CN110357574A - A kind of magnetic therapy stone material and preparation method thereof - Google Patents
A kind of magnetic therapy stone material and preparation method thereof Download PDFInfo
- Publication number
- CN110357574A CN110357574A CN201910630848.5A CN201910630848A CN110357574A CN 110357574 A CN110357574 A CN 110357574A CN 201910630848 A CN201910630848 A CN 201910630848A CN 110357574 A CN110357574 A CN 110357574A
- Authority
- CN
- China
- Prior art keywords
- parts
- stone
- magnetite
- powder
- tourmaline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of magnetic therapy stone material, the raw material including following parts by weight: 10-20 parts of stone needle, 5-15 parts of magnetite, 10-14 parts of Tourmaline tourmaline, black cholelith 3-6 parts, 2-4 parts of limonite, 5-15 parts of medical stone, 10-15 parts of germanite, 15-25 parts of rare earth, 10-20 parts of modified clay, 10-15 parts of far-infared ceramic powder, 2-10 parts of bamboo charcoal fiber powder, 1-5 parts of adhesive；A kind of preparation method of magnetic therapy stone material, (1) calcines above-mentioned ore and clay；It is put into pulverizer and is crushed after cooling；Feed powder after sieving is added in blender and is sufficiently mixed；Adhesive is added into mixed-powder, blank is made；Blank is suppressed in the mold in molding machine；Pressed proembryo is subjected to high-temperature calcination, 1000 DEG C or more of high temperature is fired；After taking out cooling down, it is processed by shot blasting by polishing machine.It rectifies a deviation to human body magnetic field itself, by enhancing human-body biological electromagnetic energy, pushes QI-blood circulation, have the function that degrading the channel, relaxing tendons and activating collaterals.
Description
Technical field
The present invention relates to magnetic therapy technical field, in particular to a kind of magnetic therapy stone material and preparation method thereof.
Background technique
Magnetic therapy is the method for being applied to collaterals of human, acupuncture point and diseased region using artificial field and treating certain diseases.Doctor
Institute's profession device for magnetotherapy is to hypertension, arthritis, headache, insomnia, coronary heart disease, gastroenteritis, facial spasm and bruise, neck
Vertebra disease etc. is effective.Only to some diseases directly to treat, some diseases are adjuvant treatment.Existing magnetotherapy stone is mostly ore
It directly uses, has a single function after polishing, it is inconvenient for use.
Summary of the invention
It is right the present invention provides a kind of magnetic therapy stone material and preparation method thereof for above-mentioned deficiency in the prior art
Human body magnetic field itself is rectified a deviation, and by enhancing human-body biological electromagnetic energy, is pushed QI-blood circulation, is reached degrading the channel, relaxing tendons and activating collaterals
Effect.
In order to achieve the above object of the invention, the technical solution adopted by the present invention are as follows:
A kind of magnetic therapy stone material, the raw material including following parts by weight: 10-20 parts of stone needle, 5-15 parts of magnetite, Tourmaline is electrical
It is 10-14 parts of stone, black cholelith 3-6 parts, 2-4 parts of limonite, 5-15 parts of medical stone, 10-15 parts of germanite, 15-25 parts of rare earth, modified glutinous
It is 10-20 parts native, 10-15 parts of far-infared ceramic powder, 2-10 parts of bamboo charcoal fiber powder, 1-5 parts of adhesive；The stone needle is Si Bin stone acupuncture needle
Stone；The magnetite is iron boron magnetite；Described adhesive is polyvinyl alcohol or carboxymethyl cellulose.
Further, a kind of magnetic therapy stone material, the raw material including following parts by weight: 15 parts of stone needle, 10 parts of magnetite, Tourmaline electricity
12 parts of gas stone, 4 parts of black cholelith, 3 parts of limonite, 10 parts of medical stone, 12 parts of germanite, 20 parts of rare earth, 15 parts of modified clay, far infrared
12 parts of ceramic powder, 6 parts of bamboo charcoal fiber powder, 4 parts of adhesive；The stone needle is nasal mucus shore stone needle；The magnetite is iron boron magnetite；It is described
Adhesive is polyvinyl alcohol or carboxymethyl cellulose.
