CN110372952A - A kind of environment protecting paper and preparation method thereof - Google Patents
A kind of environment protecting paper and preparation method thereof Download PDFInfo
- Publication number
- CN110372952A CN110372952A CN201910736659.6A CN201910736659A CN110372952A CN 110372952 A CN110372952 A CN 110372952A CN 201910736659 A CN201910736659 A CN 201910736659A CN 110372952 A CN110372952 A CN 110372952A
- Authority
- CN
- China
- Prior art keywords
- paper
- inorganic mineral
- organic resin
- mineral powder
- environment protecting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of environment protecting paper, is related to environment-friendly materials technical field, and material composition is organic resin, inorganic mineral powder and auxiliary agent, and the mass ratio of organic resin and inorganic mineral powder is 1 to 1~9, and auxiliary agent accounts for the 2~6% of organic resin and inorganic mineral powder gross mass.Preparation method, comprising the following steps: temperature is dried in inorganic mineral powder by 1;Inorganic mineral powder after organic resin, auxiliary agent and drying process is stirred mixing by 2, and 3 heat mixed material, produces paper grade (stock) feed particles using extruder;Feed particles are processed into ground paper using film laminator, inflation film manufacturing machine or paper drawing mould machine by 4, then carry out traction stretch processing;5 carry out sided corona treatment to paper surface using corona machine;Paper after 6 pairs of sided corona treatments is coated processing, obtains environment protecting paper.The invention has the benefit that keeping environment protecting paper degradation time shorter, while environment protecting paper is able to carry out writing, printing, as packaging bag and packing box, toughness is strong, waterproof, sterile, nontoxic.
Description
Technical field
The present invention relates to environment-friendly materials technical fields, in particular to a kind of environment protecting paper and preparation method thereof.
Background technique
Currently, organic resin content is higher in existing environment-friendlypaper paper product, and it is most of more than 50% or more, due to organic
Resin degradation cycle is slow, so, organic resin is largely used in environment protecting paper, although caused by reducing in paper production
Trees cut down problem, but the problem of bring organic resin pollution degradation is more serious, are unfavorable for environmental protection, it is subsequent there may be
Adverse effect can be more far-reaching.
Summary of the invention
The purpose of the present invention is to provide a kind of environment protecting papers and preparation method thereof, to solve the standby not ring of existing environmental protection paper
The problem of guarantor,
In order to realize above-mentioned purpose of the invention, the following technical scheme is adopted:
A kind of environment protecting paper, material composition are organic resin, inorganic mineral powder and auxiliary agent, the mass ratio of organic resin and inorganic mineral powder
It is 1 to 1~9, auxiliary agent accounts for the 2~6% of organic resin and inorganic mineral powder gross mass.
Further, the organic resin be linear low density polyethylene (LLDPE) (LLDPE), high density polyethylene (HDPE) (HDPE) and
Low density polyethylene (LDPE) (LDPE), linear low density polyethylene (LLDPE) (LLDPE), high density polyethylene (HDPE) (HDPE) and low density polyethylene (LDPE)
(LDPE) mass ratio is (2~5): (0.5~4): 1 between.
Further, the inorganic mineral powder is calcium carbonate, titanium dioxide and/or calcite.
Further, the inorganic mineral powder is calcium carbonate, titanium dioxide and/or calcite, additional talcum powder, wherein talcum
Powder accounts for inorganic mineral powder gross mass 5~20%.
Further, the auxiliary agent is couplant and dispersing agent, and wherein the mass ratio of couplant and dispersing agent is 2:1.
Further, the auxiliary agent be couplant and dispersing agent, applied foam agent, oxidant and/or ultraviolet screener,
Wherein the mass ratio of couplant and dispersing agent is 2:1, and foaming agent, oxidant and/or ultraviolet screener account for the gross mass 20 of auxiliary agent
~40%.
