CN110041717A - A kind of preparation method of asphalt warm-mix agent - Google Patents
A kind of preparation method of asphalt warm-mix agent Download PDFInfo
- Publication number
- CN110041717A CN110041717A CN201910236029.2A CN201910236029A CN110041717A CN 110041717 A CN110041717 A CN 110041717A CN 201910236029 A CN201910236029 A CN 201910236029A CN 110041717 A CN110041717 A CN 110041717A
- Authority
- CN
- China
- Prior art keywords
- mix
- parts
- preparation
- mass ratio
- asphalt warm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation methods of asphalt warm-mix agent, belong to road pavement Material Field.The present invention is with vermiculite, blast furnace slag configures hybrid particles as raw material, form honeycombed grain, enhance the intensity of pitch, secondly by allyl amine as raw material, in the process for forming polymer, it is deposited on inside porous particle by the copper sulfate crystal that copper sulphate is formed, it is wrapped up using the polymer of formation, the polymer being formed simultaneously non-polar group rich in and pitch have very strong binding ability, the amido wherein contained simultaneously can be very good to carry out with base-material affine, enhance the binding ability of pitch and base-material, enhance low-temperature cracking-resistance, and pitch is improved by the release of the combination water in cupric sulphate crystal and is converted into class A foam A performance, and it can preferably improve its stability using the ionic liquid of synthesis, and it can be very good to adsorb the elements such as sulphur therein, sufficiently combined, reduce viscosity , enhance warm mix effect.
Description
Technical field
The invention belongs to road pavement Material Field more particularly to a kind of preparation methods of asphalt warm-mix agent.
Background technique
Asphalt used in previous road engineering is generally divided into two types according to mix construction temperature: cold mixing drip
Green mixture CMA(Cold Mix Asphalt) and hot-mix asphalt mixture HMA(Hot Mix Asphalt).Cold-mix asphalt is mixed
Material is closed generally using emulsified asphalt or liquid asphalt and gather materials mix, making under normal temperature state, without to gathering materials and combine
Material is heated, and can save mass energy in this way.But cold-mix asphalt mixture early strength is lower, it is difficult to it is public to meet high speed
The requirement of the important engineerings such as road, Heavy Traffic road.Hot-mix asphalt mixture be widely used, the good mixing of pavement performance
Material.But in hot-mix asphalt mixture production process, pitch and building stones need the mix under 150 ~ 180 DEG C of hot conditions.Disappear
The a large amount of energy is consumed, meanwhile, the mix under hot conditions also easily causes pitch and heat ageing occurs, and reduces pitch on road surface
Active time shortens the service life of bituminous pavement.To extend the bituminous pavement service life, the prosperities such as later period the 1990s America and Europe
Country has carried out the research of warm-mixed asphalt technology.Warm-mixed asphalt technology be a kind of mix temperature between hot asphalt technology (150 ~
180 DEG C) and cold-mix asphalt technology (10 ~ 40 DEG C) between, performance reaches the pitch mixing section of (or close) hot-mix asphalt mixture
It can new technology.Usual warm mix technology is most common to be achieved in that addition warm-mixing agent, warm-mixed asphalt technology and standard hot asphalt
It compares, temperature can reduce 20 ~ 30 DEG C.Warm-mixed asphalt technology has many advantages: reduction bituminous mixture and construction first
Temperature, can be with 20% or more energy saving;Asphalt storage temperature reduces simultaneously, the mobility enhancing under lower temperature;Separately
Outside, extend the asphalt pavement construction phase, expand application range.
There are three types of most common asphalt warm-mix agents: organic matter warm-mixing agent, chemical warm-mixing agent and foam warm-mixing agent.Organic matter temperature
Mixing agent is usually paraffin, fatty acid amide etc.;Chemical warm-mixing agent is usually emulsifier and polymer etc.;Foam warm-mixing agent is will to lack
Amount water, which is added in pitch, forms foam, to reduce the viscosity of pitch, to achieve the purpose that reduce mix temperature.
