CN110295497A - A kind of aging-resistant flame-proof type canvas maceration extract - Google Patents
A kind of aging-resistant flame-proof type canvas maceration extract Download PDFInfo
- Publication number
- CN110295497A CN110295497A CN201910456243.9A CN201910456243A CN110295497A CN 110295497 A CN110295497 A CN 110295497A CN 201910456243 A CN201910456243 A CN 201910456243A CN 110295497 A CN110295497 A CN 110295497A
- Authority
- CN
- China
- Prior art keywords
- liquid
- parts
- maceration extract
- canvas
- aging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aging-resistant flame-proof type canvas maceration extract, including A liquid and B liquid, the wherein raw material in A liquid are as follows: water-based acrylic resin lotion, ptfe emulsion, dilute hydrochloric acid, montmorillonite, fire retardant and deionized water;Raw material in B liquid are as follows: silane coupling agent, age resister nano-titanium dioxide, epoxy curing agent, filler, butadiene-vinylpyridine copylymer latex, aqueous slkali and deionized water;When work, first openpore canvas is immersed in A liquid, after drying, then is immersed in B liquid, then drying and processing.The present invention is poor for canvas maceration extract flame retardant effect in the prior art, the technical problems such as roller surface formation convex block influence production are easily adhered to improve, by the way that age resister and suitable flame-retardant formulations are added into maceration extract, the surface that maceration extract is coated in canvas has preferable fire retardant performance, maceration extract is not easy to be adhered to the surface of roll during canvas is processed simultaneously, reduce the artificial worry except material, improves production efficiency.
Description
Technical field
The present invention relates to cloth maceration extract field more particularly to a kind of aging-resistant flame-proof type canvas maceration extracts.
Background technique
Existing Zhi Bu manufacturer is in order to improve the service performance of canvas, it will usually come to canvas in such a way that more baths are impregnated
It is surface modified, usually the surface of canvas can be first chemically treated, then the leaching by it by having fire proofing again
It is surface-treated in stain liquid, is then dried again, batched.And phosphorus flame retardant has nothing as a kind of halogen-free flame retardants
The advantages that poison, good flame retardation effect, it is used in the fields such as house cloth, fireproof facing material already.There is canvas more preferably to hinder
Fuel efficiency fruit, and the bond properties between rubber is more preferable, it has also become textile technology field urgent need to solve the problem at present.And
Existing canvas is on surface after chemical treatment, and in the sun, the chemical substance on surface is easy aging, becomes for exposure for a long time
Firmly, thus more easily by rain erosion.And existing maceration extract tends to be adhered to during conveying cloth drying
The surface of roll will be piled into soil block on the surface of roll after a period of time, influence the machine-shaping of cloth.
Against the above technical problems, the invention discloses a kind of aging-resistant flame-proof type canvas maceration extract, by maceration extract
Middle addition age resister and suitable flame-retardant formulations, the surface that maceration extract is coated in canvas have preferable fire protection flame retarding
Can, while maceration extract is not easy to be adhered to the surface of roll during canvas is processed, and reduces the artificial worry except material, improves
Production efficiency.
Summary of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide a kind of aging-resistant flame-proof type canvas maceration extract,
It is poor to solve canvas maceration extract flame retardant effect in the prior art, roller surface is easily adhered in process forms convex block shadow
Ring the technical problems such as production;The present invention can have preferable fire retardant performance, while the process that maceration extract is processed in canvas
In be not easy to be adhered to the surface of roll, reduce the artificial worry except material, improve production efficiency.
In order to solve the above technical problems, the invention discloses a kind of aging-resistant flame-proof type canvas maceration extracts, including A liquid and B
Liquid, the wherein raw material in A liquid are as follows: water-based acrylic resin lotion, ptfe emulsion, dilute hydrochloric acid, montmorillonite, fire retardant and
Deionized water;Water-soluble acrylic ester coating in A liquid is made of the copolymer resins of active cross-linking functional group, is made
The paint film of three-dimensional-structure is cross-linked to form between active function groups in film forming.And its price is low, pollution-free;Polytetrafluoroethylene (PTFE) simultaneously
Lotion has excellent chemical stability, corrosion resistance, leakproofness, high lubrication and non-stickiness and good anti-aging endurance etc..
