CN110003826A - A kind of melt pressure sensitive gluing agent - Google Patents
A kind of melt pressure sensitive gluing agent Download PDFInfo
- Publication number
- CN110003826A CN110003826A CN201910210509.1A CN201910210509A CN110003826A CN 110003826 A CN110003826 A CN 110003826A CN 201910210509 A CN201910210509 A CN 201910210509A CN 110003826 A CN110003826 A CN 110003826A
- Authority
- CN
- China
- Prior art keywords
- parts
- pressure sensitive
- melt pressure
- gluing agent
- mixed material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of melt pressure sensitive gluing agent, it is related to technical field of chemistry and chemical engineering, the raw material including following parts by weight: 20-40 parts of thermoplastic elastomer (TPE), 15-25 parts of plasticizer, 40-55 parts of tackifying resin, 0.1-0.5 parts of antioxidant；The tackifying resin is C5 Petropols and rosin resin is the mixture of 1-2:1 in mass ratio.Melt pressure sensitive gluing agent of the invention not only solves the poor problem of existing melt pressure sensitive gluing agent oxidation and heat resistant property, while ensure that product produced has compared with high-adhesive-strength.
Description
Technical field
The present invention relates to technical field of chemistry and chemical engineering, especially a kind of melt pressure sensitive gluing agent.
Background technique
The agent of melt pressure sensitive gluing is used extensively at home, the accounting also cumulative year after year in the use of adhesive, mainly
Since melt pressure sensitive gluing agent is pollution-free, quick solidifying, high production efficiency, production cost are relatively low, future, which has, is widely answered
Use prospect.
Application No. is a kind of melt pressure sensitive gluing agent of 2013106232510 patent disclosure, innovative point is to use
A kind of light color liquid resin replaces traditional Petropols as tackifying resin, alleviates made using Petropols to a certain extent
The problem of at high cost brought by raw materials for production and environmental pollution, but light color liquid resin preparation process is complicated, production effect
Industrialization demand is not satisfied in rate, processing cost, it is difficult to practical.
Application No. is a kind of polyester hot melting pressure sensitive adhesives of 2015109342390 patent disclosure and preparation method thereof, in nitrogen
In compression ring border, by modified poly ester elastomer in 170-230 DEG C and antioxidant, tackifying resin, plasticizer and filler melt blending,
Obtain polyester hot melting pressure sensitive adhesive.Pressure sensitive adhesive heat resistance made from the above method and anti-aging oxidation susceptibility are good, but bond strong
Spend small, oil resistant poor solvent resistance.
At present for the research of melt pressure sensitive gluing agent in terms of a few thing has also been made, but on the whole also in having needed
The kind stage.
Summary of the invention
The purpose of the present invention is being directed to the prior art problem of melt pressure sensitive gluing agent, a kind of melt pressure sensitive gluing is provided
Agent, it not only solves the poor problem of existing melt pressure sensitive gluing agent oxidation and heat resistant property, while ensure that product produced
With compared with high-adhesive-strength.
To achieve the above object, the invention adopts the following technical scheme: including the raw material of following parts by weight:
20-40 parts of thermoplastic elastomer (TPE), 15-25 parts of plasticizer, 40-55 parts of tackifying resin, 0.1-0.5 parts of antioxidant；
The tackifying resin is C5 Petropols and rosin resin is the mixture of 1-2:1 in mass ratio.
Further, the thermoplastic elastomer (TPE) is SIS1120 and SIS1250 is the mixture of 1-4:1 in mass ratio.
Further, the plasticizer is naphthenic oil 4010.
Further, the antioxidant is antioxidant 1010.
It further additionally provides, a kind of preparation method of melt pressure sensitive gluing agent includes the following steps:
(1) 15-25 parts and antioxidant 0.1-0.5 parts of plasticizer are placed in Temperature control stirrer, are stirred evenly, whipping temp is
110-130 DEG C, obtain mixed material A;
(2) thermoplastic elastomer (TPE) 20-40 parts is added in the mixed material A made from step (1), stirring to thermoplastic elastomer (TPE) is melted
Change uniformly, whipping temp is 140-160 DEG C, obtains mixed material B;
(3) tackifying resin 40-55 parts is added in the mixed material B made from step (2), stirs evenly, whipping temp 180-
200 DEG C to get melt pressure sensitive gluing agent.
The utility model has the advantages that compared with the prior art, the advantages of the present invention are as follows: it not only solves existing melt pressure sensitive gluing
The poor problem of agent oxidation and heat resistant property, while ensure that product produced has compared with high-adhesive-strength.
