CN110079060A - Improve level-dyeing property Masterbatch and preparation method thereof - Google Patents
Improve level-dyeing property Masterbatch and preparation method thereof Download PDFInfo
- Publication number
- CN110079060A CN110079060A CN201910254884.6A CN201910254884A CN110079060A CN 110079060 A CN110079060 A CN 110079060A CN 201910254884 A CN201910254884 A CN 201910254884A CN 110079060 A CN110079060 A CN 110079060A
- Authority
- CN
- China
- Prior art keywords
- super absorbent
- absorbent resin
- dyeing property
- masterbatch
- level
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of raising level-dyeing property Masterbatch and preparation method thereof.The raw material composition of the Masterbatch includes vector resin and super absorbent resin, and super absorbent resin is the graft copolymer that starch or at least two hydrophilic monomer of cellulose graft are formed, and is adsorbed with disperse dyes in super absorbent resin.The application adds super absorbent resin to load disperse dyes in Masterbatch, it distributed countless three-dimensional space network structures in super absorbent resin made of being graft-polymerized as starch and at least two hydrophilic monomers, when the super absorbent resin is immersed in the suspension of disperse dyes, disperse dyes can enter three-dimensional space network structure with water, after being dried to super absorbent resin, hydrone evaporation, and disperse dyes then and are firmly locked in super absorbent resin.Polyester fiber is made using the Masterbatch, disperse dyes were not only can be uniformly dispersed to polyester fiber, but also will not be migrated, and farthest ensured the level-dyeing property of disperse dyes.
Description
Technical field
The invention belongs to Masterbatch technical fields, and in particular to a kind of raising level-dyeing property Masterbatch and preparation method thereof.
Background technique
Level-dyeing property refers to dyestuff ability of self level dyeing on the fabric in dyeing course.It is removed by dye molecule and fiber
Outside the impact on physical properties of matrix, also by the system of many factors such as dyeing condition such as temperature, dyeing rate, dyeing assistant used
About.Therefore, mode fabric direct invasion dyed into dyestuff is often difficult to obtain the preferable fabric of level-dyeing property.
In order to improve the level-dyeing property of fabric, application No. is the Chinese invention patent applications of CN 201710599876.6 to disclose
A kind of for improving the Color master batch of terylene ribbon level-dyeing property, which is made of the raw material of following parts by weight: double
15-30 parts of phenol A type liquid-state epoxy resin, 5-10 parts of natural organic dye, 1-5 parts of nonylphenol polyoxyethylene ether, cetanol 0.5-2
Part, 0.5-2 parts of tri (propylene glycol) diacrylate, 0.05-0.5 parts of trihydroxymethylpropanyltri diglycidyl ether, the poly- horse of hydrolysis
Come 0.05-0.5 parts of acid anhydrides.
In use, above-mentioned Color master batch is added in 5 times of weight waters, it is warming up to reflux state insulated and stirred 15min,
Obtain dye liquor;Then the dye liquor is used for the dyeing of terylene ribbon using traditional dyeing.
The Color master batch is disadvantageous in that: only with bisphenol A-type liquid epoxy resin and other auxiliary agents load dye
Material, when use, are still required that dye liquor is made, and this traditional dyeing makes the resin of carried dye and auxiliary agent is still
It is attached to PET fiber surface, is inevitably present traditional dyeing process limitation caused by level-dyeing property;And only adhere to
Fiber surface fuel there is also the problem of dyefastness difference, the dye molecule for having adsorbed on the fabric, which is still easy to happen, to be moved
It moves, can this keep the level-dyeing property of fabric to also proposed very big challenge.
Summary of the invention
Present invention purpose is to provide a kind of raising level-dyeing property Masterbatch and preparation method thereof, uses the Masterbatch energy
Limitation of the traditional dyeing process to dyeing polyester fibers is enough broken through, improves disperse dyes to the level-dyeing property of dyeing polyester fibers.
For achieving the above object, the technical solution of the application is as follows:
A kind of raising level-dyeing property Masterbatch, raw material composition include vector resin and super absorbent resin, the high water absorption
Property resin be graft copolymer that starch or at least two hydrophilic monomer of cellulose graft are formed, the super absorbent resin
Inside it is adsorbed with disperse dyes.
