CN110036078A - Insulating properties shading printing ink and insulating component - Google Patents
Insulating properties shading printing ink and insulating component Download PDFInfo
- Publication number
- CN110036078A CN110036078A CN201880004831.2A CN201880004831A CN110036078A CN 110036078 A CN110036078 A CN 110036078A CN 201880004831 A CN201880004831 A CN 201880004831A CN 110036078 A CN110036078 A CN 110036078A
- Authority
- CN
- China
- Prior art keywords
- resin
- insulating properties
- printing ink
- bamboo charcoal
- shading
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of insulating properties shading printing ink, contains bamboo charcoal and adhesive resin.
Description
Cross reference
The application is based on the Japanese patent application 2017-095498 that on May 12nd, 2017 submits, CLAIM OF PRIORITY,
The application will be all included in disclosed in it.
Technical field
The present invention relates to a kind of insulating properties shading printing ink and insulating component.
Background technique
In correlative technology field, there are various performance requirements in addition to printing to ink.Wherein, in field of electronic device,
It is required that using while there is shading purposes and insulation performance black ink.As such black ink, generally using carbon black or
Iron oxide.
However, carbon black is used in electronic instrumentation, because its is conductive, there is a problem of impedance value deficiency.
In other words, although improving the proportional quantity of carbon black, shaded effect can be obtained, electric conductivity is also got higher, and as a result insulating properties will drop
It is low.In other words, there are shifting relationships between insulating properties and covering power.To solve this problem, 1 (day of patent document
Present patent application JP 2001-207079A) in disclose the technology of the carbon black covered about surface by resin.
In addition, seeking the fresh oil ink material of energy alternative carbon black and iron oxide always from the viewpoint of environmental protection.
As the ink material of not welding, for example, in patent document 2 (Japanese patent application JP2008-179737A), it is open
A kind of related technology of ink, the ink include the carbon powder that may be added to that in food of specified particle diameter.
Subject to be solved by the invention
But technology disclosed in Patent Document 2, for the purpose of being to add in food, it is not to be conceived to electronics to set
The technology on spare way.In addition, from foodsafety angle is ensured, using the special adhesive tree that can be used for food addition
For rouge as precondition etc., the material made it possible for is also very limited.
The means to solve the problem
The present inventor develops the electronic equipment ink of the not welding of alternative previous carbon black with keen determination, and result of study is first
Secondary discovery can be enable high covering power and high-insulativity and be deposited by using bamboo charcoal.
Here usually, the plant origins such as charcoal and bamboo charcoal and charcoal from other organic matter sources are conductive
Can, and the electric conductivity is different with the variation of the conditions such as firing temperature.
Therefore, the present inventor can stablize from exploitation obtains the viewpoint of high-insulativity ink and studies, and is not to be conceived to bamboo
The conductive characteristic that charcoal itself has, and it is conceived to the distinctive configuration aspects of bamboo charcoal.Also, it was found that adhesive resin is covered on ink
In bamboo charcoal entire outer surface and the interior surface that is formed of the distinctive structure of bamboo charcoal itself, make possessed by adhesive resin
Insulating properties is more effective and stablizes.It has also been found that bamboo charcoal is compared with other charcoals, it is easier to adhesive resin (binder
Resin it) ties and good covering can be obtained.Moreover, by using bamboo charcoal, not only obtain high covering, and by with gluing
The combination of agent resin, the ink for realizing high covering and high-insulativity and depositing.
Summary of the invention
The present invention provides a kind of insulating properties shading printing ink containing bamboo charcoal and adhesive resin.
In addition, the present invention provides a kind of insulating component, specifically includes substrate, and is formed on the substrate described
Insulating properties shading printing ink film.
Invention effect
According to the present invention, the insulating properties shading that can provide the environmental protection that can make high-insulativity and high covering and deposit prints
Brush ink.
The implementation form of invention
Insulating properties shading printing ink
Hereinafter, it is described in detail about implementation form of the invention.
