CN110130613A - A kind of glue of exempting from is drowned oneself the production method on floor - Google Patents
A kind of glue of exempting from is drowned oneself the production method on floor Download PDFInfo
- Publication number
- CN110130613A CN110130613A CN201910418566.9A CN201910418566A CN110130613A CN 110130613 A CN110130613 A CN 110130613A CN 201910418566 A CN201910418566 A CN 201910418566A CN 110130613 A CN110130613 A CN 110130613A
- Authority
- CN
- China
- Prior art keywords
- layer
- substrate
- temperature
- floor
- exempting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of glue of exempting from that can simplify process flow to drown oneself floor, comprising: the wearing layer that sets gradually from top to bottom prints color film layer, substrate upper layer, Gitterfasern layer, substrate middle layer, substrate lower layer and on-slip film layer；By weight percentage, the substrate upper layer, substrate middle layer and substrate lower layer are made of the calcium carbonate of 14.5~15.5% PVC resin powder, 0.7~0.8% Environment-friendlycalcium calcium zinc stabilizer, 0.7~0.8% carbon black and 8.5~9.5% plasticizer and 74~75%.The invention also discloses a kind of above-mentioned glue of exempting to drown oneself the production method on floor.The present invention raises the ratio of filler material calcium carbonate substantially by the formula of improvement substrate, in this way, substrate upper layer, substrate middle layer and substrate lower layer can be substantially reduced process flow, be reduced manufacturing cost using unified formula；In addition, the present invention further reduced production cost by improving combination process.
Description
Technical field
Exempt from glue the present invention relates to a kind of plastic floor and preparation method thereof more particularly to one kind to drown oneself floor and its system
Make method.
Background technique
It is well known that exempting from glue drowns oneself floor with good toughness and elasticity, installation rear stability is good, mats formation conveniently.Mesh
Before, traditional glue of exempting from is drowned oneself floor, and structure generally includes: the wearing layer that sets gradually from top to bottom prints color film layer, substrate
Upper layer, Gitterfasern layer, substrate middle layer and substrate lower layer and on-slip film layer.In the actual production process, on the substrate
Layer, substrate middle layer, substrate lower layer are respectively adopted different formulas and are made, and process flow is longer, considerably increases production cost；And
And it is currently used exempt from glue drown oneself floor combination process it is more complicated, further increase production cost.
Summary of the invention
A kind of it can simplify process flow, the technical problems to be solved by the present invention are: providing to reduce production cost
Exempt from glue to drown oneself floor.
In order to solve the above technical problems, the technical solution adopted by the present invention are as follows: one kind exempts from glue and drowns oneself floor, comprising: from upper
Wearing layer, the color film layer of printing, substrate upper layer, Gitterfasern layer, substrate middle layer, substrate lower layer and the on-slip film set gradually under and
Layer；By weight percentage, the substrate upper layer, substrate middle layer and substrate lower layer by 14.5~15.5% polyvinyl chloride resin
Powder, 0.7~0.8% Environment-friendlycalcium calcium zinc stabilizer, 0.7~0.8% carbon black and 8.5~9.5% plasticizer and 74~
75% calcium carbonate is made.
As a preferred embodiment, exempt from glue in described one kind to drown oneself in floor, the substrate upper layer, substrate middle layer and
The weight ratio of PVC resin powder and calcium carbonate in substrate lower layer is 1:4.9~5.1.
As a preferred embodiment, exempt from glue in described one kind to drown oneself in floor, the plasticizer is using DOTP environmental protection
Plasticizer.
As a preferred embodiment, to exempt from glue in described one kind to drown oneself in floor, the wearing layer uses PVC material,
It is with a thickness of 0.5 ± 0.1 millimeter.
As a preferred embodiment, exempt from glue in described one kind to drown oneself in floor, the on-slip film layer uses PVC material
Matter, if bottom is vertically arranged with the continuous waveform shading that the depth of arterial highway lateral direction penetrating is 0.5 ± 0.1 millimeter.
