CN110090791A - A kind of floor nano-liquid crystal film plating process - Google Patents
A kind of floor nano-liquid crystal film plating process Download PDFInfo
- Publication number
- CN110090791A CN110090791A CN201910517793.7A CN201910517793A CN110090791A CN 110090791 A CN110090791 A CN 110090791A CN 201910517793 A CN201910517793 A CN 201910517793A CN 110090791 A CN110090791 A CN 110090791A
- Authority
- CN
- China
- Prior art keywords
- floor
- liquid crystal
- nano
- pretreating agent
- plated film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of floor nano-liquid crystal film plating process, the following steps are included: (1) prepares pretreating agent: the pretreating agent adds water to mix by oxalic acid and alum: the polishing on (2) floor: after the pretreating agent is uniformly sprayed on the floor that need to be handled, carrying out polishing and deep clean to floor by crystal plane retreading machine lower wire cotton；(3) floor-cleaning: the steel wool clast and dust and dirt of crystal plane retreading machine are exhausted using high power vacuum cleaner；(4) degreasing is cleaned: being carried out degreasing to floor using the fiber cloth for soaking alcohol and is cleaned 2 times；(5) after floor is thoroughly dried, using fiber mop, nano-liquid crystal plated film oil is equably uniformly applied to floor surface and waits for the dry nano-liquid crystal plated film for completing floor by dynamics.Floor nano-liquid crystal film plating process of the invention enhances nano-liquid crystal plated film in the adhesive force of body surface, and nano-liquid crystal plated film oil is very smooth during smearing, obtains optimal practical function.
Description
Technical field
The present invention relates to coating process, and in particular to the nano-liquid crystal film plating process of a kind of timber floor, plastic floor.
Background technique
Good floor is not only it is noted that daily cleaning, floor protecting same important, timber floor and plastic floor, such as
Fruit maintenance is improper, is easy to scratch, is not easy to arrange；It is irradiated with ultraviolet radiation and can fade for a long time, it may appear that floor cracking influences floor
Service life.
Floor nano-liquid crystal plated film oil is a kind of novel nano antifouling product, after being applied to floor, by with hydroxyl
Base gas phase reaction film-forming, this protective film is after material surface is formed, and such as the invisible glass of same layer, doing cleaning becomes
It is abnormal simple；Simultaneously realize floor water repellent, anti-pollution, it is wear-resisting, anti-skidding, easily arrange, anti-paste, anti-graffiti, resisting ultraviolet radiation, suppression
Bacterium and other effects, base compensate for floor wax and all deficiency of essential oil.After nano-liquid crystal plated film oil film-forming, protective film is formed
Molecular structure it is very small, the 51 percent of the hair width of people are equivalent to, than hydrone, even than hundreds of bacterium monomers
It also wants small, infiltration can not be adhered to using the hydrone in rear material, bacterium, spot, effectively extend floor maintenance period, however
During practice of construction, adhesive force caused by nano-liquid crystal plated film oil is directly brushed is bad, leverages the reality of floor plated film
Border using effect and service life, but for improve adhesive force polished using sand paper, caused by paint surface damage or surface damage it is irreversible
Turn；More since the bad adhesive force of floor-cleaning effect is not strong, by drag effects in painting process, make to smear it is not smooth enough and
It applies unevenly, so that floor plated film overall effect be made to have a greatly reduced quality.
Summary of the invention
For above situation, the object of the present invention is to provide a kind of floor nano-liquid crystal film plating process, enhance nano-liquid crystal
For plated film in the adhesive force of body surface, nano-liquid crystal plated film oil is very smooth during smearing, obtains optimal practical function,
And service life 2 years or more of floor after plated film can be extended.