CN101602862A discloses a kind of warm-mixed asphalt additive and preparation method thereof, which is by the way that deionized water to be added
Into the polyvinyl alcohol water solution being made into advance, rosin quaternary ammonium salt, aromatic hydrocarbon quaternary ammonium salt emulsifier, aliphatic hydrocarbon are then sequentially added
Quaternary ammonium salt emulsifier, anionic surfactant, stirring and dissolving, then by the polyacrylamide solution being made into advance and three second
Hydramine is added, and mixing to is finished product after being uniformly dissolved.The additive can be substantially reduced pitch and mix and stir temperature, and pitch is mixed
It closes and expects that every pavement performance index also complies with requirement, but the additive component is complicated, increases the difficulty and cost of preparation, no
Conducive to practical application and low-temperature cracking-resistance reduces;CN102268189A discloses a kind of warm-mixed asphalt additive and its preparation side
Method, it is in dicyandiamide solution using a kind of additive of organic silicon modified by polyether polymer composition.It can be effectively reduced and mix and stir
40 DEG C of temperature or so, and warm-mixed asphalt low-temperature cracking-resistance is not less than hot asphalt, but lacks relevant test method and instance number
According to support.Therefore researching and developing a kind of pitch, crack resistance remains unchanged good warm-mixing agent at low temperature, it is quite necessary to.
Summary of the invention
The technical problems to be solved by the invention: pitch is easily led to for current warm-mixing agent, what low-temperature cracking-resistance reduced asks
Topic, the present invention provides a kind of preparation methods of asphalt warm-mix agent.
In order to solve the above technical problems, the present invention is using technical solution as described below:
A kind of preparation method of asphalt warm-mix agent, the preparation method include the following steps:
(1) hybrid particles and hydrochloric acid 1:4 in mass ratio~6 are subjected to ultrasonic vibration, stood, filtering collects filter residue, by weight
Number meter takes 200~250 parts of water, 40~45 parts of allyl amines, 30~33 parts of filter residues, 13~15 parts of copper sulphate, 3~7 parts of auxiliary
Agent, 2~5 parts of initiators;
(2) water, filter residue and copper sulphate are put into reaction kettle first, using nitrogen protection, adjust pH to 5.0~5.0, be heated to
85~90 DEG C, heat preservation is cooled to 2~6 DEG C, and allyl amine, adjuvant stirring is added, is warming up to 55~60 DEG C, initiator is added,
It is stirred to react;
(3) after the completion of reaction, pH is adjusted, is stood, material is collected out in discharging, takes 200~250 parts of ethyl alcohol, 60~80 parts of dischargings
Object, 13~19 parts of urethanes, 13~16 parts of tetramethylguanidine, 7~11 parts of additives, 2~5 parts of surfactants;
(4) first by ethyl alcohol, go out material, part urethanes, tetramethylguanidine are put into reactor, in 3~5 DEG C of addition additions
Agent and surfactant, stirring are warming up to 13~19 DEG C, and stirring heat preservation stands, discharges, is freeze-dried, washing, then freezes dry
It is dry to get asphalt warm-mix agent.
Hybrid particles are vermiculite, blast furnace slag 9:1 in mass ratio~3 mixing in the step (1), carry out ball milling, cross 500 mesh
Sieve collects sieving particle to get hybrid particles.
The adjuvant is glutaraldehyde, glutaric anhydride 7:2~4 in mass ratio mix.
The initiator is to mix ammonium persulfate, sodium bisulfate 3:1~4 in mass ratio.
The additive the preparation method comprises the following steps: by maize pulp, distilled water 1:4~8 in mass ratio, mixed, 60~
75 DEG C preheating, add the emulsifier of maize pulp quality 10~15%, be warming up to 90~95 DEG C, add maize pulp quality 3~
The mix monomer of maize pulp quality 48~52% is added in 6% potassium peroxydisulfate, stirring, reacts, and addition maize pulp quality 14~
26% regulator, the reaction was continued, stands, cooling, discharges, and is spray-dried, washing, dry to get additive.
