CN110171172A - The production method of the craftwork of multilayer material - Google Patents
The production method of the craftwork of multilayer material Download PDFInfo
- Publication number
- CN110171172A CN110171172A CN201910601818.1A CN201910601818A CN110171172A CN 110171172 A CN110171172 A CN 110171172A CN 201910601818 A CN201910601818 A CN 201910601818A CN 110171172 A CN110171172 A CN 110171172A
- Authority
- CN
- China
- Prior art keywords
- inner cavity
- production method
- layer solution
- cavity mould
- multilayer material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the production methods of multilayer material production multilayer bottle-shaped container, have outer cavity mould, comprising the following steps: the internal layer solution got ready is used to prepare the inner cavity with bottleneck by S1, and material and its size and shape are depending on reality;The inner cavity that preparation is completed is placed in outer cavity mould by S2, exposes oral area;The outer layer solution got ready is injected outer cavity mould until filling the full outer cavity mould by S3;S4 cooling, solidification processing;S5 demoulding;S6 annealing.The beneficial effects of the invention are that unlike material is combined, multilayered structure is realized, and preparation method through the invention, exocoel no longer need to be attached by the periphery of bottle mouth position with inner cavity;In addition, be no longer between exocoel and inner cavity it is hollow, but solid, therefore, when outer layer select be the materials such as plastics, anti-collision effect can be effectively played.The characteristics of one integral piece glassware shape and interior shape are different shape in this way, can also be by plastics forms the artistic effect of inside and outside not similar shape, and the plastics liquid of different colours or effect can also be injected by outside cavity mould, changes more patterns out.
Description
Technical field
The present invention relates to the manufacture craft of multilayer bottle-shaped container, specifically a kind of production of the craftwork of multilayer material
Method.
Background technique
Vial or plastic bottle are single layer at present, and shape is roughly the same with cavity shape, cannot achieve inside and outside different shape
Artistic effect.The traditional manufacturing technique of double-layer glass are as follows: step 1: glass liner pipe cutting;Second step, glass liner
Back cover;Third step, glass shell pipe cutting;Step 4: liner and shell sealing;Step 5: by shell back cover, wherein traditional work
It needs to carry out 2 back covers to glass in skill, i.e., back cover is carried out respectively to liner back cover and shell, there are complex procedures, wastes
Material, high production cost problem.Double-layer plastic bottle is that liner and shape is fabricated separately, then by being assembled into bilayer, because there are
Space, makes that container integrally becomes thick or inner cavity capacity is too small, and the artistic expression of appearance multilayer is not natural enough.
Secondly, present Glass Craft is since the melting temperature of unlike material is different, therefore, it is difficult to make unlike material
Combination, also limit the purposes of such craftwork in this way.
Summary of the invention
The present invention overcomes problem of the existing technology, propose that a kind of process is simple, and low manufacture cost saves material
Multilayer material container production method.
In view of the defect of the prior art, the invention adopts the following technical scheme:
The production method of the craftwork of multilayer material has outer cavity mould, comprising the following steps:
The production method of the craftwork of multilayer material has outer cavity mould, comprising the following steps:
S1 the internal layer solution got ready is used to prepare the inner cavity with bottleneck, material and its size and shape according to practical and
It is fixed;
The inner cavity that preparation is completed is placed in outer cavity mould by S2, exposes bottleneck;
The outer layer solution got ready is injected outer cavity mould until filling the full outer cavity mould by S3;
S4 cooling, solidification processing;
S5 demoulding;
S6 annealing.
It should be noted that the internal layer solution is glass or plastic solution.
It should be noted that annealing after completing the step 1.
It should be noted that the outer layer solution is plastic solution.
It should be noted that the outer layer solution in the step 3 is by the inner cavity except the surface of bottleneck portion is all wrapped up.
It should be noted that the inner cavity in the step 2 is except in the surface of bottleneck portion and the top of the outer cavity mould
Seamless surface fitting.
It should be noted that there is no air between the surface of internal cavity and outer layer solution.
Another implementation of the invention: the production method of multilayer material container has outer cavity mould, including following step
It is rapid:
S1 the internal layer solution got ready is used to prepare the inner cavity with bottleneck, material and its size and shape according to practical and
It is fixed;
The inner cavity that preparation is completed is placed in outer cavity mould by S2, exposes bottleneck;
The outer layer solution got ready is injected outer cavity mould until filling the full outer cavity mould by S3;
S4 cooling, solidification processing;
S5 demoulding;
S6 annealing.
It should be noted that the internal layer solution is glass or plastic solution;The outer layer solution is plastic solution.
It should be noted that the bottleneck in the step 2 stretches out in outside the outer cavity mould;Glass in the step 3
Liquid all wraps up on the surface of the inner cavity, does not have air between the surface of internal cavity and glass metal.
