CN110339537A - A kind of swimming cap production technology - Google Patents

A kind of swimming cap production technology Download PDF

Info

Publication number
CN110339537A
CN110339537A CN201910444101.0A CN201910444101A CN110339537A CN 110339537 A CN110339537 A CN 110339537A CN 201910444101 A CN201910444101 A CN 201910444101A CN 110339537 A CN110339537 A CN 110339537A
Authority
CN
China
Prior art keywords
antioxidant
swimming cap
raw material
adhesive tape
sulphur
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910444101.0A
Other languages
Chinese (zh)
Inventor
任兆军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHUZHOU JUNYUE HIGH POLYMER NEW MATERIAL Co Ltd
Original Assignee
CHUZHOU JUNYUE HIGH POLYMER NEW MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHUZHOU JUNYUE HIGH POLYMER NEW MATERIAL Co Ltd filed Critical CHUZHOU JUNYUE HIGH POLYMER NEW MATERIAL Co Ltd
Priority to CN201910444101.0A priority Critical patent/CN110339537A/en
Publication of CN110339537A publication Critical patent/CN110339537A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of swimming cap production technologies, the swimming cap raw materials for production include sizing material raw material and adhesive tape raw material, the sizing material raw material includes TPC, zinc oxide, stearic acid, paraffin, antioxidant SP, antioxidant 2246, titanium dioxide, white carbon black, activated Calcium carbonate, white factice, sulphur, Vulcanization accelerator TMTD, captax, diphenylguanidine 0, vaseline, the raw material of the adhesive tape includes TPC, zinc oxide, stearic acid, altax, diphenylguanidine, promotor PX, antioxidant 2246, antioxidant MB, anti-aging agent KB, antiscorching agent, ingot is blue, titanium dioxide, plasticizer, white factice, foaming agent, sulphur, aromatic naphtha, the swimming cap great variety of models that the present invention is processed by dry gum method technique, appearance is bright-coloured, cap body is sturdy, moulding is generous, elasticity is good, air-tightness is good, it is unlikely to deform, effectively Extend physical life.

Description

A kind of swimming cap production technology
Technical field
The present invention relates to swimming cap manufacture field more particularly to a kind of swimming cap production technologies.
Background technique
Currently, domestic market mostly uses natural emulsion infusion process to produce swimming cap, the swimming cap feature that method produces in this is arm It is thin, body is light, bright in luster, but the swimming cap style that this kind of mode is processed is few, and cap body is too thin, explains that Chengdu is general, and appearance Generally, therefore, it is proposed that a kind of swimming cap production technology.
Summary of the invention
The purpose of the present invention is to provide a kind of swimming cap production technologies, solve the problems, such as proposed in background technique.
To achieve the above object, the invention provides the following technical scheme: a kind of swimming cap production technology, the swimming cap production are former Material includes sizing material raw material and adhesive tape raw material, and the sizing material raw material includes TPC, zinc oxide, stearic acid, paraffin, antioxidant SP, prevents Old agent 2246, titanium dioxide, white carbon black, activated Calcium carbonate, white factice, sulphur, Vulcanization accelerator TMTD, captax, diphenylguanidine 0, Vaseline, the raw material of the adhesive tape include TPC, zinc oxide, stearic acid, altax, diphenylguanidine, promotor PX, anti-aging agent 2246, antioxidant MB, anti-aging agent KB, antiscorching agent, ingot orchid, titanium dioxide, plasticizer, white factice, foaming agent, sulphur, aromatic naphtha, institute It is as follows to state swimming cap procedure of processing:
S1, sizing material and adhesive tape are prepared；
S2, pattern printing, bushing is put on film, takes a small amount of mill base to drop down by bushing with scraper plate and forms pattern on film, Blanking is cut after mill base dries；
Packed film is enclosed on cylindric head mould, and glues interface by S3, molding, circular top cover is then pasted, finally by cap Crimping at mouthful；
S4, vulcanization, it is interior after cap demoulding to be set off with hardboard, it lies against and is vulcanized on vulcanized vehicle into vulcanizing tank；
S5, adhesive tape, demoulding checks when the product vulcanizated is cooled to 50 DEG C or less, by the product inversion boot after passed examination Adhesive glue item is carried out on ceramic former.
As a kind of preferred embodiment of the invention, it is described prepare sizing material method be will quantitatively TPC in open refining Plasticate 5-10min on glue machine, then it is static for 24 hours, then by zinc oxide, stearic acid, paraffin, antioxidant SP, antioxidant 2246, titanium It white powder, white carbon black, activated Calcium carbonate, white factice, sulphur, Vulcanization accelerator TMTD, captax, diphenylguanidine, vaseline and plasticates Material be kneaded to obtain sizing material.
As a kind of preferred embodiment of the invention, the preparation method of the adhesive tape be will TPC quantitatively, zinc oxide, Stearic acid, altax, diphenylguanidine, promotor PX, antioxidant 2246, antioxidant MB, anti-aging agent KB, antiscorching agent, ingot orchid, titanium White powder, plasticizer, white factice, foaming agent, sulphur, aromatic naphtha are kneaded on rubber mixing machine, then using vulcanizing press into Row vulcanization, vulcanizes sandwich rubber into strips, vulcanization time 5min.
As a kind of preferred embodiment of the invention, curing temperature is 135 DEG C in the S4, vulcanization time 20min.
As a kind of preferred embodiment of the invention, the vulcanizing tank is for the vulcanizing tank of porcelain head dummy formula or with pellet type One of vulcanizing tank.
Compared with prior art, beneficial effects of the present invention are as follows:
1. swimming cap production technology of the invention, the swimming cap great variety of models processed by dry gum method technique, appearance is bright-coloured, cap body is endured In fact, moulding is generous, and elasticity is good, air-tightness is good, is unlikely to deform, effectively extends physical life.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below with reference to Specific embodiment, the present invention is further explained.
Embodiment one
90 parts of TPC are plasticated 5-10min on opening rubber mixing machine, then it is static for 24 hours, then by 415 parts of zinc oxide, 115 parts Stearic acid, 0.19 part of paraffin, 1 part of antioxidant SP, 1 part of antioxidant 2246,15 parts of titanium dioxides, 8 parts of white carbon blacks, 20 parts of active carbonic acids Calcium, 4 parts of white factices, 0.15 part of sulphur, 118 parts of Vulcanization accelerator TMTDs, 0.18 part of captax, 0.17 part of diphenylguanidine, 3 parts of vaseline It is kneaded to obtain sizing material with the material plasticated, then by 100 parts of TPC, 5 parts of zinc oxide, 215 parts of stearic acid, 2 parts of promotions Agent DM, 0.14 part of diphenylguanidine, 0.15 part of promotor PX, 1 part of antioxidant 2246,115 parts of antioxidant MBs, 115 parts of anti-aging agent KB, 0.14 part of antiscorching agent, 0.12 part of ingot orchid, 0.12 part of titanium dioxide, 215 plasticizer, 50 parts of white factices, 6 parts of foaming agents, 3 parts of sulphur, 10 parts of aromatic naphtha are kneaded on rubber mixing machine, are then vulcanized using vulcanizing press, vulcanize sandwich rubber into strips, sulphur The change time is 5min, and bushing is put on film, takes a small amount of mill base to drop down by bushing with scraper plate and formed on film by pattern printing Pattern cuts blanking after mill base dries, and packed film is enclosed on cylindric head mould, and glue interface, then pastes circle Shape top cover, it is interior after cap demoulding to be set off with hardboard finally by crimping at cap mouth, it lies against and enters vulcanizing tank on vulcanized vehicle Vulcanized, curing temperature is 135 DEG C, vulcanization time 20min, and demoulding is examined when the product vulcanizated is cooled to 50 DEG C or less It looks into, the product inversion boot after passed examination is subjected to adhesive glue item on ceramic former.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto, Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.

