CN110273324A - A kind of good middle gloss Alhue paper preparation process of pigment inks adaptability - Google Patents
A kind of good middle gloss Alhue paper preparation process of pigment inks adaptability Download PDFInfo
- Publication number
- CN110273324A CN110273324A CN201910357091.7A CN201910357091A CN110273324A CN 110273324 A CN110273324 A CN 110273324A CN 201910357091 A CN201910357091 A CN 201910357091A CN 110273324 A CN110273324 A CN 110273324A
- Authority
- CN
- China
- Prior art keywords
- coating
- gloss
- paper
- pigment inks
- preparation process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses being a kind of good middle gloss Alhue paper preparation process of pigment inks adaptability, including prepares blotting coating, prepares gloss coating, coating ink absorbing layer, drying, matte management, coating gloss layer；Through Alhue paper made from preparation process of the present invention, coloring fixation when solving the problems, such as to be printed with pigment inks is easy to colour, print screen UV radiation, upper coloration is good, and it is long to hold the color time with good pigment inks applicability.In addition, be coated in two times when coating gloss layer, make paper in pile effects, solve the problems, such as reflective when paper, the board light direct projection of advertisement, promotes print pattern visual effect, meet the special requirement of the paper, board prepared advertising.
Description
Technical field
The present invention relates to color ink jet printer paper preparation process, the good middle gloss ink-jet of specifically a kind of pigment inks adaptability
Printing paper preparation process.
Background technique
With the development of digital imaging techniques, the demand to color ink jet printer paper is more and more.It is color ink jet printed
Paper is a kind of processing paper of coating, it is to be coated deep processing on common printed paper base plinth, is mainly applied on its surface
Cloth coating, being allowed to that water-based ink can be absorbed again can be such that ink droplet does not spread to periphery, thus completely keep original color and
Clarity.
Ink jet printing paper is divided into dumb light color ink jet printer paper, middle gloss color ink jet printer paper and high glaze currently on the market
Color ink jet printer paper, wherein middle gloss color ink jet printer paper is mainly used for advertising, application amount is considerable.General spray
The paper structure of black printing paper is divided into base, ink absorbing layer and gloss layer, and there are two types of the inks used in colour print, dyestuff
Ink and pigment inks, wherein the partial size of dye ink is small, and when printing can penetrate the gloss layer and ink absorbing layer of paper, reaches base, from
And fixed by the color fixing agent in paper coating, to colour；It compares, the partial size of pigment inks is larger, it is difficult to penetrate gloss layer
Or ink absorbing layer, to can not colour.
However dye ink not resistant to corrosion, the time, which has been grown, to fade, and advertisement especially outdoors is difficult to by exposing to the weather
Holding for picture is kept coloration and to hold the color time；And pigment inks are corroded compared to dye ink energy uvioresistant, keep Color time long
Advantage.Therefore it needs to prepare a kind of color ink jet printer paper, pigment inks can be penetrated, solve the problems, such as fixation.
It is typically mounted at obvious position additionally, due to paper, the board of advertisement, generally there is light direct projection, this requires production
The paper of advertisement, board paper can not be reflective strong, influence visual effect, it is therefore desirable to prepare a kind of color ink jet printer paper, it is full
The reflectance needs of the paper, board prepared advertising enough.
Summary of the invention
It is an object of the present invention to overcome the above deficiencies, and providing a kind of pigment inks adaptability, good middle gloss ink-jet is beaten
Printing paper preparation process not only solves pigment inks fixation to prepare a kind of good middle gloss Alhue paper of pigment inks adaptability
The problem of, moreover it is possible to meet the reflectance needs of the paper, board prepared advertising.
Specific technical solution is as follows:
A kind of good middle gloss Alhue paper preparation process of pigment inks adaptability, comprises the following steps that
S1: ink absorbing layer and gloss coating prepares coating coating: are prepared according to formula respectively.
