CN110257717B - High-end bearing steel material for machine tool bearing ring and manufacturing method thereof - Google Patents

High-end bearing steel material for machine tool bearing ring and manufacturing method thereof Download PDF

Info

Publication number
CN110257717B
CN110257717B CN201910676601.7A CN201910676601A CN110257717B CN 110257717 B CN110257717 B CN 110257717B CN 201910676601 A CN201910676601 A CN 201910676601A CN 110257717 B CN110257717 B CN 110257717B
Authority
CN
China
Prior art keywords
steel
equal
slag
temperature
refining
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201910676601.7A
Other languages
Chinese (zh)
Other versions
CN110257717A (en
Inventor
熊洪进
陈列
董贵文
李彬
王强
马忠存
陈迦杉
杨平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jianlong Beiman Special Steel Co Ltd
Original Assignee
Jianlong Beiman Special Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jianlong Beiman Special Steel Co Ltd filed Critical Jianlong Beiman Special Steel Co Ltd
Priority to CN201910676601.7A priority Critical patent/CN110257717B/en
Publication of CN110257717A publication Critical patent/CN110257717A/en
Application granted granted Critical
Publication of CN110257717B publication Critical patent/CN110257717B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a high-end bearing steel material for a machine tool bearing ring and a manufacturing method thereof, belonging to the technical field of special steel smelting and forging. The invention provides a high-end bearing steel material for a bearing ring of a machine tool and a manufacturing method thereof, aiming at solving the problem that the performance of the steel material can not meet the requirements of a high-end numerical control machine tool due to the segregation and the reticular distribution of carbides in the steel material for the bearing ring. According to the invention, Ni, Mo and rare earth elements are added on the basis of the existing bearing steel, the contents of Al and Cu are strictly controlled, and good mechanical property indexes are provided for steel materials; the carbide is effectively diffused in the manufacturing process, the carbide level of the steel material is improved, the steel material for the machine tool bearing ring has high elastic limit, tensile strength, contact fatigue strength and wear resistance, and the phenomena of fatigue peeling, clamping and the like of the material can be effectively reduced.

Description

High-end bearing steel material for machine tool bearing ring and manufacturing method thereof
Technical Field
The invention belongs to the technical field of special steel smelting and forging, and particularly relates to a high-end bearing steel material for a machine tool bearing ring and a manufacturing method thereof.
Background
With the rapid development of numerical control technology, the industrial technology of machine tools is also rapidly developed. The high-speed machining can effectively improve the machining efficiency of the machine tool and shorten the machining period of the workpiece. This requires that the machine spindle and its associated components be adapted to the requirements of high speed machining. At present, the main shaft bearing of the numerical control machine tool is basically limited to four structural types, namely an angular contact ball bearing, a cylindrical roller bearing, a bidirectional thrust angular contact ball bearing, a tapered roller bearing and the like.
The bearing ring is an annular part of a radial rolling bearing having one or more raceways and is subjected to extreme pressures and frictional forces during operation, so that high and uniform hardness and wear resistance as well as a high elastic limit are required for the steel material for the bearing ring. The requirements on the uniformity of chemical compositions of bearing steel, the content and distribution of non-metallic inclusions, the distribution of carbides and the like are all very strict, and the steel is one of the most strict steel types in all steel production.
The high-carbon chromium bearing steel is a steel material containing about 1% of carbon and about 1.5% of chromium, and is widely applied to manufacturing various bearings. However, because the existing bearing steel material for the bearing ring has defects in the processes of alloying treatment, forging temperature and the like, carbide segregation exists in the structure of the ring and the carbide is distributed in the material in a net shape, so that the brittleness of the material is obviously increased. In the quenching process, due to the action of thermal stress and phase stress, the inner wall of the bearing ring has the defects of black spots and holes, and cracks can be generated under the action of external force in a grinding process in serious cases. Along with the higher and higher requirements of high-speed processing and other high-end numerical control machines on the performance of bearing rings, the existing high-carbon chromium bearing steel material cannot meet the requirements of the high-end numerical control machines.
Disclosure of Invention
The invention provides a high-end bearing steel material for a machine tool bearing ring and a manufacturing method thereof, aiming at solving the problem that the properties of the steel material can not meet the requirements of a high-end numerical control machine tool due to the segregation and the net distribution of carbides in the steel material for the bearing ring.
The technical scheme of the invention is as follows:
the high-end bearing steel material for the bearing ring of the machine tool comprises the following chemical components in percentage by mass: 0.93-0.98%, Si: 0.15 to 0.35%, Mn: 0.25-0.45%, Cr: 1.45-1.60%, Ni: 0.05 to 0.10%, Mo: 0.02-0.08%, Al: 0.015-0.035%, Cu: 0.06-0.10%, P is less than or equal to 0.010%, S is less than or equal to 0.008%, Nb: 0.010-0.045%, less than or equal to 0.020% of Y, less than or equal to 0.010% of Ce, less than or equal to 0.0015% of Ti, less than or equal to 0.0020% of O, less than or equal to 0.040% of As, less than or equal to 0.030% of Sn, less than or equal to 0.0050% of Sb, less than or equal to 0.0020% of Pb, more than or equal to 2.0% of Si + Mn + Cr, and the balance of Fe and inevitable.
The invention provides a manufacturing method of a high-end bearing steel material for a machine tool bearing ring, which comprises the steps of electric furnace → LF refining and VD process → die casting → hot feeding/cold covering → heating rolling → slow cooling → spheroidizing annealing;
the electric furnace comprises the following steps:
charging pig iron, molten iron or steel materials into the electric furnace, wherein the steel materials are non-Ti-containing steel materials; when the temperature of the molten steel is more than or equal to 1580 ℃ and the content of C is more than or equal to 0.30 percent, discharging steel from the electric furnace, and adding novel composite slag, aluminum ingots, alloys and lime along with the discharged molten steel in the steel discharging process;
in the LF refining and VD process:
heating the molten steel to 1550 ℃ after reaching a refining position, adding ferrosilicon and novel composite slag for slagging, adding a diffusion deoxidizer in batches for slagging after the slag is completely smelted, and when the slag reaches the condition of a refining slag system, namely CaO 46-55 percent and SiO2≤7％，Al2O3Controlling the refining time of the white slag to realize molten steel deoxidation when the content of MgO is less than or equal to 8 percent and is 32-38 percent; white slagAfter refining, controlling argon flow under certain vacuum degree to perform soft blowing on the molten steel, adding a ladle covering agent after dispersion, and continuing the soft blowing for a certain time under certain argon flow;
in the die casting process:
and pouring the molten steel after soft blowing under the protection of argon, wherein a type I ingot mould is used for casting ingots, the mould temperature is ensured to be 30-80 ℃, and the inner surface of the ingot mould is cleaned. When the mold is seated, the tail brick hole and the water button hole at the bottom of the mold must be aligned, the heat insulation plate assembly is flush with the lower edge of the cap opening, the gap is tightly plugged, and the cap opening of the steel ingot mold is tightly covered by an iron plate when the casting is waited, so that dust is prevented from entering the steel ingot mold.
