CN110286055A - A kind of permeable rate test method of adhesive - Google Patents
A kind of permeable rate test method of adhesive Download PDFInfo
- Publication number
- CN110286055A CN110286055A CN201910687711.3A CN201910687711A CN110286055A CN 110286055 A CN110286055 A CN 110286055A CN 201910687711 A CN201910687711 A CN 201910687711A CN 110286055 A CN110286055 A CN 110286055A
- Authority
- CN
- China
- Prior art keywords
- moisture vapor
- vapor transmission
- cup
- transmission cup
- sample
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of permeable rate test method of adhesive comprising the following steps: step 1: sample preparation: coating adhesive to be measured on the filter cloth of certain mesh number, uses its normal cure technique completion of cure;Step 2: the production of moisture vapor transmission cup: desiccant being put into clean cup ware;The cup ware for filling desiccant is put into moisture vapor transmission cup, then moisture vapor transmission cup is put on glass platform, sample is placed on moisture vapor transmission cup center, in addition fixing the position of sample with guider ring after cup ring, adds gland;Guider ring is removed, sealing wax is poured in a groove;After wax solidification to be sealed, gland and cup platform are removed, sealing wax is removed;Step 3: weighing the moisture vapor transmission cup sealed;Step 4: moisture vapor transmission cup being put into climatic chamber (60 DEG C/90%RH), is taken out afterwards for 24 hours, is put into the drier under 23 ± 2 DEG C of environment, is weighed after balancing 30min;Step 5: moisture vapor transmission cup being reentered into climatic chamber after weighing;Step 6: step 5 is repeated, until mass incremental is not more than 5% twice for front and back.
Description
Technical field
The present invention relates to a kind of permeable rate test method of adhesive, the permeable rate test method of the adhesive can be used
To the permeability rate of the various adhesive for being not easy to prepare membrane material needed for conventional permeability rate is tested.
Background technique
Existing permeable rate test method is mainly with plastic film and the cup type method of sheet material water vapor permeability test method
(GB1037-1988) based on, specific method is to be put into desiccant in cup to be put into glass ware, and membrane material is sealed cup with sealing wax
Ware prepares moisture vapor transmission cup, and moisture vapor transmission cup is then put into climatic chamber (60 DEG C/90%RH), and for 24 hours, title is taken out after 48h, 96h
Weight, and by retest so that until its front and back mass incremental is no more than 5%, then by moisture-vapor transmission formula into
The permeability rate of material is calculated in row.
Its shortcoming are as follows: it requires test material that can be prepared as film and sheet material, just can be convenient test.And big portion
It is not easy to be prepared as film and sheet material, especially film thickness after the adhesive solidification divided to be micron-sized film and sheet material, so this
The test method of permeability rate is less applicable in most adhesive.
Summary of the invention
The technical problem to be solved in the present invention is that: overcome existing permeable rate test method not to be suitable for most of gluing
The problem of agent, provides a kind of permeable rate test method of adhesive.
To solve the above problems, the present invention proposes a kind of following technical proposal: permeable rate test method of adhesive, packet
Include the following steps:
Step 1: sample preparation: coating adhesive to be measured on the filter cloth of certain mesh number, has been solidified using its normal cure technique
Entirely, its thickness is tested using calibrator, chooses the sample of film thickness needed for providing, guarantee that effective area is greater than 25cm2, it is made
3 groups of samples;
Step 2: preparing moisture vapor transmission cup: desiccant being put into clean cup ware, additional amount should make desiccant away from sample table
Face about 3mm is advisable;
The cup ware for filling desiccant is put into moisture vapor transmission cup, then moisture vapor transmission cup is put on glass platform, sample is placed on moisture vapor transmission cup
Gland is added in addition fixing the position of sample with guider ring after cup ring in center;
Guider ring carefully is removed, the sealing wax of melting is poured in the groove for being filled in moisture vapor transmission cup, is not allowed after sealing wax solidification
It cracks and bubble;
After wax solidification to be sealed, gland and cup platform are removed, the sealing wax for being sticked to moisture vapor transmission cup side and bottom is removed;
Step 3: weighing the moisture vapor transmission cup sealed;
Step 4: moisture vapor transmission cup being put into climatic chamber (60 DEG C/90%RH), is taken out afterwards for 24 hours, 23 ± 2 DEG C of environment are put into
Under drier in, balance 30min after weighed;
Step 5: moisture vapor transmission cup is reentered into climatic chamber after weighing, be per interval time for weighing twice later for 24 hours,
48h or 96h;
Step 6: step 5 is repeated, until mass incremental can terminate to test no more than 5% twice for front and back.
