CN110092624A - A kind of wheat stalk ash self-insulating concrete and preparation method thereof - Google Patents
A kind of wheat stalk ash self-insulating concrete and preparation method thereof Download PDFInfo
- Publication number
- CN110092624A CN110092624A CN201910410801.8A CN201910410801A CN110092624A CN 110092624 A CN110092624 A CN 110092624A CN 201910410801 A CN201910410801 A CN 201910410801A CN 110092624 A CN110092624 A CN 110092624A
- Authority
- CN
- China
- Prior art keywords
- wheat stalk
- cement
- ash
- mass ratio
- polystyrene foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of wheat stalk ash self-insulating concrete and preparation method thereof, concrete material component and its mass ratio are as follows: cement: wheat stalk ash: water: polystyrene foam=(2.5-3.0): (6.5-7.0): (0.18-0.2): (0.032-0.034) that mass concentration is 10%, cement is mixed with wheat stalk ash, obtains mixture;Water is added into mixture, obtains wheat stalk buck mud;The fine uniform foam of 1 ± 0.1mm is made by foaming machine in foamed polystyrene agent aqueous solution, polystyrene foam and wheat stalk buck mud are injected into mold after being sufficiently mixed with pouring pump, the condition of mold constant temperature and humidity after injection foam and wheat stalk buck mud are sufficiently mixed conserves 2~3 days, natural curing 7~10 days again after demoulding, obtain wheat stalk ash concrete test block, the advantages that present invention has good heat insulating, and production cost is low, and machinability is strong.
Description
Technical field
The present invention relates to technical field of concrete preparation, in particular to a kind of wheat stalk ash self-insulating concrete and its system
Preparation Method.
Background technique
China is a large agricultural country, and agricultural crops are resourceful.But being continuously increased with farm output, agricultural are useless
Gurry also increases therewith, and according to statistics, China crops biomass-stalk annual yield removes small part up to 6.4 hundred million tons
Outside for papermaking, sheet fabrication, most of stalk resource is fallen into disuse or on-site incineration, and the straw ash of generation does not only take up soil
Ground, while also generating volume of smoke and CO2, this causes serious influence to local environment.
Other biomass are compared to, the temperature of wheat stalk harvest season is high, easy drying, easily collecting;Wheat stalk ash
Impurity is few, matter is pure, be free of poisonous and harmful element, and have the characteristics that high activity, cheapness and high stability, can be used as original
Material is used for the production and processing of construction material.Research also found that the thermal resistance for adding a certain amount of straw ash concrete is higher than
Normal concrete is able to achieve concrete self-insulating function.
Polystyrene foam (Expanded Polystyrene abbreviation EPS) is a kind of light polymer.It is
Foaming agent is added using polystyrene resin, while heating is softened, and is generated gas, is formed a kind of bubble of rigid closed cell structure
Foam plastics.It has that relative density small (1.05g/cm3), thermal conductivity is low, water imbibition is small, impact resisting vibrating, heat-insulated, sound insulation, anti-
The advantages that tide, vibration damping, excellent dielectric properties, be widely used for mechanical equipment, instrument and meter, home electric, craftwork and other
The shock-resistant packaging material of valuable product easy to damage and the packaging of fast food.As global economy develops rapidly, polystyrene
The discarding amount of foamed plastics is growing day by day.These waste and old polystyrene foam plastics deals are light, volume is big, itself have again resistance to
The features such as aging, difficult corrosion, become a great problem of garbage disposal, the regeneration of expanded polystyrene (EPS) in recent years becomes industrial circle
One of the problem of most paying close attention to.
Summary of the invention
In order to overcome the above-mentioned deficiencies of the prior art, it is mixed that the purpose of the present invention is to provide a kind of wheat stalk ash self-heat conservings
Wheat stalk ash, foamed polystyrene agent aqueous solution and cement mixing can be prepared into concrete by solidifying soil and preparation method thereof,
The advantages that present invention has good heat insulating, and production cost is low, and machinability is strong, to realize the utilization again of resource, makes to build
It is more preferable to build thermal insulation property.
To achieve the goals above, the technical solution adopted by the present invention is that:
A kind of wheat stalk ash self-insulating concrete, raw material components and its mass ratio are as follows: cement: wheat stalk ash: water:
Polystyrene foam=(2.5-3.0): (6.5-7.0): (0.18-0.2): (0.032-0.034) that mass concentration is 10%.
