CN110255941A - A kind of desulfurized gypsum reuse method - Google Patents
A kind of desulfurized gypsum reuse method Download PDFInfo
- Publication number
- CN110255941A CN110255941A CN201910685570.1A CN201910685570A CN110255941A CN 110255941 A CN110255941 A CN 110255941A CN 201910685570 A CN201910685570 A CN 201910685570A CN 110255941 A CN110255941 A CN 110255941A
- Authority
- CN
- China
- Prior art keywords
- desulfurized gypsum
- slag
- follows
- wet slag
- granulated blast
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of desulfurized gypsum reuse methods, and desulfurized gypsum is added to wet slag and is prepared in ground granulated blast furnace slag process, mixed ground granulated blast furnace slag;Before the mixed ground granulated blast furnace slag preparation, to desulfurized gypsum and wet slag is ground and data comparison, specifically: A, sample drying;B, it is crushed, mixing and C, each self-grind acquisition grinding data simultaneously compare, desulfurized gypsum reuse method of the invention, produce not influencing just to generate, utilize desulfurized gypsum under the premise of not reducing ground granulated blast furnace slag quality;Requirements of the national standard is fully achieved in the product of preparation, has very high utility value in the utilization of cement, mortar and concrete and uses meaning.
Description
Technical field
The present invention relates to the waste utilization techniques in a kind of steelmaking process, and in particular to a kind of desulfurized gypsum recycling side
Method belongs to the waste utilization technology field in steelmaking process.
Background technique
Desulfurized gypsum is sulfur removal technology byproduct, and country's recycling and reusing is low at present, few mainly by pad ditch, pad road
Number for cement mixing adjust cement setting time, improve strength of cement, such as Chinese Patent Application No.:
200810030651.X the desulfurization gypsum slurrying batching method in manufacture of cement, belongs to technical field of cement production.Starchiness and
Powdered desulfurized gypsum is all not easy to the use of cement plant measuring belt scale ingredient.The invention is characterized in that desulfurized gypsum and water
Charge ratio (weight) are as follows: desulfurized gypsum: water=1: 1 ~ 5, according to charge ratio, sticky desulfurized gypsum and water are launched to stirring
Mixed diluting in machine, is stirred with blender, and the desulfurized gypsum dilution for meeting concentration requirement is made;Desulfurized gypsum dilution
With the charge ratio (weight) of clinker are as follows: desulfurized gypsum dilution: clinker=1: 4 ~ 8, according to charge ratio, shape will be stirred
It is ripe that desulfurized gypsum dilution under state by slush pump conveying, by flowmeter regime flow and by nozzle is ejected into cement
On material, but since the desulfurized gypsum moisture of steel plant's discharge is larger, outward transport utilization rate is relatively low, and normal time accumulation is caused to cause ring
Border pollution.
Summary of the invention
To solve the above problems, passing through desulfurized gypsum and wet mine the invention proposes a kind of desulfurized gypsum reuse method
Slag co-ground makes ground granulated blast furnace slag, and meeting its finished product, " GB/T 18046-2017 is for cement, mortar and mixes
Ground granulated blast furnace slag in solidifying soil " technical requirements.
Desulfurized gypsum is added to wet slag and prepares ground granulated blast furnace slag work by desulfurized gypsum reuse method of the invention
In sequence, mixed ground granulated blast furnace slag.
Further, the wet slag and desulfurized gypsum weight ratio are as follows: 10:1.
Further, the wet slag, desulfurized gypsum and desulfurized gypsum weight ratio are as follows: 10:5:1.
Further, before the mixed ground granulated blast furnace slag preparation, to desulfurized gypsum and wet slag grinding and data
Comparison.