The application adds super absorbent resin to load disperse dyes, by starch and at least two parents in the Masterbatch
It distributed the countless three-dimensional space network structures for being used to accommodate water in super absorbent resin made of aqueous monomers are graft-polymerized,
When immersing the super absorbent resin in the suspension of disperse dyes, disperse dyes can enter these three-dimensional space with dampening
Network structure, after being dried to super absorbent resin, hydrone evaporation, and disperse dyes then and are firmly locked in height
In water-absorbing resins.Polyester fiber is made using the Masterbatch containing this super absorbent resin, disperse dyes can uniformly divide
It is dissipated in polyester fiber, and will not migrate, farthest ensure the level-dyeing property of disperse dyes.
In above-mentioned raising level-dyeing property Masterbatch, the super absorbent resin surface has porous structure.High water absorption
The porous structure of property resin surface is capable of increasing the specific surface area of super absorbent resin, can not only improve the absorption of disperse dyes
Amount, and disperse dyes can be promoted quickly to be adsorbed in its three-dimensional space network structure.
In above-mentioned raising level-dyeing property Masterbatch, in the super absorbent resin, percent opening is greater than 50%.
The super absorbent resin that can satisfy the application condition has very much, as the reality more conventional, use scope is wider
Example is applied, in above-mentioned raising level-dyeing property Masterbatch, the super absorbent resin is Starch-Acrylic acid-Acrylamide ternary
Graft copolymer.Certainly, in addition to Starch-Acrylic acid-Acrylamide ternary graft copolymer, those skilled in the art can be selected
Other kinds of ternary (or more member) graft copolymer, as long as being formed with three-dimensional space network structure in these graft copolymers
It is suitable for the application.
In above-mentioned raising level-dyeing property Masterbatch, according to the mass fraction, raw material composition include 85-99 part vector resins with
1-15 parts of super absorbent resins.
In above-mentioned raising level-dyeing property Masterbatch, the vector resin is PET resin.
The preparation method of the described raising level-dyeing property Masterbatch the following steps are included:
(1) super absorbent resin is obtained;
(2) disperse dyes and dispersing aid are ground to after partial size is 2 μm or less and are mixed in water, suspension is made;
(3) super absorbent resin is immersed in the suspension, under 30 DEG C of waters bath with thermostatic control, makes high water absorption
Property resin sufficiently adsorbs;
(4) super absorbent resin of abundant absorption suspension is dry, grinding obtains super absorbent resin micro mist;
(5) preset mass parts are pressed, after the super absorbent resin micro mist is blended with vector resin, extruding pelletization,
Obtain the raising level-dyeing property Masterbatch.
In the preparation method of above-mentioned raising level-dyeing property Masterbatch, in step (1), the system of the super absorbent resin
Preparation Method the following steps are included:
(a) starch for accounting for total monomer quality (i.e. the quality of acrylic acid and acrylamide and) 3% is added in the reaction vessel
With 25-30mL water, 80 DEG C are heated to, makes starch gelatinization, obtains gelatinization of starch solution;
(b) when gelatinization of starch solution is cooled to 40-50 DEG C, initiator is added under nitrogen protection;
The initiator can select ammonium persulfate-sodium sulfite to cause system, the initiator and total monomer
Molar ratio is (2-5): 1000.Initiator amount is excessive, will lead to crosslinking it is too fast, system viscosity is uprushed, and product is caused to gush.
(c) in lye and acrylic acid to a mole degree of neutralization be 65-70%, obtain acrylic acid neutralizer;
(d) it is added drop-wise in gelatinization of starch solution after mixing acrylic acid neutralizer and acrylamide with molar ratio 10:3, together
When crosslinking agent and foaming agent are added into gelatinization of starch solution, be stirred to react 3h at 60 DEG C;
The crosslinking agent can select N, N '-methylene-bisacrylamide, mole of the crosslinking agent and total monomer
Than for (0.2-0.3): 1000.It is appropriate that suitable crosslinking agent can ensure to be crosslinked, and makes to hold in the three-dimensional space network being cross-linked to form
The space of Na Shui reaches maximum as much as possible, and crosslinking agent is excessive or the suction of the very few three-dimensional space network that can all influence to be cross-linked to form
Water water retention property.
The foaming agent can select bicarbonate, such as sodium bicarbonate and/or saleratus, the use of the foaming agent
Amount and the molar ratio of total monomer are (2-6): 1000.
(e) sufficiently after reaction, reaction product is precipitated with dehydrated alcohol, filters, obtains after being washed with acetone to precipitating
Obtain solid polymer;After the fixed polymer drying, grind into powder obtains the super absorbent resin.