A kind of preparation method of wheat stalk ash self-insulating concrete, the steps include:
Step 1: according to mass ratio be (2.5-3.0) by cement and wheat stalk ash: (6.5-7.0) is mixed, and is mixed
Close object;
Step 2: adding water into the mixture that step 1 obtains, and the mass ratio of mixture and water is 1:(0.18-
0.2) wheat stalk buck mud, is obtained;
Step 3: foamed polystyrene agent aqueous solution is made up to the fine uniform foam shape of 1 ± 0.1mm of foaming machine
The polystyrene foam that mass concentration is 10%, polystyrene foam and wheat stalk buck mud use pouring pump after being sufficiently mixed
It is injected into mold;The mass ratio of polystyrene foam and wheat stalk buck mud: (0.032-0.034): 1;
Step 4: the mold constant temperature and humidity of polystyrene foam and wheat stalk buck mud after injection is sufficiently mixed
Condition conserve 2~3 days, natural curing 7~10 days again after demoulding obtain wheat stalk ash concrete test block.
The condition of step four constant temperature and humidity are as follows: maintenance room temperature is constant at 20 DEG C ± 2 DEG C, and humidity is maintained at
95%RH or more.
The cement uses 42.5R ordinary portland cement.
Beneficial effects of the present invention:
The present invention uses wheat stalk ash, cement and polystyrene foam for material, has good heat insulating, production cost
It is low, the advantages that machinability is strong, to realize the utilization again of resource, keep building heat preservation performance more preferable.After tested, in other ginsengs
In the identical situation of number, the heat insulating coefficient of the concrete made from the method for the present invention is improved than the heat insulating coefficient of normal concrete
3%.
Specific embodiment
Below with reference to embodiment, invention is further described in detail.
Embodiment 1
A kind of wheat stalk ash self-insulating concrete, raw material components and its mass ratio are as follows: cement: wheat stalk ash: water:
Polystyrene foam=3:6.5:0.18:0.032 that mass concentration is 10%;The cement is 42.5R ordinary portland cement.
A kind of preparation method of wheat stalk ash self-insulating concrete, the steps include:
Step 1: cement is mixed with wheat stalk ash according to mass ratio for 3:6.5, obtains mixture, cement uses
42.5R ordinary portland cement;
Step 2: adding water into the mixture that step 1 obtains, and the mass ratio of mixture and water is 1:0.18, obtains
Wheat stalk buck mud;
Step 3: foamed polystyrene agent aqueous solution is made up to the fine uniform foam shape of 1 ± 0.1mm of foaming machine
The polystyrene foam that mass concentration is 10%, polystyrene foam and wheat stalk buck mud use pouring pump after being sufficiently mixed
It is injected into mold;The mass ratio of polystyrene foam and wheat stalk buck mud: 0.032:1;
Step 4: will inject the mold after foam and wheat stalk buck mud are sufficiently mixed temperature be 20 DEG C ± 2 DEG C,
The constant temperature and humidity condition that humidity is 95%RH conserves 2 days, natural curing 7 days again after demoulding, obtain wheat stalk ash concrete from
Keep the temperature test block.
After detection, wheat stalk ash concrete self-insulating test block thermal coefficient is 0.125W/ (m2K), thermal resistance is about general
8 times of logical concrete, strength grade is not less than MU5.
Embodiment 2
A kind of wheat stalk ash self-insulating concrete, raw material components and its mass ratio are as follows: cement: wheat stalk ash: water:
Polystyrene foam=2.5:6.5:0.19:0.033 that mass concentration is 10%;The cement is 42.5R normal silicate water
Mud.
A kind of wheat stalk ash self-insulating concrete and preparation method thereof, the steps include:
Step 1: cement is mixed with wheat stalk ash according to mass ratio for 2.5:6.5, obtains mixture, cement is adopted
With 42.5R ordinary portland cement;
Step 2: adding water into the mixture that step 1 obtains, and the mass ratio of mixture and water is 1:0.19, obtains
Wheat stalk buck mud;
Step 3: foamed polystyrene agent aqueous solution is made up to the fine uniform foam shape of 1 ± 0.1mm of foaming machine
The polystyrene foam that mass concentration is 10%, polystyrene foam and wheat stalk buck mud use pouring pump after being sufficiently mixed
It is injected into mold;The mass ratio of polystyrene foam and wheat stalk buck mud: 0.033:1;
Step 4: will inject the mold after foam and wheat stalk buck mud are sufficiently mixed temperature be 20 DEG C ± 2 DEG C,
Humidity is that the condition of the constant temperature and humidity of 95%RH conserves 3 days, and natural curing 8 days again after demoulding obtain wheat stalk ash concrete
Self-heat conserving test block.
