CN110254104A - A kind of process of surface treatment of transparent material - Google Patents
A kind of process of surface treatment of transparent material Download PDFInfo
- Publication number
- CN110254104A CN110254104A CN201910546560.XA CN201910546560A CN110254104A CN 110254104 A CN110254104 A CN 110254104A CN 201910546560 A CN201910546560 A CN 201910546560A CN 110254104 A CN110254104 A CN 110254104A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- spray
- surface treatment
- water
- transparent material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of process of surface treatment of transparent material, include the following steps: S1, spray-applied primer: in the back side spray-applied primer of workpiece to be processed；S2, water transfer: being pre-printed with required pattern for water-soluble film, makes the activation of the pattern on film at ink state using solvent, pattern is needed on by print workpiece using hydraulic pressure, will be rinsed with water completely by remaining impurity on print workpiece, and then be baked to；S3, topcoating: being protected spraying PU transparent varnish by the surface of print workpiece, the body surface for having sprayed finishing coat be dried, and obtains finished product after dry.Water is transferred the ontology front spray-applied primer in production technology and is changed as ontology back side spray-applied primer by the present invention, the finished product finished has translucent effect when there is light emitting source at product rear, light emitting source can be shown in product front, it solves the prior art and is limited only to surface treatment texture, if the problem that product rear has light emitting source that can not be shown in product front.
Description
Technical field
The present invention relates to transparent material processing technique field, specially a kind of process of surface treatment of transparent material.
Background technique
Water transfer is to do dissolution medium using water the transfer paper with multicolour pattern or transfer film are carried out the one of picture and text transfer
Kind printing.The purposes of the raising of requirement with people to product packaging and decoration, water transfer is more and more extensive.Its indirect printing
Principle and perfect printing effect solve the problems, such as many product surfaces decoration, it is more complicated to be mainly used for various shape
The transfer of product surface picture and text.
Water transfer technique has two classes, and one is water gauge transfer technique, another kind is water coating transfer technique.The former is main complete
At the transfer of text and description pattern, the latter then tends to completely be transferred in entire product surface.Coating transfer technique makes
Picture and text are carried with the aqueous film in a kind of dissolve easily in water.Since water coating membrane tension is splendid, it is easy to be wound in
Product surface forms picture and text layer, and product surface obtains completely different appearance just as spray painting.It is coated on the work of any shape
On part, solve the problems, such as that stereo product prints for manufacturer.It is curved draped also to add different lines, such as skin in product surface
Line, wood grain, emerald line and marble line etc., while also can avoid the diastema often occurred in general space of a whole page stamp.And in printing-flow,
It can be avoided because needing to spray one layer of priming paint increase adhesion strength or addition background color so product surface is not required to contact with print film
Damage product surface and its integrality.
Existing water transfer production technology is first in material front spray-applied primer, and then water transfers, and sprays matt and spray
Shipment after painting bloom UV, this technique is limited only to surface treatment texture, if product rear has light emitting source that can not be shown in product just
Face, for this purpose, it is proposed that a kind of process of surface treatment of transparent material.
Summary of the invention
The purpose of the present invention is to provide a kind of process of surface treatment of transparent material, to solve to mention in above-mentioned background technique
Out the problem of.
To achieve the above object, the invention provides the following technical scheme: a kind of process of surface treatment of transparent material, including
Following steps:
S1, spray-applied primer: in the back side spray-applied primer of workpiece to be processed；
S2, water transfer: being pre-printed with required pattern for water-soluble film, makes the activation of the pattern on film at oil using solvent
Pattern is needed on by print workpiece using hydraulic pressure, will be rinsed with water completely, then by remaining impurity on print workpiece by ink-condition
It will be dried by print workpiece；
S3, topcoating: being protected spraying PU transparent varnish by the surface of print workpiece, will spray the body surface of finishing coat
It is dried, obtains finished product after dry.
Preferably, the base coat thickness sprayed in the step S1 is 5-50 μm.
Preferably, metal, ceramics and glass pieces are put into the temperature baking in oven with 140 DEG C in the step S2
20min, plastic workpiece are put into oven and toast 60min with 70 DEG C of temperature.
Preferably, it will be put into oven by print workpiece after spray paint in the step S3 dry with 70 DEG C of temperature
12h。
Preferably, spraying sub-gloss varnish is also needed in the step S3, then sprays bloom ultraviolet-cured paint.
Compared with prior art, the beneficial effects of the present invention are: water is transferred the ontology front in production technology by the present invention
Spray-applied primer is changed as ontology back side spray-applied primer, and the finished product so finished has translucent effect when there is light emitting source at product rear
When, light emitting source can be shown in product front, the prior art is solved and be limited only to surface treatment texture, if product rear has
Light emitting source can not be shown in the problem in product front.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The present invention provides a kind of technical solution: a kind of process of surface treatment of transparent material includes the following steps:
S1, spray-applied primer: in the back side spray-applied primer of workpiece to be processed；
S2, water transfer: being pre-printed with required pattern for water-soluble film, makes the activation of the pattern on film at oil using solvent
Pattern is needed on by print workpiece using hydraulic pressure, will be rinsed with water completely, then by remaining impurity on print workpiece by ink-condition
It will be dried by print workpiece；
S3, topcoating: being protected spraying PU transparent varnish by the surface of print workpiece, will spray the body surface of finishing coat
It is dried, obtains finished product after dry.