The emulsifier is neopelex, any one in lauryl sodium sulfate.
The mix monomer is that acrylamide, acrylic acid and styrene 2:1~5:2 in mass ratio are mixed.
The regulator is melamine, lactic acid 4:1~3 in mass ratio mix.
The additive formic acid, lactic acid and tetrafluoro boric acid 3:4:1~4 in mass ratio mix.
The surfactant is dodecyl polyoxyethylene ether sodium sulfovinate, any one in cocounut oil acyl diglycollic amide
Kind.
The present invention is compared with other methods, and advantageous effects are:
The present invention configures hybrid particles as raw material using vermiculite, blast furnace slag, forms honeycombed grain, enhances the intensity of pitch,
It is secondary to be deposited on by the copper sulfate crystal that copper sulphate is formed more as raw material in the process for forming polymer by allyl amine
Inside the particle of hole, it is wrapped up using the polymer of formation, the polymer being formed simultaneously non-polar group rich in
With pitch have very strong binding ability, while the amido wherein contained can be very good with base-material carry out it is affine, enhance drip
The green binding ability with base-material, enhances low-temperature cracking-resistance, and improve by the release of the combination water in cupric sulphate crystal
Pitch is converted into class A foam A performance, and can preferably improve its stability using the ionic liquid of synthesis, and can be very
The elements such as good absorption sulphur therein, are sufficiently combined, and viscosity is reduced, and enhance warm mix effect.
Specific embodiment
Hybrid particles are vermiculite, blast furnace slag 9:1 in mass ratio~3 mixing, carry out ball milling, cross 500 meshes, collect sieving
Grain is to get hybrid particles.
Adjuvant is glutaraldehyde, glutaric anhydride 7:2~4 in mass ratio mix.
Initiator is to mix ammonium persulfate, sodium bisulfate 3:1~4 in mass ratio.
Additive the preparation method comprises the following steps: by maize pulp, distilled water 1:4~8 in mass ratio, mixed, at 60~75 DEG C
Preheat 30min, add the emulsifier of maize pulp quality 10~15%, be warming up to 90~95 DEG C, add maize pulp quality 3~
6% potassium peroxydisulfate stirs 7h, and the mix monomer of maize pulp quality 48~52% is added, and reacts 9h, and maize pulp quality 14 is added
~26% regulator, the reaction was continued 4h stand 2h, are cooled to room temperature, and discharge, spray drying, dry using ethanol washing,
Up to additive.
Emulsifier is neopelex, any one in lauryl sodium sulfate.
Mix monomer is that acrylamide, acrylic acid and styrene 2:1~5:2 in mass ratio are mixed.
Regulator is melamine, lactic acid 4:1~3 in mass ratio mix.
Additive formic acid, lactic acid and tetrafluoro boric acid 3:4:1~4 in mass ratio mix.
Surfactant is dodecyl polyoxyethylene ether sodium sulfovinate, any one in cocounut oil acyl diglycollic amide.
A kind of preparation method of asphalt warm-mix agent, the preparation method include the following steps:
(1) hybrid particles and hydrochloric acid 1:4 in mass ratio~6 being subjected to ultrasonic vibration 20min, stands 3h, filter residue is collected in filtering,
According to parts by weight, 200~250 parts of water, 40~45 parts of allyl amines, 30~33 parts of filter residues, 13~15 parts of copper sulphate, 3~7 are taken
Part adjuvant, 2~5 parts of initiators;
(2) water, filter residue and copper sulphate are put into reaction kettle first, using nitrogen protection, adjust pH to 5.0~5.5, be heated to
85~90 DEG C, 6h is kept the temperature, is cooled to 2~6 DEG C, allyl amine, adjuvant stirring is added, is warming up to 55~60 DEG C, is added and causes
Agent is stirred to react 5h;
(3) after the completion of reaction, adjust pH, stand 3h, discharging, collect out material, take 200~250 parts of ethyl alcohol, 60~80 parts go out
Material, 13~19 parts of urethanes, 13~16 parts of tetramethylguanidine, 7~11 parts of additives, 2~5 parts of surfactants;
(4) first by ethyl alcohol, go out material, part urethanes, tetramethylguanidine are put into reactor, in 3~5 DEG C of addition additions
Agent and surfactant stir 6h, are warming up to 13~19 DEG C, and stirring heat preservation 2h stands 1h, discharges, and freeze-drying uses petroleum
Ether washing, then be freeze-dried to get asphalt warm-mix agent.