Insulating properties shading of the invention printing ink, contains bamboo charcoal and adhesive resin.
Bamboo charcoal is the substance used as black ink, is the charcoal obtained after bamboo is fired.
Bamboo is readily available and cheap, and from the viewpoint of circular form resource, is not welding
Material.There are many bamboo type, such as usually using true bamboo, henon bamboo, Meng Zongzhu, cloth bag bamboo, black bamboo, female bamboo, root song bamboo etc..These
Type both can be used alone, and can also be used in mixed way two kinds or more.
The method for cooking of bamboo is also to have the charcoal using materials such as stainless steels it is well known that there is the method fired in charcoal kiln
Change the mechanical method for cooking of furnace.In addition, in the mechanical method for cooking using retort, also comprising using heating vapor in anaerobic
The method heated in compression ring border.In addition, firing condition, when being fired with charcoal kiln, under 400~1000 DEG C of high temperature, burns
A few days~mono- week processed or so when firing using retort machinery, such as under 400 DEG C~1000 DEG C high temperature, fires 6~8 hours left sides
It is right.But when being heated with heating vapor, Chang 15 divides short time interior progress in~1 hour or so.
Bamboo charcoal usually more generates subtleer hole than charcoal etc..In these subtle holes, macro pipeline (macrotubes)
Gapless arrangement forms a kind of so-called honeycomb structure, in these macro pipelines, draws nutrition and moisture of bamboo etc.
Tracheid charing crystallization, and subtleer micro-pipe is further formed on its inner wall.Further, since the fibre structure of bamboo is vertical
To arrangement, linearly, therefore these fine holes are also easier mutually linear aggregation arrangement.The average pore size of macro pipeline is big
Generally at 10~40 μm, the average pore size of micro-pipe is probably in 1~5nm.
In addition, more containing silicic acid and potassium in bamboo, these elements have when being fired into bamboo charcoal and are solidified into glass
The property of state.Therefore, bamboo charcoal is typically considered to than charcoal etc. more containing the substance of glassy state.
The specific surface area of bamboo charcoal, such as the numerical value calculated with the BET multipoint method of nitrogen adsorption, preferably in 100m2/ g with
On, more preferably in 200m2/ g or more.
On the other hand, the specific surface area of bamboo charcoal, preferably 1,000m2/ g is hereinafter, more preferably in 500m2/ g or less.By
Covering power can be improved in this.
The measurement of the specific surface area of bamboo charcoal can be measured according to JIS Z8830.
Partial size (the D of the 50% of bamboo charcoal50) preferably at 0.05 μm or more, more preferably at 1 μm or more, still more preferably from 2.5 μm.
It is hereby achieved that dispersibility appropriate.
On the other hand, the partial size (D of the 50% of bamboo charcoal50) preferably at 10 μm hereinafter, more preferably at 8.0 μm hereinafter, more excellent again
It is selected as 5.0 μm or less.It is possible thereby to form film appropriate, and covering power can be improved.
In addition, the 90% of bamboo charcoal partial size (D90) preferably at 20 μm hereinafter, more preferably at 10 μm or less.
Furthermore partial size (the D of the 50% of bamboo charcoal50) and 90% partial size (D90) measurement, such as laser refraction can be used
Size distribution is measured to acquire by volume reference with scattering method.
The content of bamboo charcoal, solid component of the insulating properties shading in printing ink of opposite 100 parts by weight, preferably in 40 weights
Part or more is measured, more preferably more than 70 parts by weight.Thus, it is possible to maintain printing characteristic, covering is improved, also can be improved insulation
Property.
On the other hand, the content of bamboo charcoal uses the solid component printed in ink relative to 100 parts by weight of insulation shadings,
It is preferred that in 90 parts by weight hereinafter, more preferably below 80 parts by weight.It is possible thereby to obtain mobility appropriate, good print is completed
Brush.