Further, the grinding and data comparison are specific as follows:
A, sample is dried;Before grinding, desulfurized gypsum and wet slag are put into 105 DEG C of drying boxes and dried;
B, it is crushed, mixing, after completing drying, then desulfurized gypsum is sent into jaw crusher and breakage is carried out to roller, cross 5mm square hole
Sieve makes its granularity whole≤5mm, completes to mix well in feeding V-type batch mixer after being sieved;
C, each self-grind acquisition grinding data simultaneously compare, specific as follows:
A, wet slag 5000g grinds 120min;Inspection data is as follows: density 2.9g/cm3, specific surface area 450m2/ kg, 7d is living
Sex index: 95%, 28 days activity indexs 110%, presetting periods are than 119%, chloride ion: 0.03%, loss on ignition: 0.4%, insoluble matter:
0.1%, sulfur trioxide: 0.2%, fluidity ratio: 103%;
B, wet slag 5000g, desulfurized gypsum 500g grind 120min;Inspection data density 3.3g/cm3, specific surface area 468m2/
Kg, 7d activity index: 100%, 28 days activity indexs 106%, presetting periods are than 115%, chloride ion: 0.04%, loss on ignition: 0.8%,
Insoluble matter: 0.3%, sulfur trioxide: 0.6%, fluidity ratio: 110%;
C, wet slag 5000g, desulfurized gypsum 1000g grind 120min;Inspection data are as follows: density 3.7g/cm3, specific surface area
480m2/ kg, 7d activity index: 107%, 28 days activity indexs 110%, presetting periods are than 111%, chloride ion: 0.05%, loss on ignition:
0.9%, insoluble matter: 0.7%, sulfur trioxide: 0.9%, fluidity ratio: 108%;
D, wet slag 5000g, desulfurized gypsum 500g grind 110min.Inspection data are as follows: density 3.3g/cm3, specific surface area
445m2/ kg, 7d activity index: 96%, 28 days activity indexs 108%, presetting periods are than 115%, chloride ion: 0.04%, loss on ignition:
0.8%, insoluble matter: 0.3%, sulfur trioxide: 0.6%, fluidity ratio: 110%.
Compared with prior art, desulfurized gypsum reuse method of the invention is not influencing just to generate production, no the present invention
Desulfurized gypsum is utilized under the premise of reducing ground granulated blast furnace slag quality;Requirements of the national standard is fully achieved in the product of preparation,
There is very high utility value in cement, mortar and concrete utilization and uses meaning.
Specific embodiment
Desulfurized gypsum is added to wet slag and prepares ground granulated blast furnace slag work by desulfurized gypsum reuse method of the invention
In sequence, mixed ground granulated blast furnace slag.
In another embodiment, the wet slag and desulfurized gypsum weight ratio are as follows: 10:1.
In another embodiment, the wet slag, desulfurized gypsum and desulfurized gypsum weight ratio are as follows: 10:5:1.
Wherein, before the mixed ground granulated blast furnace slag preparation, to desulfurized gypsum and wet slag grinding and data comparison;
The grinding and data comparison are specific as follows:
A, sample is dried;Before grinding, desulfurized gypsum and wet slag are put into 105 DEG C of drying boxes and dried;
B, it is crushed, mixing, after completing drying, then desulfurized gypsum is sent into jaw crusher and breakage is carried out to roller, cross 5mm square hole
Sieve makes its granularity whole≤5mm, completes to mix well in feeding V-type batch mixer after being sieved;
C, each self-grind acquisition grinding data simultaneously compare, specific as follows:
A, wet slag 5000g grinds 120min;Inspection data is as follows: density 2.9g/cm3, specific surface area 450m2/ kg, 7d is living
Sex index: 95%, 28 days activity indexs 110%, presetting periods are than 119%, chloride ion: 0.03%, loss on ignition: 0.4%, insoluble matter:
0.1%, sulfur trioxide: 0.2%, fluidity ratio: 103%;
B, wet slag 5000g, desulfurized gypsum 500g grind 120min;Inspection data density 3.3g/cm3, specific surface area 468m2/
Kg, 7d activity index: 100%, 28 days activity indexs 106%, presetting periods are than 115%, chloride ion: 0.04%, loss on ignition: 0.8%,
Insoluble matter: 0.3%, sulfur trioxide: 0.6%, fluidity ratio: 110%;
C, wet slag 5000g, desulfurized gypsum 1000g grind 120min;Inspection data are as follows: density 3.7g/cm3, specific surface area
480m2/ kg, 7d activity index: 107%, 28 days activity indexs 110%, presetting periods are than 111%, chloride ion: 0.05%, loss on ignition:
0.9%, insoluble matter: 0.7%, sulfur trioxide: 0.9%, fluidity ratio: 108%;
D, wet slag 5000g, desulfurized gypsum 500g grind 110min.Inspection data are as follows: density 3.3g/cm3, specific surface area
445m2/ kg, 7d activity index: 96%, 28 days activity indexs 108%, presetting periods are than 115%, chloride ion: 0.04%, loss on ignition:
0.8%, insoluble matter: 0.3%, sulfur trioxide: 0.6%, fluidity ratio: 110%.