The temperature of the molten steel is 1505-1510 ℃ during pouring, the molten steel is ensured to stably rise in the pouring process, and a certain cap opening feeding time is controlled;
in the heating rolling process:
heating the steel ingot with uniform and constant temperature to 850 ℃ at a certain heating rate, preserving heat for a certain time, then heating to 1230-1240 ℃ within a certain heating time, preserving heat for a certain time, and tapping and rolling, wherein the tapping temperature is 1120-1200 ℃; the initial rolling temperature is 1120 ℃, the water is cooled in the rolling process, and the final rolling temperature is 780 ℃;
in the spheroidizing annealing process:
setting the heat preservation time of the rolled steel at 810 +/-10 ℃ according to the weight of the rolled steel, then reducing the temperature to 710 +/-10 ℃ at a certain cooling speed, reducing the temperature of the steel at 710 +/-10 ℃ to 1.5 times of the heat preservation time of the steel at 810 +/-10 ℃, reducing the temperature to 500 ℃ at a certain cooling speed, preserving the heat for 1h, and finally cooling along with the furnace, discharging and air cooling.
Further, in the electric furnace process, the time for recarburizing and adding the novel composite slag, the aluminum ingot, the alloy and the lime is as follows:
sequentially adding carbon powder, novel composite slag and aluminum ingots when tapping for 3-5 tons; adding alloy when tapping for 10-15 tons; adding the novel composite slag and lime again when tapping for 20-25 tons; the addition amount of carbon powder is controlled by the fact that the content of C in the LF refining position is 0.85-0.95%, the addition amount of alloy is controlled by the fact that chemical components except Si in the LF refining position reach the lower limit of specification, and the content of aluminum in the LF refining position is 0.030-0.040%.
Further, the alloy comprises low-titanium high-chromium and medium-carbon ferromanganese;
the low-titanium high-chromium alloy comprises the following components in percentage by mass: cr: 60.2%, C: 0.18%, Si: 0.7%, P: 0.03%, S: 0.02%, Ti: 0.003 percent, and the balance of Fe and inevitable impurities;
the medium carbon ferromanganese comprises the following components in percentage by mass: mn: 79.45%, C: 1.47%, Si: 1.62%, P: 0.191% and the balance Fe and inevitable impurities.
Further, in the electric furnace process, the novel composite slag comprises the following components in percentage by mass: CaO: 46%, MgO: 2.2% of Fe2O3：0.6％、Al2O3：40％、SiO2：0.2％，H2O: 0.17%, the balance being other metal oxides and unavoidable impurities.
Further, in the LF refining and VD process, the ferrosilicon comprises the following components in percentage by mass: si: 76.7%, C: 0.01 percent of Ti, 0.013 percent of Ti, and the balance of other metal oxides and inevitable impurities;
the diffusion deoxidizer comprises a mixture of aluminum particles and carbon powder in a weight ratio of 1:1 and a mixture of carbon powder and silicon powder in a weight ratio of 1: 1; according to the slagging condition of a refining slag system, aluminum particles and carbon powder are mixed and deoxidized in the early stage of refining, and carbon powder and silicon powder are mixed and deoxidized in the later stage; and the white slag refining time is 30-50 min.
Further, in the LF refining and VD process, the vacuum degree is 67Pa, the argon flow under vacuum is 20-40 NL/min, and the soft blowing time under vacuum is 20-30 min; the flow of argon gas after diffusion is 10-40 NL/min, and the soft blowing time after diffusion is 30-40 min; the ladle covering agent comprises the following components in percentage by mass: SiO 22：20.00～30.00％、CaO：23.00～33.00％、Al2O3: 8.00-20.00%, C: 10.00-20.00%, the rest is other metal oxides and unavoidable impurities.
Furthermore, in the die casting process, the pressure of the protective argon is 0.02-0.03 MPa, the special protective slag for bearing steel is used and cast in a hanging mode, the casting reflux needs to be timely, the casting flow is adjusted after casting, and the flow adjustment which is not small or large in the casting process is strictly forbidden;
the special covering slag for bearing steel comprises the following components in percentage by mass: SiO 22：34.00～44.00％、CaO：9.00～19.00％、Al2O3Less than or equal to 12.00 percent, C: 11.00-21.00%, MgO less than or equal to 8.00%, and the balance of other metal oxides and unavoidable impurities;
the height of the hanger is 250-300 mm from the die bottom; the feeding time of the cap opening is 240 s.
Further, in the heating rolling process, the steel ingot with uniform and constant temperature is kept at 500-700 ℃ for 90min to reach uniform and constant temperature; the temperature rising speed is 75 ℃/h; the heat preservation time at 850 ℃ is 30 min; the temperature rise time is 3-5 h; the heat preservation time at 1230-1240 ℃ is 9-14 h.
Further, the heat preservation time of the steel at 810 +/-10 ℃ in the spheroidizing annealing process is T, wherein T is 10+ Q/2, and Q is the weight of the steel and the unit is ton; the cooling speed of cooling to 710 +/-10 ℃ is 10-15 ℃/h; the cooling speed of cooling to 500 ℃ is 15-20 ℃/h.
The invention has the beneficial effects that:
the high-end bearing steel material for the machine tool bearing ring, provided by the invention, is added with Ni and Mo elements and rare earth elements on the basis of the existing bearing steel material, the contents of Al and Cu are strictly controlled, and good mechanical property indexes are provided for the steel material. Compared with available high-carbon chromium bearing steel, the high-end bearing steel material for machine tool bearing ring has the features of higher purity, homogeneous carbide distribution, T [ O ] not more than 6ppm, Ti not more than 10ppm, Ds not more than 0.5 level, maximum inclusion size not more than 15 micron, no micro pore and carbide liquation, etc. The invention makes a breakthrough progress on the control of the oxygen content, the titanium content and the large-particle inclusions in the steel.
The manufacturing method of the high-end bearing steel material for the machine tool bearing ring has the advantages that the high-temperature diffusion time is 9-14 hours in the heating and rolling stage, the controlled cold rolling is adopted, the carbide is effectively diffused, the carbide level is further improved, and the better low-power quality is obtained. The invention also adopts a spheroidizing isothermal annealing process, can eliminate hard and brittle lamellar pearlite and reticular cementite after hot rolling to form a globular pearlite structure, wherein the cementite is globular particles and is dispersedly distributed on a ferrite matrix, the hardness is lower than that of lamellar pearlite, the cementite is convenient for cutting processing, austenite grains are not easy to grow during quenching and heating, and a workpiece is not easy to deform and crack during cooling.