Hybrid particles are vermiculite, blast furnace slag 9:1 in mass ratio mixing, carry out ball milling, cross 500 meshes, collect sieving particle,
Up to hybrid particles.
Adjuvant is glutaraldehyde, glutaric anhydride 7:2 in mass ratio is mixed.
Initiator is to mix ammonium persulfate, sodium bisulfate 3:1 in mass ratio.
Additive the preparation method comprises the following steps: by maize pulp, distilled water 1:4 in mass ratio, mixed, 60 DEG C preheat
30min adds the emulsifier of maize pulp quality 10%, is warming up to 90 DEG C, adds the potassium peroxydisulfate of maize pulp quality 3%,
7h is stirred, the mix monomer of maize pulp quality 48% is added, reacts 9h, the regulator of maize pulp quality 14% is added, is continued anti-
4h is answered, 2h is stood, is cooled to room temperature, is discharged, spray drying is dry to get additive using ethanol washing.
Emulsifier is neopelex.
Mix monomer is that acrylamide, acrylic acid and styrene 2:1:2 in mass ratio are mixed.
Regulator is melamine, lactic acid 4:1 in mass ratio is mixed.
Additive formic acid, lactic acid and tetrafluoro boric acid 3:4:1 in mass ratio are mixed.
Surfactant is dodecyl polyoxyethylene ether sodium sulfovinate.
A kind of preparation method of asphalt warm-mix agent, the preparation method include the following steps:
(1) hybrid particles and hydrochloric acid 1:4 in mass ratio are subjected to ultrasonic vibration 20min, stand 3h, filter residue is collected in filtering, by weight
Number meter is measured, 200 parts of water, 40 parts of allyl amines, 30 parts of filter residues, 13 parts of copper sulphate, 3 parts of adjuvants, 2 parts of initiators are taken;
(2) water, filter residue and copper sulphate are put into reaction kettle first, using nitrogen protection, adjust pH to 5.0, be heated to 85 DEG C,
6h is kept the temperature, is cooled to 2 DEG C, allyl amine, adjuvant stirring is added, is warming up to 55 DEG C, initiator is added, is stirred to react 5h;
(3) after the completion of reaction, adjust pH, stand 3h, discharging, collect out material, take 200 parts of ethyl alcohol, 60 parts go out material, 13 parts
Urethanes, 13 parts of tetramethylguanidine, 7 parts of additives, 2 parts of surfactants;
(4) first by ethyl alcohol, go out material, part urethanes, tetramethylguanidine are put into reactor, in 3 DEG C of addition additives
And surfactant, 6h is stirred, is warming up to 13 DEG C, stirring heat preservation 2h stands 1h, discharges, and freeze-drying is washed using petroleum ether
It washs, then is freeze-dried to get asphalt warm-mix agent.
Hybrid particles are vermiculite, blast furnace slag 9:3 in mass ratio mixing, carry out ball milling, cross 500 meshes, collect sieving particle,
Up to hybrid particles.
Adjuvant is glutaraldehyde, glutaric anhydride 7:4 in mass ratio is mixed.
Initiator is to mix ammonium persulfate, sodium bisulfate 3:4 in mass ratio.
