CN110181804A - A kind of jewelry manufacture method based on 3d printing technique - Google Patents

A kind of jewelry manufacture method based on 3d printing technique Download PDF

Info

Publication number
CN110181804A
CN110181804A CN201910430631.XA CN201910430631A CN110181804A CN 110181804 A CN110181804 A CN 110181804A CN 201910430631 A CN201910430631 A CN 201910430631A CN 110181804 A CN110181804 A CN 110181804A
Authority
CN
China
Prior art keywords
weight
parts
printing
printer
jewellery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910430631.XA
Other languages
Chinese (zh)
Inventor
王奕修
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Elf World Culture Co Ltd
Original Assignee
Beijing Elf World Culture Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Elf World Culture Co Ltd filed Critical Beijing Elf World Culture Co Ltd
Priority to CN201910430631.XA priority Critical patent/CN110181804A/en
Publication of CN110181804A publication Critical patent/CN110181804A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of jewelry manufacture method based on 3d printing technique, comprising the following steps: modeling, using 3DMax, Maya, CAD software carries out three-dimensional modeling to jewellery, obtains three-dimensional data, and then processing is repaired；Slicing treatment, by design software by scan come three-dimensional data be sliced, then by 3D printer control software be read out；It is printed, meanwhile, it is packed into 3D printing material, debugs print platform, print parameters are set, 3D printer is started, then printer is started to work, material can print layer by layer, be bonded between layers by glue, and fix pattern according to cross section；Post-processing, compared with prior art, the present invention is with following the utility model has the advantages that making jewellery by 3D printing technique, it is not only easy to make, it can satisfy the demand of user individual customization simultaneously, a kind of novel 3D printing material prescription is proposed simultaneously, to adapt to needs of the jewellery in 3D printing.

Description

A kind of jewelry manufacture method based on 3d printing technique
Technical field
The present invention is a kind of jewelry manufacture method based on 3d printing technique.
Background technique
3D printing technique is a kind of form of layered manufacturing technology, and principle is created by being layered added material to article Produce material object.Traditional jewelry manufacture is realized by complicated step, so involving great expense, if can pass through 3D Printing technique makes jewellery, not only easy to make, while can satisfy the demand of user individual customization.
Summary of the invention
In view of the deficienciess of the prior art, it is an object of the present invention to provide a kind of jewelry manufacture sides based on 3d printing technique Method, to solve the problems mentioned in the above background technology.
To achieve the goals above, the present invention is to realize by the following technical solutions: one kind is based on 3d printing technique Jewelry manufacture method, comprising the following steps:
Modeling, using 3DMax, Maya, CAD software carries out three-dimensional modeling to jewellery, obtains three-dimensional data, and then processing is repaired It is multiple；
Slicing treatment, by design software by scan come three-dimensional data be sliced, then pass through 3D printer control Software processed is read out；
It is printed, meanwhile, it is packed into 3D printing material, debugs print platform, sets print parameters, starts 3D printer, Then printer is started to work, and material can be printed layer by layer, be bonded between layers by glue, and according to Pattern is fixed in cross section；
Post-processing, the jewellery completed to printing are processed by shot blasting, that is, pass through sand paper polishing or bead-blast or steam These three smooth technologies are handled, and are then stood, force to solidify, remove powder, cladding, form jewellery finished product.
Further, in modeling process, user first according to itself the case where, select suitable jewellery, then herein On the basis of, it is changed accordingly, inputs in 3D software and completely restore the 3D model of object.
Further, in slicing treatment, by design software, A Jing scans the three-dimensional data come and is divided into multiple groups number According to data include packed density, angle, shell, design the path of printing, and by the file storage after slice at .gcode lattice Formula, then software is controlled by 3D printer .gcode file is sent to printer and controls the parameter of 3D printer.
Further, the 3D printing material includes polylactic acid, thermoplastic elastomer (TPE), graphene, nano dye, polyphenylene oxide Sulfone, nano metal material, polyisocyanates, stabilizer, thickener, color fixing agent.
Further, the 3D printing material is made of the raw material of following parts by weight: polylactic acid 50-60 parts by weight, thermoplastic Property elastomer 2-5 parts by weight, graphene 1-4 parts by weight, nano dye 3-6 parts by weight, Poly-s 179 2-7 parts by weight, nanogold Belong to material 1-5 parts by weight, polyisocyanates 3-5 parts by weight, stabilizer 2-4 parts by weight, thickener 3-6 parts by weight, color fixing agent 2-4 Parts by weight.
Beneficial effects of the present invention: a kind of jewelry manufacture method based on 3d printing technique of the invention passes through 3D printing Technology makes jewellery, not only easy to make, while can satisfy the demand of user individual customization, while proposing a kind of new The 3D printing material prescription of type, to adapt to needs of the jewellery in 3D printing.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below with reference to Specific embodiment, the present invention is further explained.
The present invention provides a kind of technical solution: a kind of jewelry manufacture method based on 3d printing technique, comprising the following steps:
Modeling, using 3DMax, Maya, CAD software carries out three-dimensional modeling to jewellery, obtains three-dimensional data, and then processing is repaired It is multiple；
Slicing treatment, by design software by scan come three-dimensional data be sliced, then pass through 3D printer control Software processed is read out；
It is printed, meanwhile, it is packed into 3D printing material, debugs print platform, sets print parameters, starts 3D printer, Then printer is started to work, and material can be printed layer by layer, be bonded between layers by glue, and according to Pattern is fixed in cross section；
Post-processing, the jewellery completed to printing are processed by shot blasting, that is, pass through sand paper polishing or bead-blast or steam These three smooth technologies are handled, and are then stood, force to solidify, remove powder, cladding, form jewellery finished product.
In modeling process, user first according to itself the case where, select suitable jewellery, then on this basis, into The corresponding change of row, inputs in 3D software and completely restores the 3D model of object.
In slicing treatment, by design software, A Jing scans the three-dimensional data come and is divided into multi-group data, and data include Packed density, angle, shell design the path of printing, and by the file storage after slice at .gcode format, then pass through 3D .gcode file is sent to printer and controls the parameter of 3D printer by printer control software.
As an embodiment of the present invention: 3D printing material includes polylactic acid, thermoplastic elastomer (TPE), graphene, nanometer Pigment, Poly-s 179, nano metal material, polyisocyanates, stabilizer, thickener, color fixing agent.
As an embodiment of the present invention: 3D printing material is made of the raw material of following parts by weight: polylactic acid 50-60 weight Measure part, thermoplastic elastomer (TPE) 2-5 parts by weight, graphene 1-4 parts by weight, nano dye 3-6 parts by weight, Poly-s 179 2-7 weight Part, nano metal material 1-5 parts by weight, polyisocyanates 3-5 parts by weight, stabilizer 2-4 parts by weight, thickener 3-6 parts by weight, Color fixing agent 2-4 parts by weight.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from spirit of the invention or In the case where essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state Bright restriction, it is intended that including all changes that fall within the meaning and scope of the equivalent elements of the claims in the present invention It is interior.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art The other embodiments being understood that.