The machine tool bearing ring produced by the steel material can meet the requirements of high-end numerical control machines, and has high elastic limit, tensile strength and contact fatigue strength, high hardenability and necessary hardenability so as to ensure high wear resistance and certain impact toughness; good dimensional or tissue stability; can effectively reduce the phenomena of material fatigue peeling, seizing and the like.
Drawings
FIG. 1 is a photomicrograph of a high-end bearing steel material for a machine tool bearing ring produced in example 8 of the present invention;
FIG. 2 is a photograph of a metallographic microscope showing examination of nonmetallic inclusions in a high-end bearing steel material for a machine tool bearing ring, which is produced in example 8 of the present invention, at a magnification of 100 times;
FIG. 3 is a photograph of a metallographic microscope showing examination of nonmetallic inclusions in a high-end bearing steel material for a machine tool bearing ring, which is produced in example 8 of the present invention, at a magnification of 100 times;
FIG. 4 is a carbide strip photograph of a high-end bearing steel material for a machine tool bearing ring produced in example 8 of the present invention, which is taken under a metallographic microscope and in which a bright field image is magnified by 100 times;
FIG. 5 is a carbide mesh picture of a high-end bearing steel material for a machine tool bearing ring produced in example 8 of the present invention, which is collected under a metallographic microscope and magnified by 200 times in a bright field image.
Detailed Description
The technical solutions of the present invention are further described below with reference to the following examples, but the present invention is not limited thereto, and any modifications or equivalent substitutions may be made to the technical solutions of the present invention without departing from the spirit and scope of the technical solutions of the present invention.
Example 1
The embodiment provides a high-end bearing steel material for a machine tool bearing ring, which comprises the following chemical components in percentage by mass: 0.93-0.98%, Si: 0.15 to 0.35%, Mn: 0.25-0.45%, Cr: 1.45-1.60%, Ni: 0.05 to 0.10%, Mo: 0.02-0.08%, Al: 0.015-0.035%, Cu: 0.06-0.10%, P is less than or equal to 0.010%, S is less than or equal to 0.008%, Nb: 0.010-0.045%, less than or equal to 0.020% of Y, less than or equal to 0.010% of Ce, less than or equal to 0.0015% of Ti, less than or equal to 0.0020% of O, less than or equal to 0.040% of As, less than or equal to 0.030% of Sn, less than or equal to 0.0050% of Sb, less than or equal to 0.0020% of Pb, more than or equal to 2.0% of Si + Mn + Cr, and the balance of Fe and inevitable.
Carbon is an important element influencing the performance of steel, and is one of important elements ensuring that bearing steel can have sufficient hardenability, hardness value and wear resistance. The carbon strengthening effect is high, the carbon content in the steel is increased, the yield point and the tensile strength are increased, but the toughness is obviously reduced, and in order to improve the use safety and reliability of the bearing steel, and consider controlling and reducing the carbon segregation of the steel ingot and improving the uniformity of carbide, the carbon component is designed to be 0.93-0.98%.
The Cr element is a carbide-forming element, and mainly functions to improve the hardenability and corrosion resistance of the steel, and can improve the strength, hardness, wear resistance, elastic limit and yield limit. The distribution of carbides in the steel and the size of its particles can be significantly changed. Chromium also reduces the tendency of the steel to overheat and the rate of surface decarburization. Cr is designed according to 1.45-1.60 percent, so that the hardenability and wear resistance of the steel can be improved, the dimensional stability or the structure stability is improved, and the corrosion resistance and the antioxidation of the steel can be improved; and can prevent too high a chromium content from easily forming large carbides.
The Mn element can obviously improve the hardenability of the steel, part of Mn is dissolved in ferrite to improve the hardness and the strength of the ferrite, the shape of the steel grade S can be fixed, sulfides such as MnS and the like with small harm to the performance of the steel can be formed, and the generation of FeS can be reduced or inhibited. Mn can improve the strength of steel, weaken and eliminate the adverse effect of sulfur, improve the solid solution strengthening effect and improve the hardenability, yield strength and tensile strength of steel, and the steel grade has the components of 0.25-0.45% according to the requirement and is controlled to be 0.35-0.40% according to the upper limit so as to ensure the residual austenite amount of the steel grade and stabilize the overheating sensitivity, crack tendency and dimensional stability of the steel. However, Cr and Mn in the steel can increase the temper brittleness sensitivity of the material at 250-450 ℃, namely, the brittle transition temperature is increased, simultaneously, the impact value of toughness fracture and the fracture toughness value are reduced, in order to reduce the adverse effect of manganese, the Mo element needs to be increased, the content range of the Mo element is 0.02-0.08%, the hardenability and the tempering resistance are improved, the annealing structure is refined, the quenching deformation is reduced, the fatigue strength is improved, and the mechanical property is improved.
In order to ensure that the steel material has enough hardenability in the using process, the total content of the three elements of Si, Mn and Cr is controlled, and the total content of Si, Mn and Cr is designed to be more than or equal to 2.0 percent.
Ni is designed according to 0.05-0.10% and is the most effective alloy element for improving the toughness of steel, the toughening mechanism of the alloy is that the material matrix is easy to slide in a cross way at low temperature, and the toughness can be improved by adding Ni regardless of the structure. Meanwhile, the Cu and Mo elements are designed into a control interval, so that the comprehensive corrosion resistance better than that of Cu and Ni can be obtained, the Cu content is designed according to 0.06-0.10%, and the corrosion resistance stability of the steel is enhanced.
The Al content is designed to be 0.015-0.035%, the quality problems of low coarsening temperature and coarse grain structure of the steel due to grain size can be avoided, enough fine and dispersedly distributed refractory compound AlN is formed in the steel, the growth of austenite grains is prevented together with fine and dispersedly distributed carbon and nitride V (C, N), and the grain size grade can be improved to be more than or equal to 8.5 grade.
The designed Nb content is 0.010-0.045%, and as one of the most main microalloy elements, niobium can be dissolved in a higher temperature region of austenite and can be re-precipitated at a low temperature. Therefore, the alloy can inhibit the growth of crystal grains and can be subjected to precipitation strengthening, and is one of the most important microalloy elements in the controlled rolling and controlled cooling process. In medium-high carbon steel, the remarkable grain refinement of niobium can improve the fineness and uniformity of a microstructure, and the effect of improving the ductility and toughness of the steel is achieved; niobium is a strong carbide former and has a great influence on the diffusion of carbon and the formation of carbides. Thereby affecting the quantity, size, form and distribution of carbide and reducing the decarburization sensitivity.