In the preparation method of above-mentioned raising level-dyeing property Masterbatch, in step (4), it is dried in vacuo at 120-140 DEG C
8-10h。
Present invention also provides the raising level-dyeing property Masterbatch to prepare the application in polyester fiber, the application
Include: that described 3-6 parts of raising level-dyeing property Masterbatch are blended with 95-97 parts of normal polyester, is blended after vacuum dried
Melt spinning obtains the polyester fiber.
Compared with prior art, the application has the beneficial effect that:
In the raising level-dyeing property Masterbatch of the application added with super absorbent resin to load disperse dyes, by starch with
It distributed the countless three-dimensional spaces for being used to accommodate water in super absorbent resin made of at least two hydrophilic monomers are graft-polymerized
Between network structure, when by the super absorbent resin immerse disperse dyes suspension in when, disperse dyes can enter with dampening
These three-dimensional space network structures, after being dried to super absorbent resin, hydrone evaporation, and disperse dyes are then and quilt
It is firmly locked in super absorbent resin.Polyester fiber, dispersion dye are made using the Masterbatch containing this super absorbent resin
Material was not only can be uniformly dispersed to polyester fiber, but also will not be migrated, and farthest ensured the level-dyeing property of disperse dyes.
Specific embodiment
Specific embodiment is set forth below, and further details of the technical solution of the present invention.
Embodiment 1
1, super absorbent resin is prepared
A kind of preparation method of super absorbent resin of the present embodiment the following steps are included:
(a) starch for accounting for total monomer quality (i.e. the quality of acrylic acid and acrylamide and) 3% is added in the reaction vessel
With 25-30mL water, 80 DEG C are heated to, makes starch gelatinization, obtains gelatinization of starch solution;
(b) when gelatinization of starch solution is cooled to 40-50 DEG C, ammonium persulfate-sodium sulfite is added under nitrogen protection and draws
Hair system, the ammonium persulfate-sodium sulfite cause system (concentration of ammonium persulfate and sodium sulfite is 0.05mol/L) and total
The molar ratio of monomer is 3:1000;
(c) it uses in sodium hydroxide solution and acrylic acid to mole degree of neutralization is 70%, obtain acrylic acid neutralizer;
(d) gelatinization of starch solution is added drop-wise to after mixing acrylic acid neutralizer and acrylamide with monomer mole ratio 10:3
In, while the N that concentration is 0.1mol/L, N '-methylene-bisacrylamide (crosslinking agent, the friendship being added into gelatinization of starch solution
The molar ratio for joining agent and total monomer is 0.3:1000), 3h is stirred to react at 60 DEG C;
(e) sufficiently after reaction, reaction product is precipitated with dehydrated alcohol, filters, obtains after being washed with acetone to precipitating
Obtain solid polymer;Fixed polymer is placed at 135 DEG C dry vacuum drying 8-10h, grind into powder obtains the present embodiment
Super absorbent resin.
2, Masterbatch is prepared
A kind of preparation method for improving level-dyeing property Masterbatch of the present embodiment, comprising the following steps:
(1) super absorbent resin of above-mentioned preparation is taken, it is spare;
(2) disperse dyes and dispersing aid are ground to after partial size is 2 μm or less and are mixed in water, suspension is made;
The present embodiment has randomly selected low form disperse yellow 3 (No. CAS: 2832-40-8) as disperse dyes, chooses NNO
Add water after mixing disperse dyes according to mass ratio 1:1.5 with dispersing aid as dispersing aid, as corpusculed handle to
Spray drying after partial size reaches 2 μm or less, is made dyestuff finished product, then takes and dyestuff is mixed in deionized water, be configured to concentration
For 1% suspension;
(3) super absorbent resin is immersed in suspension, under 30 DEG C of waters bath with thermostatic control, inhales super absorbent resin sufficiently
It is attached;
(4) super absorbent resin of abundant absorption suspension is placed at 135 DEG C and is dried in vacuo 10h, ground, obtain high inhale
Water-base resin micro mist;
(5) after taking 10 parts of super absorbent resin micro mists to be blended with 90 parts of vector resins, extruding pelletization (twin-screw extrusion temperature
It is 240-273 DEG C), obtain the raising level-dyeing property Masterbatch of the present embodiment.
