CN110357048A - A kind of cubic boron nitride washes material method - Google Patents
A kind of cubic boron nitride washes material method Download PDFInfo
- Publication number
- CN110357048A CN110357048A CN201910595282.7A CN201910595282A CN110357048A CN 110357048 A CN110357048 A CN 110357048A CN 201910595282 A CN201910595282 A CN 201910595282A CN 110357048 A CN110357048 A CN 110357048A
- Authority
- CN
- China
- Prior art keywords
- washing machine
- water
- material washing
- boron nitride
- cubic boron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Material method is washed the present invention provides a kind of cubic boron nitride, belongs to purifying super-hard materials technical field.Specifically wash material method are as follows: the cubic boron nitride after shaping is put into material washing machine, hydrochloric acid is added, is stood;After standing, water is added in material washing machine, the acidity of solution in material washing machine is diluted, then liquid is poured out;Material washing machine is put into supersonic wave cleaning machine, the height of drinking-water pipe downlink in material washing machine is adjusted, starts material washing machine, is worked according to the order for adding water-forward direction stirring-reverse agitating function-is static-to draw water;After above-mentioned steps recycle at least 3 times, supersonic wave cleaning machine is opened, previous step is continued cycling through;When the pH of solution in material washing machine is neutrality, conductivity≤3 terminate cleaning;It is finally rinsed with pure water and completes to wash material.This method is that material method is washed in automation, can be improved labor efficiency, reduces labor intensity, be conducive to industrialized production.
Description
Technical field
The invention belongs to purifying super-hard materials technical field, in particular to a kind of cubic boron nitride washes material method.
Background technique
Cubic boron nitride (cBN) is lazy with the high rigidity for being only second to diamond and better than the thermal stability of diamond and chemistry
Property, being used as superabrasive is made various grinding wheels and cutter, for the processing of ferrous material, has efficient, accurate, energy conservation
The advantages that with automation, is especially high-accuracy manufacture field in modern times processing and is widely used.
Up to the present, the cBN cleaning after shaping mainly manually rushes WATER-WASHING METHOD repeatedly, i.e., every 3 myriagram of basin charge is drawn, and adds
Water is stirred, precipitates, is poured out, repeatedly until the water after washing material reaches neutral.This method advantage is easy to operate, the disadvantage is that
Manpower is consumed very much, is once fed intake few, water consumption is big, and the used time is longer, is unfavorable for industrialized production.
Summary of the invention
In view of the above technical problems, material method is washed the purpose of the present invention is to provide a kind of cubic boron nitride.This method
Material method is washed for automation, can be improved labor efficiency, labor intensity is reduced, is conducive to industrialized production.
To achieve the above object, the technical solution adopted by the present invention are as follows:
A kind of cubic boron nitride washes material method, comprising the following steps:
(1) cubic boron nitride after shaping is put into material washing machine, and the hydrochloric acid that mass concentration is 37% is added, and after mixing evenly, is stood
1h;
(2) after standing, water is added in material washing machine, the acidity of solution in material washing machine is diluted, then liquid is poured out;
(3) material washing machine is put into supersonic wave cleaning machine, adjusts the height of drinking-water pipe downlink in material washing machine, started material washing machine, press
According to the order work for adding water-forward direction stirring-reverse agitating function-is static-to draw water;
(4) after step (3) recycles at least 3 times, supersonic wave cleaning machine is opened, step (3) are continued cycling through;
(5) pH and conductivity of solution in material washing machine are tested, pH is neutrality, and conductivity≤3 terminate cleaning;
(6) cubic boron nitride in material washing machine is taken out, is placed in dryer, first rinsed with room temperature pure water, after drying again with 60 ~
100 DEG C of pure water rinses.
As currently preferred, height of the end of drinking-water pipe apart from charge level is not less than 5mm in the step (3), takes out
CBN granularity≤500 mesh in water out.In the present invention, the height of drinking-water pipe downlink is height of the end apart from charge level of drinking-water pipe
Degree, the distance of the high discharge feed side in the end of specially drinking-water pipe.
