.
2, the preparation of ferronickel slag inorganic fiber paper pulp
Ferronickel slag inorfil is chopped into the section of 3mm, is removed the gred through desilting tank, is removed in ferronickel slag inorfil not
The ferronickel solid impurity particle is directly melted down, melts wire drawing again by the ferronickel solid impurity particle of thawing.And it is made according to following quality proportioning
Slurries:
Melamine liquid 6%, leaf fibre 6%, ferronickel slag inorfil 4%, polyurethanes thickener 0.1%, calcium carbonate
0.15%, phosphate ester starch 0.5%, methacrylate 1%, water surplus.Above-mentioned solution is continued under conditions of 80 ± 5 DEG C
1.5h is stirred, then is further removed the gred by desander, after being cooled to room temperature, to obtain uniform ferronickel slag inorganic fibre paper
Slurry.
Ferronickel slag fibre diameter obtained is 2~3 μm, and length 3-10cm belongs to fine fibre.
3, the preparation of paper product
Above-mentioned ferronickel slag inorganic fiber paper pulp is delivered in paper machine, manufactured semi-finished product drying processing system after copy paper
At paper product.
The fibrillating of fiber also has large effect to Paper Brittleness, and the fibrillating of fiber is conducive to page stress
Dispersion, can reduce the brittleness of page, improve toughness.
Complete analysis is carried out to ferronickel slag it is found that its main chemical compositions is SiO2: 52.15%, Al2O3: 4.77%, Fe2O3:
5.5%, CaO:32.71%, MgO:4.42% etc., due to the low feature of the high magnesium of calcium, prepared laterite ferronickel slag fibrous paper tool
There is the characteristics of ultra-fine, ultra-soft and flexible.
The present invention produces ferronickel inorfil using electric smelter, compared with prior art without burning coal, both saves energy
Source, and the problem of effective solution environmental pollution.There are no the technologies for using ferronickel slag fiber papermaking currently on the market, incite somebody to action this
The paper product of inventive method preparation is detected with paper made from the prior art on the market, obtains the resistance to of present invention paper product produced
Broken, tensile strength, tearability have promotion.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art within the technical scope of the present disclosure, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (10)
1. a kind of preparation method of ferronickel slag inorganic fiber paper pulp, which is characterized in that preparation process is as follows:
The preparation of S1, ferronickel slag inorfil, preparation process include:
S11, ferronickel clinker slurry is mixed with lime, lead oxide and zinc oxide;
S12, slurries are made in the slurry high-temperature calcination that completion is mixed in S11;
S13, alumina silicate is added to slurry made of the calcining, pull-out when slurry being made to become cotton-shaped cotton, and collect ferronickel slag
Inorfil;
The preparation of S2, ferronickel slag inorganic fiber paper pulp, preparation process include:
Ferronickel slag inorfil made from S1 is shredded, then adds softening agent, paper pulp fiber, thickener, modifying agent, modified thickening
Agent, binder, water carry out slurrying;
S3, the made slurries of S2 are increased into temperature and continue to stir, further removed the gred, arrive ferronickel slag after being cooled to room temperature
Inorganic fiber paper pulp.
2. the preparation method of ferronickel slag inorganic fiber paper pulp according to claim 1, which is characterized in that each ingredient in S11
Ratio is the ferronickel clinker slurry 80-85wt%, the lime 10-15wt%, the lead oxide 0.5-3.5wt%, described
Zinc oxide 4-7wt%;
1800-2200 DEG C of calcination temperature of high temperature electric smelter described in S12, time 30-60min;
It is 0.03-0.1wt% that alumina silicate described in S13, which accounts for its ratio for mixing slurry,;
Each composition quality proportion is the softening agent 1-6%, the paper pulp fiber 0.1-10%, the thickener 0.05- in S2
0.5%, the modifying agent 0.05-0.2%, the modified thickener 0.3-1.2%, the binder 1-4%, water surplus;
It is 80 ± 5 DEG C that solution described in S3, which increases temperature, mixing time 1-2h.
3. the preparation method of ferronickel slag inorganic fiber paper pulp according to claim 1, which is characterized in that ferronickel described in step S1
1-3 μm of diameter of slag inorfil, the ferronickel slag inorfil is cut into the section of 3-6mm in length 3-10cm, step S2, it is described
Slagging-off melts down the ferronickel solid impurity particle to remove the ferronickel solid impurity particle not melted in the ferronickel slag inorfil, again
Melt wire drawing.
4. the preparation method of ferronickel slag inorganic fiber paper pulp according to claim 1, which is characterized in that the softening agent is water
One or more of property polyurethane resin, polyvinyl acetate, aqueous epoxy resins, melamine liquid, polyacrylic acid substance
Mixture.
5. the preparation method of ferronickel slag inorganic fiber paper pulp according to claim 1, which is characterized in that the paper pulp fiber is
The mixture of plant fiber and ferronickel slag inorfil, two kinds of mixture mixing quality ratios are 3-7: 7-3.
6. the preparation method of ferronickel slag inorganic fiber paper pulp according to claim 1, which is characterized in that the binder is poly-
The mixture of one or more of vinyl alcohol, epoxy resin, methacrylate binder etc. substance.
7. the preparation method of ferronickel slag inorganic fiber paper pulp according to claim 1, which is characterized in that the thickener is fibre
Tie up one of plain class thickener, polyacrylate, association type polyurethane thickener.
8. the preparation method of ferronickel slag inorganic fiber paper pulp according to claim 1, which is characterized in that the modifying agent is hydrogen
The mixture of one or more of sodium oxide molybdena, calcium hydroxide, calcium carbonate substance.
9. the preparation method of ferronickel slag inorganic fiber paper pulp according to claim 1, which is characterized in that the modified thickener
For the mixture of one or more of oxidized starch, cationic starch, anionic starch, dialdehyde starch, phosphate ester starch.
10. the preparation method of ferronickel slag inorganic fiber paper pulp according to claim 5, which is characterized in that the plant fiber
For lumber fibre, leaf fibre, waste paper.