3, polyester fiber is prepared
4 parts of raising level-dyeing property Masterbatch of above-mentioned preparation are blended in a high speed mixer with 96 parts of normal polyester, through true
It dallies and carries out blend melt spinning after rousing oven drying on single screw rod spinning machine, 270-288 DEG C of spinning temperature, spinning speed
1000m/min, line density 204dtex, the drafting multiple 3.5 of spun filament, obtain the polyester fiber of the present embodiment.
Embodiment 2
1, preparation has the super absorbent resin of porous structure
A kind of preparation method of super absorbent resin of the present embodiment the following steps are included:
(a) starch for accounting for total monomer quality (i.e. the quality of acrylic acid and acrylamide and) 3% is added in the reaction vessel
With 25-30mL water, 80 DEG C are heated to, makes starch gelatinization, obtains gelatinization of starch solution;
(b) when gelatinization of starch solution is cooled to 40-50 DEG C, ammonium persulfate-sodium sulfite is added under nitrogen protection and draws
Hair system, the ammonium persulfate-sodium sulfite cause system (concentration of ammonium persulfate and sodium sulfite is 0.05mol/L) and total
The molar ratio of monomer is 3:1000;
(c) it uses in sodium hydroxide solution and acrylic acid to mole degree of neutralization is 70%, obtain acrylic acid neutralizer;
(d) gelatinization of starch solution is added drop-wise to after mixing acrylic acid neutralizer and acrylamide with monomer mole ratio 10:3
In, while the N that concentration is 0.1mol/L, N '-methylene-bisacrylamide (crosslinking agent, the friendship being added into gelatinization of starch solution
The molar ratio for joining agent and total monomer be 0.3:1000) and concentration be 0.2mol/L sodium bicarbonate (foaming agent, the foaming agent with always
The molar ratio of monomer is 4:1000), 3h is stirred to react at 60 DEG C;
(e) sufficiently after reaction, reaction product is precipitated with dehydrated alcohol, filters, obtains after being washed with acetone to precipitating
Obtain solid polymer;Fixed polymer is placed at 135 DEG C dry vacuum drying 8-10h, grind into powder obtains the present embodiment
The super absorbent resin with porous structure.
2, Masterbatch is prepared
A kind of preparation method for improving level-dyeing property Masterbatch of the present embodiment, comprising the following steps:
(1) super absorbent resin of above-mentioned preparation is taken, it is spare;
(2) disperse dyes and dispersing aid are ground to after partial size is 2 μm or less and are mixed in water, suspension is made;
The present embodiment has randomly selected low form disperse yellow 3 (No. CAS: 2832-40-8) as disperse dyes, chooses NNO
Add water after mixing disperse dyes according to mass ratio 1:1.5 with dispersing aid as dispersing aid, as corpusculed handle to
Spray drying after partial size reaches 2 μm or less, is made dyestuff finished product, then takes and dyestuff is mixed in deionized water, be configured to concentration
For 1% suspension;
(3) super absorbent resin is immersed in suspension, under 30 DEG C of waters bath with thermostatic control, inhales super absorbent resin sufficiently
It is attached;
(4) super absorbent resin of abundant absorption suspension is placed at 135 DEG C and is dried in vacuo 10h, ground, obtain high inhale
Water-base resin micro mist;
(5) after taking 10 parts of super absorbent resin micro mists to be blended with 90 parts of vector resins, extruding pelletization (twin-screw extrusion temperature
It is 240-273 DEG C), obtain the raising level-dyeing property Masterbatch of the present embodiment.
3, polyester fiber is prepared
4 parts of raising level-dyeing property Masterbatch of above-mentioned preparation are blended in a high speed mixer with 96 parts of normal polyester, through true
It dallies and carries out blend melt spinning after rousing oven drying on single screw rod spinning machine, 270-288 DEG C of spinning temperature, spinning speed
1000m/min, line density 204dtex, the drafting multiple 3.5 of spun filament, obtain the polyester fiber of the present embodiment.
Comparative example 1
Conventional polyester fiber is dyed using disperse yellow 3 using traditional dye bath colouring method.
Every dyeability of the polyester fiber of embodiment 1, embodiment 2 and comparative example 1 preparation is tested respectively.
(1) level-dyeing property is tested: being taken up an official post in polyester fiber and is taken at 8 points, measures it in the K/S value of maximum absorption wave strong point, and press
The average color depth K/S value and relative deviation Sr (λ) of following formula calculating each point;Relative deviation Sr (λ) value is smaller, and level-dyeing property is better:
Test result is shown in Table 1.