The above technical solution is further limited in that calculation method are as follows: steam penetrating capacity WVT=24 Δ m/ (A
t)
In formula: WVT: steam penetrating capacity, g/m2·24h;
T: the interval time twice after mass incremental is stable, h;
Mass incremental in the Δ m:t time, g;
A: the area of sample moisture vapor permeable, m2。
The above technical solution is further limited in that vapor transfer rate is excessive as samples in step 5, it also can be to initial balance
Time and weighing interval time adjust accordingly, but should control moisture vapor transmission cup increment not less than 5mg.
The above technical solution is further limited in that when weighing every time, moisture vapor transmission cup sequencing should be consistent in step 6,
The weighing time must not exceed the 1% of interval time, and the desiccant in slight vibration moisture vapor transmission cup is answered to keep it mixed up and down after weighing every time
It closes, desiccant moisture absorption total increment must not exceed 10%.
The invention has the following advantages: a kind of permeable rate test method of adhesive of the present invention solves adhesive not
The problem of easily carrying out permeability rate test;It is easy to operate, convenient and low in cost.
Specific embodiment
The present invention proposes a kind of permeable rate test method of adhesive, including the following steps:
Step 1: sample preparation: being coated on 800 mesh filter clothes (mesh number adjusting can be carried out according to the requirement of different viscosities adhesive)
Adhesive to be measured is tested its thickness using calibrator, it is thick to be chosen glue film needed for providing using its normal cure technique completion of cure
The sample of degree guarantees that effective area is greater than 25cm2, 3 groups of samples are made;
Step 2: the production of moisture vapor transmission cup: desiccant being put into clean cup ware, additional amount should make desiccant away from sample
Surface about 3mm is advisable;
The cup ware for filling desiccant is put into moisture vapor transmission cup, then moisture vapor transmission cup is put on glass platform, sample is placed on moisture vapor transmission cup
Gland is added in addition fixing the position of sample with guider ring after cup ring in center;
Guider ring carefully is removed, the sealing wax of melting is poured in the groove for being filled in moisture vapor transmission cup, is not allowed after sealing wax solidification
It cracks and bubble;
After wax solidification to be sealed, gland and cup platform are removed, the sealing wax for being sticked to moisture vapor transmission cup side and bottom is removed;
Step 3: weighing the moisture vapor transmission cup sealed;
Step 4: moisture vapor transmission cup being put into climatic chamber (60 DEG C/90%RH), is taken out afterwards for 24 hours, 23 ± 2 DEG C of environment are put into
Under drier in, balance 30min after weighed;
Note: the equilibrium step should all be carried out by weighing every time later.
Step 5: moisture vapor transmission cup is reentered into climatic chamber after weighing, be per interval time for weighing twice later for 24 hours,
48h or 96h;
Note: vapor transfer rate is excessive as samples, can also adjust accordingly to initial equilibration time and weighing interval time, but should control
Moisture vapor transmission cup increment processed is not less than 5mg.
Step 6: step 5 is repeated, until mass incremental can terminate to test no more than 5% twice for front and back.
Note: when weighing every time, moisture vapor transmission cup sequencing should be consistent, and the weighing time must not exceed the 1% of interval time, every time
The desiccant in slight vibration moisture vapor transmission cup is answered to mix it up and down after weighing.Desiccant moisture absorption total increment must not exceed 10%.
Calculation method:
Steam penetrating capacity WVT=24 Δ m/ (At)
In formula: WVT: steam penetrating capacity, g/m2·24h;
T: the interval time twice after mass incremental is stable, h;
Mass incremental in the Δ m:t time, g;
A: the area of sample moisture vapor permeable, m2
Embodiment 1
Choose glue to be measured:
UV adhesive: the 3781 of Le Tai company,
According to above-mentioned adhesive permeable rate test method the step of, the permeability rate of testing glue.
