CN110053318A - A kind of cloth base composite plate and preparation method thereof - Google Patents
A kind of cloth base composite plate and preparation method thereof Download PDFInfo
- Publication number
- CN110053318A CN110053318A CN201910238360.8A CN201910238360A CN110053318A CN 110053318 A CN110053318 A CN 110053318A CN 201910238360 A CN201910238360 A CN 201910238360A CN 110053318 A CN110053318 A CN 110053318A
- Authority
- CN
- China
- Prior art keywords
- cloth
- composite plate
- base composite
- production method
- cloth base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to plate manufacturing technology field, a kind of cloth base composite plate and preparation method thereof is disclosed.The production method of cloth base composite plate includes that cloth is glued and is tiled using adhesive, to obtain fabric template；Fabric template is subjected to cold pressing sizing, solidification, to obtain blanket；Blanket is stacked on the surface layer cloth after sizing, then carries out cold pressing sizing, finally obtains cloth base composite plate.The production method can make cloth base composite plate using scrap fabric, economic and environment-friendly, and have preferable mechanical strength.Be made by the production method of above-mentioned cloth base composite plate, thus its cost is relatively low, and have preferable mechanical strength.
Description
Technical field
The present invention relates to plate manufacturing technology fields, in particular to a kind of cloth base composite plate and preparation method thereof.
Background technique
People are in great demand to textile in daily life, this just inherently generates a large amount of waste textiles.Due to
The channel of waste textile recovery processing application is limited, be easy to cause waste.And in Furniture manufacture, craftwork, construction material, dress
Plate all can be often used in exterior material.But existing plate raw material may higher cost, and be unable to satisfy it is some special
Performance requirement.
Summary of the invention
The purpose of the present invention includes providing a kind of production method of cloth base composite plate, can make cloth using scrap fabric
Base composite plate, it is economic and environment-friendly, and there is preferable mechanical strength.
Another object of the present invention includes providing a kind of cloth base composite plate, by the production method of above-mentioned cloth base composite plate
It is made, cost is relatively low, and has preferable mechanical strength.
The embodiment of the present invention is achieved in that
In a first aspect, the present invention provides a kind of production method of cloth base composite plate, comprising:
Cloth is glued and is tiled using adhesive, to obtain fabric template；
Fabric template is subjected to cold pressing sizing, solidification, to obtain blanket；
Blanket is stacked on the surface layer cloth after sizing, then carries out cold pressing sizing.
In an embodiment of the present invention:
Cloth includes cotton, fiber crops, fabric one or more in staple fibre.
In an embodiment of the present invention, cloth is glued and is tiled using adhesive, to obtain fabric template
The step of include:
The cloth of multi-disc is glued；
Cloth overlapping, tiling after multi-disc is glued.
In an embodiment of the present invention:
Cloth is sheet, cloth with a thickness of 0.1~2mm.
In an embodiment of the present invention:
Adhesive includes epoxy resin and curing agent.
In an embodiment of the present invention:
Curing agent accounts for 10~20wt% of adhesive total amount.
In an embodiment of the present invention:
Epoxy resin is E51 type epoxy resin, and curing agent is W593 type curing agent.
In an embodiment of the present invention:
Cloth is glued and is tiled using adhesive, the step of to obtain fabric template in, cloth, which is laid in, to be coated with
In the template of release agent.
In an embodiment of the present invention:
The pressure for carrying out cold pressing sizing to fabric template is 0.4~0.55Mpa, and the blanket and surface layer cloth to overlapping carry out cold
The pressure of pressure sizing is 0.3~0.38MPa.
Second aspect, the present invention also provides a kind of prepared cloth base of the production method by above-mentioned cloth base composite plate is compound
Plate.
The beneficial effect of the embodiment of the present invention is:
The production method of the cloth base composite plate of the embodiment of the present invention includes that cloth is glued and is tiled using adhesive,
To obtain fabric template；Fabric template is subjected to cold pressing sizing, solidification, to obtain blanket；Blanket is stacked in the face after sizing
On layer cloth, then cold pressing sizing is carried out, finally obtains cloth base composite plate.The production method can be multiple using scrap fabric production cloth base
Plywood, it is economic and environment-friendly, and there is preferable mechanical strength.