S2: coating ink absorbing layer: it will be sent after body paper reel to the base paper roll stand of coating machine with paper machine, then imposed by coating machine
The blotting coating prepared in application step S1；
S3: it drying: under the conditions of 140 DEG C of printing paper after coating blotting coating in step S2, thoroughly dries, in case subsequent place
Reason；
S4: matte management: by step S3 dry after printing paper, be sent into super dumb light roller group squeeze it is smooth, it is spare；
S5: coating gloss layer: the printing paper in step S4 after matte management is sent to the paper frame of coating machine with paper machine again
On, then the gloss coating prepared in application step S1 is imposed by coating machine, the good middle light of pigment inks adaptability is made after dry
Damp Alhue paper.
The good middle gloss Alhue paper preparation process of pigment inks adaptability above-mentioned, blotting coating described in step S1
Preparation are as follows: by weight: SiO2:100~110 part, PVA aqueous solution: 225~235 parts, VAE lotion: 55~65 parts, fixation
Agent: 50~60 parts, brightening agent: 3~5 parts, defoaming agent: 0.6~0.7 part, deionized water: 530~550 parts；First will at room temperature
SiO2 and color fixing agent, which add to be added in deionized water together, stirs 45min, and then addition PVA aqueous solution and VAE lotion are mixed into
Adhesive and brightening agent, are eventually adding defoaming agent, are uniformly mixed, and obtain blotting coating.The wherein adhesive
Mixing speed when with defoaming being that side stirring is just added, and being eventually adding defoaming agent is 300~500r/min, then again with
The revolving speed of 500~1000r/min stirs 5~10min.
The good middle gloss Alhue paper preparation process of pigment inks adaptability above-mentioned, gloss coating described in step S1
Preparation are as follows: take by weight: PVA:20 parts, acrylic emulsion: 80 parts are added in 100 parts of deionized waters, be dispersed with stirring
It is even, that is, obtain gloss coating.It should be noted that mixing speed is no more than 150r/min when being dispersed with stirring.
The good middle gloss Alhue paper preparation process of pigment inks adaptability above-mentioned, gloss layer described in step S6 are divided into
It is coated with twice, and for the first time after coating coating, need to be through drying, again after matte management, then second is coated with.
As preferred scheme, the coated weight control that ink absorbing layer is coated with described in step S2 is 10g/m2.
As preferred scheme, the coated weight control of gloss layer described in step S6 is 10g/m2.
As further preferred scheme, the coating of the gloss coating, first time coated weight control is 6 g/m2, the
Secondary coated weight control is 4g/m2.
The beneficial effects of the present invention are:
The present invention starts in terms of formulation for coating material and coating processes come two, in terms of formulation for coating material, is tested ink absorbing layer and gloss
The formula of coating advanced optimizes, and each group distribution ratio is more reasonable, conducive to pigment inks penetrate and fixation；Pass through in coating
Matte management process keeps the paper surface of coating smooth, and the amount of pigment of coating can be saved when coating again；Through the present invention
Alhue paper made from preparation process, coloring fixation when solving the problems, such as to be printed with pigment inks have good pigment
Black applicability is easy to colour, and print screen UV radiation, upper coloration is good, and it is long to hold the color time.In addition, when coating gloss layer,
It is coated in two times, makes paper in pile effects, solve the problems, such as reflective when paper, the board light direct projection of advertisement, promotion print pattern
Visual effect meets the special requirement of the paper, board prepared advertising.And coated in two times when coating gloss layer, form flannelette
Effect keeps it non-reflective under strong light；So that the color ink jet printer paper for making the preparation process becomes a kind of novel
Advertisement paper, improve that China color ink jet printer paper paint preparation process is horizontal and paper layer quality level, have good
Application value.
