CN110026746A - Aluminium end socket processing method - Google Patents
Aluminium end socket processing method Download PDFInfo
- Publication number
- CN110026746A CN110026746A CN201910434920.7A CN201910434920A CN110026746A CN 110026746 A CN110026746 A CN 110026746A CN 201910434920 A CN201910434920 A CN 201910434920A CN 110026746 A CN110026746 A CN 110026746A
- Authority
- CN
- China
- Prior art keywords
- end socket
- aluminium
- blank plate
- cut
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aluminium end socket processing methods, Step 1: selection is cut: carrying out being cut into blank plate according to the size of wanted molding aluminium end socket；Step 2: deburred: blank periphery deburred is clean, and aluminium blank plate surface protective film retains；Step 3: welding: blank plate being carried out splicing welding, weld grinding is cleaned out；Step 4: drum pressure: upper/lower die wraps up flexible material, and aluminium blank plate is placed on lower mold, is suppressed aluminium blank plate；Step 5: spinning: wrapping up flexible material, the small r arc of spinning in spinning machine head；Step 6: trimming: before trimming, applying up-protective layer in end socket inner face and cut off extra straight flange according to wanted head skirt requirement for height；Step 7: groove: according to requiring, corresponding groove of polishing；Step 8: examining: testing after qualification aluminium end socket size obtained, surface quality up to the end socket of required preparation.
Description
Technical field
The invention belongs to Manufacturing Technology of Back-Covers, in particular to a kind of aluminium end socket processing method.
Background technique
2.6, its surface is easy to scratch aluminium material specific gravity, and the end socket that aluminium is produced is typically all with this
Color, if generating scratch in production, will not will affect end socket beauty in outer surface oiling paint or figure layer.
Summary of the invention
Aiming at the problems existing in the prior art, the purpose of the present invention is a kind of aluminium end socket processing technology thereof, Ke Yiyou
Effect prevents plowing from aluminium and shows to provide aluminium end socket aesthetics.
In order to achieve the above-mentioned object of the invention, the technical solution adopted by the present invention are as follows:
A kind of aluminium end socket processing method, which is characterized in that production carries out in the steps below:
Step 1: selection is cut: carrying out being cut into blank plate according to the size of wanted molding aluminium end socket；
Step 2: deburred: blank periphery deburred is clean, and aluminium blank plate surface protective film retains；
Step 3: welding: blank plate being carried out splicing welding, weld grinding is cleaned out；
Step 4: drum pressure: upper/lower die wrap up flexible material, aluminium blank plate is placed on lower mold, to aluminium blank plate into
Row compacting；
Step 5: spinning: wrapping up flexible material, the small r arc of spinning in spinning machine head；
Step 6: trimming: before trimming, applying up-protective layer in end socket inner face and cut according to wanted head skirt requirement for height
Except extra straight flange；
Step 7: groove: according to requiring, corresponding groove of polishing；
Step 8: examining: testing after qualification aluminium end socket size obtained, surface quality up to the envelope of required preparation
Head.
Blank plate in the step 1 is there are cutting surplus, after the welding in the step 3, then need to weld seam into
Row non-destructive testing.
The utility model has the advantages that
The advantageous point of the present invention compared with the prior art: the safeguard measure in aluminium end socket processing and making process can effectively be kept away
Exempt to scratch aluminium material surface, improves aluminium end socket aesthetics.
Specific embodiment
Combined with specific embodiments below, the present invention is further illustrated.
The aluminium end socket processing method of the present embodiment, manufacture craft carry out in the steps below:
Step 1: selection is cut: carrying out being cut into blank plate according to the size of wanted molding aluminium end socket；
Step 2: deburred: blank periphery deburred is clean, and aluminium blank plate surface protective film retains；
Step 3: welding: blank plate being carried out splicing welding, weld grinding is cleaned out；
Step 4: drum pressure: upper/lower die wrap up flexible material, aluminium blank plate is placed on lower mold, to aluminium blank plate into
Row compacting；
Step 5: spinning: wrapping up flexible material, the small r arc of spinning in spinning machine head；
Step 6: trimming: before trimming, applying up-protective layer in end socket inner face and cut according to wanted head skirt requirement for height
Except extra straight flange；
Step 7: groove: according to requiring, corresponding groove of polishing；
Step 8: examining: testing after qualification aluminium end socket size obtained, surface quality up to the envelope of required preparation
Head.
Blank plate in the step 1 is there are cutting surplus, after the welding in the step 3, then need to weld seam into
Row non-destructive testing.
The present invention is to the safeguard measure in aluminium end socket processing and making process it is possible to prevente effectively from scuffing aluminium material surface, improves aluminium
End socket aesthetics.
The above examples only illustrate the technical idea of the present invention, and this does not limit the scope of protection of the present invention, all
According to the technical idea provided by the invention, any changes made on the basis of the technical scheme each falls within the scope of the present invention
Within；The technology that the present invention is not directed to can be realized by the prior art.
Claims (2)
1. a kind of aluminium end socket processing method, which is characterized in that production carries out in the steps below:
Step 1: selection is cut: carrying out being cut into blank plate according to the size of wanted molding aluminium end socket；
Step 2: deburred: blank periphery deburred is clean, and aluminium blank plate surface protective film retains；
Step 3: welding: blank plate being carried out splicing welding, weld grinding is cleaned out；
Step 4: drum pressure: upper/lower die wraps up flexible material, and aluminium blank plate is placed on lower mold, is pressed aluminium blank plate
System；
Step 5: spinning: wrapping up flexible material, the small r arc of spinning in spinning machine head；
Step 6: trimming: before trimming, applying up-protective layer in end socket inner face, according to wanted head skirt requirement for height, cut off more
Remaining straight flange；
Step 7: groove: according to requiring, corresponding groove of polishing；
Step 8: examining: testing after qualification aluminium end socket size obtained, surface quality up to the end socket of required preparation.
2. aluminium end socket processing method according to claim 1, it is characterised in that: the blank plate in the step 1
There are cut surplus after the welding in the step 3 then to need to carry out non-destructive testing weld seam.