CN110372948A - The special overlay film steel band of armoured cable - Google Patents
The special overlay film steel band of armoured cable Download PDFInfo
- Publication number
- CN110372948A CN110372948A CN201910317871.9A CN201910317871A CN110372948A CN 110372948 A CN110372948 A CN 110372948A CN 201910317871 A CN201910317871 A CN 201910317871A CN 110372948 A CN110372948 A CN 110372948A
- Authority
- CN
- China
- Prior art keywords
- parts
- steel band
- overlay film
- plastic film
- ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of special overlay film steel bands of armoured cable, including steel belt layer and plastic film layers, the plastic film layers are covered on steel belt layer, one or both sides in lower surface, the plastic film layers include the material of following parts by weight: 65 ~ 80 parts of ethylene-vinyl acetate copolymer, 10 ~ 25 parts of hydrogenated styrene-butadiene block copolymer, 5 ~ 12 parts of acrylic resin, 3 ~ 10 parts of White Mineral Oil, 2 ~ 6 parts of ethylene acrylic acid co polymer, 2 ~ 5 parts of nanometer calcium carbonate, 3, 3 ' -0.3 ~ 1 part of dilauryl thiodipropionates, 2, 2- oxalyl amido-bis- [ethyl -3- (3, 5- di-tert-butyl-hydroxy phenyl)] 0.1 ~ 0.5 part of propionic ester, 0.1 ~ 0.3 part of pigment.The armoured cable is with special overlay film steel band after being made into optical cable, the cable core wrapped up by it is corroded from moisture, still there can be good toughness without cracking by repeatedly bending simultaneously, and plastic film is easy to completely strip with the sheath on the outside of it from steel band, is not in situations such as being torn, tear up.
Description
Technical field
The present invention relates to a kind of overlay film steel band more particularly to a kind of special overlay film steel bands of armoured cable.
Background technique
Composite steel-plastic belt is mainly used for communications optical cable, communication cable outer jacket, is bonded together composition synthesis with protective cover material
Sheath acts the moisture-proof layer for protecting cable core to corrode from moisture, while having armouring effect to cable core, resists extraneous effect
Power lay etc. in various applications for communications optical cable, communication cable and provides mechanical protection, guarantees the stability, reliably of application
Property.However, needing to realize fully stripped state between steel band and protective cover material when finished product cable is constructed, i.e., after stripping outer jacket, steel band covers
Also complete band removes film, only remaining base steel band.It is remained on armouring embossing base steel band if any overlay film after steel band and external sheath layer removing, just
It will affect electric conductivity.Because the optical cable is by will be after shield strips outside optical cable at the tower top section, steel band is directly filled with transmitting in cable
It sets earthed system to be welded, Lai Shixian conducting function, to cause the damage of the communications cable after avoiding base station from being struck by lightning.Such as
Fruit strips after sheath skin on base steel band also there are overlay film residual, just will affect the welding effect of steel band and tower top emitter.Cause
How this, provide a kind of direction that easily peelable overlay film steel band is made great efforts as those skilled in the art.
Summary of the invention
It is an object of that present invention to provide a kind of special overlay film steel band of armoured cable, which is making of special overlay film steel band
After optical cable, by its wrap up cable core from moisture corrode, while can by repeatedly bending still have good toughness and
It will not cracking, and plastic film is easy to completely strip with the sheath on the outside of it from steel band, is not in be torn, tear up
Situations such as.
In order to achieve the above objectives, the technical solution adopted by the present invention is that: a kind of armoured cable special overlay film steel band, including steel
Belt and plastic film layers, the plastic film layers are covered on the one or both sides in steel belt layer upper and lower surfaces, and feature exists
In: the plastic film layers include the material of following parts by weight:
65 ~ 80 parts of ethylene-vinyl acetate copolymer,
10 ~ 25 parts of hydrogenated styrene-butadiene block copolymer,
5 ~ 12 parts of acrylic resin,
3 ~ 10 parts of White Mineral Oil,
2 ~ 6 parts of ethylene acrylic acid co polymer,
2 ~ 5 parts of nanometer calcium carbonate,
3,3 ' -0.3 ~ 1 part of dilauryl thiodipropionates,
0.1 ~ 0.5 part of propionic ester of 2,2- oxalyl amidos-bis- [ethyl -3- (3,5- di-tert-butyl-hydroxy phenyl)],
0.1 ~ 0.3 part of pigment.