Table 1
Polyester fiber | Relative deviation Sr (λ) |
Embodiment 1 | 0.80124 |
Embodiment 2 | 0.80121 |
Comparative example 1 | 1.21973 |
Seen from table 1, polyester fiber prepared by embodiment 1 and embodiment 2, K/S value relative standard deviation values are only about
0.8, and the K/S value relative standard deviation values of comparative example are up to 1.2;Show that the polyester fiber of the application preparation has splendid level dyeing
Property.
(2) color fastness is tested: by GB/T 3920-2008, " textile color stability tests rub resistance color jail to fastness to rubbing
Degree " test, soaping fastness is by GB/T 3921-2008 " textile color stability test WASHING COLOR FASTNESS " test;Test result is shown in Table
2。
Table 2
As can be seen from Table 2, polyester fiber prepared by embodiment 1 and embodiment 2 shows excellent color under each test
Fastness, and the color fastness of a kind of the comparative example polyester fiber using conventional dye bath method dyeing acquisition is then poor.
Claims (10)
1. a kind of raising level-dyeing property Masterbatch, which is characterized in that raw material composition includes vector resin and super absorbent resin, described
Super absorbent resin be graft copolymer that starch or at least two hydrophilic monomer of cellulose graft are formed, it is described high to inhale
Disperse dyes are adsorbed in water-base resin.
2. improving level-dyeing property Masterbatch as described in claim 1, which is characterized in that the super absorbent resin surface has
Porous structure.
3. improving level-dyeing property Masterbatch as described in claim 1, which is characterized in that in the super absorbent resin, aperture
Rate is greater than 50%.
4. the raising level-dyeing property Masterbatch as described in any one of claim 1-3, which is characterized in that the high-hydroscopicity
Resin is Starch-Acrylic acid-Acrylamide ternary graft copolymer.
5. the raising level-dyeing property Masterbatch as described in any one of claim 1-3, which is characterized in that according to the mass fraction,
Raw material composition includes 85-99 parts of vector resins and 1-15 parts of super absorbent resins.
6. the raising level-dyeing property Masterbatch as described in any one of claim 1-3, which is characterized in that the vector resin
For PET resin.
7. the preparation method of the raising level-dyeing property Masterbatch as described in any one of claim 1-6, which is characterized in that including
Following steps:
(1) super absorbent resin is obtained;
(2) disperse dyes and dispersing aid are ground to after partial size is 2 μm or less and are mixed in water, suspension is made;
(3) super absorbent resin is immersed in the suspension, under 30 DEG C of waters bath with thermostatic control, makes high-hydroscopicity tree
Rouge sufficiently adsorbs;
(4) super absorbent resin of abundant absorption suspension is dry, grinding obtains super absorbent resin micro mist;
(5) preset mass parts are pressed, after the super absorbent resin micro mist is blended with vector resin, extruding pelletization is obtained
The raising level-dyeing property Masterbatch.
8. improving the preparation method of level-dyeing property Masterbatch as claimed in claim 7, which is characterized in that described in step (1)
The preparation method of super absorbent resin the following steps are included:
(a) starch and 25-30mL water for accounting for total monomer quality 3% are added in the reaction vessel, heating makes starch gelatinization, obtains
Gelatinization of starch solution;
(b) when gelatinization of starch solution is cooled to 40-50 DEG C, initiator is added under nitrogen protection;
(c) in lye and acrylic acid to a mole degree of neutralization be 65-70%, obtain acrylic acid neutralizer;
(d) it is added drop-wise in gelatinization of starch solution after mixing acrylic acid neutralizer and acrylamide with molar ratio 10:3, while to
Crosslinking agent and foaming agent are added in gelatinization of starch solution, is stirred to react 3h at 60 DEG C;
(e) sufficiently after reaction, reaction product is precipitated with dehydrated alcohol, is filtered after being washed with acetone to precipitating, consolidate
Body polymer;After the fixed polymer drying, grind into powder obtains the super absorbent resin.
9. improving the preparation method of level-dyeing property Masterbatch as claimed in claim 7, which is characterized in that in step (4), in 120-
8-10h is dried in vacuo at 140 DEG C.
10. the raising level-dyeing property Masterbatch as described in any one of claim 1-6 is preparing the application in polyester fiber.