Additive the preparation method comprises the following steps: by maize pulp, distilled water 1:8 in mass ratio, mixed, 75 DEG C preheat
30min adds the emulsifier of maize pulp quality 15%, is warming up to 95 DEG C, adds the potassium peroxydisulfate of maize pulp quality 6%,
7h is stirred, the mix monomer of maize pulp quality 52% is added, reacts 9h, the regulator of maize pulp quality 26% is added, is continued anti-
4h is answered, 2h is stood, is cooled to room temperature, is discharged, spray drying is dry to get additive using ethanol washing.
Emulsifier is lauryl sodium sulfate.
Mix monomer is that acrylamide, acrylic acid and styrene 2:5:2 in mass ratio are mixed.
Regulator is melamine, lactic acid 4:3 in mass ratio is mixed.
Additive formic acid, lactic acid and tetrafluoro boric acid 3:4:4 in mass ratio are mixed.
Surfactant is cocounut oil acyl diglycollic amide.
A kind of preparation method of asphalt warm-mix agent, the preparation method include the following steps:
(1) hybrid particles and hydrochloric acid 1:6 in mass ratio are subjected to ultrasonic vibration 20min, stand 3h, filter residue is collected in filtering, by weight
Number meter is measured, 250 parts of water, 45 parts of allyl amines, 33 parts of filter residues, 15 parts of copper sulphate, 7 parts of adjuvants, 5 parts of initiators are taken;
(2) water, filter residue and copper sulphate are put into reaction kettle first, using nitrogen protection, adjust pH to 5.5, be heated to 90 DEG C,
6h is kept the temperature, is cooled to 6 DEG C, allyl amine, adjuvant stirring is added, is warming up to 60 DEG C, initiator is added, is stirred to react 5h;
(3) after the completion of reaction, adjust pH, stand 3h, discharging, collect out material, take 250 parts of ethyl alcohol, 80 parts go out material, 19 parts
Urethanes, 16 parts of tetramethylguanidine, 11 parts of additives, 5 parts of surfactants;
(4) first by ethyl alcohol, go out material, part urethanes, tetramethylguanidine are put into reactor, in 5 DEG C of addition additives
And surfactant, 6h is stirred, is warming up to 19 DEG C, stirring heat preservation 2h stands 1h, discharges, and freeze-drying is washed using petroleum ether
It washs, then is freeze-dried to get asphalt warm-mix agent.
Hybrid particles are vermiculite, blast furnace slag 9:2 in mass ratio mixing, carry out ball milling, cross 500 meshes, collect sieving particle,
Up to hybrid particles.
Adjuvant is glutaraldehyde, glutaric anhydride 7:3 in mass ratio is mixed.
Initiator is to mix ammonium persulfate, sodium bisulfate 3:2 in mass ratio.
Additive the preparation method comprises the following steps: by maize pulp, distilled water 1:6 in mass ratio, mixed, 65 DEG C preheat
30min adds the emulsifier of maize pulp quality 12%, is warming up to 93 DEG C, adds the potassium peroxydisulfate of maize pulp quality 5%,
7h is stirred, the mix monomer of maize pulp quality 50% is added, reacts 9h, the regulator of maize pulp quality 20% is added, is continued anti-
4h is answered, 2h is stood, is cooled to room temperature, is discharged, spray drying is dry to get additive using ethanol washing.
Emulsifier is neopelex.
Mix monomer is that acrylamide, acrylic acid and styrene 2:3:2 in mass ratio are mixed.
Regulator is melamine, lactic acid 4:2 in mass ratio is mixed.
Additive formic acid, lactic acid and tetrafluoro boric acid 3:4:3 in mass ratio are mixed.
Surfactant is dodecyl polyoxyethylene ether sodium sulfovinate.