The beneficial effects of the invention are that unlike material is combined, and preparation method through the invention, exocoel with
Inner cavity no longer needs to be attached by the periphery of bottle mouth position;In addition, be no longer between exocoel and inner cavity it is hollow, but solid, because
This, what it is when outer layer selection is the materials such as plastics, can effectively play anti-collision effect.One integral piece glassware shape is with interior shape in this way
Different shape, can also be by plastics the characteristics of, form the artistic effect of inside and outside not similar shape, can also be infused by outside cavity mould
The plastics liquid for entering different colours or effect changes more patterns out.
Specific embodiment
The invention will be further described below, it should be noted that before following embodiment is with the technical program
It mentions, the detailed implementation method and specific operation process are given, but protection scope of the present invention is not limited to the present embodiment.
Embodiment 1
The present invention is the container production method of multilayer material, has outer cavity mould, comprising the following steps:
S1 the internal layer solution got ready is used to prepare the inner cavity with bottleneck, material and its size and shape according to practical and
It is fixed;
The inner cavity that preparation is completed is placed in outer cavity mould by S2, exposes oral area;
The outer layer solution got ready is injected outer cavity mould until filling the full outer cavity mould by S3;
S4 cooling, solidification processing;
S5 demoulding;
S6 annealing.
It should be noted that the internal layer solution is glass metal.
It should be noted that annealing after completing the step 1.
It should be noted that the outer layer solution is plastic solution.
It should be noted that the outer layer solution in the step 3 all wraps up on the surface of the inner cavity.
It should be noted that table in surface of the inner cavity in the step 2 in addition to oral area and the top of the outer cavity mould
Face is seamless applying.
It should be noted that there is no air between the surface of internal cavity and outer layer solution.
Embodiment 2
As another embodiment of the present invention, following steps:
The production method of multilayer material container has outer cavity mould, comprising the following steps:
S1 the internal layer solution got ready is used to prepare the inner cavity with bottleneck, material and its size and shape according to practical and
It is fixed;
The inner cavity that preparation is completed is placed in outer cavity mould by S2, exposes bottleneck;
The outer layer solution got ready is injected outer cavity mould until filling the full outer cavity mould by S3;
S4 cooling, solidification processing;
S5 demoulding;
S6 annealing.
It should be noted that the internal layer solution is glass metal;The outer layer solution is plastic solution.
It should be noted that the bottleneck in the step 2 stretches out in outside the outer cavity mould;Glass in the step 3
Liquid all wraps up on the surface of the inner cavity, does not have air between the surface of internal cavity and glass metal.
For those skilled in the art, it can be provided various corresponding according to above technical solution and design
Change and modification, and all these change and modification, should be construed as being included in this practical invention scope of protection of the claims it
It is interior.
Claims (10)
1. the production method of the bottle-shaped container of multilayer material has outer cavity mould, which comprises the following steps:
The internal layer solution got ready is used to prepare the inner cavity with bottleneck by S1, and material and its size and shape are depending on reality;
The inner cavity that preparation is completed is placed in outer cavity mould by S2, exposes oral area;
The outer layer solution got ready is injected outer cavity mould until filling the full outer cavity mould by S3;
S4 cooling, solidification processing;
S5 demoulding;
S6 annealing.
2. the container production method of multilayer material according to claim 1, which is characterized in that the internal layer solution is glass
Or plastics liquid.
3. the container production method of multilayer material according to claim 1, which is characterized in that it is laggard to complete the step 1
Row annealing.
4. the container production method of multilayer material according to claim 1, which is characterized in that the outer layer solution is plastics
Solution.
5. the container production method of multilayer material according to claim 1, which is characterized in that the outer layer in the step 3
Solution all wraps up on the surface of the inner cavity.
6. the container production method of multilayer material according to claim 1, which is characterized in that the inner cavity in the step 2
Except the top inner surface of container finish and the outer cavity mould is seamless applying.
7. the production method of the craftwork of multilayer material according to claim 1, which is characterized in that the surface of internal cavity with
There is no air between outer layer solution.
8. the production method of the craftwork of multilayer material has outer cavity mould, which comprises the following steps:
The internal layer solution got ready is used to prepare the inner cavity with bottleneck by S1, and material and its size and shape are depending on reality;
The inner cavity that preparation is completed is placed in outer cavity mould by S2, exposes oral area;
The outer layer solution got ready is injected outer cavity mould until filling the full outer cavity mould by S3;
S4 cooling, solidification processing;
S5 demoulding;
S6 annealing.
9. the production method of the craftwork of multilayer material according to claim 5, which is characterized in that the internal layer solution is
Glass or plastics;The outer layer solution is plastic solution.
10. the production method of the craftwork of multilayer material according to claim 5, which is characterized in that in the step 2
Bottleneck stretches out in outside the outer cavity mould;Plastics liquid in the step 3 all wraps up on the surface of the inner cavity, the inner cavity
There is no air between surface and plastics liquid.