CN110359321A - A kind of method that nano-cellulose/PVA mixed slurry prepares fruit tray - Google Patents
A kind of method that nano-cellulose/PVA mixed slurry prepares fruit tray Download PDFInfo
- Publication number
- CN110359321A CN110359321A CN201910536999.4A CN201910536999A CN110359321A CN 110359321 A CN110359321 A CN 110359321A CN 201910536999 A CN201910536999 A CN 201910536999A CN 110359321 A CN110359321 A CN 110359321A
- Authority
- CN
- China
- Prior art keywords
- cellulose
- nano
- pva
- added
- fruit tray
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the methods that a kind of nano-cellulose/PVA mixed slurry prepares fruit tray, this method is to disperse microcrystalline cellulose in deionized water, and it is added 2,2,6,6- tetramethyl piperidine -1- oxygroups and NaBr carry out magnetic agitation again, a NaClO is added in per half an hour, the microcrystalline cellulose aoxidized, by centrifuge washing microcrystalline cellulose, nano-cellulose of dialysing to obtain;PVA is added to heating water bath in dimethyl sulfoxide and the mixed solvent system of deionized water and obtains PVA solution;It is added in slurry after nanofiber is mixed with PVA solution, then is made through vacuum filtration, thermocompression forming, transfer trimming.Using the present invention, microcrystalline cellulose is made to mix to be then added in slurry with PVA material after nano-cellulose and prepares fruit tray, has better water-resistance and physical strength, simultaneously, the fruit tray degradation material and safe and harmless of slurry preparation, it is environmentally protective.
Description
Technical field
The present invention relates to the methods that a kind of nano-cellulose/PVA mixed slurry prepares fruit tray.
Background technique
More and more important for the theory of our times green and environmental protection, people increasingly pay attention to for green safe, respectively
All advance in the theory for thinking environmentally protective sustainable development in a field.Fruit tray currently on the market is using plastics material mostly
Expect, not only non-degradable, but also is runed counter to sustainable development idea.Therefore, it now invented a kind of fiber fruit tray, but make
Standby fiber fruit tray is all lacking in water-resistance and physical strength, this utilizes nano-cellulose PVA material and slurry
Mixing prepare fruit tray again and can be enhanced be fruit tray water-resistance and physical strength performance.Nano-cellulose PVA mixing
Slurry prepare fruit tray preparation will bring great convenience to people's lives, while will also bring significant economic benefit and
Social benefit.
Summary of the invention
The purpose of the present invention is to the deficiencies of existing fiber fruit tray product, and water-resistance and physics can be enhanced by providing
The method that a kind of nano-cellulose/PVA mixed slurry of strength character prepares fruit tray.
The technical solution adopted by the present invention is that: a kind of method that nano-cellulose/PVA mixed slurry prepares fruit tray,
It is characterized in that it includes the following steps:
(1) in deionized water by microcrystalline cellulose dispersion, and 2 are added thereto, 2,6,6- tetramethyl piperidine -1- oxygroups and
NaBr;
(2) said mixture is subjected to magnetic agitation, while per half an hour is added a NaClO and is added several into mixture
Microcrystalline cellulose that is secondary, being aoxidized;
(3) microcrystalline cellulose for being aoxidized the water washing of deoxidation by centrifugation, dialysis, then obtains nano-cellulose;
(4) 4g~5gPVA is added in dimethyl sulfoxide and the mixed solvent system of deionized water, and carries out heating water bath and obtains
It is spare to PVA solution;
(5) nanofiber that step (3) obtains is added in the PVA solution that step (4) obtains and is further mixed, obtained
Mixed liquor is added in slurry, obtains mixed slurry;
(6) mixed slurry is sent to molding machine, molding fruit tray product is made through vacuum filtration, thermocompression forming, transfer trimming.
The method that a kind of nano-cellulose/PVA mixed slurry prepares fruit tray, it is characterised in that step (1)
Are as follows: by concentration be 1.5%~2% microcrystalline cellulose be dispersed in 450ml ~ 550ml deionized water, and thereto be added 90~
2,2,6,6- tetramethyl piperidine -1- the oxygroup and 100~200ml concentration of 110mg is 1~2%NaBr.
The method that a kind of nano-cellulose/PVA mixed slurry prepares fruit tray, it is characterised in that step (2)
Are as follows: mixture obtained by step (1) is subjected to magnetic agitation under 600~700rpm speed, while per half an hour into mixture
The NaClO that 10~12ml concentration is 10~15% is added, maintaining PH is 11~12, and reacting after 3~4h terminates.
The method that a kind of nano-cellulose/PVA mixed slurry prepares fruit tray, it is characterised in that step (3)
Washing times are preferably 3~5 times, and dialysis time is preferably 60~80h.
The method that a kind of nano-cellulose/PVA mixed slurry prepares fruit tray, it is characterised in that step (4)
The mixed solvent system of dimethyl sulfoxide (DMSO) and deionized water, the wherein liquor ratio of dimethyl sulfoxide and deionized water
It is preferably 2 ︰ 1, the PVA concentration in mixture is preferably 8~12%.
The method that a kind of nano-cellulose/PVA mixed slurry prepares fruit tray, it is characterised in that step (4)
Bath temperature be preferably 80~100 DEG C, heating time is preferably 2~4h.