Technical scheme is as follows: a kind of floor nano-liquid crystal film plating process, comprising the following steps:
(1) prepare pretreating agent: the pretreating agent adds water to mix by oxalic acid and alum, the oxalic acid and alum, water
Ratio is 8:2:100, and it is stand-by to be formulated pretreating agent according to the ratio:
(2) polishing on floor: after the pretreating agent is uniformly sprayed on the floor that need to be handled, by below crystal plane retreading machine
Steel wool carries out polishing and deep clean to floor, is uniformly dried pretreating agent by crystal plane retreading machine；
(3) floor-cleaning: the steel wool clast and dust and dirt of crystal plane retreading machine are exhausted using high power vacuum cleaner；
(4) degreasing is cleaned: being carried out degreasing to floor using the fiber cloth for soaking alcohol and is cleaned 2 times；
(5) nano-liquid crystal plated film: after floor is thoroughly dried, using fiber mop, dynamics is equably by nano-liquid crystal plated film oil
It is uniformly applied to floor surface and waits for the dry nano-liquid crystal plated film for completing floor.
Preferably, the steel wool that the crystal plane retreading machine uses is No. 0 or No. 1 steel wool.
Preferably, the fountain height that the pretreating agent is sprayed to floor is 30-50ml/ ㎡, and it is clear that floor both can reach depth
Clean, crystal plane retreading machine can also will dry pretreating agent uniformly.
Preferably, the alcohol concentration that step (4) the degreasing cleaning uses is greater than 75%.
Floor nano-liquid crystal film plating process of the invention, is formulated using crystal plane retreading machine combination oxalic acid and alum and water
Pretreating agent, crystal face machine steel wool and floor friction rise thermal process in, by steel wool friction generate physics it is micro-
Theomorphism removes spot trace and does not hurt floor surface, while pretreating agent carries out timber floor or plastic floor surface
Deep clean, pretreating agent ingredient mesoxalic acid plays the role of cleaning ceride, grease, lubrication, and alum can play stabilizer
Effect, finally by using alcohol to carry out reinforcing ungrease treatment to floor, reinforces the effect of its surface adhesion force, side of the invention
Method is clean while steel wool becomes trace in the miniflow that floor surface friction generates can solve adhesion problem from the root, together
When pretreating agent ingredient in oxalic acid and alum lubrication property solve the problems, such as that plated film oil is not smooth enough during smearing.
Floor nano-liquid crystal film plating process of the invention enhances nano-liquid crystal plated film in the adhesive force of body surface, warp
The floor surface of processing is crossed, it is very smooth during smearing, to obtain ideal perception, and with can extending after plated film
Service life 2 years or more of plate.
Specific embodiment
Below with reference to embodiment, technical solution of the present invention is described in more detail:
Embodiment 1
A kind of floor nano-liquid crystal film plating process, comprising the following steps:
(1) prepare pretreating agent: the pretreating agent is mixed by oxalic acid and alum, water, takes oxalic acid 8kg, 2 kg of alum, water
100 kg, alum is ground into after powder be mixed evenly with oxalic acid and water it is to be used；
(2) polishing on floor: after the pretreating agent is uniformly sprayed on the floor that need to be handled, fountain height is logical for 30ml/ ㎡
The frictional force for crossing crystal plane retreading machine lower wire cotton carries out polishing and deep clean to floor, will be pre-processed by crystal plane retreading machine
Agent dries uniformly, and the crystal plane retreading machine steel wool selects No. 0 steel wool；
(3) floor-cleaning: the steel wool clast and dust and dirt of crystal plane retreading machine are exhausted using high power vacuum cleaner；
(4) degreasing is cleaned: carrying out degreasing cleaning 2 times to floor using the fiber cloth that concentration is 75% alcohol is soaked；
(5) nano-liquid crystal plated film: after floor is thoroughly dried, nano-liquid crystal plated film oil dynamics is uniformly smeared using fiber mop
The dry nano-liquid crystal plated film for completing floor is waited in floor surface.