A kind of preparation method of asphalt warm-mix agent, the preparation method include the following steps:
(1) hybrid particles and hydrochloric acid 1:5 in mass ratio are subjected to ultrasonic vibration 20min, stand 3h, filter residue is collected in filtering, by weight
Number meter is measured, 230 parts of water, 42 parts of allyl amines, 32 parts of filter residues, 14 parts of copper sulphate, 5 parts of adjuvants, 3 parts of initiators are taken;
(2) water, filter residue and copper sulphate are put into reaction kettle first, using nitrogen protection, adjust pH to 5.2, be heated to 88 DEG C,
6h is kept the temperature, is cooled to 4 DEG C, allyl amine, adjuvant stirring is added, is warming up to 58 DEG C, initiator is added, is stirred to react 5h;
(3) after the completion of reaction, adjust pH, stand 3h, discharging, collect out material, take 230 parts of ethyl alcohol, 70 parts go out material, 15 parts
Urethanes, 15 parts of tetramethylguanidine, 10 parts of additives, 3 parts of surfactants;
(4) first by ethyl alcohol, go out material, part urethanes, tetramethylguanidine are put into reactor, in 4 DEG C of addition additives
And surfactant, 6h is stirred, is warming up to 15 DEG C, stirring heat preservation 2h stands 1h, discharges, and freeze-drying is washed using petroleum ether
It washs, then is freeze-dried to get asphalt warm-mix agent.
Hybrid particles are vermiculite, blast furnace slag 9:3 in mass ratio mixing, carry out ball milling, cross 500 meshes, collect sieving particle,
Up to hybrid particles.
Adjuvant is glutaraldehyde, glutaric anhydride 7:4 in mass ratio is mixed.
Initiator is to mix ammonium persulfate, sodium bisulfate 3:4 in mass ratio.
Emulsifier is lauryl sodium sulfate.
Mix monomer is that acrylamide, acrylic acid and styrene 2:5:2 in mass ratio are mixed.
Regulator is melamine, lactic acid 4:3 in mass ratio is mixed.
Additive formic acid, lactic acid and tetrafluoro boric acid 3:4:4 in mass ratio are mixed.
Surfactant is cocounut oil acyl diglycollic amide.
A kind of preparation method of asphalt warm-mix agent, the preparation method include the following steps:
(1) hybrid particles and hydrochloric acid 1:6 in mass ratio are subjected to ultrasonic vibration 20min, stand 3h, filter residue is collected in filtering, by weight
Number meter is measured, 250 parts of water, 45 parts of allyl amines, 33 parts of filter residues, 15 parts of copper sulphate, 7 parts of adjuvants, 5 parts of initiators are taken;
(2) water, filter residue and copper sulphate are put into reaction kettle first, using nitrogen protection, adjust pH to 5.5, be heated to 90 DEG C,
6h is kept the temperature, is cooled to 6 DEG C, allyl amine, adjuvant stirring is added, is warming up to 60 DEG C, initiator is added, is stirred to react 5h;
(3) after the completion of reaction, adjust pH, stand 3h, discharging, collect out material, take 250 parts of ethyl alcohol, 80 parts go out material, 19 parts
Urethanes, 16 parts of tetramethylguanidine, 5 parts of surfactants;
(4) first by ethyl alcohol, go out material, part urethanes, tetramethylguanidine are put into reactor, in 5 DEG C of additions surfaces work
Property agent, stir 6h, be warming up to 19 DEG C, stirring heat preservation 2h stands 1h, discharges, and freeze-drying using petroleum ether, then freezes
Drying is to get asphalt warm-mix agent.
Commercially available asphalt warm-mix agent.
The asphalt warm-mix agent that above-described embodiment is obtained with comparative example is detected, Warm-Mix Bitumen Mixture low-temperature cracking-resistance
It is detected according to " standard specification for construction and acceptance of highway asphalt pavement " JTG F40-2004, temperature control is at 20 DEG C, bending tensile strength
Bigger, the crack resistance of mixture is stronger;Maximum flexural-tensile strain is bigger, and the crack resistance of mixture is stronger, obtained result such as 1 institute of table
Show.