The cloth base composite plate of the embodiment of the present invention, be made by the production method of above-mentioned cloth base composite plate, therefore its at
This is lower, and has preferable mechanical strength.
Detailed description of the invention
In order to illustrate the technical solution of the embodiments of the present invention more clearly, below will be to needed in the embodiment attached
Figure is briefly described, it should be understood that the following drawings illustrates only certain embodiments of the present invention, therefore is not construed as pair
The restriction of range for those of ordinary skill in the art without creative efforts, can also be according to this
A little attached drawings obtain other relevant attached drawings.
Fig. 1 is the flow chart of cloth base composite plate and preparation method thereof in the embodiment of the present invention.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention
In attached drawing, technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is
A part of the embodiment of the present invention, instead of all the embodiments.The present invention being usually described and illustrated herein in the accompanying drawings is implemented
The component of example can be arranged and be designed with a variety of different configurations.The person that is not specified actual conditions in embodiment, according to conventional strip
The condition that part or manufacturer suggest carries out.Reagents or instruments used without specified manufacturer, being can be by commercially available purchase
The conventional products of acquisition.
Cloth base composite plate of the embodiment of the present invention and preparation method thereof is specifically described below.
The cloth base composite plate of the embodiment of the present invention carries out the manufacture of composite plate using cloth, can use scrap fabric,
Therefore have the characteristics that economic and environment-friendly.Fig. 1 is the flow chart of cloth base composite plate and preparation method thereof in the embodiment of the present invention, please be joined
According to Fig. 1, the production method of the embodiment of the present invention includes the following steps.
One, cloth sorted, cut
Cloth is sorted, selects the fabric types of needs, such as from material, selects cotton, fiber crops, in artificial fiber
One or more kinds of is blended.Artificial fiber can be petroleum derivation product, the chemical fibre products such as including polyester fiber.System as needed
The size of the cloth base composite plate of work, cuts cloth (usually sheet), cloth can be directly cut into final finished
Size.The fabric of heterogeneity embodies different behaviors in sizing engineering.It is had preferably after pure cotton fabric infiltration glue
Extensibility, such as one piece of 250mm × 250mm sports cloth, the side for 270mm × 270mm can be sprawled after sizing with brush
Cloth, and thickness change very little.There is no spreading form after the sizing of dacron cloth, the cloth transparency increases.Therefore, it is answered when making plate
The performance of cloth is considered, to select suitable cloth and cut suitably sized.Reply cloth does and suitably cuts out, can be in order to
Mat formation, plate should as far as possible uniformly, to prevent mechanics weak spot on the direction sprawled.
Two, fabric template is made
The cloth cut is glued using adhesive.Cloth after sizing is laid in the template for being coated with release agent
On.In an embodiment of the present invention, multi-panel can be glued, the cloth after being then glued multi-disc is overlapped, is flat
Paving, to reach the thickness of needs.In an alternate embodiment of the invention, the thickness of single piece of material can be 0.1~2mm.For certain warps
The bulk cloth of the latitude opposite sex, should interlock and elaborate, and prevent different directions from shrinking unevenness and cause to deform.In addition, adhesive is made in gravity
It is easier infiltration downwards with lower, therefore the cloth sizing for being generally layed in bottom is less slightly, the cloth sizing for being layed in upper layer is slightly more.
The adhesive of the embodiment of the present invention includes epoxy resin and curing agent.Further, epoxy resin is chosen as E51
Type epoxy resin, curing agent are W593 type curing agent.Further, curing agent accounts for 10~20wt% of adhesive total amount.In this way
Adhesive ingredients and ratio so that the cloth base composite plate produced has outstanding color fastness to light, static bending strength and interior
Bond strength.