Above-described embodiment is only better embodiment of the invention, therefore all according to structure described in present patent application range
It makes, the equivalent change or modification that feature and principle are done, is included in the scope of the patent application of the present invention.
Claims (5)
1. a kind of desulfurized gypsum reuse method, it is characterised in that: desulfurized gypsum is added to wet slag and prepares granulated blast-furnace mine
In ground-slag process, mixed ground granulated blast furnace slag.
2. desulfurized gypsum reuse method according to claim 1, it is characterised in that: the wet slag and desulfurized gypsum weight
Measure ratio are as follows: 10:1.
3. desulfurized gypsum reuse method according to claim 1, it is characterised in that: the wet slag, desulfurized gypsum and
Desulfurized gypsum weight ratio are as follows: 10:5:1.
4. desulfurized gypsum reuse method according to claim 1, it is characterised in that: the mixed granulated blast-furnace slag
Before powder preparation, to desulfurized gypsum and wet slag grinding and data comparison.
5. desulfurized gypsum reuse method according to claim 4, it is characterised in that: the grinding and data comparison are specific
It is as follows:
A, sample is dried;Before grinding, desulfurized gypsum and wet slag are put into 105 DEG C of drying boxes and dried;
B, it is crushed, mixing, after completing drying, then desulfurized gypsum is sent into jaw crusher and breakage is carried out to roller, cross 5mm square hole
Sieve makes its granularity whole≤5mm, completes to mix well in feeding V-type batch mixer after being sieved;
C, each self-grind acquisition grinding data simultaneously compare, specific as follows:
A, wet slag 5000g grinds 120min;Inspection data is as follows: density 2.9g/cm3, specific surface area 450m2/ kg, 7d activity
Index: 95%, 28 days activity indexs 110%, presetting periods are than 119%, chloride ion: 0.03%, loss on ignition: 0.4%, insoluble matter:
0.1%, sulfur trioxide: 0.2%, fluidity ratio: 103%;
B, wet slag 5000g, desulfurized gypsum 500g grind 120min;Inspection data density 3.3g/cm3, specific surface area 468m2/
Kg, 7d activity index: 100%, 28 days activity indexs 106%, presetting periods are than 115%, chloride ion: 0.04%, loss on ignition: 0.8%,
Insoluble matter: 0.3%, sulfur trioxide: 0.6%, fluidity ratio: 110%;
C, wet slag 5000g, desulfurized gypsum 1000g grind 120min;Inspection data are as follows: density 3.7g/cm3, specific surface area
480m2/ kg, 7d activity index: 107%, 28 days activity indexs 110%, presetting periods are than 111%, chloride ion: 0.05%, loss on ignition:
0.9%, insoluble matter: 0.7%, sulfur trioxide: 0.9%, fluidity ratio: 108%;
D, wet slag 5000g, desulfurized gypsum 500g grind 110min;Inspection data are as follows: density 3.3g/cm3, specific surface area
445m2/ kg, 7d activity index: 96%, 28 days activity indexs 108%, presetting periods are than 115%, chloride ion: 0.04%, loss on ignition:
0.8%, insoluble matter: 0.3%, sulfur trioxide: 0.6%, fluidity ratio: 110%.