Embodiment one:
A kind of process of surface treatment of transparent material, includes the following steps:
S1, spray-applied primer: in the back side spray-applied primer of workpiece to be processed, the base coat thickness of spraying is 5-50 μm；
S2, water transfer: being pre-printed with required pattern for water-soluble film, makes the activation of the pattern on film at oil using solvent
Pattern is needed on by print workpiece using hydraulic pressure, will be rinsed with water completely, then by remaining impurity on print workpiece by ink-condition
It will be dried by print workpiece；
S3, topcoating: being protected spraying PU transparent varnish by the surface of print workpiece, will spray the body surface of finishing coat
It is dried, obtains finished product after dry.
Embodiment two:
A kind of process of surface treatment of transparent material, includes the following steps:
S1, spray-applied primer: in the back side spray-applied primer of workpiece to be processed, the base coat thickness of spraying is 5-50 μm；
S2, water transfer: being pre-printed with required pattern for water-soluble film, makes the activation of the pattern on film at oil using solvent
Pattern is needed on by print workpiece using hydraulic pressure, will be rinsed with water completely, then by remaining impurity on print workpiece by ink-condition
It will be dried by print workpiece, metal, ceramics and glass pieces are put into oven and toast 20min with 140 DEG C of temperature, and plastic workpiece is put
Enter in oven and toasts 60min with 70 DEG C of temperature；
S3, topcoating: being protected spraying PU transparent varnish by the surface of print workpiece, will spray the body surface of finishing coat
It is dried, obtains finished product after dry.
Embodiment three:
A kind of process of surface treatment of transparent material, includes the following steps:
S1, spray-applied primer: in the back side spray-applied primer of workpiece to be processed, the base coat thickness of spraying is 5-50 μm；
S2, water transfer: being pre-printed with required pattern for water-soluble film, makes the activation of the pattern on film at oil using solvent
Pattern is needed on by print workpiece using hydraulic pressure, will be rinsed with water completely, then by remaining impurity on print workpiece by ink-condition
It will be dried by print workpiece, metal, ceramics and glass pieces are put into oven and toast 20min with 140 DEG C of temperature, and plastic workpiece is put
Enter in oven and toasts 60min with 70 DEG C of temperature；
S3, topcoating: being protected spraying PU transparent varnish by the surface of print workpiece, will spray the body surface of finishing coat
It is dried, obtains finished product after dry, the dry 12h of temperature that will be put by print workpiece in oven with 70 DEG C after spray paint,
Make to spend face together with by print workpiece permanent bond.
Example IV:
A kind of process of surface treatment of transparent material, includes the following steps:
S1, spray-applied primer: in the back side spray-applied primer of workpiece to be processed, the base coat thickness of spraying is 5-50 μm；
S2, water transfer: being pre-printed with required pattern for water-soluble film, makes the activation of the pattern on film at oil using solvent
Pattern is needed on by print workpiece using hydraulic pressure, will be rinsed with water completely, then by remaining impurity on print workpiece by ink-condition
It will be dried by print workpiece, metal, ceramics and glass pieces are put into oven and toast 20min with 140 DEG C of temperature, and plastic workpiece is put
Enter in oven and toasts 60min with 70 DEG C of temperature；
S3, topcoating: being protected spraying PU transparent varnish by the surface of print workpiece, will spray the body surface of finishing coat
It is dried, obtains finished product after dry, the dry 12h of temperature that will be put by print workpiece in oven with 70 DEG C after spray paint,
Make to spend face together with by print workpiece permanent bond, also needs spraying sub-gloss varnish, then spray bloom ultraviolet-cured paint.
Water is transferred the ontology front spray-applied primer in production technology and is changed as ontology back side spray-applied primer by the present invention, such as
This finished product finished has translucent effect when there is light emitting source at product rear, and light emitting source can be shown in product front, solved
The prior art is limited only to surface treatment texture, if the problem that product rear has light emitting source that can not be shown in product front.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (5)
1. a kind of process of surface treatment of transparent material, characterized by the following steps:
S1, spray-applied primer: in the back side spray-applied primer of workpiece to be processed；
S2, water transfer: being pre-printed with required pattern for water-soluble film, makes the activation of the pattern on film at ink-like using solvent
Pattern is needed on by print workpiece using hydraulic pressure, will be rinsed with water completely by remaining impurity on print workpiece by state, then will be by
Print workpiece drying；
S3, topcoating: being protected spraying PU transparent varnish by the surface of print workpiece, and the body surface for having sprayed finishing coat is carried out
It is dry, finished product is obtained after dry.
2. a kind of process of surface treatment of transparent material according to claim 1, it is characterised in that: sprayed in the step S1
The base coat thickness of painting is 5-50 μm.
3. a kind of process of surface treatment of transparent material according to claim 1, it is characterised in that: golden in the step S2
Category, ceramics and glass pieces are put into oven and toast 20min with 140 DEG C of temperature, and plastic workpiece is put into oven with 70 DEG C
Temperature toasts 60min.
4. a kind of process of surface treatment of transparent material according to claim 1, it is characterised in that: in the step S3
The dry 12h of temperature that will be put by print workpiece in oven with 70 DEG C after spray paint.
5. a kind of process of surface treatment of transparent material according to claim 1, it is characterised in that: in the step S3 also
Sub-gloss varnish need to be sprayed, bloom ultraviolet-cured paint is then sprayed.