Table 1:
Detection project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 |
Bending tensile strength/MPa | 10.2 | 10.1 | 10.1 | 9.8 | 7.7 |
Maximum flexural-tensile strain/10-6 | 3150.9 | 3149.2 | 3149.6 | 3100.6 | 2895.2 |
In summary, asphalt warm-mix agent effect of the invention is more preferable as can be seen from Table 1, is worth of widely use, it is described above only
For preferred mode of the invention, it is not intended to limit the invention, it is all within the spirits and principles of the present invention, made any to repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of preparation method of asphalt warm-mix agent, which is characterized in that the preparation method includes the following steps:
(1) hybrid particles and hydrochloric acid 1:4 in mass ratio~6 are subjected to ultrasonic vibration, stood, filtering collects filter residue, by weight
Number meter takes 200~250 parts of water, 40~45 parts of allyl amines, 30~33 parts of filter residues, 13~15 parts of copper sulphate, 3~7 parts of auxiliary
Agent, 2~5 parts of initiators;
(2) water, filter residue and copper sulphate are put into reaction kettle first, using nitrogen protection, adjust pH to 5.0~5.5, be heated to
85~90 DEG C, heat preservation is cooled to 2~6 DEG C, and allyl amine, adjuvant stirring is added, is warming up to 55~60 DEG C, initiator is added,
It is stirred to react;
(3) after the completion of reaction, pH is adjusted, is stood, material is collected out in discharging, takes 200~250 parts of ethyl alcohol, 60~80 parts of dischargings
Object, 13~19 parts of urethanes, 13~16 parts of tetramethylguanidine, 7~11 parts of additives, 2~5 parts of surfactants;
(4) first by ethyl alcohol, go out material, part urethanes, tetramethylguanidine are put into reactor, in 3~5 DEG C of addition additions
Agent and surfactant, stirring are warming up to 13~19 DEG C, and stirring heat preservation stands, discharges, is freeze-dried, washing, then freezes dry
It is dry to get asphalt warm-mix agent.
2. the preparation method of asphalt warm-mix agent according to claim 1, which is characterized in that hybrid particles in the step (1)
For vermiculite, blast furnace slag 9:1 in mass ratio~3 mixing, ball milling is carried out, crosses 500 meshes, collects sieving particle to get hybrid particles.
3. the preparation method of asphalt warm-mix agent according to claim 1, which is characterized in that the adjuvant is glutaraldehyde, penta
Dicarboxylic anhydride 7:2~4 in mass ratio mix.
4. the preparation method of asphalt warm-mix agent according to claim 1, which is characterized in that the initiator is by persulfuric acid
Ammonium, sodium bisulfate 3:1~4 in mass ratio mix.
5. the preparation method of asphalt warm-mix agent according to claim 1, which is characterized in that the preparation method of the additive
Are as follows: by maize pulp, distilled water 1:4~8 in mass ratio, mixed, 60~75 DEG C preheat, add maize pulp quality 10~
15% emulsifier is warming up to 90~95 DEG C, adds the potassium peroxydisulfate of maize pulp quality 3~6%, and maize pulp is added in stirring
The regulator of maize pulp quality 14~26% is added in the mix monomer of quality 48~52%, reaction, and the reaction was continued, stands, cold
But, it discharges, is spray-dried, washing is dry to get additive.
6. the preparation method of asphalt warm-mix agent according to claim 5, which is characterized in that the emulsifier is detergent alkylate
Any one in sodium sulfonate, lauryl sodium sulfate.
7. the preparation method of asphalt warm-mix agent according to claim 5, which is characterized in that the mix monomer is acryloyl
Amine, acrylic acid and styrene 2:1~5:2 in mass ratio are mixed.
8. the preparation method of asphalt warm-mix agent according to claim 1, which is characterized in that the regulator be melamine,
Lactic acid 4:1~3 in mass ratio mix.
9. the preparation method of asphalt warm-mix agent according to claim 1, which is characterized in that the additive formic acid, lactic acid and
Tetrafluoro boric acid 3:4:1~4 in mass ratio mix.
10. the preparation method of asphalt warm-mix agent according to claim 1, which is characterized in that the surfactant is 12
Any one in polyoxyethylene alkyl ether sulfate sodium, cocounut oil acyl diglycollic amide.