Claims (5)

1. a kind of swimming cap production technology, it is characterised in that: the swimming cap raw materials for production include sizing material raw material and adhesive tape raw material, described Sizing material raw material includes TPC, zinc oxide, stearic acid, paraffin, antioxidant SP, antioxidant 2246, titanium dioxide, white carbon black, active carbonic acid Calcium, white factice, sulphur, Vulcanization accelerator TMTD, captax, diphenylguanidine, vaseline, the raw material of the adhesive tape include TPC, oxidation Zinc, stearic acid, altax, diphenylguanidine, promotor PX, antioxidant 2246, antioxidant MB, anti-aging agent KB, antiscorching agent, ingot be blue, Titanium dioxide, plasticizer, white factice, foaming agent, sulphur, aromatic naphtha, the swimming cap procedure of processing are as follows:
S1, sizing material and adhesive tape are prepared；
S2, pattern printing, bushing is put on film, takes a small amount of mill base to drop down by bushing with scraper plate and forms pattern on film, Blanking is cut after mill base dries；
Packed film is enclosed on cylindric head mould, and glues interface by S3, molding, circular top cover is then pasted, finally by cap Crimping at mouthful；
S4, vulcanization, it is interior after cap demoulding to be set off with hardboard, it lies against and is vulcanized on vulcanized vehicle into vulcanizing tank；
S5, adhesive tape, demoulding checks when the product vulcanizated is cooled to 50 DEG C or less, by the product inversion boot after passed examination Adhesive glue item is carried out on ceramic former.
2. a kind of swimming cap production technology according to claim 1, it is characterised in that: the sizing material method for preparing is that will quantify TPC plasticate on opening rubber mixing machine 5-10min, then it is static for 24 hours, then by zinc oxide, stearic acid, paraffin, anti-aging agent SP, antioxidant 2246, titanium dioxide, white carbon black, activated Calcium carbonate, white factice, sulphur, Vulcanization accelerator TMTD, captax, promotor D, vaseline and the material plasticated are kneaded to obtain sizing material.
3. a kind of swimming cap production technology according to claim 1, it is characterised in that: the preparation method of the adhesive tape is that will determine The TPC of amount, zinc oxide, stearic acid, altax, diphenylguanidine, promotor PX, antioxidant 2246, antioxidant MB, anti-aging agent KB, Antiscorching agent, ingot orchid, titanium dioxide, plasticizer, white factice, foaming agent, sulphur, aromatic naphtha are kneaded on rubber mixing machine, are then adopted Vulcanized with vulcanizing press, vulcanizes sandwich rubber into strips, vulcanization time 5min.
4. a kind of swimming cap production technology according to claim 1, it is characterised in that: curing temperature is 135 DEG C in the S4, Vulcanization time 20min.
5. a kind of swimming cap production technology according to claim 1, it is characterised in that: the vulcanizing tank is porcelain head dummy formula One of vulcanizing tank or the vulcanizing tank with pellet type.
CN201910444101.0A 2019-05-27 2019-05-27 A kind of swimming cap production technology Pending CN110339537A (en)