After detection, wheat stalk ash concrete self-insulating test block thermal coefficient is 0.155W/ (m2K), thermal resistance is about general
9 times of logical concrete, strength grade is not less than MU5.
Embodiment 3
A kind of wheat stalk ash self-insulating concrete, raw material components and its mass ratio are as follows: cement: wheat stalk ash: water:
Polystyrene foam=3:7:0.20:0.034 that mass concentration is 10%;The cement is 42.5R ordinary portland cement.
A kind of wheat stalk ash self-insulating concrete and preparation method thereof, the steps include:
Step 1: cement is mixed with wheat stalk ash according to mass ratio for 3:7, obtains mixture, cement uses
42.5R ordinary portland cement;
Step 2: adding water into the mixture that step 1 obtains, and the mass ratio of mixture and water is 1:0.20, obtains
Wheat stalk buck mud;
Step 3: foamed polystyrene agent aqueous solution is made up to the fine uniform foam shape of 1 ± 0.1mm of foaming machine
The polystyrene foam that mass concentration is 10%, polystyrene foam and wheat stalk buck mud use pouring pump after being sufficiently mixed
It is injected into mold;The mass ratio of polystyrene foam and wheat stalk buck mud: 0.034:1;
Step 4: will inject the mold temperature after foam and wheat stalk buck mud are sufficiently mixed be 20 DEG C ± 2 DEG C, it is wet
Degree is that the condition of the constant temperature and humidity of 95%RH conserves 3 days, natural curing 10 days again after demoulding, obtain wheat stalk ash concrete from
Keep the temperature test block.
After detection, wheat stalk ash concrete self-insulating test block thermal coefficient is 0.215W/ (m2K), thermal resistance is about general
10 times of logical concrete, strength grade is not less than MU5.
Claims (10)
1. a kind of wheat stalk ash self-insulating concrete, it is characterised in that: its raw material components and its mass ratio are as follows: cement: wheat
Straw ash: water: polystyrene foam=(2.5-3.0): (6.5-7.0): (0.18-0.2) that mass concentration is 10%:
(0.032-0.034)。
2. a kind of wheat stalk ash self-insulating concrete according to claim 1, it is characterised in that: its raw material components and its
Mass ratio are as follows: cement: wheat stalk ash: water: polystyrene foam=3 that mass concentration is 10%: 6.5: 0.18: 0.032;Institute
Stating cement is 42.5R ordinary portland cement.
3. a kind of wheat stalk ash self-insulating concrete according to claim 1, it is characterised in that: its raw material components and its
Mass ratio are as follows: cement: wheat stalk ash: water: polystyrene foam=2.5 that mass concentration is 10%: 6.5: 0.19: 0.033;
The cement is 42.5R ordinary portland cement.
4. a kind of wheat stalk ash self-insulating concrete according to claim 1, it is characterised in that: its raw material components and its
Mass ratio are as follows: cement: wheat stalk ash: water: polystyrene foam=3 that mass concentration is 10%: 7: 0.20: 0.034;It is described
Cement is 42.5R ordinary portland cement.
5. a kind of wheat stalk ash self-insulating concrete according to claim 1, it is characterised in that: the cement uses
42.5R ordinary portland cement.
6. a kind of preparation method of wheat stalk ash self-insulating concrete, it is characterised in that: the steps include:
Step 1: according to mass ratio be (2.5-3.0) by cement and wheat stalk ash: (6.5-7.0) is mixed, and is mixed
Object;
Step 2: adding water into the mixture that step 1 obtains, and the mass ratio of mixture and water is 1: (0.18-0.2) is obtained
To wheat stalk buck mud;
Step 3: foamed polystyrene agent aqueous solution is made up to the quality of the fine uniform foam shape of 1 ± 0.1mm of foaming machine
The polystyrene foam that concentration is 10%, polystyrene foam and wheat stalk buck mud are injected after being sufficiently mixed with pouring pump
Into mold;The mass ratio of polystyrene foam and wheat stalk buck mud: (0.032-0.034): 1;
Step 4: the mold temperature after injection foam and wheat stalk buck mud are sufficiently mixed is 20 DEG C ± 2 DEG C, humidity is
The condition of the constant temperature and humidity of 95%RH conserves 2~3 days, and natural curing 7~10 days again after demoulding obtain wheat stalk ash concrete
Test block.