A kind of preparation method of environment protecting paper, comprising the following steps:
(1) inorganic mineral powder is heated to the oC of 90oC~150 in miberal powder air drier, 10~50min is kept the temperature, is dried
Processing, is then down to room temperature;
(2) inorganic mineral powder after organic resin, auxiliary agent and drying process is stirred under the conditions of 120 DEG C~150 DEG C, is stirred
Speed at least 750r/min, 30~45 min of mixing time are uniformly mixed and obtain mixed material, wherein organic resin and inorganic mine
The mass ratio of powder is 1:(1~9), auxiliary agent accounts for the 2~6% of organic resin and inorganic mineral powder gross mass;
(3) mixed material is warmed to 120oC~155oC, produces paper grade (stock) feed particles using extruder, particle is straight
The cylindrical body of 2~3 mm of diameter;
(4) feed particles are processed by ground paper using film laminator, inflation film manufacturing machine or paper drawing mould machine, then carry out traction stretch processing, until
With a thickness of 0.05~1.2mm;
(5) sided corona treatment is carried out to paper surface using corona machine, corona machine power 4KW to 6KW realizes that origin of force is paid on surface
Reason;
(6) processing is coated to the paper after sided corona treatment, obtains environment protecting paper, mono- 2.45m of finished paper width 0.6m.
Compared with prior art, the invention has the benefit that the preparation method of this environment protecting paper largely reduces organic resin
Application, keep environment protecting paper degradation time shorter, achieve the purpose that really environmental protection, while environment protecting paper is able to carry out writing, printing, work
For packaging bag and packing box, toughness is strong, and waterproof is sterile, nontoxic, effectively reduces the felling of trees, as being used on paper of new generation,
Instead of conventional paper, there is very big meaning.
Specific embodiment
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will
Understand, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the invention.It is not specified in embodiment specific
Condition person carries out according to conventional conditions or manufacturer's recommended conditions.Reagents or instruments used without specified manufacturer is
The conventional products that can be obtained by commercially available purchase.
Embodiment 1
The present embodiment mainly produces the environmentally friendly sheet type such as packaging bag of the needs compared with strong pulling force or gift box, and wherein organic resin selects
Taking LLDPE:LDPE:HDPE mass ratio is respectively 2:1:1, and inorganic mineral powder chooses calcium carbonate: talcum powder: the mass ratio of titanium dioxide
Respectively 7:2:1, auxiliary agent choose coupling agent and dispersing agent, and coupling agent chooses HSt stearic acid, and dispersing agent is chosen YX-A06, accounted for altogether
Organic resin and inorganic mineral powder gross mass 2%.
A kind of its raw material of environment protecting paper is divided into organic resin, calcium carbonate, talcum powder, titanium dioxide, coupling agent and dispersing agent.
Its organic resin and inorganic mineral powder mass ratio are 1:1;LLDPE:LDPE:HDPE mass ratio is respectively in organic resin
2:1:1;Calcium carbonate in inorganic mineral powder: talcum powder: the mass ratio of titanium dioxide is respectively 7:2:1;Coupling agent and dispersing agent occupy machine
The mass ratio of the 2% of resin and inorganic mineral powder gross mass, couplant and dispersing agent is 2:1.
A kind of environmental protection paper Preparation Method and step
(1) inorganic mineral powder is heated in miberal powder air drier 90oC, keeps the temperature 10min, is dried, is then down to
Room temperature;
(2) inorganic mineral powder after organic resin, auxiliary agent and drying process is stirred under the conditions of 120 DEG C, mixing speed
750r/min, 30 min of mixing time are uniformly mixed and obtain mixed material, and wherein the mass ratio of organic resin and inorganic mineral powder is
1:1, auxiliary agent account for the 2% of organic resin and inorganic mineral powder gross mass;
(3) mixed material is warmed to 120oC, produces paper grade (stock) feed particles using extruder, particle is 2 mm of diameter
Cylindrical body;
(4) feed particles are processed by ground paper using film laminator, inflation film manufacturing machine or paper drawing mould machine, then carry out traction stretch processing, until
With a thickness of 0.05mm;
(5) sided corona treatment is carried out to paper surface using corona machine, corona machine power 4KW realizes that surface is paid and puts forth effort to handle;
(6) processing is coated to the paper after sided corona treatment, obtains environment protecting paper.
Embodiment 2
The present embodiment mainly produces the environmentally friendly sheet type of the sun-proof colour fading of degradable efflorescence prevention, and wherein organic resin chooses LLDPE:
LDPE:HDPE mass ratio is respectively 7:2:1, and inorganic mineral powder chooses calcite: talcum powder: the mass ratio of titanium dioxide is respectively 7:
2:1, auxiliary agent choose coupling agent, dispersing agent, antioxidant and ultraviolet screener, and coupling agent chooses HSt stearic acid, and dispersing agent is chosen
YX-A06, antioxidant choose model 1010, and ultraviolet screener chooses UV-531 light stabilizer, account for organic resin and inorganic altogether
Miberal powder gross mass 6%.