The rare earth Ce has low melting point, strong affinity with harmful gases in metallurgy, strong deoxidation and desulfurization effects, molten steel purification and alloying effects, so that inclusions in steel are denatured, and various properties of the steel are improved; however, the content should not exceed 0.015% or more, since the hot workability is deteriorated, Ce is controlled to 0.010% or less.
The rare earth element Y can spheroidize the residual inclusion in the steel to refine crystal grains and prolong the service life of the bearing steel, and the Y is controlled to be less than or equal to 0.020%.
Example 2
The embodiment provides a manufacturing method of a high-end bearing steel material for a machine tool bearing ring, which comprises an electric furnace → LF refining and VD process → die casting → hot feeding/cover cooling → hot rolling → slow cooling → spheroidizing annealing;
the electric furnace comprises the following steps:
charging pig iron, molten iron or steel materials into the electric furnace, discharging oxidizing slag when the temperature of molten steel is more than or equal to 1580 ℃ and the content of C is more than or equal to 0.30%, tapping steel from the electric furnace, carburizing the molten steel during tapping, and adding novel composite slag, aluminum ingots, alloys and lime;
in the LF refining and VD process:
heating the molten steel to 1550 ℃ after reaching a refining position, adding ferrosilicon and novel composite slag for slagging, adding a diffusion deoxidizer in batches for slagging after the slag is completely smelted, and when the slag reaches the condition of a refining slag system, namely CaO 46-55 percent and SiO2≤7％，Al2O3Controlling the refining time of the white slag to realize molten steel deoxidation when the content of MgO is less than or equal to 8 percent and is 32-38 percent; after the white slag is refined, controlling the argon flow under a certain vacuum degree to perform soft blowing on the molten steel, adding a ladle covering agent after the molten steel is diffused, and continuing the soft blowing for a certain time under a certain argon flow;
in the die casting process:
pouring the molten steel after soft blowing under the protection of argon in the whole process, wherein the temperature of the molten steel is 1505-1510 ℃ during pouring, the molten steel is ensured to rise stably in the pouring process, and a certain capping feeding time is controlled;
in the heating rolling process:
heating the steel ingot with uniform and constant temperature to 850 ℃ at a certain heating rate, preserving heat for a certain time, then heating to 1230-1240 ℃ within a certain heating time, preserving heat for a certain time, and tapping and rolling, wherein the tapping temperature is 1120-1200 ℃; the initial rolling temperature is 1120 ℃, the water is cooled in the rolling process, and the final rolling temperature is 780 ℃;
in the spheroidizing annealing process:
setting the heat preservation time of the rolled steel at 810 +/-10 ℃ according to the weight of the rolled steel, then reducing the temperature to 710 +/-10 ℃ at a certain cooling speed, reducing the temperature of the steel at 710 +/-10 ℃ to 1.5 times of the heat preservation time of the steel at 810 +/-10 ℃, reducing the temperature to 500 ℃ at a certain cooling speed, preserving the heat for 1h, and finally cooling along with the furnace, discharging and air cooling.
Example 3
The difference between the present embodiment and embodiment 2 is only that, in the electric furnace process of the manufacturing method of the high-end bearing steel material for the machine tool bearing ring of the present embodiment:
charging pig iron, molten iron or steel materials into an electric furnace according to the weight ratio of 4:6, wherein the steel materials are steel materials not containing Ti; when the temperature of the molten steel is more than or equal to 1580 ℃ and the content of C is more than or equal to 0.30 percent, the oxidizing slag is discharged, the electric furnace tapping is started, the steel amount remained in the electric furnace is more than 7 tons in the tapping process, the oxidizing slag is prevented from being brought out in the tapping process, and FeO and P in the oxidizing slag are brought into the oxidizing slag in the tapping process2O5、TiO2The molten steel is reduced to P, Ti in the refining process, so that the molten steel is rephosphorized and titanium is increased, and therefore, no oxide slag is brought out in the tapping process.
Carburizing along with steel liquid steel tapping in the steel tapping process, and adding novel composite slag, aluminum ingots, alloys and lime;
taking 30-ton steel tapping as reference, and sequentially adding carbon powder, 100Kg of novel composite slag and 30Kg of aluminum ingot when 3-5 tons of steel are tapped; adding alloy when tapping for 10-15 tons; adding 200Kg of novel composite slag and 300Kg of lime again when tapping 20-25 tons; the addition amount of carbon powder is controlled by the fact that the content of C in the LF refining position is 0.85-0.95%, the addition amount of alloy is controlled by the fact that chemical components except Si in the LF refining position reach the lower limit of specification, and the content of aluminum in the LF refining position is 0.030-0.040%.
The novel composite slag in the embodiment comprises the following components in percentage by mass: CaO: 46%, MgO: 2.2% of Fe2O3：0.6％、Al2O3：40％、SiO2：0.2％，H2O: 0.17%, the balance being other metal oxides and unavoidable impurities.
The alloy used in this example includes low titanium high chromium fecr55c0.25ii and medium carbon ferromanganese femn 78c2.0;
the low-titanium high-chromium FeCr55C0.25II comprises the following components in percentage by mass: cr: 60.2%, C: 0.18%, Si: 0.7%, P: 0.03%, S: 0.02%, Ti: 0.003 percent, and the balance of Fe and inevitable impurities;
the medium carbon ferromanganese FeMn78C2.0 comprises the following components in percentage by mass: mn: 79.45%, C: 1.47%, Si: 1.62%, P: 0.191% and the balance Fe and inevitable impurities.
The high-end bearing steel material for the machine tool bearing ring, provided by the invention, is added with Ni and Mo elements and rare earth elements on the basis of the existing bearing steel material, the contents of Al and Cu are strictly controlled, and good mechanical property indexes are provided for the steel material.
