CN110367649A - Single side glues manufacturing method of shoes - Google Patents
Single side glues manufacturing method of shoes Download PDFInfo
- Publication number
- CN110367649A CN110367649A CN201910473531.5A CN201910473531A CN110367649A CN 110367649 A CN110367649 A CN 110367649A CN 201910473531 A CN201910473531 A CN 201910473531A CN 110367649 A CN110367649 A CN 110367649A
- Authority
- CN
- China
- Prior art keywords
- parts
- indsole
- heel
- outer bottom
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses single sides to glue manufacturing method of shoes, and method is the following steps are included: A, production mold: mold used in production outer bottom, indsole and heel;B, it makes sole: the outer bottom of fusing, indsole and heel material is poured into respectively in the mold of outer bottom, indsole and heel;C, depanning: after natural cooling, outer bottom, indsole and heel are taken out from the mold of outer bottom, indsole and heel respectively;D, deburring and grinding process deburring, polishing: are carried out to the outside of outer bottom, indsole and heel using trimmer and sander.The present invention uses three Mold Making outer bottoms, indsole and heel, the accuracy of outer bottom, indsole and heel production can be improved, using gluing three times, it will be bonded between outer bottom and heel, between outer bottom and indsole and between vamp and indsole, technique clear and smooth, the division of labor is clear, is not in that the viscous phenomenon of leakage occurs, has ensured the quality of this shoes.
Description
Technical field
The present invention relates to shoes processing technique field, specially single side glues manufacturing method of shoes.
Background technique
Shoes are a kind of tools that people protect the foot against wound, and earliest people do not allow foot to feel bad to overcome special circumstances
Or it is injured, fur shoes are just invented, shoes till now, are formed this present appearance, various patterns function
Shoes are seen everywhere, and shoes are made of sole and vamp, and sole is made of outer bottom, indsole and heel, but in the prior art, due to
Process is unintelligible, the viscous phenomenon of leakage often occurs and occurs, so that the quality of shoes is reduced, for this purpose, it is proposed that single side gluing system
Shoes method.
Summary of the invention
The purpose of the present invention is to provide single sides to glue manufacturing method of shoes, to solve the problems mentioned in the above background technology.
To achieve the above object, the invention provides the following technical scheme: single side glues manufacturing method of shoes, method includes following
Step:
A, mold is made: mold used in production outer bottom, indsole and heel;
B, it makes sole: the outer bottom of fusing, indsole and heel material is poured into the mold of outer bottom, indsole and heel respectively
In;
C, depanning: after natural cooling, outer bottom, indsole and heel are taken from the mold of outer bottom, indsole and heel respectively
Out;
D, deburring and burnishing part deburring, polishing: are carried out to the outside of outer bottom, indsole and heel using trimmer and sander
Reason;
E, first time upper glue bond: being coated with one layer of glue at the top of heel, and the bottom surface of outer bottom be placed in glue surface,
After perfectly aligned, it will be pressed between outer bottom and heel using press machine;
F, second of upper glue bond: being coated with one layer of glue at the top of outer bottom, and the bottom surface of indsole be placed in glue surface,
After perfectly aligned, it will be pressed between outer bottom and indsole using press machine;
G, it makes vamp: Multilayer plus material being bonded using glue, and fabric is cut into the size of needs by cutting knife
And shape;
H, the upper glue bond of third time: a painting tree lace is drawn in the outside of indsole in advance, and glue is uniformly applied to gluing
On line, then vamp is placed on glue, and is pressed by press machine;
I, the glue of outer bottom, indsole, heel and vamp outer surface frictioning: is struck off using doctor kiss coater;
J, drying: the shoes prepared are dried using drying device.
Preferably, the outer bottom is by EVA, tackifier, white carbon black, nitrile rubber, polyvinyl chloride, activating agent and calcium stearate
Composition, the component of parts by weight are as follows: 80~150 parts of EVA;3~8 parts of tackifier;2~6 parts of white carbon black;Nitrile rubber 30~
50 parts;10~18 parts of polyvinyl chloride;2~5 parts of activating agent;3~8 parts of calcium stearate;Indsole by blown rubber, high pressure polyethylene,
Inorganic filling material, dibutyl phthalate, acetylene carbon black, nano silica and promotor composition, parts by weight
Component are as follows: 80~130 parts of blown rubber;25~35 parts of high pressure polyethylene;15~25 parts of inorganic filling material;Phthalic acid two
10~20 parts of butyl ester;15~22 parts of acetylene carbon black;3~8 parts of nano silica;8~15 parts of promotor;Heel by anti-wear agent,
Dihydroxy polypropylene oxide ether, nano silica, surface modifier, ethylene propylene diene rubber, magnesia, stearic acid and glass fibers
Dimension composition, the component of parts by weight are as follows: 8~14 parts of anti-wear agent;40~60 parts of dihydroxy polypropylene oxide ether;Nanometer titanium dioxide
5~15 parts of silicon;2~5 parts of surface modifier;30~40 parts of ethylene propylene diene rubber;1~4 part of magnesia;2~4 parts of stearic acid;Glass
10~15 parts of glass fiber.