Further, a kind of preparation method of magnetic therapy stone material,
(1) above-mentioned stone needle, magnetite, Tourmaline tourmaline, black cholelith, limonite, medical stone, germanite, rare earth, modification is glutinous
Soil calcines 3-5h at 840-880 DEG C；
(2) it is put into pulverizer and is crushed after being cooled to room temperature, cross 200-400 mesh screen；
(3) feed powder after sieving is added in blender and is sufficiently mixed, far-infared ceramic powder, bamboo charcoal fiber powder is added, stirs
Mix 10-15min；
(4) adhesive is added into mixed-powder, blank is made；
(5) it is suppressed in the mold by blank in molding machine；
(6) pressed proembryo is subjected to high-temperature calcination, 1000 DEG C or more of high temperature is fired；
(7) it after taking out cooling down, is processed by shot blasting by polishing machine.
The invention has the benefit that firing again after plurality of raw materials mixing, structure is more stable, various shapes user
Just, vdiverse in function, magnetic therapy effect is more preferable；Stone needle reaches some treatments and health care effect by crystallite, infrared and pulse wave band
Fruit；Containing abundant rare mineral matter in black cholelith, and naturally contain magnetic；Far-infared ceramic powder can release after absorbing extraneous thermal energy
The far infrared that wavelength is 4-14 microns, is easily absorbed by the body；Germanite contains various trace elements, the starting wave and human body distributed
Inner cell carries out resonance, promotes blood circulation, enhancing metabolism；It rectifies a deviation to human body magnetic field itself, passes through enhancing
Human-body biological electromagnetic energy pushes QI-blood circulation, has the function that degrading the channel, relaxing tendons and activating collaterals.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below technical solution in the embodiment of the present invention into
Row clearly and completely describes.
Embodiment one: a kind of magnetic therapy stone material includes the raw material of following parts by weight: 10 magnetite 5 of stone needle, Tourmaline tourmaline 10
Part, 3 parts of black cholelith, 2 parts of limonite, 5 parts of medical stone, 10 parts of germanite, 15 parts of rare earth, 10 parts of modified clay, far-infared ceramic powder
10 parts, 2 parts of bamboo charcoal fiber powder, 1 part of adhesive；The stone needle is nasal mucus shore stone needle；The magnetite is iron boron magnetite；Described adhesive
For polyvinyl alcohol or carboxymethyl cellulose.
A kind of preparation method of magnetic therapy stone material,
(1) above-mentioned stone needle, magnetite, Tourmaline tourmaline, black cholelith, limonite, medical stone, germanite, rare earth, modification is glutinous
Soil calcines 3h at 840 DEG C；
(2) it is put into pulverizer and is crushed after being cooled to room temperature, cross 200 mesh screens；
(3) feed powder after sieving is added in blender and is sufficiently mixed, far-infared ceramic powder, bamboo charcoal fiber powder is added, stirs
Mix 10min；
(4) adhesive is added into mixed-powder, blank is made；
(5) it is suppressed in the mold by blank in molding machine；
(6) pressed proembryo is subjected to high-temperature calcination, 1000 DEG C or more of high temperature is fired；
(7) it after taking out cooling down, is processed by shot blasting by polishing machine.
Embodiment two: a kind of magnetic therapy stone material, the raw material including following parts by weight: 15 parts of stone needle, 10 parts of magnetite, Tourmaline
12 parts of tourmaline, 4 parts of black cholelith is 3 parts of limonite, 10 parts of medical stone, 12 parts of germanite, 20 parts of rare earth, 15 parts of modified clay, remote red
12 parts of outer ceramic powder, 6 parts of bamboo charcoal fiber powder, 4 parts of adhesive；The stone needle is nasal mucus shore stone needle；The magnetite is iron boron magnetite；Institute
Stating adhesive is polyvinyl alcohol or carboxymethyl cellulose.
A kind of preparation method of magnetic therapy stone material,
(1) above-mentioned stone needle, magnetite, Tourmaline tourmaline, black cholelith, limonite, medical stone, germanite, rare earth, modification is glutinous
Soil burns 4h 860；
(2) it is put into pulverizer and is crushed after being cooled to room temperature, cross 300 mesh screens；
(3) feed powder after sieving is added in blender and is sufficiently mixed, far-infared ceramic powder, bamboo charcoal fiber powder is added, stirs
Mix 12min；
(4) adhesive is added into mixed-powder, blank is made；
(5) it is suppressed in the mold by blank in molding machine；
(6) pressed proembryo is subjected to high-temperature calcination, 1000 DEG C or more of high temperature is fired；
(7) it after taking out cooling down, is processed by shot blasting by polishing machine.