As a preferred embodiment, exempt from glue in described one kind to drown oneself in floor, the substrate upper layer, substrate middle layer and
The density of substrate lower layer is 1.9 ± 0.01g/cm3。
The present invention also provides a kind of glue of exempting from that can simplify combination process to drown oneself the production method on floor, step packet
It includes:
A) raw material is blended: by the material rate on the invention production substrate upper layer, substrate middle layer and substrate lower layer, choosing
PVC resin powder, stabilizer, carbon black, plasticizer and calcium carbonate pass through stirring 5~8 minutes；
B) produce substrate: the raw material after step a) is blended carries out internally mix, during internally mix, pressure control 0.5~
Between 0.8Mpa, after raw material knot frustillatum, discharging to mill equipment, by mill equipment machine-shaping, during mill,
Successively pass through three pairs of hot briquetting rollers, the preceding roll temperature of first pair of hot briquetting roller is 135~145 DEG C, rear roll temperature be 145~
155 DEG C, the preceding roll temperature of second pair of hot briquetting roller is 140~150 DEG C, rear roll temperature is 150~160 DEG C, and third is to heating
The preceding roll temperature of forming roller is 150~160 DEG C, rear roll temperature is 160~170 DEG C；Then, it is cooled down by chill roll, it is cold
But the temperature of roller is 40 ± 2 DEG C, finally, cutting into required length；
C) by wearing layer, the color film layer of printing, substrate upper layer, Gitterfasern layer, substrate middle layer, substrate lower layer and on-slip film layer
Hot combined processing is carried out using hot press, in process, successively by the bringing-up section as first segment, heats at least 20 points
Clock, temperature control between 135~140 DEG C, and pressure controls between 5~6Mpa, then pass through second segment, herein therebetween, pressure
Power controls between 7~9Mpa, continues heating 5 minutes or more, temperature controls between 135~140 DEG C, then natural cooling 5
Minute or more, then successively pass through the third as natural cooling section, the 4th section, the pressure of third section is controlled in 10~12Mpa
Between, the time, the 4th section of pressure was 15 ± 1Mpa, and the time was at 10 minutes or more at 15 minutes or more；
D) after heat is compound, semi-finished product is placed on thermostatic chamber and are cooled down, constant temperature room temperature is 23 ± 2 DEG C, relatively wet
After degree is 50 ± 2%, constant temperature at least 24 hours, surface UV and tempering are carried out to the semi-finished product, UV gram weight is 11
~14g/m2, after being 50 ± 2 DEG C of baking oven section levelling by temperature, handled using ultraviolet curing, the production that UV processing is completed
Product carry out tempering, heat 600 ± 10 revs/min of net revolving speed, and the temperature of outlet piece is 90~95 DEG C, after tempering,
Cooling using cooling water, the temperature of cooling water is 21~25 DEG C；
E) it after surface UV tempering, rests on and does within thermostatic chamber 72 hours or more health processing, constant temperature room temperature is 23 ± 2
DEG C, relative humidity 50 ± 2%；
F) product after health is put into punching machine and is cut, then, the sheet material obtained after cutting is repaired
Side obtains finished product.
As a preferred embodiment, it is described it is a kind of exempt from the production method that glue drowns oneself floor, in the step a)
Mixing speed controls between 1200~1500 revs/min
The beneficial effects of the present invention are: the present invention by improve formula, allow filler material calcium carbonate ratio substantially
Up-regulation, in this way, substrate upper layer, substrate middle layer and substrate lower layer can be substantially reduced process flow, be dropped using unified formula
Low manufacturing cost；In addition, the present invention by improving combination process, further reduced production cost, and make obtained to exempt from glue
Floor of drowning oneself has following characteristics:
1, wear-resistant pressure-resistant: superpower wear-resistant, shock resistance, indeformable, reusable, service life are usually in 20~30 years.
