CN110003867A - 一种速溶工程用化学泥浆 - Google Patents
一种速溶工程用化学泥浆 Download PDFInfo
- Publication number
- CN110003867A CN110003867A CN201910373005.1A CN201910373005A CN110003867A CN 110003867 A CN110003867 A CN 110003867A CN 201910373005 A CN201910373005 A CN 201910373005A CN 110003867 A CN110003867 A CN 110003867A
- Authority
- CN
- China
- Prior art keywords
- urea
- pam
- chemical slurry
- instant
- polyacrylamide pam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种速溶工程用化学泥浆,其特征在于:由以下质量百分比的组份构成:聚丙烯酰胺PAM 38‑45%,尿素 38‑45%,可分散乳胶粉 1‑4%,纯碱 8‑20%。本发明通过聚丙烯酰胺PAM与针状尿素的最佳配伍,实现物理和化学双效应提高聚丙烯酰胺PAM的溶解速度,将传统PAM溶解速度有60‑120分钟提速至1‑2分钟,远超目前所有市售化学泥浆产品,明显减少使用浪费,更加省工省时。
Description
技术领域
本发明涉及工程用化学泥浆领域,具体讲是涉及一种高粘度的速溶型工程用化学泥浆的配方和生产加工方法。
背景技术
旋挖钻孔灌注桩是一项隐蔽性地下连续作业一次性完成的施工技术,特别是在旋挖钻孔期间,在复杂地层地段施工中,为了确保施工质量,要向孔内不断添加在钻孔开工前制作的泥浆来确保使孔壁不发生坍塌。典型作业场景就是打桩机打桩、钻井设备钻井。在打桩机打桩、钻井设备钻井等场合必须使用泥浆护壁,提高塑性粘度、静切力和动切力,以增强钻井液对钻屑的悬浮和携带能力;同时降低滤失量,形成致密泥饼,增强造壁性。传统的泥浆采用钠基膨润土为主生产,钠基膨润土在打桩时的使用量很大,每个桩基需要5-6吨膨润土。工地开工之前都要进行大量膨润土采购进行先期泥浆调制。而膨润土的一个问题是价格逐步走高,另一个问题是打桩对膨润土需求量太大,平原交通方便,运输不构成障碍,但是对于偏远山区、交通不便的地区大量膨润土的运输成为一个大问题。
解决的办法是采用化学泥浆,化学泥浆是以高分子聚合物PAM为主、辅以其它添加剂生产的,化学泥浆造浆效果好,自身添加量小,造浆仅需添加万分之几重量比比例的化学泥浆就可以,对运输的需求极大的降低。目前市场的化学泥浆都是由高分子聚合物PAM,防渗剂可分散乳胶粉,PH值调节剂纯碱,按比例混合而成。主要成分聚丙烯酰胺PAM的特性是分子量越高在水中的溶解越缓慢,分子量低达不到使用的要求。这就产生一个严重问题,目前市场的化学泥浆在使用过程中溶解缓慢,全部溶解需60-120min,溶解时需要匀速添加并不断搅拌,添加快了会在水中形成坨,成坨的聚丙烯酰胺不会再继续溶解,浪费物料,添加慢了费时费工。
发明内容
本发明的目的在于克服上述传统技术的不足之处,提供一种溶解快速的速溶工程用化学泥浆。
本发明的目的是通过以下技术措施来达到的:
一种速溶工程用化学泥浆,其特征在于:由以下质量百分比的组份构成:
聚丙烯酰胺PAM 38-45%,
尿素 38-45%,
可分散乳胶粉 1-4%,
纯碱 8-20%。
作为一种优选方案,所述各组份的质量百分比为:
聚丙烯酰胺PAM 40%,
尿素 40%,