A kind of its raw material of environment protecting paper is divided into organic resin, calcite, talcum powder, titanium dioxide, coupling agent, dispersing agent, antioxygen
Agent and ultraviolet screener.
Its organic resin and inorganic mineral powder mass ratio are 2:8;LLDPE:LDPE:HDPE mass ratio is respectively in organic resin
7:2:1;Calcite in inorganic mineral powder: talcum powder: the mass ratio of titanium dioxide is respectively 7:2:1;It is coupling agent, dispersing agent, anti-oxidant
Agent and ultraviolet screener account for the 6% of organic resin and inorganic mineral powder gross mass, couplant: dispersing agent: antioxidant: antiultraviolet
The mass ratio of agent is 2:1:1:1.
A kind of preparation method of environment protecting paper, comprising the following steps:
(1) inorganic mineral powder is heated in miberal powder air drier 150 oC, keeps the temperature 50min, is dried, then drops
To room temperature;
(2) inorganic mineral powder after organic resin, auxiliary agent and drying process is stirred under the conditions of 150 DEG C, mixing speed
1200r/min, 45 min of mixing time are uniformly mixed and obtain mixed material, wherein the mass ratio of organic resin and inorganic mineral powder
For 2:8, auxiliary agent accounts for the 6% of organic resin and inorganic mineral powder gross mass;
(3) mixed material is warmed to 155oC, produces paper grade (stock) feed particles using extruder, particle is 3 mm of diameter
Cylindrical body;
(4) feed particles are processed by ground paper using film laminator, inflation film manufacturing machine or paper drawing mould machine, then carry out traction stretch processing, until
With a thickness of 1.2mm;
(5) sided corona treatment is carried out to paper surface using corona machine, corona machine power 5KW realizes that surface is paid and puts forth effort to handle;
(6) processing is coated to the paper after sided corona treatment, obtains environment protecting paper.
Embodiment 3
The present embodiment mainly produces the wrapping paper or corrugation sheet type of degradable efflorescence prevention, and wherein organic resin chooses LLDPE:
LDPE:HDPE mass ratio is respectively 5:1:4, and inorganic mineral powder chooses calcite: calcium carbonate: the mass ratio of talcum powder is respectively 5:
4:1, auxiliary agent choose coupling agent and dispersing agent, and coupling agent chooses HSt stearic acid, and dispersing agent chooses YX-A06, accounts for organic resin altogether
With inorganic mineral powder gross mass 3%.
A kind of its raw material of environment protecting paper is divided into organic resin, calcite, talcum powder, calcium carbonate, coupling agent and dispersing agent.
Its organic resin and inorganic mineral powder mass ratio are 1:9;LLDPE:LDPE:HDPE mass ratio is respectively in organic resin
5:1:4;Calcite in inorganic mineral powder: calcium carbonate: the mass ratio of talcum powder is respectively 5:4:1;Coupling agent and dispersing agent occupy machine
The 3% of resin and inorganic mineral powder gross mass, couplant: the mass ratio of dispersing agent is 2:1.
A kind of preparation method of environment protecting paper, comprising the following steps:
(1) inorganic mineral powder is heated in miberal powder air drier 100oC, keeps the temperature 30min, is dried, then drops
To room temperature;
(2) inorganic mineral powder after organic resin, auxiliary agent and drying process is stirred under the conditions of 130 DEG C, mixing speed
900r/min, 40 min of mixing time are uniformly mixed and obtain mixed material, and wherein the mass ratio of organic resin and inorganic mineral powder is
1:9, auxiliary agent account for the 3% of organic resin and inorganic mineral powder gross mass;
(3) mixed material is warmed to 130oC, produces paper grade (stock) feed particles using extruder, particle is 2.5 mm of diameter
Cylindrical body;
(4) feed particles are processed by ground paper using film laminator, inflation film manufacturing machine or paper drawing mould machine, then carry out traction stretch processing, until
With a thickness of 1mm ' '
(5) sided corona treatment is carried out to paper surface using corona machine, corona machine power 6KW realizes that surface is paid and puts forth effort to handle;
(6) processing is coated to the paper after sided corona treatment, obtains environment protecting paper.
Embodiment 4
The present embodiment mainly produces degradable efflorescence prevention, the archive files environmental protection sheet type that can be saved for a long time, wherein organic tree
It is respectively 3:4:1 that rouge, which chooses LLDPE:LDPE:HDPE mass ratio, and inorganic mineral powder chooses calcium carbonate, and auxiliary agent is chosen coupling agent, divided
Powder and antioxidant, coupling agent choose HSt stearic acid, and dispersing agent chooses YX-A06, and antioxidant is chosen model 1010, helped
Agent accounts for organic resin and inorganic mineral powder gross mass 4% altogether.