2, sound absorption properties are strong: exempting from glue and drown oneself the distinctive surface layer in floor and plastic cement bed course after seamless processing, can sufficiently play suction
The effect of sound, maximum can completely cut off the noise of 15~19db, not only solve the worry of noise, but also solve carpet daily maintenance
Difficult problem.
3, comfortable foot feeling: after seamless processing, supporting force is strong for the surface layer of compact structure and high-elastic bed course, buffers weight, glass
Glass vessel drop to the ground it is not easily broken, guarantee comfortable foot feeling, close to carpet, the place for being very suitable to the elderly and child makes
With.
4, anti-skid safety: exempt from glue and drown oneself floor under local pressure effect, instantaneous flexible deformation can be generated, so that surface
Coefficient of friction increases immediately, and when walking is not easy to slip.For hospital architecture, anti-skidding design is the function of needing special consideration
It is required that especially paediatrics, geriatric ward and bone fracture ward.
5, environment-protecting clean: it is environmentally protective, it is formaldehydeless, radiationless, containing antipathogenic composition, it can inhibit the attachment and taste of bacterium
It is raw, reach the stringent use standard of hospital.
6, easy to maintain: easy to clean, freedom from repairs is not afraid of water logging and greasy dirt, the erosion of the chemical substances such as diluted acid, alkali, generally
It is cleaned with wet mop, it is time saving and energy saving.
7, it is widely used: drowning oneself the unique material in floor and superpower performance since PVC exempts from glue, in addition mating formation conveniently, apply
Work is quick, highly-safe, is widely used in healthcare environment, environment, office space, hotel industry, retail business and Ministry of Light Industry
The various crowded public places such as door.
Detailed description of the invention
Fig. 1 is the structural schematic diagram on floor of the present invention of drowning oneself.
Appended drawing reference in Fig. 1 are as follows: 1, wearing layer, 2, the color film layer of printing, 3, substrate upper layer, 4, Gitterfasern layer, 5, base
Material middle layer, 6, substrate lower layer, 7, on-slip film layer.
Specific embodiment
With reference to the accompanying drawing, described in the present invention is described in detail it is a kind of exempt from glue drown oneself floor and its production method it is specific
Embodiment.
It drowns oneself floor as shown in Figure 1, one kind of the present invention exempts from glue, comprising: the wearing layer set gradually from top to bottom
1, color film layer 2, substrate upper layer 3, Gitterfasern layer 4, substrate middle layer 5, substrate lower layer 6 and on-slip film layer 7 are printed；The substrate
Upper layer 3, substrate middle layer 5 and substrate lower layer 6 are by 14.5~15.5% PVC resin powder, 0.7~0.8% DOTP environmental protection calcium
Zinc stabilizer, 0.7~0.8% carbon black and 8.5~9.5% environment-friendly plasticizer and 74~75% calcium carbonate are made, and
And the weight ratio on substrate upper layer 3, substrate middle layer 5 and PVC resin powder and calcium carbonate in substrate lower layer 6 is 1:4.9~5.1.