From the viewpoint of making ink characteristics more appropriate, bamboo charcoal surface can also carry out physical or chemically handle.
Adhesive resin is used to dispersion bamboo charcoal, forms printing film and uses.
Adhesive resin, as long as the resin of chemical organic synthesis, can be used diversified resin.From with bamboo
The intermiscibility of charcoal is good, from the perspective of making high-insulativity and covering in more high level and depositing, adhesive resin, preferably from
Vinyl chloride-vinyl acetate copolymer resin (being also referred to as " vinyl chloride resin " in the present specification), acrylic resin, polyester resin,
Epoxy resin, polycarbonate resin, polyolefin resin, synthetic rubber, celluosic resin, maleic acid resin, phenolic resin, poly- ammonia
Ester resin, polyamide, polyimide resin, melamine resin, phenoxy resin, active energy ray-curable tree
The modifier of rouge, above-mentioned resin, and the one or more kinds of resins chosen from the modifier of natural resin.Wherein,
More preferable vinyl chloride-vinyl acetate copolymer resin, acrylic resin, polyester resin or epoxy resin or these resins
Modifier, preferred polyester resin.
The content of adhesive resin, the bamboo charcoal of opposite 100 parts by weight, preferably more than 10 parts by weight, more preferably in 20 weights
Part or more is measured, on the other hand, preferably in 150 parts by weight hereinafter, more preferably below 120 parts by weight.According to the lower limit value with
On setting, good printing can be obtained, on the other hand, can be in more high level according to upper limit value setting below
On make insulating properties and covering and deposit.
Insulating properties shading of the invention can make insulating properties and screening because containing bamboo charcoal and adhesive resin with printing ink
Lid is simultaneously deposited.The details of this mechanism is although indefinite, but as described above, bamboo charcoal, usually contains than charcoal more thin
Micro- hole has the structure of the fine holes gapless arrangement of referred to as honeycomb structure.Therefore, the entrance of these fine holes with
And the inside in hole can flow into adhesive resin.In addition, because bamboo charcoal is usually more than charcoal containing vitreous substance, therefore
It is considered better than charcoal with the wetting quality of adhesive resin.
As a result, forming the state that adhesive resin seals bamboo charcoal, hidden even if increasing the proportional quantity of bamboo charcoal with improving
Gai Xing, is also able to suppress the reduction of impedance value, therefore enables insulating properties and covering and deposit, this can speculate.Into
And insulating properties shading of the invention printing ink, even with the occasion of the relatively high bamboo charcoal of electric conductivity, as described above,
Since bamboo charcoal is glued agent resin seal, good insulating properties can be obtained.
Insulating properties shading of the invention can make to insulate by meeting the following conditions with printing ink under high levels
Property and covering are simultaneously deposited.Such reason is although indefinite, and still, the present inventor is hidden in research repeatedly using the insulating properties of bamboo charcoal
For light in printing ink, discovery, can be effective by the way that optical concentration (OD) value in the condition is controlled in a specific range
Reach and realizes the covering for being suitble to insulating properties shading printing ink application and insulating properties and the index deposited.
Insulating properties shading of the invention printing ink is the printing testing machine (RKPrint of 6 mils using steel wire diameter
Coat Instruments Ltd., manufacture, cross bar No.2), it is pulled with 50mm/ seconds movement speeds, is applied on the glass substrate
It smears, optical concentration (OD) value of obtained film, preferably 1.0 or more, 7.0 or less.The film is at 80 DEG C, by 60
It is available after minute is dry.
Optical concentration (OD) value of the film, from the viewpoint of obtaining covering, more preferably 3.5 or more.Another party
Face, optical coating (OD) value of the film, goes out from the viewpoints such as good ink mobility, printing characteristic and adhesion are obtained
Hair, more preferably below 6.0.