Example 4
The difference between the present embodiment and embodiment 3 is only that, in the manufacturing method LF refining and VD process of the high-end bearing steel material for the machine tool bearing ring of the present embodiment:
the temperature of the molten steel starts to rise after the molten steel reaches a refining position, ferrosilicon is added in the temperature rise process, and the ferrosilicon TFeSi75-A used in the embodiment comprises the following components in percentage by mass: si: 76.7%, C: 0.01 percent of Ti, 0.013 percent of Ti, and the balance of other metal oxides and inevitable impurities;
heating the refining position to 1550 ℃, adding 250Kg of novel composite slag for slagging when the weight of the molten steel is 30 tons, and adding a diffusion deoxidizer in batches for slagging after the slag is completely smelted, wherein the diffusion deoxidizer comprises a mixture of aluminum particles and carbon powder in a weight ratio of 1:1 and a mixture of carbon powder and silicon powder in a weight ratio of 1: 1; according to the slagging condition of a refining slag system, aluminum particles and carbon powder are mixed and deoxidized in the early stage of refining, and carbon powder and silicon powder are mixed and deoxidized in the later stage;
when the slag reaches the condition of refining slag system, namely CaO 46-55%, SiO2≤7％，Al2O3Controlling the refining time of the white slag to realize molten steel deoxidation when the content of MgO is less than or equal to 8 percent and is 32-38 percent; the refining time of the white slag is more than 30min, and in order to ensure that the molten steel is fully deoxidized at the refining position, the refining time of the white slag can be further controlled to be more than 50 min.
After refining of the white slag is completed, controlling the argon flow to be 20-40 NL/min under the vacuum degree of 67Pa, carrying out soft blowing on the molten steel for 20-30 min, adding a ladle covering agent after dispersion, and carrying out soft blowing for 30-40 min under the argon flow of 10-40 NL/min;
the ladle covering agent used in the embodiment comprises the following components in percentage by mass: SiO 22：20.00～30.00％、CaO：23.00～33.00％、Al2O3: 8.00-20.00%, C: 10.00-20.00%, the rest is other metal oxides and unavoidable impurities. The ladle covering agent has the functions of heat preservation and air isolation, can reduce the temperature drop loss of the molten steel and prevent the secondary oxidation of the molten steel.
In the embodiment, CaO accounts for 46-55% and SiO accounts for2≤7％，Al2O3The refining slag system with the content of 32-38% and the content of MgO less than or equal to 8% can fully adsorb the impurities, further improve the purity of the finished steel and further reduce the level of the non-metallic impurities.
Example 5
The difference between the present embodiment and embodiment 4 is only that, in the manufacturing method die casting process of the high-end bearing steel material for the machine tool bearing ring of the present embodiment:
pouring the molten steel after soft blowing under the protection of argon with the pressure of 0.02-0.03 MPa in the whole process, wherein the distance between the lower edge of the argon protective cover and the upper edge of the horn nozzle brick is less than or equal to 200 mm;
and the ingot casting uses a class I ingot mould, the mould temperature is ensured to be 30-80 ℃, and the inner surface of the ingot mould is cleaned. When the mold is seated, the tail brick hole and the water button hole at the bottom of the mold must be aligned, the heat insulation plate assembly is flush with the lower edge of the cap opening, the gap is tightly plugged, and the cap opening of the steel ingot mold is tightly covered by an iron plate when the casting is waited, so that dust is prevented from entering the steel ingot mold.
The temperature of molten steel is 1505-1510 ℃ during pouring, and special covering slag for bearing steel is used and poured in a hanging mode in the die casting process, wherein the height of hanging is 250-300 mm from the die bottom; pouring reflux needs to be timely, pouring flow is adjusted after pouring, flow adjustment which is small and large in the pouring process is strictly forbidden, and stable rising of molten steel in the pouring process is guaranteed. Note that the cap feeding is carried out, and the cap feeding time is controlled at 240s under the condition of ensuring no scattered flow.
The special covering slag for bearing steel in the embodiment comprises the following components in percentage by mass: SiO 22：34.00～44.00％、CaO：9.00～19.00％、Al2O3Less than or equal to 12.00 percent, C: 11.00-21.00%, MgO less than or equal to 8.00%, and the balance of other metal oxides and unavoidable impurities;
the embodiment adopts the die casting process, can fully solve the problem of the water storage port in the continuous casting process, and simultaneously adopts the die casting process to cast the steel ingot, so that the segregation of carbide in the ingot is smaller than that of the continuous casting process, and a good structure can be provided for controlling the carbide in the rolling process.
Example 6
The difference between the present embodiment and embodiment 5 is only that, in the manufacturing method of the high-end bearing steel material for the machine tool bearing ring of the present embodiment, during the heating and rolling process:
putting the ingot obtained by die casting into a heating furnace in sequence, keeping the temperature of all ingots below 700 ℃ for 90min, enabling all ingots to have uniform and constant temperature, then heating the ingot to 850 ℃ at a heating rate of 75 ℃/h, keeping the temperature for 30min, reducing the temperature difference between the surface and the interior of the ingot, and improving the soaking effect; then heating the steel ingot to 1230-1240 ℃ within 3-5 h, preserving heat for 9-14 h, improving carbide segregation by high-temperature diffusion, improving carbide uniformity, and tapping after heat preservation is finished; the tapping temperature is 1120-1200 ℃; the initial rolling temperature is 1120 ℃, the water cooling is carried out in the rolling process, the cooling speed is controlled, the carbide precipitation is controlled, and the final rolling temperature is 780 ℃.
In the embodiment, the high-temperature diffusion time in the heating and rolling stage is 9-14 hours, and the carbide is effectively diffused through high-temperature diffusion; the rolling process is cooled by water, the cooling speed is controlled, and the carbide precipitation is controlled. Through high-temperature diffusion and controlled cold rolling, the carbide can be effectively diffused, so that the carbide level is further improved, and meanwhile, the low-power quality is good.
Example 7
The difference between the present embodiment and embodiment 6 is only that in the spheroidizing annealing process of the manufacturing method of the high-end bearing steel material for the machine tool bearing ring of the present embodiment:
setting the heat preservation time of the rolled steel at 810 +/-10 ℃ according to the weight of the rolled steel, wherein if the heat preservation time is T, the T is 10+ Q/2, and Q is the weight of the steel and the unit is ton;
and then reducing the temperature to 710 +/-10 ℃ at a cooling speed of 10-15 ℃/h, keeping the temperature of the steel at 710 +/-10 ℃ 1.5 times of the temperature of the steel at 810 +/-10 ℃, reducing the temperature to 500 ℃ at a cooling speed of 15-20 ℃/h, keeping the temperature for 1h, finally cooling the steel along with the furnace for 3h, and then discharging the steel out of the furnace for air cooling.
In the embodiment, spheroidizing isothermal annealing is carried out, namely, the steel is heated to 20 ℃ above AC1, the temperature is kept for 10+ Q/2, the steel is cooled to the temperature of Ar1 at the speed of less than 20 ℃/h along with a furnace to carry out isothermal treatment, the isothermal treatment time is 1.5 times of the heating and heat-preserving time, the steel is cooled to 500 ℃ along with the furnace to carry out heat preservation for 1 hour after the isothermal treatment, and the steel is naturally cooled for about 3 hours in the furnace and then taken out of the furnace for air cooling, hard and brittle lamellar pearlite and reticular cementite after hot rolling can be eliminated.