A kind of its raw material of environment protecting paper is divided into organic resin, calcium carbonate, coupling agent, dispersing agent, antioxidant.
Its organic resin and inorganic mineral powder mass ratio are 3:7;LLDPE:LDPE:HDPE mass ratio is respectively in organic resin
4:2:1;Coupling agent, dispersing agent and antioxidant account for the 3% of organic resin and inorganic mineral powder gross mass altogether, couplant: dispersing agent:
The mass ratio of antioxidant is 2:1:2.
The preparation method is the same as that of Example 1
Embodiment 5
It is respectively 4:2:1 that organic resin, which chooses LLDPE:LDPE:HDPE mass ratio, in the present embodiment, and inorganic mineral powder chooses carbonic acid
Calcium and talcum powder, wherein talcum powder accounts for inorganic mineral powder gross mass 5%, and auxiliary agent chooses coupling agent, dispersing agent and foaming agent, coupling agent
HSt stearic acid is chosen, dispersing agent chooses YX-A06, and foaming agent chooses model AC. azodicarbonamide, and auxiliary agent occupies machine tree altogether
Rouge and inorganic mineral powder gross mass 4%, foaming agent, which is added, can mitigate environmentally friendly paper weight.
A kind of its raw material of environment protecting paper is divided into organic resin, calcium carbonate, talcum powder, coupling agent, dispersing agent, foaming agent.
Its organic resin and inorganic mineral powder mass ratio are 4:6;LLDPE:LDPE:HDPE mass ratio is respectively in organic resin
4:2:1;Calcium carbonate and talcum powder in inorganic mineral powder, wherein talcum powder accounts for inorganic mineral powder gross mass 5%, coupling agent, dispersing agent and hair
Infusion accounts for the 3% of organic resin and inorganic mineral powder gross mass altogether, couplant: dispersing agent: the mass ratio of foaming agent is 2:1:2.
The preparation method is the same as that of Example 1
Embodiment 6
It is respectively 4:2:1 that organic resin, which chooses LLDPE:LDPE:HDPE mass ratio, in the present embodiment, and inorganic mineral powder chooses carbonic acid
Calcium and talcum powder, wherein talcum powder accounts for inorganic mineral powder gross mass 20%, and auxiliary agent chooses coupling agent, dispersing agent and ultraviolet screener, even
Mixture chooses HSt stearic acid, and dispersing agent chooses YX-A06, and ultraviolet screener chooses UV-531 light stabilizer, and auxiliary agent occupies machine altogether
Resin and inorganic mineral powder gross mass 4%.
A kind of its raw material of environment protecting paper is divided into organic resin, calcium carbonate, talcum powder, coupling agent, dispersing agent, ultraviolet screener.
Its organic resin and inorganic mineral powder mass ratio are 3:7;LLDPE:LDPE:HDPE mass ratio is respectively in organic resin
4:2:1;Calcium carbonate and talcum powder in inorganic mineral powder, wherein talcum powder accounts for inorganic mineral powder gross mass 20%, coupling agent, dispersing agent and
Ultraviolet screener accounts for the 3% of organic resin and inorganic mineral powder gross mass altogether, couplant: dispersing agent: the mass ratio of ultraviolet screener is
2:1:2.
The preparation method is the same as that of Example 1
Embodiment 7
It is respectively 4:2:1 that organic resin, which chooses LLDPE:LDPE:HDPE mass ratio, in the present embodiment, and inorganic mineral powder chooses carbonic acid
Calcium and talcum powder, wherein talcum powder accounts for inorganic mineral powder gross mass 10%, and auxiliary agent chooses coupling agent, dispersing agent and foaming agent, coupling agent
HSt stearic acid is chosen, dispersing agent chooses YX-A06, and foaming agent chooses model AC. azodicarbonamide, and auxiliary agent occupies machine tree altogether
Rouge and inorganic mineral powder gross mass 4%.
A kind of its raw material of environment protecting paper is divided into organic resin, calcium carbonate, talcum powder, coupling agent, dispersing agent, foaming agent.