Preferably, the glue in described step E, F and H is by curing agent, epoxy resin, neoprene, tackifying resin, sulphur
Change promotor, polyisobutene, hexanedioic acid dioctyl ester, antioxidant and coupling agent composition, the component of parts by weight are as follows: curing agent
2~6 parts;5~10 parts of epoxy resin;40~50 parts of neoprene;10~18 parts of tackifying resin;2~4 parts of vulcanization accelerator;It is poly-
2~5 parts of isobutene;1~4 part of hexanedioic acid dioctyl ester;1~3 part of antioxidant;4~10 parts of coupling agent.
Preferably, the glue in the step G is one of paste box glue, white glue with vinyl or polyurethane adhesive.
Preferably, the drying temperature in the step J is 40~60 DEG C, and drying time is 3~5h.
Compared with prior art, beneficial effects of the present invention are as follows:
The present invention uses three Mold Making outer bottoms, indsole and heel, and the accurate of outer bottom, indsole and heel production can be improved
Degree will be bonded, technique is clear between outer bottom and heel, between outer bottom and indsole and between vamp and indsole using gluing three times
Clear smoothness, the division of labor is clear, is not in that the viscous phenomenon of leakage occurs, has ensured the quality of this shoes.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
Embodiment one:
Single side glue manufacturing method of shoes, method the following steps are included:
A, mold is made: mold used in production outer bottom, indsole and heel;
B, it makes sole: the outer bottom of fusing, indsole and heel material is poured into the mold of outer bottom, indsole and heel respectively
In;
C, depanning: after natural cooling, outer bottom, indsole and heel are taken from the mold of outer bottom, indsole and heel respectively
Out;
D, deburring and burnishing part deburring, polishing: are carried out to the outside of outer bottom, indsole and heel using trimmer and sander
Reason;
E, first time upper glue bond: being coated with one layer of glue at the top of heel, and the bottom surface of outer bottom be placed in glue surface,
After perfectly aligned, it will be pressed between outer bottom and heel using press machine;
F, second of upper glue bond: being coated with one layer of glue at the top of outer bottom, and the bottom surface of indsole be placed in glue surface,
After perfectly aligned, it will be pressed between outer bottom and indsole using press machine;
G, it makes vamp: Multilayer plus material being bonded using glue, and fabric is cut into the size of needs by cutting knife
And shape;
H, the upper glue bond of third time: a painting tree lace is drawn in the outside of indsole in advance, and glue is uniformly applied to gluing
On line, then vamp is placed on glue, and is pressed by press machine;
I, the glue of outer bottom, indsole, heel and vamp outer surface frictioning: is struck off using doctor kiss coater;
J, drying: the shoes prepared are dried using drying device.
Using three Mold Making outer bottoms, indsole and heel, the accuracy of outer bottom, indsole and heel production can be improved, adopt
With gluing three times, will be bonded between outer bottom and heel, between outer bottom and indsole and between vamp and indsole, technique clearly flows
Freely, the division of labor is clear, is not in that the viscous phenomenon of leakage occurs, has ensured the quality of this shoes.
Outer bottom is made of EVA, tackifier, white carbon black, nitrile rubber, polyvinyl chloride, activating agent and calcium stearate, weight
The component of number are as follows: 80 parts of EVA;3 parts of tackifier;2 parts of white carbon black;30 parts of nitrile rubber;10 parts of polyvinyl chloride;Activating agent 2
Part;3 parts of calcium stearate;Indsole is by blown rubber, high pressure polyethylene, inorganic filling material, dibutyl phthalate, acetylene charcoal
Black, nano silica and promotor composition, the component of parts by weight are as follows: 80 parts of blown rubber;25 parts of high pressure polyethylene;Nothing
15 parts of machine packing material;10 parts of dibutyl phthalate;15 parts of acetylene carbon black;3 parts of nano silica;8 parts of promotor;Shoes
It follows by anti-wear agent, dihydroxy polypropylene oxide ether, nano silica, surface modifier, ethylene propylene diene rubber, magnesia, hard
Resin acid and glass fibre composition, the component of parts by weight are as follows: 8 parts of anti-wear agent;40 parts of dihydroxy polypropylene oxide ether;Nanometer two
5 parts of silica;2 parts of surface modifier;30 parts of ethylene propylene diene rubber;1 part of magnesia;2 parts of stearic acid;10 parts of glass fibre.