Example 8
The embodiment provides a manufacturing method of a high-end bearing steel material for a machine tool bearing ring, which comprises an electric furnace → LF refining and VD process → die casting → hot feeding/cover cooling → heating rolling → slow cooling → spheroidizing annealing;
in the process of an electric furnace:
30 tons of pig iron, molten iron or steel materials are loaded into an electric furnace, and the steel materials are steel materials without Ti; when the temperature of the molten steel is more than or equal to 1580 ℃ and the content of C is more than or equal to 0.30%, discharging the oxidizing slag, wherein the steel quantity remained in the electric furnace is more than 7 tons in the steel discharging process, and the oxidizing slag is prevented from being brought out in the steel discharging process; carburizing along with steel liquid steel tapping in the steel tapping process, and adding novel composite slag, aluminum ingots, alloys and lime;
sequentially adding carbon powder, 100Kg of novel composite slag and 30Kg of aluminum ingot when tapping for 3-5 tons; adding alloy when tapping for 10-15 tons; adding 200Kg of novel composite slag and 300Kg of lime again when tapping 20-25 tons; wherein the adding amount of carbon powder is controlled by the content of C in the position of LF refining position of 0.85-0.95%, and the content of aluminum in the position of LF refining position of 0.030-0.040%.
The novel composite slag in the embodiment comprises the following components in percentage by mass: CaO: 46%, MgO: 2.2% of Fe2O3：0.6％、Al2O3：40％、SiO2：0.2％，H2O: 0.17%, the balance being other metal oxides and unavoidable impurities.
The addition amount of the alloy is controlled by controlling the chemical components except Si in the LF refining position to reach the lower limit of the specification, and the design specification (mass percentage) of the chemical components of the bearing steel of the embodiment is shown in Table 1:
TABLE 1
Element(s) C Si Mn Cr Ni Mo Al Cu P S
Lower limit of 0.93 0.15 0.25 1.45 0.05 0.02 0.015 0.06 ≤ ≤
Upper limit of 0.98 0.35 0.45 1.60 0.10 0.08 0.035 0.10 0.010 0.008
Element(s) Nb Y Ce Ti O As Sn Sb Pb Si+Mn+Cr
Lower limit of 0.010 ≤ ≤ ≤ ≤ ≤ ≤ ≤ ≤ ≥
Upper limit of 0.045 0.020 0.010 0.0015 0.0020 0.040 0.030 0.0050 0.0020 2.0
The alloys used in this example include low titanium, high chromium and medium carbon ferromanganese;
the low-titanium high-chromium FeCr55C0.25II used in the embodiment comprises the following components in percentage by mass: cr: 60.2%, C: 0.18%, Si: 0.7%, P: 0.03%, S: 0.02%, Ti: 0.003 percent, and the balance of Fe and inevitable impurities;
the medium carbon ferromanganese femn78c2.0 used in the embodiment comprises the following components in percentage by mass: mn: 79.45%, C: 1.47%, Si: 1.62%, P: 0.191% and the balance Fe and inevitable impurities.
The adding amount of low titanium and high chromium is 19.5Kg/t and the adding amount of medium carbon ferromanganese is 2.3Kg/t in terms of the unit of adding amount of steel per ton,
in the LF refining and VD process:
the temperature of the molten steel starts to rise after the molten steel reaches a refining position, ferrosilicon is added in the temperature rise process, and the ferrosilicon TFeSi75-A used in the embodiment comprises the following components in percentage by mass: si: 76.7%, C: 0.01 percent of Ti, 0.013 percent of Ti and the balance of other metal oxides and inevitable impurities, wherein the addition amount of the ferrosilicon is calculated by the unit of the addition amount of each ton of steel; 1.8 Kg/t.
Heating the refining position to 1550 ℃, adding 250Kg of novel composite slag for slagging when the weight of the molten steel is 30 tons, and adding a diffusion deoxidizer in batches for slagging after the slag is completely smelted, wherein the diffusion deoxidizer comprises a mixture of aluminum particles and carbon powder in a weight ratio of 1:1 and a mixture of carbon powder and silicon powder in a weight ratio of 1: 1; according to the slagging condition of a refining slag system, 30-40 kg of aluminum particles and carbon powder are mixed and deoxidized in the early stage of refining, and 60-80 kg of carbon powder and silicon powder are mixed and deoxidized in the later stage;
when the slag reaches the condition of refining slag system, namely CaO 46-55%, SiO2≤7％，Al2O3Controlling the refining time of the white slag to realize molten steel deoxidation when the content of MgO is less than or equal to 8 percent and is 32-38 percent; the refining time of the white slag is more than 30min, and in order to ensure that the molten steel is fully deoxidized at the refining position, the refining time of the white slag can be further controlled to be more than 50 min.
After refining of the white slag is completed, controlling the argon flow to be 20-40 NL/min under the vacuum degree of 67Pa, carrying out soft blowing on the molten steel for 20-30 min, adding a ladle covering agent after dispersion, and carrying out soft blowing for 30-40 min under the argon flow of 10-40 NL/min;
the ladle covering agent used in the embodiment comprises the following components in percentage by mass: SiO 22：20.00～30.00％、CaO：23.00～33.00％、Al2O3: 8.00-20.00%, C: 10.00-20.00%, the rest is other metal oxides and unavoidable impurities.
In the die casting process:
pouring the molten steel after soft blowing under the protection of argon with the pressure of 0.02-0.03 MPa in the whole process, wherein the distance between the lower edge of the argon protective cover and the upper edge of the horn nozzle brick is less than or equal to 200 mm;
and the ingot casting uses a class I ingot mould, the mould temperature is ensured to be 30-80 ℃, and the inner surface of the ingot mould is cleaned. When the mold is seated, the tail brick hole and the water button hole at the bottom of the mold must be aligned, the heat insulation plate assembly is flush with the lower edge of the cap opening, the gap is tightly plugged, and the cap opening of the steel ingot mold is tightly covered by an iron plate when the casting is waited, so that dust is prevented from entering the steel ingot mold.
The temperature of molten steel is 1505-1510 ℃ during pouring, and special covering slag for bearing steel is used and poured in a hanging mode in the die casting process, wherein the height of hanging is 250-300 mm from the die bottom; pouring reflux needs to be timely, pouring flow is adjusted after pouring, flow adjustment which is small and large in the pouring process is strictly forbidden, and stable rising of molten steel in the pouring process is guaranteed. Note that the cap feeding is carried out, and the cap feeding time is controlled at 240s under the condition of ensuring no scattered flow.