Water-based acrylic resin lotion and fire proofing can also be uniformly dispersed in the surface of canvas by ptfe emulsion.It covers
De- soil plays the role of carrier, and fire proofing can be adsorbed on to its surface, dispersion more evenly.Raw material in B liquid are as follows:
Silane coupling agent, age resister nano-titanium dioxide, epoxy curing agent, filler, butadiene-vinylpyridine copylymer latex, aqueous slkali and deionization
Water;When work, first openpore canvas is immersed in A liquid, after drying, then is immersed in B liquid, then drying and processing.
Further, fire retardant is phosphorus flame retardant in A liquid, and phosphorus flame retardant high-temp combustion will not release in the process again
More harmful halogen gas, it is more environmentally-friendly, and its flame retardant property is more excellent.
Further, phosphorus flame retardant is cyclic phosphate, melamine polyphosphate or polyphosphate.
Further, in A liquid each raw material components by weight percent are as follows: 30~50 parts of water-based acrylic resin lotion, polytetrafluoroethyl-ne
15~20 parts of alkene lotion, 5~8 parts of montmorillonite, 2~3 parts of fire retardant, 50~80 parts of deionized water, the pH value of A liquid is 3~5.
Further, in B liquid filler be pigment and silicon carbide powder, silicon carbide high temperature resistant with higher, high-heat performance,
Its surface that lotion in B liquid can be also uniformly dispersed in canvas simultaneously.
Further, in B liquid each raw material components by weight percent are as follows: 15~18 parts of silane coupling agent, age resister nano-silica
3~5 parts of titanium of change, 13~15 parts of epoxy curing agent, 2~3 parts of filler, 35~50 parts of butadiene-vinylpyridine copylymer latex, deionized water 50~80
Part, the pH value of B liquid is 8~10.
Further, in order to preferably be convenient for forming ammonium root complex ion with other macromolecules, in increase is intermolecular, aqueous slkali
The ammonia spirit for being 28% for mass concentration.
It is fire-retardant for canvas maceration extract in the prior art the invention discloses a kind of aging-resistant flame-proof type canvas maceration extract
Effect is poor, easily adhered in process roller surface formed convex block influence production etc. technical problems improve, pass through to
Age resister and suitable flame-retardant formulations are added in maceration extract, the surface that maceration extract is coated in canvas has preferable fire prevention resistance
Performance is fired, while maceration extract is not easy to be adhered to the surface of roll during canvas is processed, reduces the artificial worry except material,
Improve production efficiency.
Specific embodiment
It elaborates below to the embodiment of the present invention, the present embodiment carries out under the premise of the technical scheme of the present invention
Implement, the detailed implementation method and specific operation process are given, but protection scope of the present invention is not limited to following implementation
Example.
Embodiment 1
Embodiment 1 discloses a kind of aging-resistant flame-proof type canvas maceration extract, including A liquid and B liquid, wherein the raw material in A liquid
Are as follows: water-based acrylic resin lotion, ptfe emulsion, dilute hydrochloric acid, montmorillonite, fire retardant and deionized water;Each original in A liquid
The components by weight percent of material are as follows: 30 parts of water-based acrylic resin lotion, 15 parts of ptfe emulsion, 5 parts of montmorillonite, 2 parts of fire retardant,
50 parts of deionized water, the pH value of A liquid is 3.
Raw material in B liquid are as follows: silane coupling agent, age resister nano-titanium dioxide, epoxy curing agent, filler, fourth
Pyrrole latex, aqueous slkali and deionized water;The components by weight percent of each raw material in B liquid are as follows: 15 parts of silane coupling agent, age resister nanometer two
3 parts of titanium oxide, 13 parts of epoxy curing agent, 2 parts of filler, 35 parts of butadiene-vinylpyridine copylymer latex, 50 parts of deionized water, the pH value of B liquid is 8.B
Filler is the pigment of 1 parts by weight and the silicon carbide powder of 1 parts by weight in liquid.In order to preferably be convenient for forming ammonium with other macromolecules
Root complex ion, in increase is intermolecular, aqueous slkali is the ammonia spirit that mass concentration is 28%.When work, first openpore canvas is soaked
Stain is in A liquid, after drying, then is immersed in B liquid, then drying and processing.Fire retardant is phosphorus flame retardant cyclic phosphate in A liquid.Phosphorus
Flame retardant will not release more harmful halogen gas in the process by high-temp combustion again, more environmentally-friendly, and its flame retardant property
It is more excellent.