It, can be in order to control optical concentration (OD) value of the film in insulating properties shading of the invention in printing ink
By the firing temperature, the type according to the selection adhesive resin such as average grain diameter and specific surface area, control bamboo that control bamboo charcoal
The when control bamboo charcoal of matching of charcoal and adhesive resin finally obtains the degree of scatter etc. of adhesive resin.In addition, to control
Degree of scatter, according to bamboo charcoal and the combination of adhesive resin etc., can for example, by shearing force intensity in selection dispersing apparatus with
And number of processes etc. carries out.
Furthermore (OD) value refers to logarithm the numerical value of the transmitance (T%) of the light indicated.In general, OD value
It is higher, it is meant that the transmitance of light is lower.
In addition, OD value can be measured for example, by densimeter " model 341C " (manufacture of X-Rite company).
In addition, insulating properties shading of the invention with printing ink within the scope of the effect of the invention, can also be with
The pigment other than bamboo charcoal is added in allotment.This occasion, for the amount of the bamboo charcoal in whole pigment, from obtaining high-insulativity
Viewpoint is set out, and preferably more than 50% mass, more preferably more than 80% mass, 100% mass can also be with.
Furthermore insulating properties shading of the invention printing ink, can also containing well-known ink additive at
Point.As well-known ink additive, such as there are the stabilizers such as solvent, antioxidant, levelling agent, defoaming agent, thickening
The interfacial agents such as agent, sagging inhibitor, Ricinate, antistatic agent, antifoggant, paraffin, slipping agent, coupling agent, silane are even
Join various additives such as agent, near infrared ray absorption etc..
As solvent, for example, have Mineral spirits, toluene, dimethylbenzene, carbon atom number 8~11 the nytrons such as aromatic hydrocarbon
Object;Ethyl acetate, butyl acetate, isobutyl acetate, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol (DEG)
Monobutyl ether acetate, dibasic acid ester (DBE) (bis- salt base acid エ ス テ Le) etc. esters;Ethylene glycol list ether, diethylene glycol list
The ether class such as methyl ether, diethylene glycol (DEG);The ketone such as methyl ethyl ketone, methyl iso-butyl ketone (MIBK), isobutyrone, cyclohexanone, isophorone
Class;The alcohols such as methanol, ethyl alcohol, isopropanol, n-butanol, isobutanol, diacetone alcohol, 3- methyl -3- methoxybutanol.It can be independent
It is used above using one kind of these solvents, or two kinds of mixing.Wherein, it is preferable to use ketone, esters and hydrocarbon.
Insulating properties shading printing ink, is to be mixed to form bamboo charcoal and adhesive resin with well-known method.
For example, bamboo charcoal is added in adhesive resin, dispersed using dispersal device appropriate, ink can be obtained.At this moment, from handle
From the perspective of optical concentration (OD) value control in a specific range under the conditions of described, for example, using the grinding point of three rollers
The occasion in bulk set, each long line pressure of roller are set in 20N/mm~60N/mm, to apply shearing force appropriate, and by number of processes
(number of pass times) is set in 2 times or more and is preferred.
Insulating properties shading of the invention printing ink, particularly suitable for needing the smart phone of shading performance, putting down
The printing etc. with touch function protection panels being arranged on the electronic equipments such as plate computer, auto-navigation system and intercom.If
The backlight in electronic equipment can be blocked in use using insulating properties shading of the invention printing ink, also can get hidden
This highly concealed type of electrode wiring of electronic equipment internal is hidden, and the maloperation of electronic equipment can be prevented.
Insulating component
Insulating component of the invention, including substrate and the insulating properties shading formed on the substrate printing ink
Film.
Substrate is not particularly limited, can be from polyester, polyamide, polycarbonate, acrylic acid, polyurethane, polyolefin, quartz
Glass, soda-lime glass, alkali-free glass, sapphire glass, chemically toughened glass and the selection use from its composite material
One or two or more kinds of materials and formed.The substrate formed by these materials, surface can also implement antifog processing, tempering
The conductive film process of processing, antireflection process, hot line cutting process, coloring treatment or ITO (tin indium oxide).In addition, substrate
Shape be not particularly limited.