Specific embodiment
The present invention will in conjunction with the embodiments be clearly and completely described technical solution of the present invention below:
Embodiment 1:
A kind of good middle gloss Alhue paper of pigment inks adaptability is prepared according to invented technology, is comprised the following steps that
S1: ink absorbing layer and gloss coating prepares coating coating: are prepared according to formula respectively.The preparation of the blotting coating
Are as follows: by weight: SiO2:100~110 part, PVA aqueous solution: 225~235 parts, VAE lotion: 55~65 parts, color fixing agent: 50~
60 parts, brightening agent: 3~5 parts, defoaming agent: 0.6~0.7 part, deionized water: 530~550 parts；At room temperature first by SiO2 and fixation
Agent, which adds to be added in deionized water together, stirs 45min, be then added adhesive that PVA aqueous solution and VAE lotion are mixed into and
Brightening agent is eventually adding defoaming agent, is uniformly mixed, and obtains blotting coating.The wherein adhesive and defoaming be
Side stirring is just added, and mixing speed when being eventually adding defoaming agent is 300~500r/min, then again with 500~1000r/
The revolving speed of min stirs 5~10min.The preparation of the gloss coating are as follows: take by weight: PVA:20 parts, acrylic emulsion:
80 parts are added in 100 parts of deionized waters, are dispersed with stirring uniformly, i.e. acquisition gloss coating.It should be noted that when being dispersed with stirring,
Its mixing speed is no more than 150r/min.
S2: coating ink absorbing layer: it will be sent after body paper reel to the base paper roll stand of coating machine with paper machine, then imposed by coating machine
The blotting coating prepared in application step S1；The coated weight control of the coating ink absorbing layer is 10g/m2.
S3: drying: under the conditions of 140 DEG C of printing paper after coating blotting coating in step S2, thoroughly drying, in case after
Continuous processing；
S4: matte management: by step S3 dry after printing paper, be sent into super dumb light roller group squeeze it is smooth, it is spare；Institute
The super dumb light roller group stated is made of the first steel rider, the second steel rider and rubber covered roll, wherein the hardness of the first steel rider and the second steel rider
It is 90-95 degree, the hardness of rubber covered roll is 70 degree.There are rotation speeds between first steel rider, the second steel and roller rubber covered roll
Difference, printing paper are passed through from the gap of the first steel rider and rubber covered roll, are carried out double times into rubber covered roll and the second steel rider gap and are squeezed,
Then it sends out, printing paper surface can be made smooth.
S5: coating gloss layer: the printing paper in step S4 after matte management is sent to coating machine with paper machine again
On paper frame, then the gloss coating prepared in application step S1 being imposed by coating machine, the gloss layer is divided into be coated with twice, and the
, need to be through drying, again after matte management after primary coating coating, then second is coated with.The coated weight of the gloss layer controls
10g/m2, the control of first time coated weight are 6 g/m2, and second of coated weight control is 4g/m2.Coating coating finishes after drying
The good middle gloss Alhue paper of pigment inks adaptability is made.Coating gloss layer is to make printing paper surface in suede in two times
Face effect keeps paper print screen vision soft, will not be strong and dazzling because of light.
Embodiment 2:
The performance of the middle gloss Alhue paper good to the pigment inks adaptability for stating preparation in embodiment 1 is measured, as a result such as
Under:
Glossiness (75 °) (%): 15.8
Whiteness (CIE, D65/10 °): 95
Opacity (%): 96.66
Smoothness (s): 25.4
Water-resistance (%): 22
It spreads and sinks in infiltration: 6.1
Color density: 0.92/1.15/1.05(cyan/magenta/yellow color).
Therefore, by the printing paper of present invention process preparation, not only pigment inks adaptability is good, but also performance indexes is equal
Well.Its paper is in pile effects, keeps paper print screen vision soft, feature that will not be strong and dazzling because of light, especially suitable
It shares in outdoor advertisement, high-end commercial affairs publicity.Pigment inks energy uvioresistant corrodes, and holds coloration by force and to hold color of long duration；Also can
Meet precious photo, the needs of the printing collection of commemorative pattern.