7. a kind of preparation method of wheat stalk ash self-insulating concrete according to claim 6, it is characterised in that: it is walked
Suddenly are as follows:
Step 1: cement is mixed with wheat stalk ash according to mass ratio for 3: 6.5, obtains mixture, cement uses 42.5R
Ordinary portland cement;
Step 2: adding water into the mixture that step 1 obtains, and the mass ratio of mixture and water is 1: 0.18, obtains wheat
Straw ash cement slurry;
Step 3: foamed polystyrene agent aqueous solution is made up to the quality of the fine uniform foam shape of 1 ± 0.1mm of foaming machine
The polystyrene foam that concentration is 10%, polystyrene foam and wheat stalk buck mud are injected after being sufficiently mixed with pouring pump
Into mold;The mass ratio of polystyrene foam and wheat stalk buck mud: 0.032: 1;
Step 4: the mold temperature after injection foam and wheat stalk buck mud are sufficiently mixed is 20 DEG C ± 2 DEG C, humidity is
The condition of the constant temperature and humidity of 95%RH conserves 2 days, and natural curing 7 days again after demoulding obtain wheat stalk ash concrete self-insulating
Test block.
8. a kind of preparation method of wheat stalk ash self-insulating concrete according to claim 6, it is characterised in that: it is walked
Suddenly are as follows:
Step 1: cement is mixed with wheat stalk ash according to mass ratio for 2.5: 6.5, obtains mixture, cement uses
42.5R ordinary portland cement;
Step 2: adding water into the mixture that step 1 obtains, and the mass ratio of mixture and water is 1: 0.19, obtains wheat
Straw ash cement slurry;
Step 3: foamed polystyrene agent aqueous solution is made up to the quality of the fine uniform foam shape of 1 ± 0.1mm of foaming machine
The polystyrene foam that concentration is 10%, polystyrene foam and wheat stalk buck mud are injected after being sufficiently mixed with pouring pump
Into mold;The mass ratio of polystyrene foam and wheat stalk buck mud: 0.033: 1;
Step 4: the mold temperature after injection foam and wheat stalk buck mud are sufficiently mixed is 20 DEG C ± 2 DEG C, humidity is
The condition of the constant temperature and humidity of 95%RH conserves 3 days, and natural curing 8 days again after demoulding obtain wheat stalk ash concrete self-insulating
Test block.
9. a kind of preparation method of wheat stalk ash self-insulating concrete according to claim 6, it is characterised in that: it is walked
Suddenly are as follows:
Step 1: cement is mixed with wheat stalk ash according to mass ratio for 3: 7, obtains mixture, cement is general using 42.5R
Logical portland cement;
Step 2: adding water into the mixture that step 1 obtains, and the mass ratio of mixture and water is 1: 0.20, obtains wheat
Straw ash cement slurry;
Step 3: foamed polystyrene agent aqueous solution is made up to the quality of the fine uniform foam shape of 1 ± 0.1mm of foaming machine
The polystyrene foam that concentration is 10%, polystyrene foam and wheat stalk buck mud are injected after being sufficiently mixed with pouring pump
Into mold;The mass ratio of polystyrene foam and wheat stalk buck mud: 0.034: 1;
Step 4: the mold temperature after injection foam and wheat stalk buck mud are sufficiently mixed is 20 DEG C ± 2 DEG C, humidity is
The condition of the constant temperature and humidity of 95%RH conserves 3 days, and natural curing 10 days again after demoulding obtain wheat stalk ash concrete self-insulating
Test block.
10. a kind of preparation method of wheat stalk ash self-insulating concrete according to claim 6, it is characterised in that: institute
The condition of four constant temperature and humidity of the step of stating are as follows: maintenance room temperature is constant at 20 DEG C ± 2 DEG C, and humidity is maintained at 95%RH or more.