Embodiment 2
Embodiment 2 discloses a kind of aging-resistant flame-proof type canvas maceration extract, including A liquid and B liquid, wherein the raw material in A liquid
Are as follows: water-based acrylic resin lotion, ptfe emulsion, dilute hydrochloric acid, montmorillonite, fire retardant and deionized water;Each original in A liquid
The components by weight percent of material are as follows: 50 parts of water-based acrylic resin lotion, 15 parts of ptfe emulsion, 8 parts of montmorillonite, 3 parts of fire retardant,
50 parts of deionized water, the pH value of A liquid is 5.
Raw material in B liquid are as follows: silane coupling agent, age resister nano-titanium dioxide, epoxy curing agent, filler, fourth
Pyrrole latex, aqueous slkali and deionized water;The components by weight percent of each raw material in B liquid are as follows: 18 parts of silane coupling agent, age resister nanometer two
5 parts of titanium oxide, 15 parts of epoxy curing agent, 3 parts of filler, 50 parts of butadiene-vinylpyridine copylymer latex, 50 parts of deionized water, the pH value of B liquid is 10.
Filler is the pigment and 1.5 parts of silicon carbide powders of 0.5 parts by weight in B liquid.When work, first openpore canvas is immersed in A liquid, is dried
It after dry, then is immersed in B liquid, then drying and processing, fire retardant is phosphorus flame retardant melamine polyphosphate in A liquid.
Embodiment 3
Embodiment 3 discloses a kind of aging-resistant flame-proof type canvas maceration extract, including A liquid and B liquid, wherein the raw material in A liquid
Are as follows: water-based acrylic resin lotion, ptfe emulsion, dilute hydrochloric acid, montmorillonite, fire retardant and deionized water;Each original in A liquid
The components by weight percent of material are as follows: 40 parts of water-based acrylic resin lotion, 20 parts of ptfe emulsion, 5 parts of montmorillonite, 3 parts of fire retardant,
70 parts of deionized water, the pH value of A liquid is 5.
Raw material in B liquid are as follows: silane coupling agent, age resister nano-titanium dioxide, epoxy curing agent, filler, fourth
Pyrrole latex, aqueous slkali and deionized water;The components by weight percent of each raw material in B liquid are as follows: 18 parts of silane coupling agent, age resister nanometer two
5 parts of titanium oxide, 15 parts of epoxy curing agent, 3 parts of filler, 50 parts of butadiene-vinylpyridine copylymer latex, 80 parts of deionized water, the pH value of B liquid is 10.
Filler is 0.3 part of pigment and 1.7 parts of silicon carbide powders in B liquid.When work, first openpore canvas is immersed in A liquid, after drying,
It is immersed in B liquid again, then drying and processing.Fire retardant is phosphorus flame retardant melamine polyphosphate in the present embodiment A liquid.
Embodiment 4
Embodiment 4 discloses a kind of aging-resistant flame-proof type canvas maceration extract, including A liquid and B liquid, wherein the raw material in A liquid
Are as follows: water-based acrylic resin lotion, ptfe emulsion, dilute hydrochloric acid, montmorillonite, fire retardant and deionized water;Each original in A liquid
The components by weight percent of material are as follows: 30 parts of water-based acrylic resin lotion, 20 parts of ptfe emulsion, 6 parts of montmorillonite, 3 parts of fire retardant,
80 parts of deionized water, the pH value of A liquid is 3.