The forming method of film is not particularly limited, and well-known method can be used.In addition, coating thickness is for example
3~200 μm.
Insulating component includes, for example, the band touch function protection panels etc. of the electronic equipment.
In addition, insulating component is also possible to list in substrate and the insulating properties shading between printing ink film layer
Layer has other multilayers.Furthermore, it is possible to have the film layer that multilayer is made of the insulating properties shading with printing ink.
For example, the film layer that can be made of with overlying multiple layers white ink on it can also be to insulate described in laminated multi-layer on substrate
Property shading with printing ink constitute film layer.
The application method of bamboo charcoal
The application method of bamboo charcoal of the invention is used bamboo charcoal as insulating properties shading printing ink.Therefore,
Insulating properties and covering can be made and deposit by providing, and use the environment amenable ink of recyclable resource.
Form of implementation of the invention is explained above, these are illustrations of the invention, can also be using other than the above each
Kind other forms.
Specific embodiment
Embodiment 1
In the following, according to embodiment, the present invention will be described in detail.But the contents of the present invention are not limited to embodiment.
Pigment
The pigment used in embodiment and comparative example, as shown in the following table 1,2.
Table 1
Table 2
Title | The name of an article | Manufacturing firm's name |
Carbon black E | SPECIAL BLACK 4 | EVONIC INDUSTRIES |
Iron oxide F | TODACOLOR KN-320 | Family field industry (strain) |
Adhesive resin
The adhesive resin used in embodiment and comparative example, as shown in table 3 below.
Table 3
<embodiment 1~11>
The mixture for matching (parts by weight) shown in table 4 in order to obtain, is added organic solvent (different Buddhist in adhesive resin
That ketone, the manufacture of EVONIK industrial group) and bamboo charcoal, it is pre-mixed with rotary wings formula pony mixer.Then, using three
Roller apparatus for grinding and dispersing (manufacture of BUHLER Co., Ltd., SDY-200 type), is being set as 40N/mm for the long line pressure of roller, by secondary
Dispersed under conditions of number 2 times, obtains ink.
<comparative example 1~9>
(parts by weight) are matched according to shown in table 4, coconut husk charcoal D has been used to replace bamboo charcoal, it is mixed with carbon black E or iron oxide F
It closes, other ingredients are identical as Examples 1 to 9, obtain ink.
To the ink obtained in embodiment and comparative example, following measurement and evaluation have been carried out.As a result such as 4,5 institute of table
Show.
<measurement>
With the printing testing machine of 6 mil of steel wire diameter, (RK Print Coat Instruments Ltd. manufactured, cross bar
No.2), pulled with 50mm/ seconds movement speeds, ink is applied on the glass substrate, under conditions of 80 DEG C, 60 minute minute
It is dry, obtain film.Optical concentration (OD) value of obtained film is measured respectively.
<evaluation>
Insulating properties: the measurement of impedance value (Ω)
With the printing testing machine of 6 mil of steel wire diameter, (RK Print Coat Instruments Ltd. manufactured, cross bar
No.2), pulled with 50mm/ seconds movement speeds, ink is applied on the glass substrate, it is dry under conditions of 80 DEG C, 60 minutes,
Form film.
Using teraohmmeter " model SM-21E " (manufacture of East Asia electric wave Industrial Co., Ltd), the distance between measurement terminal is
15mm is gently pressing against film coated surface, measures the impedance value of film coated surface.Measurement voltage is 1kv, measures at 3, takes its average value.
Measuring measurement range of the voltage in 1kv is 1.0 × 106Ω~2.0 × 1013Ω。
Covering: visually observation evaluation
With the printing testing machine of 6 mil of steel wire diameter, (RK Print Coat Instruments Ltd. manufactured, cross bar
No.2), pulled with 50mm/ seconds movement speeds, ink is applied on the glass substrate, it is dry under conditions of 80 DEG C, 60 minutes,
Film is formed, printed article is obtained.