Embodiment 2
Choose glue to be measured:
Heat curing epoxy adhesive: Shenzhen flies the epoxy frame adhesive FER-18 of your new material limited liability company of generation,
According to above-mentioned adhesive permeable rate test method the step of, the permeability rate of testing glue.
Embodiment 3
Choose glue to be measured:
Room temperature curing silica gel: the SE9187L of Dow Corning Corporation,
According to above-mentioned adhesive permeable rate test method the step of, the permeability rate of testing glue.
Embodiment 4
Choose glue to be measured:
The double cured adhesives of photo-thermal: Shenzhen flies the OLED frame adhesive UV-729 of your new material limited liability company of generation,
According to above-mentioned adhesive permeable rate test method the step of, the permeability rate of testing glue.
Test result is as follows:
By the above results: a kind of permeable rate test method of adhesive of the present invention can be very good to test all kinds of glue
The permeability rate of stick solves the problems, such as that adhesive is not easy to carry out permeability rate test, and easy to operate, convenient, low in cost.It is
A kind of permeable rate test method of excellent adhesive.
Claims (5)
1. a kind of permeable rate test method of adhesive, which is characterized in that it includes the following steps:
Step 1: sample preparation: coating adhesive to be measured on the filter cloth of certain mesh number, using its normal cure technique completion of cure, makes
Its thickness is tested with calibrator, chooses the sample of film thickness needed for providing, guarantees that effective area is greater than 25cm2, 3 groups of samples are made
Product;
Step 2: the production of moisture vapor transmission cup: desiccant being put into clean cup ware, additional amount should make desiccant away from specimen surface
About 3mm is advisable;
The cup ware for filling desiccant is put into moisture vapor transmission cup, then moisture vapor transmission cup is put on glass platform, sample is placed on moisture vapor transmission cup center,
In addition fixing the position of sample with guider ring after cup ring, gland is added;
Guider ring carefully is removed, the sealing wax of melting is poured in the groove for being filled in moisture vapor transmission cup, does not allow to generate after sealing wax solidification
Crackle and bubble;
After wax solidification to be sealed, gland and cup platform are removed, the sealing wax for being sticked to moisture vapor transmission cup side and bottom is removed;
Step 3: weighing the moisture vapor transmission cup sealed;
Step 4: moisture vapor transmission cup being put into climatic chamber (60 DEG C/90%RH), is taken out afterwards for 24 hours, is put under 23 ± 2 DEG C of environment
In drier, weighed after balancing 30min;
Step 5: moisture vapor transmission cup is reentered into climatic chamber after weighing, be per interval time for weighing twice later for 24 hours, 48h
Or 96h;
Step 6: step 5 is repeated, until mass incremental can terminate to test no more than 5% twice for front and back.
2. a kind of permeable rate test method of adhesive according to claim 1, which is characterized in that its method for making sample be
Adhesive to be measured is coated on the filter cloth of certain mesh number, using its normal cure technique completion of cure, is tested using spiral direction finder
Its thickness chooses the sample of film thickness needed for providing.
3. a kind of permeable rate test method of adhesive according to claim 1, which is characterized in that calculation method are as follows:
Steam penetrating capacity WVT=24 Δ m/ (At)
In formula: WVT: steam penetrating capacity, g/m2·24h;
T: the interval time twice after mass incremental is stable, h;
Mass incremental in the Δ m:t time, g;
A: the area of sample moisture vapor permeable, m2。
4. a kind of permeable rate test method of adhesive according to claim 1, which is characterized in that in step 5, as samples
Vapor transfer rate is excessive, can also adjust accordingly to initial equilibration time and weighing interval time, but it is small to control moisture vapor transmission cup increment
In 5mg.
5. a kind of permeable rate test method of adhesive according to claim 1, which is characterized in that in step 6, claim every time
When amount, moisture vapor transmission cup sequencing should be consistent, and the weighing time must not exceed the 1% of interval time, answers slight vibration after weighing every time
Desiccant in moisture vapor transmission cup mixes it up and down, and desiccant moisture absorption total increment must not exceed 10%.