Further improved technical solution is as follows in above-mentioned technical proposal:
1. in above scheme, the content ratio of ethylene and acrylic acid is 100:5 ~ 7 in the ethylene acrylic acid co polymer.
2. in above scheme, the acrylic resin is that homopolypropylene, copolymer polypropylene or ethylene propylene copolymer are poly-
Propylene.
3. in above scheme, the parts by weight of the pigment are 0.13 ~ 0.21 part.
4. in above scheme, the pigment is that phthalein is green.
Due to the application of the above technical scheme, compared with the prior art, the invention has the following advantages:
1. the special overlay film steel band of armoured cable of the present invention, using 65 ~ 80 parts of ethylene-vinyl acetate copolymers as base-material in formula,
10 ~ 25 parts of hydrogenated styrene-butadiene block copolymer blendings are added, so that the plastic film obtained is with good anti-
While tide, waterproof and weatherability, there is toughness and buckle resistance, guarantee that overlay film steel band after being made into optical cable, is wrapped up by it
Cable core is corroded from moisture, while still can have good toughness without cracking by repeatedly bending, and be added to second
2 ~ 6 parts of alkene acrylic copolymer, the bonding force of plastic film is increased, increases peel strength, it is embedding with hydrogenated styrene-butadiene
Section copolymer collaboration, reach plastic film be easy completely stripped with the sheath on the outside of it from steel band, and be not in by
Situations such as tearing, tearing up;In addition, 5 ~ 12 parts of acrylic resin are also added into its formula, so that hydrogenated styrene-butadiene is embedding
The strand of section copolymer is more soft, to further enhance the flexibility of plastic film, makes it in stripping process
It is not easy to break, it is easier to be removed from steel band.
2. the special overlay film steel band of armoured cable of the present invention, 2 ~ 5 parts of nanometer calcium carbonate are added in formula, while adding white
3 ~ 10 parts of dormant oil cooperations, plastic film obtained have better tearing strength, guarantee plastic film in the mistake removed with steel band
Cheng Buhui is torn;In addition, it is bis- [ethyl -3- (3,5- di-tert-butyl-hydroxy phenyl)] that 2,2- oxalyl amido-is added in formula
0.1 ~ 0.5 part of propionic ester, has the function of metal deactivating and anti-copper evil performance, extend the service life of product.
Specific embodiment
The present invention will be further described below with reference to examples:
Embodiment 1 ~ 4: a kind of armoured cable special overlay film steel band, including steel belt layer and plastic film layers, the plastic film layers
The one or both sides being covered in steel belt layer upper and lower surfaces, it is characterised in that: the plastic film layers include following parts by weight
Material:
Table 1
The content ratio of ethylene and acrylic acid is 100:5 ~ 7 in the ethylene acrylic acid co polymer, and the acrylic resin is equal
Poly- polypropylene, copolymer polypropylene or ethylene propylene copolymer polypropylene, the parts by weight of the pigment are 0.13 ~ 0.21 part, institute
Stating pigment is that phthalein is green.
The plastic film layers of the special overlay film steel band of the armoured cable are made by following steps:
S1. 65 ~ 80 parts of ethylene-vinyl acetate copolymers are weighed, 10 ~ 25 parts of hydrogenated styrene-butadiene block copolymer, are gathered
5 ~ 12 parts of allyl resin, 3 ~ 10 parts of White Mineral Oil, 2 ~ 6 parts of ethylene acrylic acid co polymer, 2 ~ 5 parts of nanometer calcium carbonate, 3,3 '-thio two
0.3 ~ 1 part of propionic acid dilauryl, 2,2- oxalyl amido-bis- [ethyl -3-(3,5- di-tert-butyl-hydroxy phenyl)] propionic ester
0.1 ~ 0.5 part, in 0.1 ~ 0.3 part of investment high-speed mixer of pigment, be sufficiently mixed uniformly, obtain mixing masterbatch;
S2. mixing masterbatch is fed into inflation film manufacturing machine, it is thin with the plastics of special overlay film steel band to get the armoured cable through squeezing out blown film
Film layer.