Step E, the glue in F and H is by curing agent, epoxy resin, neoprene, tackifying resin, vulcanization accelerator, poly-
Isobutene, hexanedioic acid dioctyl ester, antioxidant and coupling agent composition, the component of parts by weight are as follows: 2 parts of curing agent;Asphalt mixtures modified by epoxy resin
5 parts of rouge;40 parts of neoprene;10 parts of tackifying resin;2 parts of vulcanization accelerator;2 parts of polyisobutene;1 part of hexanedioic acid dioctyl ester;It is anti-
1 part of oxidant;4 parts of coupling agent.
Glue in step G is paste box glue.
Drying temperature in step J is 40 DEG C, drying time 5h.
Embodiment two:
Single side glue manufacturing method of shoes, method the following steps are included:
A, mold is made: mold used in production outer bottom, indsole and heel;
B, it makes sole: the outer bottom of fusing, indsole and heel material is poured into the mold of outer bottom, indsole and heel respectively
In;
C, depanning: after natural cooling, outer bottom, indsole and heel are taken from the mold of outer bottom, indsole and heel respectively
Out;
D, deburring and burnishing part deburring, polishing: are carried out to the outside of outer bottom, indsole and heel using trimmer and sander
Reason;
E, first time upper glue bond: being coated with one layer of glue at the top of heel, and the bottom surface of outer bottom be placed in glue surface,
After perfectly aligned, it will be pressed between outer bottom and heel using press machine;
F, second of upper glue bond: being coated with one layer of glue at the top of outer bottom, and the bottom surface of indsole be placed in glue surface,
After perfectly aligned, it will be pressed between outer bottom and indsole using press machine;
G, it makes vamp: Multilayer plus material being bonded using glue, and fabric is cut into the size of needs by cutting knife
And shape;
H, the upper glue bond of third time: a painting tree lace is drawn in the outside of indsole in advance, and glue is uniformly applied to gluing
On line, then vamp is placed on glue, and is pressed by press machine;
I, the glue of outer bottom, indsole, heel and vamp outer surface frictioning: is struck off using doctor kiss coater;
J, drying: the shoes prepared are dried using drying device.
Using three Mold Making outer bottoms, indsole and heel, the accuracy of outer bottom, indsole and heel production can be improved, adopt
With gluing three times, will be bonded between outer bottom and heel, between outer bottom and indsole and between vamp and indsole, technique clearly flows
Freely, the division of labor is clear, is not in that the viscous phenomenon of leakage occurs, has ensured the quality of this shoes.
Outer bottom is made of EVA, tackifier, white carbon black, nitrile rubber, polyvinyl chloride, activating agent and calcium stearate, weight
The component of number are as follows: 110 parts of EVA;5 parts of tackifier;4 parts of white carbon black;40 parts of nitrile rubber;14 parts of polyvinyl chloride;Activating agent 4
Part;5 parts of calcium stearate;Indsole is by blown rubber, high pressure polyethylene, inorganic filling material, dibutyl phthalate, acetylene charcoal
Black, nano silica and promotor composition, the component of parts by weight are as follows: 100 parts of blown rubber;30 parts of high pressure polyethylene;
20 parts of inorganic filling material;15 parts of dibutyl phthalate;18 parts of acetylene carbon black;5 parts of nano silica;Promotor 12
Part;Heel is by anti-wear agent, dihydroxy polypropylene oxide ether, nano silica, surface modifier, ethylene propylene diene rubber, oxidation
Magnesium, stearic acid and glass fibre composition, the component of parts by weight are as follows: 11 parts of anti-wear agent;50 parts of dihydroxy polypropylene oxide ether;
10 parts of nano silica;3 parts of surface modifier;35 parts of ethylene propylene diene rubber;2 parts of magnesia;3 parts of stearic acid;Glass fibre
12 parts.