Embodiment 2
A kind of floor nano-liquid crystal film plating process, comprising the following steps:
(1) prepare pretreating agent: the pretreating agent is mixed by oxalic acid and alum, water, takes oxalic acid 16kg, alum 4kg, water
200kg, alum is ground into after powder be mixed evenly with oxalic acid, water it is to be used；
(2) polishing on floor: after the pretreating agent is uniformly sprayed on the floor that need to be handled, fountain height is 50ml/ ㎡, is led to
The frictional force for crossing crystal plane retreading machine lower wire cotton carries out polishing and deep clean to floor, will be pre-processed by crystal plane retreading machine
Agent dries uniformly, and the crystal plane retreading machine steel wool selects No. 0 steel wool；
(3) floor-cleaning: the steel wool clast and dust and dirt of crystal plane retreading machine are exhausted using high power vacuum cleaner；
(4) degreasing is cleaned: carrying out degreasing cleaning 2 times to floor using the fiber cloth that concentration is 80% alcohol is soaked；
(5) nano-liquid crystal plated film: it is using fiber mop, nano-liquid crystal plated film oil dynamics is uniform after floor is thoroughly dried, it applies
It smears and waits doing in floor surface, that is, complete the nano-liquid crystal plated film on floor.
Embodiment 3
A kind of floor nano-liquid crystal film plating process, comprising the following steps:
(1) prepare pretreating agent: the pretreating agent is mixed by oxalic acid and alum, water, takes oxalic acid 4kg, alum 1kg, water
50kg, alum is ground into after powder be mixed evenly with oxalic acid, water it is to be used；
(2) polishing on floor: after the pretreating agent is uniformly sprayed on the floor that need to be handled, fountain height is 40ml/ ㎡, is led to
The frictional force for crossing crystal plane retreading machine lower wire cotton carries out polishing and deep clean to floor, will be pre-processed by crystal plane retreading machine
Agent dries uniformly, and the crystal plane retreading machine steel wool selects No. 1 steel wool；
(3) floor-cleaning: the steel wool clast and dust and dirt of crystal plane retreading machine are exhausted using high power vacuum cleaner；
(4) degreasing is cleaned: carrying out degreasing cleaning 2 times to floor using the fiber cloth that concentration is 90% alcohol is soaked；
(5) nano-liquid crystal plated film: after floor is thoroughly dried, nano-liquid crystal plated film oil dynamics is uniformly smeared using fiber mop
The dry nano-liquid crystal plated film for completing floor is waited in floor surface.
Claims (4)
1. a kind of floor nano-liquid crystal film plating process, it is characterised in that the following steps are included:
(1) prepare pretreating agent: the pretreating agent adds water to mix by oxalic acid and alum, the oxalic acid and alum, water
Ratio is 8:2:100, and it is stand-by to be formulated pretreating agent according to the ratio:
(2) polishing on floor: after the pretreating agent is uniformly sprayed on the floor that need to be handled, by below crystal plane retreading machine
Steel wool carries out polishing and deep clean to floor, is uniformly dried pretreating agent by crystal plane retreading machine；
(3) floor-cleaning: the steel wool clast and dust and dirt of crystal plane retreading machine are exhausted using high power vacuum cleaner；
(4) degreasing is cleaned: being carried out degreasing to floor using the fiber cloth for soaking alcohol and is cleaned 2 times；
(5) nano-liquid crystal plated film: after floor is thoroughly dried, using fiber mop, dynamics is equably by nano-liquid crystal plated film oil
It is uniformly applied to floor surface and waits for the dry nano-liquid crystal plated film for completing floor.
2. nano-liquid crystal film plating process in floor according to claim 1, it is characterised in that the crystal plane retreading machine used
Steel wool is No. 0 or No. 1 steel wool.
3. nano-liquid crystal film plating process in floor according to claim 1, it is characterised in that the pretreating agent is sprayed to bottom
The fountain height of plate is 30-50ml/ ㎡.
4. nano-liquid crystal film plating process in floor according to claim 1, it is characterised in that step (4) the degreasing cleaning makes
Alcohol concentration is greater than 75%.