Comparative example 1 ~ 3: a kind of armoured cable special overlay film steel band, including steel belt layer and plastic film layers, the plastics are thin
Film layer is covered on the one or both sides in steel belt layer upper and lower surfaces, it is characterised in that: the plastic film layers include following weight
The material of part:
Table 2
The content ratio of ethylene and acrylic acid is 100:7 in the ethylene acrylic acid co polymer, and the acrylic resin is homopolymerization
Polypropylene, the parts by weight of the pigment are 0.13 ~ 0.21 part, and the pigment is that phthalein is green.
Preparation method is common method.
The film of each embodiment and comparative example preparation is covered on steel band after formation overlay film steel band, and performance detection data is such as
Under:
Table 3
Wherein, appearance should ensure that smooth overlay film steel strip surface, smooth, uniform, free from admixture, without piebald, and without other machinery wounds
Defect;Peel strength refers to peel strength between steel band and plastic film.
As shown in table 3, the plastic film prepared in various embodiments of the present invention either tensile strength, fracture elongation, also
It is the plastic film that peel strength is superior to comparative example, plastic film produced by the present invention is covered on formation overlay film steel on steel band
Band, after being made into optical cable, the cable core wrapped up by it corrodes overlay film steel band from moisture, while can still have by repeatedly bending
There is good toughness without cracking, and plastic film is easy to completely strip with the sheath on the outside of it from steel band, and not
It will appear situations such as being torn, tearing up, user cuts off optical cable under any length and carries out using can remove steel band manually
The sheath and plastic film of outside, convenient for being welded with emitter earthed system, Lai Shixian conducting function, to avoid base
It stands after being struck by lightning.
The above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow person skilled in the art
Scholar cans understand the content of the present invention and implement it accordingly, and it is not intended to limit the scope of the present invention.It is all according to the present invention
Equivalent change or modification made by Spirit Essence, should be covered by the protection scope of the present invention.
Claims (5)
1. a kind of armoured cable special overlay film steel band, including steel belt layer and plastic film layers, the plastic film layers are covered on steel
One or both sides in belt upper and lower surfaces, it is characterised in that: the plastic film layers include the material of following parts by weight:
65 ~ 80 parts of ethylene-vinyl acetate copolymer,
10 ~ 25 parts of hydrogenated styrene-butadiene block copolymer,
5 ~ 12 parts of acrylic resin,
3 ~ 10 parts of White Mineral Oil,
2 ~ 6 parts of ethylene acrylic acid co polymer,
2 ~ 5 parts of nanometer calcium carbonate,
3,3 ' -0.3 ~ 1 part of dilauryl thiodipropionates,
0.1 ~ 0.5 part of propionic ester of 2,2- oxalyl amidos-bis- [ethyl -3- (3,5- di-tert-butyl-hydroxy phenyl)],
0.1 ~ 0.3 part of pigment.
2. the special overlay film steel band of armoured cable according to claim 1, it is characterised in that: the ethylene acrylic acid co polymer
The content ratio of middle ethylene and acrylic acid is 100:5 ~ 7.
3. the special overlay film steel band of armoured cable according to claim 1, it is characterised in that: the acrylic resin is homopolymerization
Polypropylene, copolymer polypropylene or ethylene propylene copolymer polypropylene.
4. the special overlay film steel band of armoured cable according to claim 1, it is characterised in that: the parts by weight of the pigment are
0.13 ~ 0.21 part.
5. the special overlay film steel band of armoured cable according to claim 1, it is characterised in that: the pigment is that phthalein is green.