From printing surface side (coated surface side) fluorescent lamp of obtained printed article, by skilled expert to from
The covering situation of the light for the fluorescent lamp that glass baseplate side is seen, carries out the evaluation of 4 grades.
◎: the light of fluorescent lamp is not through completely.
Zero: the light of fluorescent lamp is through a little.
△: the light of fluorescent lamp has to be penetrated to a certain degree.
×: the light of fluorescent lamp has a great deal of transmission.
Table 4
Table 5
Claims (13)
1. a kind of insulating properties shading containing bamboo charcoal and adhesive resin printing ink.
2. insulating properties shading according to claim 1 printing ink, it is characterised in that: the content of the bamboo charcoal, relatively
In 100 parts by weight the insulating properties shading with printing ink in solid component, more than 40 parts by weight, 90 parts by weight with
Under.
3. insulating properties shading according to claim 1 or 2 printing ink, it is characterised in that: use the insulating properties shading
Ink is printed, is the printing testing machine of 6 mils with steel wire diameter, is pulled with 50mm/ seconds movement speeds, applied on the glass substrate
Cloth, getable film optical concentration (OD) value 1.0 or more, 7.0 or less.
4. insulating properties shading according to any one of claims 1 to 3 printing ink, it is characterised in that: the adhesive
Resin is from vinyl chloride-vinyl acetate copolymer resin, acrylic resin, polyester resin, epoxy resin, polycarbonate resin, gathers
Olefin resin, synthetic rubber, celluosic resin, maleic acid resin, phenolic resin, polyurethane resin, polyamide, polyamides are sub-
Polyimide resin, melamine resin, phenoxy resin, active energy ray curable resin, above-mentioned resin modifier, with
And the one or more kinds of resins chosen from the modifier of natural resin.
5. according to claim 1 to the printing ink of insulating properties shading described in 4 any one, it is characterised in that: the gluing
Agent resin is from vinyl chloride-vinyl acetate copolymer resin, acrylic resin, polyester resin and epoxy resin and these resins
Modifier in one or two or more kinds of resins for choosing.
6. according to claim 1 to the printing ink of insulating properties shading described in 5 any one, it is characterised in that: the bamboo charcoal
50% partial size at 0.05 μm or more, 10 μm or less.
7. insulating properties shading according to any one of claims 1 to 6 printing ink, it is characterised in that: the adhesive
Resin is selected from vinyl chloride-vinyl acetate copolymer resin, acrylic resin, polyester resin and epoxy resin and these resins
One of modifier is several;And 50% partial size of the bamboo charcoal is at 2.5 μm or more, 8.0 μm or less.
8. insulating properties shading according to any one of claims 1 to 7 printing ink, it is characterised in that:
The specific surface area that the bamboo charcoal is measured using the BET multipoint method of nitrogen adsorption is in 100m2/ g or more, 1,000m2/ g or less.
9. insulating properties shading according to any one of claims 1 to 8 printing ink, it is characterised in that: the ink is used
In the printing with touch function protection panels being arranged on electronic equipment.
10. a kind of insulating component, specifically includes: substrate, and the claim 1 that is formed on the substrate is to claim
The printing ink film of high-insulativity shading described in 9 any one.
11. insulating component according to claim 10, which is characterized in that the substrate is by being selected from polyester, polyamide, gathering
Carbonic ester, acrylic acid, polyurethane, polyolefin, quartz glass, soda-lime glass, alkali-free glass, sapphire glass, chemical steel
Change one of composite material of glass and above-mentioned material or several materials and is formed.
12. a kind of bamboo charcoal application method that bamboo charcoal and adhesive resin are used together as insulating properties shading with printing ink.
13. the method for manufacturing insulating properties shading printing ink with bamboo charcoal and adhesive resin.