In practical application, the polyvinyl chloride resin of the substrate upper layer 3, substrate middle layer 5 and substrate lower layer 6 using 50 kilograms
Powder, 2.5 kilograms of DOTP Environment-friendlycalcium calcium zinc stabilizer, 2.5 kilograms of carbon black, 30 kilograms of environment-friendly plasticizer, 250 kilograms of carbonic acid
Calcium is made, and the weight ratio on substrate upper layer 3, substrate middle layer 5 and PVC resin powder and calcium carbonate in substrate lower layer 6 is 1:5；It is described
Wearing layer 1 and on-slip film layer 7 be all made of PVC material, wearing layer 1 with a thickness of 0.5 ± 0.1 millimeter；The bottom of on-slip film layer 7
If the continuous waveform shading (being not drawn into figure) that the depth for being vertically arranged with arterial highway lateral direction penetrating is 0.5 ± 0.1 millimeter；Institute
The density of the substrate upper layer 3, substrate middle layer 5 and the substrate lower layer 7 that state is 1.9 ± 0.01g/cm3。
Glue of the present invention of exempting from is drowned oneself the production method on floor, and step includes:
A) raw material is blended: by the raw material ratio on power production substrate upper layer 3 of the present invention, substrate middle layer 5 and substrate lower layer 6
Example chooses PVC resin powder, stabilizer, carbon black, plasticizer and calcium carbonate, passes through stirring 5~8 minutes, the speed control of stirring
Between 1200~1500 revs/min；
B) produce substrate: the raw material after step a) is blended carries out internally mix, during internally mix, pressure control 0.5~
Between 0.8Mpa, after raw material knot frustillatum (time is usually 3~5 minutes), discharges to mill equipment, added by mill equipment
Work molding successively passes through three pairs of hot briquetting rollers during mill, and the preceding roll temperature of first pair of hot briquetting roller is 135~
145 DEG C, rear roll temperature be 145~155 DEG C, the preceding roll temperature of second pair of hot briquetting roller is 140~150 DEG C, rear roll temperature is
150~160 DEG C, third is 150~160 DEG C to the preceding roll temperature of hot briquetting roller, rear roll temperature is 160~170 DEG C；Then,
It is cooled down by chill roll, the temperature of chill roll is 40 ± 2 DEG C, finally, cutting into required length；
C) by wearing layer, the color film layer of printing, substrate upper layer, Gitterfasern layer, substrate middle layer, substrate lower layer and on-slip film layer
Hot combined processing is carried out using hot press, in process, successively by the bringing-up section as first segment, heats at least 20 points
Clock, temperature control between 135~140 DEG C, and pressure controls between 5~6Mpa, then pass through second segment, herein therebetween, pressure
Power controls between 7~9Mpa, continues heating 5 minutes or more, temperature controls between 135~140 DEG C, then natural cooling 5
Minute or more, then successively pass through the third as natural cooling section, the 4th section, the pressure of third section is controlled in 10~12Mpa
Between, the time, the 4th section of pressure was 15 ± 1Mpa, and the time was at 10 minutes or more at 15 minutes or more；
D) after heat is compound, semi-finished product is placed on thermostatic chamber and are cooled down, constant temperature room temperature is 23 ± 2 DEG C, relatively wet
After degree is 50 ± 2%, constant temperature at least 24 hours, surface UV and tempering are carried out to the semi-finished product, UV gram weight is 11
~14g/m2, after being 50 ± 2 DEG C of baking oven section levelling by temperature, handled using ultraviolet curing, the production that UV processing is completed
Product carry out tempering immediately, heat 600 ± 10 revs/min of net revolving speed, the temperature of outlet piece is 90~95 DEG C, and tempering terminates
Afterwards, cooling using cooling water immediately, the temperature of cooling water is 21~25 DEG C；
E) it after surface UV tempering, rests on and does within thermostatic chamber 72 hours or more health processing, constant temperature room temperature is 23 ± 2
DEG C, relative humidity 50 ± 2%；
F) product after health is put into punching machine and is cut, then, the sheet material obtained after cutting is repaired
Side obtains finished product.
In conclusion only presently preferred embodiments of the present invention, is not used to limit the scope of implementation of the present invention, it is all according to
Equivalent changes and modifications made by shape described in scope of the invention as claimed, construction, feature and spirit should all be included in this
In the scope of the claims of invention.
Claims (8)
- It drowns oneself floor 1. one kind exempts from glue, comprising: the wearing layer that sets gradually from top to bottom prints color film layer, substrate upper layer, grid Fibrous layer, substrate middle layer, substrate lower layer and on-slip film layer；It is characterized by: by weight percentage, the substrate upper layer, Substrate middle layer and substrate lower layer are by 14.5~15.5% PVC resin powder, 0.7~0.8% Environment-friendlycalcium calcium zinc stabilizer, 0.7 ~0.8% carbon black and 8.5~9.5% plasticizer and 74~75% calcium carbonate are made.
- 2. glue according to claim 1 of exempting from is drowned oneself floor, it is characterised in that: substrate upper layer, substrate middle layer and the base The weight ratio of PVC resin powder and calcium carbonate in material lower layer is 1:4.9~5.1.