Claims (5)

1. a kind of jewelry manufacture method based on 3d printing technique, it is characterised in that: the following steps are included:
Modeling, using 3DMax, Maya, CAD software carries out three-dimensional modeling to jewellery, obtains three-dimensional data, and then processing is repaired；
Slicing treatment, by design software by scan come three-dimensional data be sliced, then controlled by 3D printer soft Part is read out；
It is printed, meanwhile, it is packed into 3D printing material, debugs print platform, sets print parameters, starts 3D printer, then Printer is started to work, and material can be printed layer by layer, be bonded between layers by glue, and according to transversal Pattern is fixed in face；
Post-processing, the jewellery completed to printing are processed by shot blasting, i.e., smooth by sand paper polishing or bead-blast or steam These three technologies are handled, and are then stood, force to solidify, remove powder, cladding, form jewellery finished product.
2. a kind of jewelry manufacture method based on 3d printing technique according to claim 1, it is characterised in that: modeling Cheng Zhong, user first according to itself the case where, select suitable jewellery, then on this basis, changed accordingly, input The 3D model of object is completely restored in 3D software.
3. a kind of jewelry manufacture method based on 3d printing technique according to claim 1, it is characterised in that: at slice In reason, by design software, the three-dimensional data come will be scanned and be divided into multi-group data, data include packed density, angle, outer Shell designs the path of printing, and by the file storage after slice at .gcode format, then controls software by 3D printer, .gcode file is sent to printer and controls the parameter of 3D printer.
4. a kind of jewelry manufacture method based on 3d printing technique according to claim 1, it is characterised in that: the 3D is beaten Printing material includes polylactic acid, thermoplastic elastomer (TPE), graphene, nano dye, Poly-s 179, nano metal material, polyisocyanic acid Ester, stabilizer, thickener, color fixing agent.
5. a kind of jewelry manufacture method based on 3d printing technique according to claim 1, it is characterised in that: the 3D is beaten Print material is made of the raw material of following parts by weight: polylactic acid 50-60 parts by weight, thermoplastic elastomer (TPE) 2-5 parts by weight, graphene 1- 4 parts by weight, nano dye 3-6 parts by weight, Poly-s 179 2-7 parts by weight, nano metal material 1-5 parts by weight, polyisocyanates 3-5 parts by weight, stabilizer 2-4 parts by weight, thickener 3-6 parts by weight, color fixing agent 2-4 parts by weight.
CN201910430631.XA 2019-05-22 2019-05-22 A kind of jewelry manufacture method based on 3d printing technique Pending CN110181804A (en)