The type epoxy resin has preferable bonding effect to metal, timber polar materials.To non-polar material bonding compared with
Difference, therefore polyolefin based materials can be used and stick die surface in favor of demoulding.So in embodiments of the present invention, release agent can
It is selected as polyolefin release agent, such as polyethylene or polypropylene release agent.
Three, blanket is made
The fabric template that above-mentioned steps are obtained carries out cold pressing sizing, solidification, to obtain blanket.In the present embodiment, cold
Pressure sizing uses cold press, is 10~30 DEG C in temperature, carries out under conditions of 0.4~0.55MPa of pressure, and setting time 24~
30h.Solidification temperature is 10~30 DEG C.
Four, surface layer cloth is suppressed
By the surface layer cloth cut out sizing, tiling, then blanket obtained in step 3 is stacked in the surface layer after sizing
On cloth, then carry out cold pressing sizing.It is 10~30 DEG C that cold pressing in the step, which is formed in temperature, the condition of 0.3~0.38MPa of pressure
Lower progress, 10~15h of setting time.Surface layer cloth can carry out according to the needs of practical application as the outermost layer of cloth base composite plate
Material selection.
The production method of cloth base composite plate provided in an embodiment of the present invention, can be using waste fabric as raw material, using E51 type
Bisphenol A epoxide resin and W593 type curing agent are as matrix adhesive material, then pass through and scientifically and rationally control in preparation process
Operation and method parameter, obtained cloth base composite plate is with color fastness to light is good, internal bond strength is good, static bending strength is good, resistance to
High temperature performance is good, water-tolerant, environmentally friendly, no toxic gas and heavy metal release, can be used for high humility or directly with
The features such as environment of water contact and high-frequency vibration place.This utilizes the Recovery and recycle of the old textile of waste fabric and society and mentions
Condition has been supplied, there is preferably society and economic prospect.
It is introduced below by way of production method of the specific embodiment to cloth base composite plate.
Embodiment 1
The preparation method of the cloth base composite plate of the present embodiment, comprises the following steps:
(1) it sorts out the purified cotton cloth of 0.4mm thickness, cut out having a size of 500mm × 500mm；
(2) gained cloth in step (1) is glued with adhesive, the cloth after sizing, which is laid in, is coated with release agent
In template, 20 layers of tiling, the fabric template after must being glued successively are stacked；
Adhesive described in step (2) includes E51 type bisphenol A epoxide resin, W593 type curing agent, and wherein W593 type solidifies
The quality of agent is the 17% of adhesive quality；The release agent is polyolefin release agent；
(3) the fabric template for having applied glue is carried out cold pressing sizing, setting time under 22 DEG C of temperature, pressure 0.5MPa environment
Then 28h solidifies at 13 DEG C, obtains blanket；
(4) blanket is stacked on the surface layer cloth for having applied glue, is 11 DEG C in temperature, is carried out under pressure 0.32MPa environment cold
Pressure sizing, setting time 11h, then the cloth base composite plate is obtained after being demoulded.
Embodiment 2
The preparation method of the cloth base composite plate of the present embodiment, comprises the following steps:
(1) it sorts out the purified cotton cloth of 0.3mm thickness, cut out having a size of 500mm × 500mm；
(2) gained cloth in step (1) is glued with adhesive, the cloth after sizing, which is laid in, is coated with release agent
In template, 20 layers of tiling, the fabric template after must being glued successively are stacked；
Adhesive described in step (2) includes E51 type bisphenol A epoxide resin, W593 type curing agent, and wherein W593 type solidifies
The quality of agent is the 10% of adhesive quality；The release agent is polyolefin release agent；
(3) the fabric template for having applied glue is carried out cold pressing sizing, setting time under 20 DEG C of temperature, pressure 0.4MPa environment
For 24 hours, then solidify at 12 DEG C, obtain blanket；
(4) blanket is stacked on the surface layer cloth for having applied glue, is 10 DEG C in temperature, is carried out under pressure 0.3MPa environment cold
Pressure sizing, setting time 10h, then the cloth base composite plate is obtained after being demoulded.