Specific embodiment
Below by a preferred embodiment of the present invention will be described in detail.
Embodiment 1:
(1) by 4010:15 parts of naphthenic oil and antioxidant 1010: 0.5 part is placed in Temperature control stirrer, stirs evenly, whipping temp
It is 110-130 DEG C, obtains mixed material A;
(2) thermoplastic elastomer (TPE) of Shandong Ju Sheng Science and Technology Ltd. production is added in the mixed material A made from step (1)
SIS1120:20 parts and SIS1250:20 parts, stirring to thermoplastic elastomer (TPE) SIS1120 and SIS1250 is melted uniformly, stirring temperature
Degree is 140-160 DEG C, obtains mixed material B;
(3) tackifying resin (rosin resin and C5 Petropols) are added in the mixed material B made from step (2): 44.5 parts,
C5 Petropols and rosin resin content ratio are 1:1 in middle tackifying resin, are stirred evenly, and whipping temp is 180-200 DEG C, i.e.,
Obtain the agent of melt pressure sensitive gluing.
Embodiment 2:
(1) by 4010:15 parts of naphthenic oil and antioxidant 1010: 0.5 part is placed in Temperature control stirrer, stirs evenly, whipping temp
It is 110-130 DEG C, obtains mixed material A;
(2) thermoplastic elastomer (TPE) of Shandong Ju Sheng Science and Technology Ltd. production is added in the mixed material A made from step (1)
SIS1120:32 parts and SIS1250:8 parts, stirring to thermoplastic elastomer (TPE) SIS1120 and SIS1250 is melted uniformly, stirring temperature
Degree is 140-160 DEG C, obtains mixed material B;
(3) tackifying resin (rosin resin and C5 Petropols) are added in the mixed material B made from step (2): 44.5 parts,
C5 Petropols and rosin resin content ratio are 1:1 in middle tackifying resin, are stirred evenly, and whipping temp is 180-200 DEG C, i.e.,
Obtain the agent of melt pressure sensitive gluing.
Embodiment 3:
(1) by 4010:25 parts of naphthenic oil and antioxidant 1010: 0.1 part is placed in Temperature control stirrer, stirs evenly, whipping temp
It is 110-130 DEG C, obtains mixed material A;
(2) thermoplastic elastomer (TPE) of Shandong Ju Sheng Science and Technology Ltd. production is added in the mixed material A made from step (1)
SIS1120:10 parts and SIS1250:10 parts, stirring to thermoplastic elastomer (TPE) SIS1120 and SIS1250 is melted uniformly, stirring temperature
Degree is 140-160 DEG C, obtains mixed material B;
(3) tackifying resin (rosin resin and C5 Petropols) are added in the mixed material B made from step (2): 55 parts, wherein
C5 Petropols and rosin resin content ratio are 2:1 in tackifying resin, are stirred evenly, whipping temp be 180-200 DEG C to get
Melt pressure sensitive gluing agent.
Embodiment 4:
(1) by 4010:25 parts of naphthenic oil and antioxidant 1010: 0.1 part is placed in Temperature control stirrer, stirs evenly, whipping temp
It is 110-130 DEG C, obtains mixed material A;
(2) thermoplastic elastomer (TPE) of Shandong Ju Sheng Science and Technology Ltd. production is added in the mixed material A made from step (1)
SIS1120:16 parts and SIS1250:4 parts, stirring to thermoplastic elastomer (TPE) SIS1120 and SIS1250 is melted uniformly, stirring temperature
Degree is 140-160 DEG C, obtains mixed material B;
(3) tackifying resin (rosin resin and C5 Petropols) are added in the mixed material B made from step (2): 55 parts, wherein
C5 Petropols and rosin resin content ratio are 1:1 in tackifying resin, are stirred evenly, and whipping temp is 180-200 DEG C to get heat
The quick adhesive of fusion pressure.
Embodiment 5:
(1) by 4010:20 parts of naphthenic oil and antioxidant 1010: 0.1 part is placed in Temperature control stirrer, stirs evenly, whipping temp
It is 110-130 DEG C, obtains mixed material A;
(2) thermoplastic elastomer (TPE) of Shandong Ju Sheng Science and Technology Ltd. production is added in the mixed material A made from step (1)
SIS1120:20 parts and SIS1250:20 parts, stirring to thermoplastic elastomer (TPE) SIS1120 and SIS1250 is melted uniformly, stirring temperature
Degree is 140-160 DEG C, obtains mixed material B;
(3) tackifying resin (rosin resin and C5 Petropols) are added in the mixed material B made from step (2): 40 parts, wherein
C5 Petropols and rosin resin content ratio are 1:1 in tackifying resin, are stirred evenly, and whipping temp is 180-200 DEG C to get heat
The quick adhesive of fusion pressure.
