CN110230210A - A kind of lining cloth production technology that sizing tentering is synchronous - Google Patents

A kind of lining cloth production technology that sizing tentering is synchronous Download PDF

Info

Publication number
CN110230210A
CN110230210A CN201910573875.3A CN201910573875A CN110230210A CN 110230210 A CN110230210 A CN 110230210A CN 201910573875 A CN201910573875 A CN 201910573875A CN 110230210 A CN110230210 A CN 110230210A
Authority
CN
China
Prior art keywords
base fabric
baking oven
lining cloth
tentering
slurry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910573875.3A
Other languages
Chinese (zh)
Inventor
高强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Hong Sheng Lining Cloth Co Ltd
Original Assignee
Guangzhou Hong Sheng Lining Cloth Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Hong Sheng Lining Cloth Co Ltd filed Critical Guangzhou Hong Sheng Lining Cloth Co Ltd
Priority to CN201910573875.3A priority Critical patent/CN110230210A/en
Publication of CN110230210A publication Critical patent/CN110230210A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of lining cloth production technologies that sizing tentering is synchronous, include the following steps: base fabric restocking and are transmitted；Slurry coating is carried out to base fabric by slurry point head；The base fabric for being coated with slurry is carried out spreading rubber powder by duster；The rubber powder of the part of the uncoated slurry of scrim surfaces is sucked by device for inhaling powdery substances；The base fabric for sucking rubber powder is sent to the entrance of baking oven, base fabric two sides is placed on the needle plate guide rail of baking oven two sides and carries out shaping tentering, and base fabric is carried out shaping by needle plate guide rail and is conveyed into baking oven, drying sintering is carried out to base fabric by baking oven；It carries out being cooled into high resiliency lining cloth with the base fabric after drying to by being formed, and coiled by winder.Lining cloth sizing of the present invention is sintered in one with drying and completes in baking oven, base fabric is avoided to carry out also needing to carry out heating draw forming again after drying sintering is cooling after dusting, the energy consumption for needing to consume in lining cloth production process is greatly reduced, the production cost of enterprise is greatly reduced.