Embodiment 3
The preparation method of the cloth base composite plate of the present embodiment, comprises the following steps:
(1) it sorts out the purified cotton cloth of 0.5mm thickness, cut out having a size of 500mm × 500mm；
(2) gained cloth in step (1) is glued with adhesive, the cloth after sizing, which is laid in, is coated with release agent
In template, 26 layers of tiling, the fabric template after must being glued successively are stacked；
Adhesive described in step (2) includes E51 type bisphenol A epoxide resin, W593 type curing agent, and wherein W593 type solidifies
The quality of agent is the 20% of adhesive quality；The release agent is polyolefin release agent；
(3) the fabric template for having applied glue is carried out cold pressing sizing under 23 DEG C of temperature, pressure 0.55MPa environment, when sizing
Between 30h, then 17 DEG C solidify, obtain blanket；
(4) blanket is stacked on the surface layer cloth for having applied glue, is 14 DEG C in temperature, is carried out under pressure 0.38MPa environment cold
Pressure sizing, setting time 15h, then the cloth base composite plate is obtained after being demoulded.
Embodiment 4
The preparation method of the cloth base composite plate of the present embodiment, comprises the following steps:
(1) it sorts out the purified cotton cloth of 0.1mm thickness, cut out having a size of 300mm × 300mm；
(2) gained cloth in step (1) is glued with adhesive, the cloth after sizing, which is laid in, is coated with release agent
In template, 35 layers of tiling, the fabric template after must being glued successively are stacked；
Adhesive described in step (2) includes E51 type bisphenol A epoxide resin, W593 type curing agent, and wherein W593 type solidifies
The quality of agent is the 15% of adhesive quality；The release agent is polyolefin release agent；
(3) the fabric template for having applied glue is carried out cold pressing sizing under 23 DEG C of temperature, pressure 0.55MPa environment, when sizing
Between 30h, then 17 DEG C solidify, obtain blanket；
(4) blanket is stacked on the surface layer cloth for having applied glue, is 14 DEG C in temperature, is carried out under pressure 0.38MPa environment cold
Pressure sizing, setting time 15h, then the cloth base composite plate is obtained after being demoulded.
Embodiment 5
The preparation method of the cloth base composite plate of the present embodiment, comprises the following steps:
(1) it sorts out the purified cotton cloth of 1mm thickness, cut out having a size of 500mm × 500mm；
(2) gained cloth in step (1) is glued with adhesive, the cloth after sizing, which is laid in, is coated with release agent
In template, 10 layers of tiling, the fabric template after must being glued successively are stacked；
Adhesive described in step (2) includes E51 type bisphenol A epoxide resin, W593 type curing agent, and wherein W593 type solidifies
The quality of agent is the 20% of adhesive quality；The release agent is polyolefin release agent；
(3) the fabric template for having applied glue is carried out cold pressing sizing, setting time under 23 DEG C of temperature, pressure 0.5MPa environment
Then 30h solidifies at 17 DEG C, obtains blanket；
(4) blanket is stacked on the surface layer cloth for having applied glue, is 14 DEG C in temperature, is carried out under pressure 0.32MPa environment cold
Pressure sizing, setting time 15h, then the cloth base composite plate is obtained after being demoulded.
Embodiment 6
The preparation method of the cloth base composite plate of the present embodiment, comprises the following steps:
(1) it sorts out the purified cotton cloth of 2mm thickness, cut out having a size of 700mm × 500mm；
(2) gained cloth in step (1) is glued with adhesive, the cloth after sizing, which is laid in, is coated with release agent
In template, 6 layers of tiling, the fabric template after must being glued successively are stacked；
Adhesive described in step (2) includes E51 type bisphenol A epoxide resin, W593 type curing agent, and wherein W593 type solidifies
The quality of agent is the 18% of adhesive quality；The release agent is polyolefin release agent；
(3) the fabric template for having applied glue is carried out cold pressing sizing under 23 DEG C of temperature, pressure 0.55MPa environment, when sizing
Between 30h, then 23 DEG C solidify, obtain blanket；
(4) blanket is stacked on the surface layer cloth for having applied glue, is 12 DEG C in temperature, is carried out under pressure 0.38MPa environment cold
Pressure sizing, setting time 15h, then the cloth base composite plate obtained after being demoulded.