Step E, the glue in F and H is by curing agent, epoxy resin, neoprene, tackifying resin, vulcanization accelerator, poly-
Isobutene, hexanedioic acid dioctyl ester, antioxidant and coupling agent composition, the component of parts by weight are as follows: 4 parts of curing agent;Asphalt mixtures modified by epoxy resin
7 parts of rouge;45 parts of neoprene;15 parts of tackifying resin;3 parts of vulcanization accelerator;3 parts of polyisobutene;3 parts of hexanedioic acid dioctyl ester;It is anti-
2 parts of oxidant;7 parts of coupling agent.
Glue in step G is white glue with vinyl.
Drying temperature in step J is 50 DEG C, drying time 4h.
Embodiment three:
Single side glue manufacturing method of shoes, method the following steps are included:
A, mold is made: mold used in production outer bottom, indsole and heel;
B, it makes sole: the outer bottom of fusing, indsole and heel material is poured into the mold of outer bottom, indsole and heel respectively
In;
C, depanning: after natural cooling, outer bottom, indsole and heel are taken from the mold of outer bottom, indsole and heel respectively
Out;
D, deburring and burnishing part deburring, polishing: are carried out to the outside of outer bottom, indsole and heel using trimmer and sander
Reason;
E, first time upper glue bond: being coated with one layer of glue at the top of heel, and the bottom surface of outer bottom be placed in glue surface,
After perfectly aligned, it will be pressed between outer bottom and heel using press machine;
F, second of upper glue bond: being coated with one layer of glue at the top of outer bottom, and the bottom surface of indsole be placed in glue surface,
After perfectly aligned, it will be pressed between outer bottom and indsole using press machine;
G, it makes vamp: Multilayer plus material being bonded using glue, and fabric is cut into the size of needs by cutting knife
And shape;
H, the upper glue bond of third time: a painting tree lace is drawn in the outside of indsole in advance, and glue is uniformly applied to gluing
On line, then vamp is placed on glue, and is pressed by press machine;
I, the glue of outer bottom, indsole, heel and vamp outer surface frictioning: is struck off using doctor kiss coater;
J, drying: the shoes prepared are dried using drying device.
Using three Mold Making outer bottoms, indsole and heel, the accuracy of outer bottom, indsole and heel production can be improved, adopt
With gluing three times, will be bonded between outer bottom and heel, between outer bottom and indsole and between vamp and indsole, technique clearly flows
Freely, the division of labor is clear, is not in that the viscous phenomenon of leakage occurs, has ensured the quality of this shoes.
Outer bottom is made of EVA, tackifier, white carbon black, nitrile rubber, polyvinyl chloride, activating agent and calcium stearate, weight
The component of number are as follows: 150 parts of EVA;8 parts of tackifier;6 parts of white carbon black;50 parts of nitrile rubber;18 parts of polyvinyl chloride;Activating agent 5
Part;8 parts of calcium stearate;Indsole is by blown rubber, high pressure polyethylene, inorganic filling material, dibutyl phthalate, acetylene charcoal
Black, nano silica and promotor composition, the component of parts by weight are as follows: 130 parts of blown rubber;35 parts of high pressure polyethylene;
25 parts of inorganic filling material;20 parts of dibutyl phthalate;22 parts of acetylene carbon black;8 parts of nano silica;Promotor 15
Part;Heel is by anti-wear agent, dihydroxy polypropylene oxide ether, nano silica, surface modifier, ethylene propylene diene rubber, oxidation
Magnesium, stearic acid and glass fibre composition, the component of parts by weight are as follows: 14 parts of anti-wear agent;60 parts of dihydroxy polypropylene oxide ether;
15 parts of nano silica;5 parts of surface modifier;40 parts of ethylene propylene diene rubber;4 parts of magnesia;4 parts of stearic acid;Glass fibre
15 parts.
Step E, the glue in F and H is by curing agent, epoxy resin, neoprene, tackifying resin, vulcanization accelerator, poly-
Isobutene, hexanedioic acid dioctyl ester, antioxidant and coupling agent composition, the component of parts by weight are as follows: 6 parts of curing agent;Asphalt mixtures modified by epoxy resin
10 parts of rouge;50 parts of neoprene;18 parts of tackifying resin;4 parts of vulcanization accelerator;5 parts of polyisobutene;4 parts of hexanedioic acid dioctyl ester;It is anti-
3 parts of oxidant;10 parts of coupling agent.