Description

A kind of lining cloth production technology that sizing tentering is synchronous
Technical field
The present invention relates to lining cloth production field more particularly to a kind of lining cloth production technologies that sizing tentering is synchronous.
Background technique
Lining cloth is using woven fabric, knitted fabric and non-woven cloth as base fabric, using (or not using) thermal plastic high polymer chemical combination Object carries out Special Finishing processing by special mechanical, the internal layer for clothes play reinforcement, it is well-pressed the effects of, it is viscous with fabric Close the spe-cial-purpose uniform auxiliary material of (or non-adhering).
Currently, lining cloth is during production, usually by the lining cloth made carry out starching, dusting, inhale powder, drying, Heat-shaping is carried out after cooling again；This production technology is widely used in the production process of lining cloth, but this production technology has sternly The deficiency of weight, that is, need that great energy consumption is lost, and needs to carry out improvement again.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies in the prior art, provide a kind of lining cloth that sizing tentering is synchronous Production technology.
In order to solve the above technical problems, technical solution proposed by the present invention are as follows:
A kind of lining cloth production technology that sizing tentering is synchronous, includes the following steps:
Step 1: base fabric restocking is simultaneously transmitted；
Step 2: starching carries out slurry coating to the base fabric by slurry point head；
Step 3: spreading rubber powder, carries out uniformly spreading rubber powder to the base fabric for being coated with slurry by duster；
Step 4: powder is inhaled, is sucked the rubber powder of the part of the uncoated slurry of the scrim surfaces by device for inhaling powdery substances；
Further include following steps:
Step 5: the base fabric for sucking rubber powder is sent to the entrance of baking oven, by the base fabric two by sizing and tentering Side, which is placed on the needle plate guide rail of the baking oven two sides, carries out shaping tentering, and is carried out by the needle plate guide rail to the base fabric Sizing is conveyed into baking oven, carries out drying sintering to the base fabric by the baking oven；
Step 6: to formation high resiliency lining cloth after cooling down by the base fabric after being formed and drying, and pass through receipts Volume machine carries out coiled.
One of them preferred scheme of the invention is that leading portion portion is using Gas Direct-fired heat form to described in the baking oven Base fabric carries out drying sintering, and the base fabric is dried using hot air circulation in back segment portion in the baking oven.
One of them preferred scheme of the invention is that the base fabric is water spray cloth or low bullet cloth.
One of them preferred scheme of the invention is that the slurry is hot melt adhesive.
One of them of the invention preferred scheme is, the base fabric of step 1 to step 4 by by transmission device into Row is sequentially transmitted.
Compared with the prior art, the advantages of the present invention are as follows: the base fabric made successively is carried out to starching, dusting and inhales powder Afterwards, directly base fabric is transmitted in entering to dry case, needle plate guide rail is equipped in baking oven, transmission is carried out shaping to base fabric, and by baking oven to base Cloth carries out drying sintering, and lining cloth sizing of the present invention is completed in baking oven simultaneously with tentering and drying sintering, avoids base fabric and spreading It carries out also needing to carry out heating draw forming again after drying sintering is cooling after powder, greatly reduces and needed in lining cloth production process The energy consumption of consumption greatly reduces the production cost of enterprise.
Specific embodiment
To facilitate the understanding of the present invention, present invention work more comprehensively, is meticulously described below in conjunction with preferred embodiment, But the protection scope of the present invention is not limited to the following specific embodiments.
Unless otherwise defined, all technical terms used hereinafter and the normally understood meaning of those skilled in the art It is identical.Technical term used herein is intended merely to the purpose of description specific embodiment, is not intended to the limitation present invention Protection scope.
The embodiment of the invention discloses a kind of lining cloth production technologies that sizing tentering is synchronous, include the following steps:
Step 1: base fabric restocking is simultaneously transmitted, and the base fabric performed is placed on cloth storage trough, passes through leading on entering cloth rack It is conveyed on cloth roller guide transmission device；
Step 2: starching, base fabric carry out slurry coating, slurry point head to base fabric by slurry point head, by slurry point head Including doctor, cylinder and fabric guide roll, doctor include slurry pipe,
Grouting Pipe and scraper, Grouting Pipe are set to slurry pipe side and communicate with slurry pipe middle part, and scraper is located at relative to Grouting Pipe The other side for starching pipe, the other side for starching pipe, which is located above scraper, is provided with multiple slurry outlets, and cylinder is sheathed on the outer of slurry pipe, in cylinder Wall and scraper face contact, cylinder are operated by fabric guide roll below, and cylinder uses CP250/0.50 μm of micropore cylinder, really Protect point slurry uniformly, slurry is hot melt adhesive in the present embodiment, and hot melt adhesive is high adherence energy PA, PES or TPU hot melt adhesive, in two point On coating machine when applying hot melt adhesives, coat weight ranges are 5-30 grams/m；
Step 3: spreading rubber powder, the base fabric after slurry point, carries out uniformly spreading glue to the base fabric for being coated with slurry by duster Powder, rubber powder are copolyesters rubber powder and copolyamide rubber powder, are also mixed with cloth hard finishing agent in rubber powder；
Step 4: inhaling powder, after having spread rubber powder, is inhaled the rubber powder of the part of the uncoated slurry of scrim surfaces by device for inhaling powdery substances It goes；The present embodiment further includes following steps:
Step 5: the base fabric for sucking rubber powder is sent to the entrance of baking oven, base fabric two sides is placed in by sizing and tentering Tentering is carried out shaping on the needle plate guide rail of baking oven two sides, and base fabric is carried out shaping by needle plate guide rail and is conveyed into baking oven, Drying sintering is carried out to base fabric by baking oven；Specifically, two sides are equipped with needle plate guide rail, needle plate rail-sides in baking oven in the present invention Needle plate component is equipped on edge, needle plate component includes multiple thin bars, and it is similar needle-shaped, and in vertical state with needle plate guide rail, needle plate The distance between guide rail can taking human as being regulated and controled, so as to regulate and control the distance between needle plate component, in the entrance of baking oven, Base fabric is set on needle plate component, stentering forming is carried out to base fabric so as to the size that needs according to base fabric, in the present embodiment It is equipped with needle plate guide rail in baking oven, transmission is carried out shaping to base fabric, and drying sintering, lining cloth of the present invention are carried out to base fabric by baking oven Sizing is sintered in one progress simultaneously with drying and completes in baking oven, avoids base fabric and carries out drying sintering cooling after dusting Also need to carry out to heat post-tensioning sizing afterwards again.
The present embodiment also step 6: to formation high resiliency lining cloth after being cooled down by the base fabric after being formed and drying, and It is carried out by winder coiled.
The one of preferred embodiment of the present invention is that leading portion portion carries out base fabric using Gas Direct-fired heat form in baking oven Drying is sintered, and base fabric is dried using hot air circulation in back segment portion in baking oven.
The one of preferred embodiment of the present invention is that base fabric is water spray cloth or low bullet cloth.
The one of preferred embodiment of the present invention is, the base fabric of step 1 to step 4 by by transmission device progress according to Secondary transmission.
Compared with the prior art, the advantages of the present invention are as follows: the base fabric made successively is carried out to starching, dusting and inhales powder Afterwards, directly base fabric is transmitted in entering to dry case, needle plate guide rail is equipped in baking oven, transmission is carried out shaping to base fabric, and by baking oven to base Cloth carries out drying sintering, and lining cloth sizing of the present invention is completed in baking oven simultaneously with tentering and drying sintering, avoids base fabric and spreading It carries out also needing to carry out heating draw forming again after drying sintering is cooling after powder, greatly reduces and needed in lining cloth production process The energy consumption of consumption greatly reduces the production cost of enterprise.