It is obvious to a person skilled in the art that invention is not limited to the details of above-mentioned exemplary embodiment, and not
In the case where spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter from
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive.Although in addition, it should be understood that originally
Specification is described in terms of embodiments, but only includes not one technical solution, and this narrating mode of specification is only
It is only for clarity that the skilled in the art should refer to the specification as a whole, the technical solution in embodiment can also
To be properly combined, form other embodiments that can be understood by those skilled in the art.
Claims (10)
1. a kind of good middle gloss Alhue paper preparation process of pigment inks adaptability, it is characterised in that: comprise the following steps that
S1: ink absorbing layer and gloss coating prepares coating coating: are prepared according to formula respectively.
2.S2: coating ink absorbing layer: it will be sent after body paper reel to the base paper roll stand of coating machine with paper machine, then painting imposed by coating machine
The blotting coating prepared in cloth step S1；
S3: it drying: under the conditions of 140 DEG C of printing paper after coating blotting coating in step S2, thoroughly dries, in case subsequent place
Reason；
S4: matte management: by step S3 dry after printing paper, be sent into super dumb light roller group squeeze it is smooth, it is spare；
S5: coating gloss layer: the printing paper in step S4 after matte management is sent to the paper frame of coating machine with paper machine again
On, then the gloss coating prepared in application step S1 is imposed by coating machine, the good middle light of pigment inks adaptability is made after dry
Damp Alhue paper.
3. the good middle gloss Alhue paper preparation process of pigment inks adaptability according to claim 1, it is characterised in that:
The preparation of blotting coating described in step S1 are as follows: by weight: SiO2: 100~110 parts, PVA aqueous solution: 225~235 parts,
VAE lotion: 55~65 parts, color fixing agent: 50~60 parts, brightening agent: 3~5 parts, defoaming agent: 0.6~0.7 part, deionized water: 530
~550 parts；At room temperature first by SiO2Add to be added in deionized water together with color fixing agent and stir 45min, PVA aqueous solution is then added
The adhesive and brightening agent being mixed into VAE lotion, are eventually adding defoaming agent, are uniformly mixed, and obtain ink absorbing layer painting
Material.
4. the good middle gloss Alhue paper preparation process of pigment inks adaptability according to claim 1, it is characterised in that:
The preparation of gloss coating described in step S1 are as follows: take by weight: PVA:20 parts, acrylic emulsion: 80 parts are added to 100 parts
It in deionized water, is dispersed with stirring uniformly, i.e. acquisition gloss coating.
5. the good middle gloss Alhue paper preparation process of pigment inks adaptability according to claim 2, it is characterised in that:
The adhesive and defoaming are that side stirring is just added, and mixing speed when being eventually adding defoaming agent is 300~500r/min,
Then 5~10min is stirred with the revolving speed of 500~1000r/min again.
6. the good middle gloss Alhue paper preparation process of pigment inks adaptability according to claim 3, it is characterised in that:
Described when preparing gloss coating and being dispersed with stirring, mixing speed is no more than 150r/min.
7. the good middle gloss Alhue paper preparation process of pigment inks adaptability according to claim 1, it is characterised in that:
Gloss layer described in step S6 is divided into be coated with twice, and for the first time coating coating after, need to through drying, again after matte management, then
Second of coating.
8. the good middle gloss Alhue paper preparation process of pigment inks adaptability according to claim 1, it is characterised in that:
The coated weight control that ink absorbing layer is coated with described in step S2 is 10g/m2。
9. the good middle gloss Alhue paper preparation process of pigment inks adaptability according to claim 1, it is characterised in that:
The coated weight control of gloss layer described in step S6 is 10g/m2。
10. a kind of good middle gloss Alhue paper preparation process of pigment inks adaptability according to claim 1 or 6,
Be characterized in that: the coating of the gloss coating, the control of first time coated weight are 6 g/m2, second of coated weight control is 4g/
m2。