The method that a kind of nano-cellulose/PVA mixed slurry prepares fruit tray, it is characterised in that step (5)
The solid-to-liquid ratio of middle mixed liquor and over dry slurry is 1 ︰ 1000.
Using the present invention, microcrystalline cellulose is made after nano-cellulose and is mixed to get mixed liquor with PVA material, is added
Fruit tray is prepared into slurry, has better water-resistance and physical strength, meanwhile, the fruit tray of slurry preparation can drop
Material and safe and harmless is solved, it is environmentally protective.
Specific embodiment
The present invention will be further described below in conjunction with the embodiments, but the scope of protection of present invention is not limited to reality
Apply the range of example expression.
Embodiment, the method that the nano-cellulose/PVA mixed slurry prepares fruit tray include the following steps.
1, the microcrystalline cellulose that concentration is 1.5%~2% is dispersed in 450ml ~ 550ml deionized water, and thereto
2,2,6,6- tetramethyl piperidine -1- the oxygroup (TEMPO) and 100~200ml concentration that 90~110mg is added are 1~2%NaBr.
2, mixture obtained by step (1) is subjected to magnetic agitation under 600~700rpm speed, while every into mixture
The NaClO that 10~12ml concentration is 10~15% is added in half an hour, and maintaining PH is 11~12, and reacting after 3~4h terminates.
3, it by being centrifuged the microcrystalline cellulose for aoxidizing the water washing of deoxidation, dialyses 3~5 times, dialysis time is 60~
Then 80h obtains nano-cellulose.
4,4g~5gPVA is added in dimethyl sulfoxide and the mixed solvent system of deionized water, and carries out water-bath and adds
Heat obtains that PVA solution is spare, and wherein the liquor ratio of dimethyl sulfoxide and deionized water is 2 ︰ 1, the PVA concentration in mixture
Preferably 8~12%, bath temperature is 80~100 DEG C, and heating time is preferably 2~4h.
5, it will be mixed in PVA solution that obtained nanofiber is added and further, obtained mixed liquor is added to
In slurry, mixed slurry is obtained;The solid-to-liquid ratio of mixed liquor and over dry slurry is 1 ︰ 1000.
6, mixed slurry is pumped to molding machine with pipeline, molding is made through vacuum filtration, thermocompression forming, transfer trimming
Fruit tray product.
Claims (7)
1. the method that a kind of nano-cellulose/PVA mixed slurry prepares fruit tray, it is characterised in that it includes the following steps:
(1) in deionized water by microcrystalline cellulose dispersion, and 2 are added thereto, 2,6,6- tetramethyl piperidine -1- oxygroups and
NaBr;
(2) said mixture is subjected to magnetic agitation, while per half an hour is added a NaClO and is added several into mixture
Microcrystalline cellulose that is secondary, being aoxidized;
(3) microcrystalline cellulose for being aoxidized the water washing of deoxidation by centrifugation, dialysis, then obtains nano-cellulose;
(4) 4g~5gPVA is added in dimethyl sulfoxide and the mixed solvent system of deionized water, and carries out heating water bath and obtains
It is spare to PVA solution;
(5) nanofiber that step (3) obtains is added in the PVA solution that step (4) obtains and is further mixed, obtained
Mixed liquor is added in slurry, obtains mixed slurry;
(6) mixed slurry is sent to molding machine, molding fruit tray product is made through vacuum filtration, thermocompression forming, transfer trimming.
2. the method that a kind of nano-cellulose/PVA mixed slurry according to claim 1 prepares fruit tray, feature
It is step (1) are as follows: the microcrystalline cellulose that concentration is 1.5%~2% is dispersed in 450ml ~ 550ml deionized water, and to
2,2,6,6- tetramethyl piperidine -1- the oxygroup and 100~200ml concentration that 90~110mg is wherein added are 1~2%NaBr.
3. the method that a kind of nano-cellulose/PVA mixed slurry according to claim 1 prepares fruit tray, feature
It is step (2) are as follows: mixture obtained by step (1) is subjected to magnetic agitation under 600~700rpm speed, while to mixture
In per half an hour the NaClO that 10~12ml concentration is 10~15% is added, maintaining PH is 11~12, reacts knot after 3~4h
Beam.
4. the method that a kind of nano-cellulose/PVA mixed slurry according to claim 1 prepares fruit tray, feature
It is that step (3) washing times are preferably 3~5 times, dialysis time is preferably 60~80h.
5. the method that a kind of nano-cellulose/PVA mixed slurry according to claim 1 prepares fruit tray, feature
Be the mixed solvent system of dimethyl sulfoxide (DMSO) and deionized water described in step (4), wherein dimethyl sulfoxide with go
The liquor ratio of ionized water is 2 ︰ 1, and the PVA concentration in mixture is preferably 8~12%.
6. the method that a kind of nano-cellulose/PVA mixed slurry according to claim 1 prepares fruit tray, feature
The bath temperature for being step (4) is preferably 80~100 DEG C, and heating time is preferably 2~4h.
7. the method that a kind of nano-cellulose/PVA mixed slurry according to claim 1 prepares fruit tray, feature
It is that the solid-to-liquid ratio of mixed liquor and over dry slurry is 1 ︰ 1000 in step (5).