CN110066372A - A kind of polyisocyanate nylon co-catalyst - Google Patents
A kind of polyisocyanate nylon co-catalyst Download PDFInfo
- Publication number
- CN110066372A CN110066372A CN201910327173.7A CN201910327173A CN110066372A CN 110066372 A CN110066372 A CN 110066372A CN 201910327173 A CN201910327173 A CN 201910327173A CN 110066372 A CN110066372 A CN 110066372A
- Authority
- CN
- China
- Prior art keywords
- parts
- diisocyanate
- nylon
- polyisocyanate
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of polyisocyanate nylon co-catalyst, including recipe ingredient and mass parts are as follows: 25 ~ 30 parts of diformazan phenylene diisocyanate, Toluene-2,4-diisocyanate, 8 ~ 15 parts of 4- diisocyanate, 50 ~ 60 parts of ethyl acetate solvent.By the above-mentioned means, the present invention provides a kind of polyisocyanate nylon co-catalyst, tensile strength and bending strength of the nylon products under high and low temperature environment can be made significantly to reinforce, excellent toughness of material is kept, especially ensure that the safe operation of railroad train.
Description
Technical field
The present invention relates to co-catalyst field more particularly to a kind of polyisocyanate nylon co-catalysts.
Background technique
The purchase cost of existing polyisocyanate nylon co-catalyst is high, and reaction efficiency is low, is unable to satisfy industrial production
It is required that.
Summary of the invention
The invention mainly solves the technical problem of providing a kind of polyisocyanate nylon co-catalysts, can make nylon products
Tensile strength and bending strength under high and low temperature environment are significantly reinforced, and keep excellent toughness of material, especially ensure that railway
The safe operation of train.
In order to solve the above technical problems, one technical scheme adopted by the invention is that: a kind of polyisocyanate nylon is provided
Co-catalyst, including recipe ingredient and mass parts are as follows: 25 ~ 30 parts of diformazan phenylene diisocyanate, Toluene-2,4-diisocyanate, 4- diisocyanate
8 ~ 15 parts of ester, 50 ~ 60 parts of ethyl acetate solvent.
In a preferred embodiment of the present invention, recipe ingredient and mass parts are as follows: diformazan phenylene diisocyanate 53 ~ 60
Part, Toluene-2,4-diisocyanate, 15 ~ 20 parts of 4- diisocyanate, 30 ~ 37 parts of dichloromethane solvent.
In a preferred embodiment of the present invention, recipe ingredient and mass parts are as follows: 40 parts of diformazan phenylene diisocyanate, first
3 parts of benzene -2,4- diisocyanate, 45 parts of ethyl acetate solvent.
The beneficial effects of the present invention are: a kind of polyisocyanate nylon co-catalyst provided by the invention, can make nylon system
Tensile strength and bending strength of the product under high and low temperature environment are significantly reinforced, and excellent toughness of material is kept.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiments of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's all other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The embodiment of the present invention includes:
A kind of polyisocyanate nylon co-catalyst, including recipe ingredient and mass parts are as follows: diformazan phenylene diisocyanate 25 ~
30 parts, Toluene-2,4-diisocyanate, 8 ~ 15 parts of 4- diisocyanate, 50 ~ 60 parts of ethyl acetate solvent.
Wherein, recipe ingredient and mass parts are as follows: 53 ~ 60 parts of diformazan phenylene diisocyanate, Toluene-2,4-diisocyanate, 4- diisocyanate
15 ~ 20 parts, 30 ~ 37 parts of dichloromethane solvent.By the above-mentioned means, can make the co-catalyst obtained to the synthesis of nylon have compared with
High catalytic efficiency.
Further, recipe ingredient and mass parts are as follows: 40 parts of diformazan phenylene diisocyanate, Toluene-2,4-diisocyanate, 4- diisocyanate
3 parts of ester, 45 parts of ethyl acetate solvent.By the above-mentioned means, it is lower that the co-catalyst obtained can be made to have the synthesis of nylon
Preparation cost.
In conclusion nylon products can be made in high/low temperature the present invention provides a kind of polyisocyanate nylon co-catalyst
Tensile strength and bending strength under environment are significantly reinforced, and excellent toughness of material is kept, and especially ensure that the peace of railroad train
Row for the national games.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright description is applied directly or indirectly in other relevant technology necks
Domain is included within the scope of the present invention.
Claims (3)
1. a kind of polyisocyanate nylon co-catalyst, which is characterized in that including recipe ingredient and mass parts are as follows: diformazan penylene
25 ~ 30 parts of diisocyanate, Toluene-2,4-diisocyanate, 8 ~ 15 parts of 4- diisocyanate, 50 ~ 60 parts of ethyl acetate solvent.
2. the polyisocyanate nylon co-catalyst according to claim 1, which is characterized in that recipe ingredient and mass parts
Are as follows: 53 ~ 60 parts of diformazan phenylene diisocyanate, Toluene-2,4-diisocyanate, 15 ~ 20 parts of 4- diisocyanate, 30 ~ 37 parts of dichloromethane solvent.
3. polyisocyanate nylon co-catalyst according to claim 1, which is characterized in that recipe ingredient and mass parts
Are as follows: 40 parts of diformazan phenylene diisocyanate, Toluene-2,4-diisocyanate, 3 parts of 4- diisocyanate, 45 parts of ethyl acetate solvent.