As currently preferred, constant process parameters in the step (3) are as follows: 200 ~ 220s of water time, forward direction is added to stir
Time 150s, reverse agitating function time 20s are mixed, time of pumping is not less than 100s;The technological parameter of variation: the end distance of drinking-water pipe
Height, quiescent time, the cycle-index of charge level.Technological parameter is changed to be set according to different cultivars, granularity, Ball-milling Time.
As currently preferred, the cubic boron nitride of at least 90,000 ct can be once cleaned in the material washing machine.
It is shinny that cBN of the invention washes the cBN single-crystal surface that material method obtains, and it is not in plate after drying that conductivity, which reduces,
Knot, phenomena such as tumor will not be played when being made into product, is bubbled, falls off.
Compared with prior art, the invention has the benefit that
1, it is of the invention wash that material method significantly improves cubic boron nitride wash material efficiency, this method can once be washed till few 9 myriagrams
Material is drawn, and tradition washes material method once and can only wash 3 myriagrams drawing material.
2, material method of washing of the invention washes material equipment using intelligence, can significantly reduce labor intensity.
3, the clean level for washing material method energy intuitive judgment material during washing material of the invention.
Specific embodiment
Below with reference to embodiment, the present invention is described in further detail.
Embodiment 1
In the present embodiment, cBN120 reprocessing material, Ball-milling Time 3h are taken, 325/400,12 myriagram of targeted particle size is drawn, and addition is washed
In material machine, the hydrochloric acid that the mass concentration of 6000ml is 37% is then added, stands 1h after mixing evenly.It is past to wash material after standing
It is slowly added to 70L water in machine, the acidity of solution in material washing machine is diluted, then liquid is poured out.Material washing machine is placed in ultrasonic wave
In cleaning machine, height of the end apart from charge level of drinking-water pipe in material washing machine is adjusted, in the present embodiment, the end height of drinking-water pipe discharges
Face 12mm starts material washing machine, works according to the order for adding water-forward direction stirring-reverse agitating function-is static-to draw water, adds the water time
200s, positive mixing time 150s, reverse agitating function time 20s, quiescent time 135s, time of pumping 100s.Start after circulation 5 times
Supersonic wave cleaning machine.After material washing machine recycles 15 times according to above-mentioned steps again, the pH value for testing water is 7.5, conductivity 2.8.
It takes out and material is poured into dryer, start dryer;When dryer water outlet is no longer discharged, about 15L room temperature pure water is first added,
Start dryer, when dryer water outlet is no longer discharged, then adds 60 DEG C of the pure water of about 15L, drying again.Examine knot
Fruit: material surface is shinny, and particulate is not glued in non-conglomeration.Conclusion: meet acceptance criteria.
Embodiment 2
In the present embodiment, cBN230 reprocessing material, Ball-milling Time 40min are taken, 60/70,21 myriagram of targeted particle size is drawn, and addition is washed
In material machine, the hydrochloric acid that the mass concentration of 10500ml is 37% is then added, stands 1h after mixing evenly.It is past to wash after standing
It is slowly added to 70L water in material machine, the acidity of solution in material washing machine is diluted, then liquid is poured out.Material washing machine is placed in ultrasound
In wave cleaning machine, height of the end apart from charge level of drinking-water pipe in material washing machine is adjusted, in the present embodiment, the end of drinking-water pipe is higher by
Charge level 5mm starts material washing machine, works according to the order for adding water-forward direction stirring-reverse agitating function-is static-to draw water, when adding water
Between 220s, positive mixing time 150s, reverse agitating function time 20s, quiescent time 80s, time of pumping 100s.It is opened after circulation 5 times
Dynamic supersonic wave cleaning machine.After material washing machine recycles 6 times according to above-mentioned steps again, the pH value for testing water is 7.1, conductivity 2.3.
It takes out and material is poured into dryer, start dryer;When dryer water outlet is no longer discharged, the room temperature that about 15L is first added is pure
Water starts dryer, when dryer water outlet is no longer discharged, then adds 80 DEG C of the pure water of about 15L to rinse again, drying.
Inspection result: material surface is shinny, and particulate is not glued in non-conglomeration.