- 3. glue according to claim 1 of exempting from is drowned oneself floor, it is characterised in that: the plasticizer is plasticized using DOTP environmental protection Agent.
- 4. glue according to claim 1 of exempting from is drowned oneself floor, it is characterised in that: the wearing layer uses PVC material, thick Degree is 0.5 ± 0.1 millimeter.
- 5. glue according to claim 1 of exempting from is drowned oneself floor, it is characterised in that: the on-slip film layer uses PVC material, If bottom is vertically arranged with the continuous waveform shading that the depth of arterial highway lateral direction penetrating is 0.5 ± 0.1 millimeter.
- 6. glue according to claim 1 of exempting from is drowned oneself floor, it is characterised in that: substrate upper layer, substrate middle layer and the base The density of material lower layer is 1.9 ± 0.01g/cm3。
- 7. glue according to any one of claim 1 to 6 of exempting from is drowned oneself the production method on floor, step includes:A) raw material be blended: by described in claim 1 production substrate upper layer, substrate middle layer and substrate lower layer material rate, PVC resin powder, stabilizer, carbon black, plasticizer and calcium carbonate are chosen, stirring 5~8 minutes is passed through；B) produce substrate: the raw material after step a) is blended carries out internally mix, during internally mix, pressure control 0.5~ Between 0.8Mpa, after raw material knot frustillatum, discharging to mill equipment, by mill equipment machine-shaping, during mill, Successively pass through three pairs of hot briquetting rollers, the preceding roll temperature of first pair of hot briquetting roller is 135~145 DEG C, rear roll temperature be 145~ 155 DEG C, the preceding roll temperature of second pair of hot briquetting roller is 140~150 DEG C, rear roll temperature is 150~160 DEG C, and third is to heating The preceding roll temperature of forming roller is 150~160 DEG C, rear roll temperature is 160~170 DEG C；Then, it is cooled down by chill roll, it is cold But the temperature of roller is 40 ± 2 DEG C, finally, cutting into required length；C) wearing layer, the color film layer of printing, substrate upper layer, Gitterfasern layer, substrate middle layer, substrate lower layer and on-slip film layer are used Hot press carries out hot combined processing, in process, successively by the bringing-up section as first segment, heats at least 20 minutes, Temperature controls between 135~140 DEG C, and pressure controls between 5~6Mpa, then passes through second segment, herein therebetween, pressure control System continues heating 5 minutes or more, temperature controls between 135~140 DEG C, then natural cooling 5 minutes between 7~9Mpa More than, then successively pass through the third as natural cooling section, the 4th section, the pressure of third section controls between 10~12Mpa, Time, the 4th section of pressure was 15 ± 1Mpa, and the time was at 10 minutes or more at 15 minutes or more；D) after heat is compound, semi-finished product is placed on thermostatic chamber and are cooled down, constant temperature room temperature is 23 ± 2 DEG C, and relative humidity is After 50 ± 2%, constant temperature at least 24 hours, surface UV and tempering carried out to the semi-finished product, UV gram weight is 11~ 14g/m2, after being 50 ± 2 DEG C of baking oven section levelling by temperature, handled using ultraviolet curing, the product that UV processing is completed Tempering is carried out, heats 600 ± 10 revs/min of net revolving speed, the temperature of outlet piece is 90~95 DEG C, after tempering, is adopted Cooling with cooling water, the temperature of cooling water is 21~25 DEG C；E) it after surface UV tempering, resting on and does within thermostatic chamber 72 hours or more health processing, constant temperature room temperature is 23 ± 2 DEG C, Relative humidity 50 ± 2%；F) product after health is put into punching machine and is cut, then, deburring carried out to the sheet material obtained after cutting, is obtained To finished product.
- 8. glue according to claim 7 of exempting from is drowned oneself the production method on floor, it is characterised in that: the stirring in the step a) Speed control is between 1200~1500 revs/min.