Claims (5)

1. a kind of lining cloth production technology that sizing tentering is synchronous, includes the following steps:
Step 1: base fabric restocking is simultaneously transmitted；
Step 2: starching carries out slurry coating to the base fabric by slurry point head；
Step 3: spreading rubber powder, carries out uniformly spreading rubber powder to the base fabric for being coated with slurry by duster；
Step 4: powder is inhaled, is sucked the rubber powder of the part of the uncoated slurry of the scrim surfaces by device for inhaling powdery substances；
It is characterized by also including following steps:
Step 5: the base fabric for sucking rubber powder is sent to the entrance of baking oven, the base fabric two sides is put by sizing and tentering It is placed on the needle plate guide rail of the baking oven two sides and carries out shaping tentering, and the base fabric is carried out shaping by the needle plate guide rail It is conveyed into baking oven, drying sintering is carried out to the base fabric by the baking oven；
Step 6: to formation high resiliency lining cloth after cooling down by the base fabric after sizing tentering drying, and pass through winding Machine carries out coiled.
2. a kind of lining cloth production technology that sizing tentering is synchronous according to claim 1, which is characterized in that in the baking oven Leading portion portion carries out drying sintering to the base fabric using Gas Direct-fired heat form, and back segment portion uses hot air circulation in the baking oven The base fabric is dried.
3. a kind of lining cloth production technology that sizing tentering is synchronous according to claim 1, which is characterized in that the base fabric is Water spray cloth or low bullet cloth.
4. a kind of lining cloth production technology that sizing tentering is synchronous according to claim 1, which is characterized in that the slurry is Hot melt adhesive.
5. a kind of lining cloth production technology that sizing tentering is synchronous according to claim 1, which is characterized in that step 1 to step Rapid four base fabric by transmission device by being sequentially transmitted.
CN201910573875.3A 2019-06-28 2019-06-28 A kind of lining cloth production technology that sizing tentering is synchronous Pending CN110230210A (en)