Embodiment 3
In the present embodiment, cBN115 reprocessing material, Ball-milling Time 30min are taken, 100/120,18 myriagram of targeted particle size draws, is added
In material washing machine, the hydrochloric acid that the mass concentration of 9000ml is 37% is then added, stands 1h after mixing evenly.It is past to wash after standing
It is slowly added to 70L water in material machine, the acidity of solution in material washing machine is diluted, then liquid is poured out.Material washing machine is placed in ultrasound
In wave cleaning machine, height of the end apart from charge level of drinking-water pipe in material washing machine is adjusted, in the present embodiment, the end of drinking-water pipe is higher by
Charge level 8mm starts material washing machine, works according to the order for adding water-forward direction stirring-reverse agitating function-is static-to draw water, when adding water
Between 220s, positive mixing time 150s, reverse agitating function time 20s, quiescent time 100s, time of pumping 100s.It is opened after circulation 5 times
Dynamic supersonic wave cleaning machine.After material washing machine recycles 10 times according to above-mentioned steps again, the pH value for testing water is 7.3, and conductivity is
2.5.Material is taken out and pours into dryer, starts dryer;When dryer water outlet is no longer discharged, the room temperature of about 15L is first added
Pure water starts dryer, when dryer water outlet is no longer discharged, then adds 90 DEG C of the pure water of about 15L to rinse again, dries
It is dry.Inspection result: material surface is shinny, and particulate is not glued in non-conglomeration.Conclusion: meet acceptance criteria.
Embodiment 4
In the present embodiment, cBN210 reprocessing material, Ball-milling Time 1.5h are taken, 170/200,15 myriagram of targeted particle size draws, is added
In material washing machine, the hydrochloric acid that the mass concentration of 7500ml is 37% is then added, stands 1h after mixing evenly.It is past to wash after standing
It is slowly added to 70L water in material machine, the acidity of solution in material washing machine is diluted, then liquid is poured out.Material washing machine is placed in ultrasound
In wave cleaning machine, height of the end apart from charge level of drinking-water pipe in material washing machine is adjusted, in the present embodiment, the end of drinking-water pipe is higher by
Charge level 10mm starts material washing machine, works according to the order for adding water-forward direction stirring-reverse agitating function-is static-to draw water, when adding water
Between 210s, positive mixing time 150s, reverse agitating function time 20s, quiescent time 120s, time of pumping 100s.Start ultrasonic wave
Cleaning machine.After material washing machine recycles 12 times according to above-mentioned steps again, the pH value for testing water is 7.5, conductivity 2.8.Material is taken
Dryer is poured into out, starts dryer;When dryer water outlet is no longer discharged, about 15L room temperature pure water is first added, starting is got rid of
Then dry machine adds 100 DEG C of the pure water of about 15L to rinse, drying again when dryer water outlet is no longer discharged.Inspection result:
Expect that surface is shinny, particulate is not glued in non-conglomeration.Conclusion: meet acceptance criteria.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
1. a kind of cubic boron nitride washes material method, which comprises the following steps:
(1) cubic boron nitride after shaping is put into material washing machine, and the hydrochloric acid that mass concentration is 37% is added, and after mixing evenly, is stood
1h;
(2) after standing, water is added in material washing machine, the acidity of solution in material washing machine is diluted, then liquid is poured out;
(3) material washing machine is put into supersonic wave cleaning machine, adjusts the height of drinking-water pipe downlink in material washing machine, started material washing machine, press
According to the order work for adding water-forward direction stirring-reverse agitating function-is static-to draw water;
(4) after step (3) recycles at least 3 times, supersonic wave cleaning machine is opened, step (3) are continued cycling through;
(5) pH and conductivity of solution in material washing machine are tested, pH is neutrality, and conductivity≤3 terminate cleaning;
(6) cubic boron nitride in material washing machine is taken out, is placed in dryer, first rinsed with room temperature pure water, after drying again with 60 ~
100 DEG C of pure water rinses.
2. cubic boron nitride according to claim 1 washes material method, which is characterized in that drinking-water pipe in the step (3)
Height of the end apart from charge level be not less than 5mm.
3. cubic boron nitride according to claim 1 washes material method, which is characterized in that in the step (3) plus when water
Between 200 ~ 220s, positive mixing time 150s, reverse agitating function time 20s, time of pumping is not less than 100s.