可分散乳胶粉 2%,
纯碱 18%。
作为一种优选方案,所述各组份的质量百分比为:
聚丙烯酰胺PAM 45%,
尿素 45%,
可分散乳胶粉 1%,
纯碱 9%。
作为一种优选方案,所述各组份的质量百分比为:
聚丙烯酰胺PAM 38%,
尿素 38%,
可分散乳胶粉 4%,
纯碱 20%。
作为一种优选方案,所述各组份中聚丙烯酰胺PAM与尿素质量百分比相同。
作为一种优选方案,所述尿素为针状尿素。
一种化学泥浆的制备方法,包括以下步骤:
S1,准备泥浆池,清洁后注入清水;
S2,按配比比例加入上述速溶工程用化学泥浆;
S3,使用空气压缩机将气压放入池内进行泥浆充分均和即可。
本发明中PAM速溶原理:聚丙烯酰胺PAM和尿素按照1:1的比例混合,尿素通过化学作用和物理作用两方面同时提高PAM溶解速度。化学作用:入水后尿素与水形成水解物,该水解物作为链转移剂与丙烯酰胺链自由基发生反应,防止交联反应,极大的提高PAM溶解速度。物理作用:尿素十分亲水,分布在PAM颗粒中自身快速溶解的同时阻止PAM凝结成坨,加快PAM大分子溶解速度。
由于采用了上述技术方案,与现有技术相比,本发明的优点是:
本发明公开了一种速溶工程用化学泥浆,通过聚丙烯酰胺PAM与针状尿素的最佳配伍,实现物理和化学双效应提高聚丙烯酰胺PAM的溶解速度,将传统PAM溶解速度有60-120分钟提速至1-2分钟,远超目前所有市售化学泥浆产品,明显减少使用浪费,更加省工省时。
下面结合具体实施方式对本发明作进一步说明。
具体实施方式
实施例1:一种速溶工程用化学泥浆,由以下质量百分比的组份构成:
聚丙烯酰胺PAM 40%,
尿素 40%,
可分散乳胶粉 2%,
纯碱 18%。
在本实施例中,所述各组份中聚丙烯酰胺PAM与尿素质量百分比相同,所述尿素为针状尿素。
实施例2:一种速溶工程用化学泥浆,由以下质量百分比的组份构成:
聚丙烯酰胺PAM 45%,
尿素 45%,
可分散乳胶粉 1%,
纯碱 9%。
在本实施例中,所述各组份中聚丙烯酰胺PAM与尿素质量百分比相同,所述尿素为针状尿素。
实施例3:一种速溶工程用化学泥浆,由以下质量百分比的组份构成:
聚丙烯酰胺PAM 38%,
尿素 38%,
可分散乳胶粉 4%,
纯碱 20%。
在本实施例中,所述各组份中聚丙烯酰胺PAM与尿素质量百分比相同,所述尿素为针状尿素。
上述实施例中化学泥浆的制备方法,包括以下步骤:
S1,准备泥浆池,清洁后注入清水;
S2,按配比比例加入上述实施例中的速溶工程用化学泥浆;
S3,使用空气压缩机将气压放入池内进行泥浆充分均和即可。
Claims (6)
1.一种速溶工程用化学泥浆,其特征在于:由以下质量百分比的组份构成:
聚丙烯酰胺PAM 38-45%,
尿素 38-45%,
可分散乳胶粉 1-4%,
纯碱 8-20%。
2.根据权利要求1所述的一种速溶工程用化学泥浆,其特征在于:所述各组份的质量百分比为:
聚丙烯酰胺PAM 40%,
尿素 40%,
可分散乳胶粉 2%,
纯碱 18%。
3.根据权利要求1所述的一种速溶工程用化学泥浆,其特征在于:所述各组份的质量百分比为:
聚丙烯酰胺PAM 45%,
尿素 45%,
可分散乳胶粉 1%,
纯碱 9%。
4.根据权利要求1所述的一种速溶工程用化学泥浆,其特征在于:所述各组份的质量百分比为:
聚丙烯酰胺PAM 38%,
尿素 38%,
可分散乳胶粉 4%,
纯碱 20%。
5.根据权利要求1至4中任意一项所述的一种速溶工程用化学泥浆,其特征在于:所述各组份中聚丙烯酰胺PAM与尿素质量百分比相同。
6.根据权利要求1至4中任意一项所述的一种速溶工程用化学泥浆,其特征在于:所述尿素为针状尿素。