Embodiment three: a kind of magnetic therapy stone material, include the raw material of following parts by weight: 20 parts of stone needle, 15 parts of magnetite, Tourmaline is electric
14 parts of gas stone, 6 parts of black cholelith, 4 parts of limonite, 15 parts of medical stone, 15 parts of germanite, 25 parts of rare earth, 20 parts of modified clay, far infrared
10-15 parts of ceramic powder, 10 parts of bamboo charcoal fiber powder, 5 parts of adhesive；The stone needle is nasal mucus shore stone needle；The magnetite is iron boron magnetic
Stone；Described adhesive is polyvinyl alcohol or carboxymethyl cellulose.
A kind of preparation method of magnetic therapy stone material,
(1) above-mentioned stone needle, magnetite, Tourmaline tourmaline, black cholelith, limonite, medical stone, germanite, rare earth, modification is glutinous
Soil calcines 5h at 880 DEG C；
(2) it is put into pulverizer and is crushed after being cooled to room temperature, cross 400 mesh screens；
(3) feed powder after sieving is added in blender and is sufficiently mixed, far-infared ceramic powder, bamboo charcoal fiber powder is added, stirs
Mix 15min；
(4) adhesive is added into mixed-powder, blank is made；
(5) it is suppressed in the mold by blank in molding machine；
(6) pressed proembryo is subjected to high-temperature calcination, 1000 DEG C or more of high temperature is fired；
(7) it after taking out cooling down, is processed by shot blasting by polishing machine.
The above description is only a preferred embodiment of the patent of the present invention, is not intended to limit the invention patent, all at this
Made any modifications, equivalent replacements, and improvements etc., should be included in the invention patent within the spirit and principle of patent of invention
Protection scope within.
Claims (3)
1. a kind of magnetic therapy stone material, which is characterized in that the raw material including following parts by weight: 10-20 parts of stone needle, 5-15 parts of magnetite,
10-14 parts of Tourmaline tourmaline, black cholelith 3-6 parts, 2-4 parts of limonite, 5-15 parts of medical stone, 10-15 parts of germanite, rare earth 15-
25 parts, 10-20 parts of modified clay, 10-15 parts of far-infared ceramic powder, 2-10 parts of bamboo charcoal fiber powder, 1-5 parts of adhesive；
The stone needle is nasal mucus shore stone needle；
The magnetite is iron boron magnetite；
Described adhesive is polyvinyl alcohol or carboxymethyl cellulose.
2. a kind of magnetic therapy stone material according to claim 1, which is characterized in that the raw material including following parts by weight: stone needle
15 parts, 10 parts of magnetite, 12 parts of Tourmaline tourmaline, 4 parts of black cholelith, 3 parts of limonite, 10 parts of medical stone, 12 parts of germanite, rare earth 20
Part, 15 parts of modified clay, 12 parts of far-infared ceramic powder, 6 parts of bamboo charcoal fiber powder, 4 parts of adhesive；
The stone needle is nasal mucus shore stone needle；
The magnetite is iron boron magnetite；
Described adhesive is polyvinyl alcohol or carboxymethyl cellulose.
3. a kind of preparation method of magnetic therapy stone material according to claim 1,
(1) by above-mentioned stone needle, magnetite, Tourmaline tourmaline, black cholelith, limonite, medical stone, germanite, rare earth, modified clay,
3-5h is calcined at 840-880 DEG C；
(2) it is put into pulverizer and is crushed after being cooled to room temperature, cross 200-400 mesh screen；
(3) feed powder after sieving is added in blender and is sufficiently mixed, far-infared ceramic powder, bamboo charcoal fiber powder is added, stir 10-
15min；
(4) adhesive is added into mixed-powder, blank is made；
(5) it is suppressed in the mold by blank in molding machine；
(6) pressed proembryo is subjected to high-temperature calcination, 1000 DEG C or more of high temperature is fired；
(7) it after taking out cooling down, is processed by shot blasting by polishing machine.