Embodiment 7
The preparation method of the cloth base composite plate of the present embodiment, comprises the following steps:
(1) it sorts out the purified cotton cloth of 0.4mm thickness, cut out having a size of 500mm × 500mm；
(2) gained cloth in step (1) is glued with adhesive, the cloth after sizing, which is laid in, is coated with release agent
In template, 10 layers of tiling, the fabric template after must being glued successively are stacked；
Adhesive described in step (2) includes E51 type bisphenol A epoxide resin, W593 type curing agent, and wherein W593 type solidifies
The quality of agent is the 15% of adhesive quality；The release agent is polyolefin release agent；
(3) the fabric template for having applied glue is carried out cold pressing sizing under 20 DEG C of temperature, pressure 0.55MPa environment, when sizing
Between 30h, then 20 DEG C solidify, obtain blanket；
(4) blanket is stacked on the surface layer cloth for having applied glue, is 10 DEG C in temperature, is carried out under pressure 0.38MPa environment cold
Pressure sizing, setting time 10h, then the cloth base composite plate obtained after being demoulded.
Referring to ASTM D638-03 ASTM D790-03 ASTM D265-2006, be with the cloth base composite plate of embodiment 7
Sample carries out mechanical strength test, as a result such as following table.
In conclusion the production method of the cloth base composite plate of the embodiment of the present invention includes being applied using adhesive to cloth
Glue and tiling, to obtain fabric template；Fabric template is subjected to cold pressing sizing, solidification, to obtain blanket；Blanket is stacked in and is applied
On surface layer cloth after glue, then cold pressing sizing is carried out, finally obtains cloth base composite plate.The production method can utilize scrap fabric system
Make cloth base composite plate, it is economic and environment-friendly, and there is preferable mechanical strength.
The cloth base composite plate of the embodiment of the present invention, be made by the production method of above-mentioned cloth base composite plate, therefore its at
This is lower, and has preferable mechanical strength.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, made any to repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of production method of cloth base composite plate characterized by comprising
Cloth is glued and is tiled using adhesive, to obtain fabric template；
The fabric template is subjected to cold pressing sizing, solidification, to obtain blanket；
The blanket is stacked on the surface layer cloth after sizing, then carries out cold pressing sizing.
2. the production method of cloth base composite plate according to claim 1, it is characterised in that:
The cloth includes cotton, fiber crops, fabric one or more in staple fibre.
3. the production method of cloth base composite plate according to claim 1, which is characterized in that carried out using adhesive to cloth
Sizing and tiling, to include: the step of obtaining fabric template
The cloth of multi-disc is glued；
Cloth overlapping, tiling after multi-disc is glued.
4. the production method of cloth base composite plate according to claim 1, which is characterized in that the cloth is sheet, described
Cloth with a thickness of 0.1~2mm.
5. the production method of cloth base composite plate according to claim 1, which is characterized in that described adhesive includes asphalt mixtures modified by epoxy resin
Rouge and curing agent.
6. the production method of cloth base composite plate according to claim 5, which is characterized in that the curing agent accounts for the bonding
10~20wt% of agent total amount.
7. the production method of cloth base composite plate according to claim 5, which is characterized in that the epoxy resin is E51 type
Epoxy resin, the curing agent are W593 type curing agent.
8. the production method of cloth base composite plate described in any one of -7 according to claim 1, which is characterized in that use adhesive
Cloth is glued and is tiled, the step of to obtain fabric template in, the cloth is laid in the template for being coated with release agent.
9. the production method of cloth base composite plate described in any one of -7 according to claim 1, which is characterized in that the fabric
The pressure that template carries out cold pressing sizing is 0.4~0.55Mpa, and the blanket and the surface layer cloth to overlapping carry out cold pressing sizing
Pressure be 0.3~0.38MPa.
10. a kind of prepared cloth base of production method by cloth base composite plate of any of claims 1-9 is compound
Plate.