Raw material in B liquid are as follows: silane coupling agent, age resister nano-titanium dioxide, epoxy curing agent, filler, fourth
Pyrrole latex, aqueous slkali and deionized water;The components by weight percent of each raw material in B liquid are as follows: 18 parts of silane coupling agent, age resister nanometer two
5 parts of titanium oxide, 15 parts of epoxy curing agent, 3 parts of filler, 45 parts of butadiene-vinylpyridine copylymer latex, 70 parts of deionized water, the pH value of B liquid is 8.B
Filler is 0.5 part of pigment and 1.5 parts of silicon carbide powders in liquid.When work, first openpore canvas is immersed in A liquid, after drying, then
It is immersed in B liquid, then drying and processing, fire retardant is phosphorus flame retardant cyclic phosphate in A liquid in the present embodiment.
Maceration extract in above embodiments is respectively coated on to the polyester fiber canvas surface of same batch production, and is carried out
Fire-retardant, strength test.
Experiment detection:
After Finished polyester openpore canvas is immersed in above-mentioned maceration extract respectively, finished product is sent by petroleum and chemical industry new material
It is tested with quality of item Supervision Test Center, report number: HQT2-2019-04019, test basis and decision principle: Q/
HY02-2013 " the industrial impregnation synthetic fibers canvas of flame retardant type ";Inspection project: breaking strength, elongation at break, damage length
Degree, flaming combustion time, glowing time and ageing-resistant performance etc..
Test result is as follows:
By experiment detection it can be seen that each canvas has reached standard requirements, the damage of canvas in terms of flame retardant property
Also all in 10mm hereinafter, in the case where flaming combustion, burning time is also no more than 15s to length for control, has significantly not
Slight susceptibility to combustion, it is seen that the flame retardant effect of maceration extract is obviously.
When senile experiment, ageing oven model are as follows: Ci65/DMC type, light source 6.5KW, water-cooled xenon long-arc lamp, examination
It tests using continuous illumination, temperature is controlled in 45 ± 5 DEG C of ultraviolet irradiation intensity 56W/m2, after illumination in 1000 hours to canvas into
Row strength test statistics tests the canvas in above embodiments respectively, and surface occurs without obvious metachromatism, breaking strength
It is kept at radial 580N/mm or more, broadwise is kept at 110N/mm or more, hence it is evident that be more than the resistance to old of general polyester canvas
Change performance.
Claims (7)
1. a kind of aging-resistant flame-proof type canvas maceration extract, which is characterized in that including A liquid and B liquid, wherein the raw material in the A liquid
Are as follows: water-based acrylic resin lotion, ptfe emulsion, dilute hydrochloric acid, montmorillonite, fire retardant and deionized water;
Raw material in the B liquid are as follows: silane coupling agent, age resister nano-titanium dioxide, epoxy curing agent, filler, fourth
Pyrrole latex, aqueous slkali and deionized water;
When work, first openpore canvas is immersed in A liquid, after drying, then is immersed in B liquid, then drying and processing.
2. aging-resistant flame-proof type canvas maceration extract as described in claim 1, which is characterized in that fire retardant described in A liquid is phosphorus
Flame retardant.
3. aging-resistant flame-proof type canvas maceration extract as claimed in claim 2, which is characterized in that the phosphorus flame retardant is ring phosphorus
Acid esters, melamine polyphosphate or polyphosphate.
4. aging-resistant flame-proof type canvas maceration extract as described in claim 1, which is characterized in that the weight group of each raw material in A liquid
It is divided into: 30~50 parts of water-based acrylic resin lotion, 15~20 parts of ptfe emulsion, 5~8 parts of montmorillonite, fire retardant 2~
3 parts, 50~80 parts of deionized water, the pH value of A liquid is 3~5.
5. aging-resistant flame-proof type canvas maceration extract as described in claim 1, which is characterized in that filler described in B liquid is pigment
And silicon carbide powder.
6. aging-resistant flame-proof type canvas maceration extract as described in claim 1, which is characterized in that the weight group of each raw material in B liquid
It is divided into: 15~18 parts of silane coupling agent, 3~5 parts of age resister nano-titanium dioxide, 13~15 parts of epoxy curing agent, fills out
2~3 parts of material, 35~50 parts of butadiene-vinylpyridine copylymer latex, 50~80 parts of deionized water, the pH value of B liquid is 8~10.
7. aging-resistant flame-proof type canvas maceration extract as claimed in claim 6, which is characterized in that the aqueous slkali is mass concentration
For 28% ammonia spirit.