Glue in step G is polyurethane adhesive.
Drying temperature in step J is 60 DEG C, drying time 3h.
In use, the essence of outer bottom, indsole and heel production can be improved using three Mold Making outer bottoms, indsole and heel
Exactness will be bonded, technique between outer bottom and heel, between outer bottom and indsole and between vamp and indsole using gluing three times
Clear and smooth, the division of labor is clear, is not in that the viscous phenomenon of leakage occurs, has ensured the quality of this shoes.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (5)
1. single side glue manufacturing method of shoes, it is characterised in that: its method the following steps are included:
A, mold is made: mold used in production outer bottom, indsole and heel;
B, it makes sole: the outer bottom of fusing, indsole and heel material is poured into respectively in the mold of outer bottom, indsole and heel;
C, depanning: after natural cooling, outer bottom, indsole and heel are taken out from the mold of outer bottom, indsole and heel respectively;
D, deburring and grinding process deburring, polishing: are carried out to the outside of outer bottom, indsole and heel using trimmer and sander;
E, first time upper glue bond: it is coated with one layer of glue at the top of heel, and the bottom surface of outer bottom is placed in glue surface, completely
After alignment, it will be pressed between outer bottom and heel using press machine;
F, second of upper glue bond: it is coated with one layer of glue at the top of outer bottom, and the bottom surface of indsole is placed in glue surface, completely
After alignment, it will be pressed between outer bottom and indsole using press machine;
G, it makes vamp: Multilayer plus material being bonded using glue, and fabric is cut into the size and shape of needs by cutting knife
Shape;
H, the upper glue bond of third time: drawing a painting tree lace in the outside of indsole in advance, and glue be uniformly applied on tree lace,
Then vamp is placed on glue, and is pressed by press machine;
I, the glue of outer bottom, indsole, heel and vamp outer surface frictioning: is struck off using doctor kiss coater;
J, drying: the shoes prepared are dried using drying device.
2. single side according to claim 1 glues manufacturing method of shoes, it is characterised in that: the outer bottom is by EVA, tackifier, white
Carbon black, nitrile rubber, polyvinyl chloride, activating agent and calcium stearate composition, the component of parts by weight are as follows: EVA80~150 part;
3~8 parts of tackifier;2~6 parts of white carbon black;30~50 parts of nitrile rubber;10~18 parts of polyvinyl chloride;2~5 parts of activating agent;It is stearic
3~8 parts of sour calcium;Indsole by blown rubber, high pressure polyethylene, inorganic filling material, dibutyl phthalate, acetylene carbon black,
Nano silica and promotor composition, the component of parts by weight are as follows: 80~130 parts of blown rubber;High pressure polyethylene 25~
35 parts;15~25 parts of inorganic filling material;10~20 parts of dibutyl phthalate;15~22 parts of acetylene carbon black;Nano-silica
3~8 parts of SiClx;8~15 parts of promotor;Heel is changed by anti-wear agent, dihydroxy polypropylene oxide ether, nano silica, surface
Property agent, ethylene propylene diene rubber, magnesia, stearic acid and glass fibre composition, the component of parts by weight are as follows: anti-wear agent 8~14
Part;40~60 parts of dihydroxy polypropylene oxide ether;5~15 parts of nano silica;2~5 parts of surface modifier;Ethylene-propylene-diene monomer
30~40 parts of glue;1~4 part of magnesia;2~4 parts of stearic acid;10~15 parts of glass fibre.
3. single side according to claim 1 glues manufacturing method of shoes, it is characterised in that: the glue in described step E, F and H is equal
By curing agent, epoxy resin, neoprene, tackifying resin, vulcanization accelerator, polyisobutene, hexanedioic acid dioctyl ester, antioxidant
It is formed with coupling agent, the component of parts by weight are as follows: 2~6 parts of curing agent;5~10 parts of epoxy resin;Neoprene 40~50
Part;10~18 parts of tackifying resin;2~4 parts of vulcanization accelerator;2~5 parts of polyisobutene;1~4 part of hexanedioic acid dioctyl ester;It is anti-oxidant
1~3 part of agent;4~10 parts of coupling agent.
4. single side according to claim 1 glues manufacturing method of shoes, it is characterised in that: the glue in the step G is paste box
One of glue, white glue with vinyl or polyurethane adhesive.
5. single side according to claim 1 glues manufacturing method of shoes, it is characterised in that: the drying temperature in the step J is
40~60 DEG C, drying time is 3~5h.