The special covering slag for bearing steel in the embodiment comprises the following components in percentage by mass: SiO 22：34.00～44.00％、CaO：9.00～19.00％、Al2O3Less than or equal to 12.00 percent, C: 11.00-21.00%, MgO less than or equal to 8.00%, and the balance of other metal oxides and unavoidable impurities;
in the heating rolling process:
putting the ingot obtained by die casting into a heating furnace in sequence, keeping the temperature of all ingots below 700 ℃ for 90min, enabling all ingots to have uniform and constant temperature, then heating the ingot to 850 ℃ at a heating rate of 75 ℃/h, keeping the temperature for 30min, reducing the temperature difference between the surface and the interior of the ingot, and improving the soaking effect; then heating the steel ingot to 1230-1240 ℃ within 3-5 h, preserving heat for 9-14 h, improving carbide segregation by using high-temperature diffusion, improving carbide uniformity, tapping after heat preservation is finished, and tapping at 1120-1200 ℃; the initial rolling temperature is 1120 ℃, the water cooling is carried out in the rolling process, the cooling speed is controlled, the carbide precipitation is controlled, and the final rolling temperature is 780 ℃.
In the spheroidizing annealing process:
setting the heat preservation time of the rolled steel at 810 +/-10 ℃ according to the weight of the rolled steel, wherein if the heat preservation time is T, the T is 10+ Q/2, and Q is the weight of the steel and the unit is ton;
and then reducing the temperature to 710 +/-10 ℃ at a cooling speed of 10-15 ℃/h, keeping the temperature of the steel at 710 +/-10 ℃ 1.5 times of the temperature of the steel at 810 +/-10 ℃, reducing the temperature to 500 ℃ at a cooling speed of 15-20 ℃/h, keeping the temperature for 1h, finally cooling the steel along with the furnace for 3h, and then discharging the steel out of the furnace for air cooling.
The chemical compositions (mass percent) of the finished bearing steel produced in this example were examined, and the results are shown in table 2:
TABLE 2
Heat \ composition C Si Mn Cr Ni Mo Al Cu P S
1# 0.96 0.25 0.35 1.50 0.07 0.05 0.020 0.08 0.006 0.005
Heat \ composition Nb Y Ce Ti O As Sn Sb Pb Si+Mn+Cr
1# 0.015 0.007 0.050 0.0014 0.0009 0.001 0.01 0.001 0.01 2.1
Compared with the GCr15 material under the GB/T18254 condition, the bearing steel produced by the embodiment increases Ni, Mo and rare earth elements on the basis of raw materials, strictly controls the contents of Al and Cu, and provides good mechanical property indexes for the material.
FIG. 1 is a photomicrograph of a high-end bearing steel material for a machine tool bearing ring produced according to the present embodiment; the macroscopic center porosity of the strain is rated as 1.0, the general porosity is rated as 0, and the segregation is rated as 0. Therefore, the bearing steel material prepared by the embodiment has good macrostructure, and shows that the material is more compact.
The high-end bearing steel material for the machine tool bearing ring produced in the embodiment is used for cutting a metallographic sample according to the sampling requirement of GB/T18254-2002, after the width direction of the polished surface is parallel to the hot working axis, the metallographic sample is placed under a high-quality metallographic microscope for observation, an image analyzer is used for collecting bright field images, the bright field images are magnified by 100 times for observation, the results of inclusion inspection are shown in Table 3,
TABLE 3
A is thin Coarse A B is thin B coarse Fine diameter of C Coarse fraction of C D is thin D coarse Ds Number of TiN not more than 19um
0 0 0.5 0 0 0 0.5 0.5 0 0
0 0.5 0 0 0 0 0.5 0.5 0 0
0 0.5 0.5 0 0 0 0.5 0.5 0 0
0 0 0 0 0 0 0.5 0.5 0 0
0 0 0 0 0 0 0.5 0.5 0 0
0 0 0.5 0 0 0 0.5 0.5 0 0
FIG. 2 is a photograph of a metallographic microscope showing the examination of nonmetallic inclusions of a high-end bearing steel material for a machine tool bearing ring produced in accordance with the present embodiment at 100 times magnification; the length of the nonmetallic inclusions in this figure is 2 μm, and the inclusions are DS inclusions. FIG. 3 is a photograph of a metallographic microscope showing the examination of nonmetallic inclusions of a high-end bearing steel material for a machine tool bearing ring produced in accordance with the present embodiment at 100 times magnification; the length of the nonmetallic inclusions in this figure is 2 μm, and the inclusions are DS inclusions.
Therefore, the bearing steel material produced by the process method has small size of non-metallic inclusions, has high purity, and can further improve the tensile strength, blank strength and other properties of the steel material.
And (4) carrying out microscope to compare the shapes of the characteristic carbides and the gray level difference between the characteristic carbides and the matrix to complete identification and grading of the characteristic carbides.
FIG. 5 is a carbide mesh picture of a high-end bearing steel material for a machine tool bearing ring produced in example 8 of the present invention, which is collected under a metallographic microscope and magnified by 200 times in a bright field image.
FIG. 4 is a carbide strip photograph of a high-end bearing steel material for a machine tool bearing ring produced in the present example, which is obtained by collecting bright field images under a metallographic microscope and enlarging the images by 100 times, wherein the photograph shows that the carbide strip is ranked at 1.0; FIG. 5 is a photograph of a carbide network obtained by collecting a bright field image of a high-end bearing steel material for a machine tool bearing ring produced in this example under a metallographic microscope at a magnification of 200 times, showing that the carbide band is rated at 1.0.
Therefore, the steel material prepared by the embodiment has better grading results of the band shape and the net shape of the carbide, which shows that the carbide in the steel material is distributed more uniformly, and the dimensional stability and the structure stability of the steel material can be further improved. The new material produced by the process can provide higher elastic limit, tensile strength and contact fatigue strength, high hardenability and necessary hardenability for further processing and producing bearing rings or rolling bodies and the like so as to ensure high wear resistance and certain impact toughness; good dimensional or tissue stability; can effectively reduce the phenomena of material fatigue peeling, seizing and the like. The bearing ring is suitable for manufacturing machine tools.