Its organic resin and inorganic mineral powder mass ratio are 3:7;LLDPE:LDPE:HDPE mass ratio is respectively in organic resin
4:2:1;Calcium carbonate and talcum powder in inorganic mineral powder, wherein talcum powder accounts for inorganic mineral powder gross mass 10%, coupling agent, dispersing agent and
Foaming agent accounts for the 3% of organic resin and inorganic mineral powder gross mass altogether, couplant: dispersing agent: the mass ratio of foaming agent is 2:1:1.5.
The preparation method is the same as that of Example 1
1 environment protecting paper performance parameter table (existing environment protecting paper) of table
Evaluation content | Environment protecting paper | Existing environment protecting paper |
Degradation time (moon) | 0.5-1 | 24 |
Degradation rate (%) | 60-90 | 50 |
It writes adhesive rate (%) | 90 | 85 |
Toughness rate (%) | 80 | 80 |
2 environment protecting paper performance parameter table (traditional paper) of table
Evaluation content | Environment protecting paper | Traditional paper |
It writes adhesive rate (%) | 90 | 95 |
Toughness rate (%) | 80 | 10 |
Waterproof rate (%) | 100 | 10 |
Environmentally friendly rate (%) | 90 | 20 |
Tables 1 and 2 the result shows that: the application environment protecting paper is significantly better than existing environment protecting paper on degradation rate and degradation time, tough
Property and waterproof performance on be significantly better than traditional paper, and better than raw material of the timber as paper is not used, environmentally friendly rate mentions significantly
It is high.
Although illustrate and describing the present invention with specific embodiment, it will be appreciated that without departing substantially from of the invention
Many other change and modification can be made in the case where spirit and scope.It is, therefore, intended that in the following claims
Including belonging to all such changes and modifications in the scope of the invention.
Claims (7)
1. a kind of environment protecting paper, it is characterised in that: its material composition is organic resin, inorganic mineral powder and auxiliary agent, organic resin and nothing
The mass ratio of machine miberal powder is 1 to 1~9, and auxiliary agent accounts for the 2~6% of organic resin and inorganic mineral powder gross mass.
2. environment protecting paper according to claim 1, it is characterised in that: the organic resin be linear low density polyethylene (LLDPE),
High density polyethylene (HDPE) and low density polyethylene (LDPE), the interstitial of linear low density polyethylene (LLDPE), high density polyethylene (HDPE) and low density polyethylene (LDPE)
Amount is than being (2~5): (0.5~4): 1.
3. environment protecting paper according to claim 1, it is characterised in that: the inorganic mineral powder be calcium carbonate, titanium dioxide and/or
Calcite.
4. environment protecting paper according to claim 1, it is characterised in that: the inorganic mineral powder be calcium carbonate, titanium dioxide and/or
Calcite, additional talcum powder, wherein talcum powder accounts for inorganic mineral powder gross mass 5~20%.
5. environment protecting paper according to claim 1, it is characterised in that: the auxiliary agent is couplant and dispersing agent, wherein coupling
The mass ratio of mixture and dispersing agent is 2:1.
6. environment protecting paper according to claim 1, it is characterised in that: the auxiliary agent is couplant and dispersing agent, additional hair
Infusion, oxidant and/or ultraviolet screener, wherein the mass ratio of couplant and dispersing agent be 2:1, foaming agent, oxidant and/or
Ultraviolet screener accounts for the gross mass 20~40% of auxiliary agent.
7. a kind of preparation method of environment protecting paper, which comprises the following steps:
(1) inorganic mineral powder is heated to the oC of 90oC~150 in miberal powder air drier, 10~50min is kept the temperature, is dried
Processing, is then down to room temperature;
(2) inorganic mineral powder after organic resin, auxiliary agent and drying process is stirred under the conditions of 120 DEG C~150 DEG C, is stirred
Speed at least 750r/min, 30~45 min of mixing time are uniformly mixed and obtain mixed material, wherein organic resin and inorganic mine
The mass ratio of powder is 1:(1~9), auxiliary agent accounts for the 2~6% of organic resin and inorganic mineral powder gross mass;
(3) mixed material is warmed to 120oC~155oC, produces paper grade (stock) feed particles using extruder, particle is straight
The cylindrical body of 2~3 mm of diameter;
(4) feed particles are processed by ground paper using film laminator, inflation film manufacturing machine or paper drawing mould machine, then carry out traction stretch processing, until
With a thickness of 0.05~1.2mm;
(5) sided corona treatment is carried out to paper surface using corona machine, corona machine power 4KW to 6KW realizes that origin of force is paid on surface
Reason;
(6) processing is coated to the paper after sided corona treatment, obtains environment protecting paper.