Claims (4)

1. A manufacturing method of a high-end bearing steel material for a machine tool bearing ring is characterized by comprising the steps of electric furnace → LF refining and VD process → die casting → hot feeding/cover cooling → hot rolling → slow cooling → spheroidizing annealing;
the electric furnace comprises the following steps:
charging pig iron, molten iron or steel materials into an electric furnace, discharging oxide slag when the temperature of molten steel is more than or equal to 1580 ℃ and the content of C is more than or equal to 0.30%, tapping steel from the electric furnace, carburizing the molten steel, adding composite slag, aluminum ingots, alloys and lime along with the tapped molten steel in the tapping process, and sequentially adding carbon powder, composite slag and aluminum ingots when tapping 3-5 tons; adding alloy when tapping for 10-15 tons; adding the composite slag and lime again when tapping for 20-25 tons; the adding amount of carbon powder is controlled by the fact that the content of C in the LF refining position is 0.85-0.95%, the adding amount of alloy reaches the lower limit of specification by the fact that chemical components except Si in the LF refining position reach the lower limit, and the content of aluminum in the LF refining position is 0.030-0.040%;
the alloy comprises low-titanium high-chromium and medium-carbon ferromanganese;
the low-titanium high-chromium alloy comprises the following components in percentage by mass: cr: 60.2%, C: 0.18%, Si: 0.7%, P: 0.03%, S: 0.02%, Ti: 0.003 percent, and the balance of Fe and inevitable impurities;
the medium carbon ferromanganese comprises the following components in percentage by mass: mn: 79.45%, C: 1.47%, Si: 1.62%, P: 0.191 percent, and the balance of Fe and inevitable impurities; the composite slag comprises the following components in percentage by mass: CaO: 46%, MgO: 2.2% of Fe2O3：0.6%、Al2O3：40%、SiO2：0.2%，H2O: 0.17 percent, and the balance of other metal oxides and inevitable impurities;
in the LF refining and VD process:
heating the molten steel to 1550 ℃ after the molten steel reaches a refining position, adding ferrosilicon and composite slag for slagging, adding a diffusion deoxidizer in batches for slagging after the slag is completely smelted, and when the slag reaches the condition of a refining slag system, namely CaO 46-55 percent and SiO2≤7%，Al2O3Controlling the white slag refining time to realize molten steel deoxidation when the content of MgO is less than or equal to 8%, wherein the white slag refining time is 30-50 min; after refining the white slag, controlling the flow of argon to be 20-40 NL/min under the condition that the vacuum degree is less than or equal to 67Pa, carrying out soft blowing on the molten steel for 20-30 min, adding a ladle covering agent after dispersion, and continuing soft blowing for 30-40 min under the condition that the flow of argon is 10-40 NL/min;
the ferrosilicon comprises the following components in percentage by mass: si: 76.7%, C: 0.01 percent of Ti, 0.013 percent of Ti, and the balance of other metal oxides and inevitable impurities;
the diffusion deoxidizer comprises a mixture of aluminum particles and carbon powder in a weight ratio of 1:1 and a mixture of carbon powder and silicon powder in a weight ratio of 1: 1; according to the slagging condition of a refining slag system, aluminum particles and carbon powder are mixed and deoxidized in the early stage of refining, and carbon powder and silicon powder are mixed and deoxidized in the later stage;
the ladle covering agent comprises the following components in percentage by mass: SiO 22：20.00~30.00%、CaO：23.00~33.00%、Al2O3: 8.00-20.00%, C: 10.00-20.00%, the balance being other metal oxides and unavoidable impurities;
in the die casting process:
pouring the molten steel after soft blowing under the protection of argon in the whole process, wherein the temperature of the molten steel is 1505-1510 ℃ during pouring, the molten steel is ensured to rise stably in the pouring process, and a certain capping feeding time is controlled;
in the heating rolling process:
heating the steel ingot with uniform and constant temperature to 850 ℃ at a certain heating rate, preserving heat for a certain time, then heating to 1230-1240 ℃ within a certain heating time, preserving heat for a certain time, and tapping and rolling, wherein the tapping temperature is 1120-1200 ℃; the initial rolling temperature is 1120 ℃, the water is cooled in the rolling process, and the final rolling temperature is 780 ℃;
in the spheroidizing annealing process:
setting the heat preservation time of the rolled steel at 810 +/-10 ℃ according to the weight of the rolled steel, then reducing the temperature to 710 +/-10 ℃ at a certain cooling speed, reducing the temperature of the steel at 710 +/-10 ℃ to 1.5 times of the heat preservation time of the steel at 810 +/-10 ℃, reducing the temperature to 500 ℃ at a certain cooling speed, preserving the heat for 1h, and finally cooling along with the furnace, discharging and air cooling;
the high-end bearing steel material for the machine tool bearing ring comprises the following chemical components in percentage by mass: 0.93-0.98%, Si: 0.15 to 0.35%, Mn: 0.25-0.45%, Cr: 1.45-1.60%, Ni: 0.05 to 0.10%, Mo: 0.02-0.08%, Al: 0.015-0.035%, Cu: 0.06-0.10%, P is less than or equal to 0.010%, S is less than or equal to 0.008%, Nb: 0.010-0.045%, less than or equal to 0.020% of Y, less than or equal to 0.010% of Ce, less than or equal to 0.0015% of Ti, less than or equal to 0.0020% of O, less than or equal to 0.040% of As, less than or equal to 0.030% of Sn, less than or equal to 0.0050% of Sb, less than or equal to 0.0020% of Pb, more than or equal to 2.0% of Si + Mn + Cr, and the balance of Fe and inevitable.
2. The manufacturing method of the high-end bearing steel material for the machine tool bearing ring according to claim 1, characterized in that in the die casting process, the pressure of the protective argon is 0.02-0.03 MPa, the special protective slag for the bearing steel is used and is poured by adopting a hanging mode,
the special covering slag for bearing steel comprises the following components in percentage by mass: SiO 22：34.00~44.00%、CaO：9.00~19.00%、Al2O3Less than or equal to 12.00 percent, C: 11.00-21.00%, MgO less than or equal to 8.00%, and the balance of other metal oxides and unavoidable impurities;
the height of the hanger is 250-300 mm from the die bottom; the feeding time of the cap opening is 240 s.
3. The manufacturing method of the high-end bearing steel material for the machine tool bearing ring according to claim 2, wherein in the heating rolling process, the steel ingot with uniform and constant temperature is kept at 500-700 ℃ for 90min to reach uniform and constant temperature; the temperature rising speed is 75 ℃/h; the heat preservation time at 850 ℃ is 30 min; the temperature rise time is 3-5 h; the heat preservation time at 1230-1240 ℃ is 9-14 h.
4. The method for manufacturing a high-end bearing steel material for a machine tool bearing ring according to claim 3, wherein the heat preservation time of the steel material at 810 ± 10 ℃ in the spheroidizing annealing process is T, T =10+ Q/2, wherein Q is the weight of the steel material in ton; the cooling speed of cooling to 710 +/-10 ℃ is 10-15 ℃/h; the cooling speed of cooling to 500 ℃ is 15-20 ℃/h.
CN201910676601.7A 2019-07-25 2019-07-25 High-end bearing steel material for machine tool bearing ring and manufacturing method thereof Active CN110257717B (en)