Embodiment 6；
(1) by 4010:19.8 parts of naphthenic oil and antioxidant 1010: 0.2 part is placed in Temperature control stirrer, stirs evenly, stirring temperature
Degree is 110-130 DEG C, obtains mixed material A;
(2) thermoplastic elastomer (TPE) of Shandong Ju Sheng Science and Technology Ltd. production is added in the mixed material A made from step (1)
SIS1120:20 parts and SIS1250:20 parts, stirring to thermoplastic elastomer (TPE) SIS1120 and SIS1250 is melted uniformly, stirring temperature
Degree is 140-160 DEG C, obtains mixed material B;
(3) tackifying resin (rosin resin and C5 Petropols) are added in the mixed material B made from step (2): 40 parts, wherein
C5 Petropols and rosin resin content ratio are 2:1 in tackifying resin, are stirred evenly, and whipping temp is 180-200 DEG C to get heat
The quick adhesive of fusion pressure.
Embodiment 7:
(1) by 4010:20 parts of naphthenic oil and antioxidant 1010: 0.4 part is placed in Temperature control stirrer, stirs evenly, whipping temp
It is 110-130 DEG C, obtains mixed material A;
(2) thermoplastic elastomer (TPE) of Shandong Ju Sheng Science and Technology Ltd. production is added in the mixed material A made from step (1)
SIS1120:20 parts and SIS1250:10 parts, stirring to thermoplastic elastomer (TPE) SIS1120 and SIS1250 is melted uniformly, stirring temperature
Degree is 140-160 DEG C, obtains mixed material B;
(3) tackifying resin (rosin resin and C5 Petropols) are added in the mixed material B made from step (2): 49.6 parts,
C5 Petropols and rosin resin content ratio are 1:1 in middle tackifying resin, are stirred evenly, whipping temp be 180-200 DEG C to get
Melt pressure sensitive gluing agent.
The adherency of melt pressure sensitive gluing agent and oxidation and heat resistant property made from embodiment 1- embodiment 7 are as shown in table 1.
Table 1
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Embodiment 6 | Embodiment 7 | Polyester hot melting pressure sensitive adhesive (commercially available) | EVA hot-fusible pressure-sensitive adhesive (commercially available) | |
| 180 DEG C of peel strengths (N/cm) | 3.67 | 3.79 | 3.75 | 3.72 | 3.77 | 3.73 | 3.81 | 3.26 | 3.58 |
| Heat ageing peel strength (N/cm) | 2.91 | 3.08 | 3.03 | 3.01 | 3.05 | 3.02 | 3.11 | 2.43 | 2.76 |
| Hold sticky (day) | >10 | >10 | >10 | >10 | >10 | >10 | >10 | >5 | >10 |
According to above data it can be proved that melt pressure sensitive gluing agent of the present invention not only solves existing melt pressure sensitive gluing
The poor problem of agent oxidation and heat resistant property, while ensure that product produced has compared with high-adhesive-strength.
Preferred embodiment above is only used to illustrate the technical scheme of the present invention and not to limit it, although passing through above-mentioned preferred implementation
Example is described in detail the present invention, however, those skilled in the art should understand that, can be in the form and details
Various changes are made to it, without departing from claims of the present invention limited range.
Claims (5)
1. a kind of melt pressure sensitive gluing agent, which is characterized in that the raw material including following parts by weight:
20-40 parts of thermoplastic elastomer (TPE), 15-25 parts of plasticizer, 40-55 parts of tackifying resin, 0.1-0.5 parts of antioxidant；
The tackifying resin is C5 Petropols and rosin resin is the mixture of 1-2:1 in mass ratio.
2. a kind of melt pressure sensitive gluing agent according to claim 1, it is characterised in that: the thermoplastic elastomer (TPE) is
SIS1120 and SIS1250 is the mixture of 1-4:1 in mass ratio.
3. a kind of melt pressure sensitive gluing agent according to claim 1, it is characterised in that: the plasticizer is naphthenic oil
4010。
4. a kind of melt pressure sensitive gluing agent according to claim 1, it is characterised in that: the antioxidant is antioxidant
1010。
5. the preparation method of melt pressure sensitive gluing agent according to any one of claims 1 to 4, which is characterized in that including
Following steps:
(1) 15-25 parts and antioxidant 0.1-0.5 parts of plasticizer are placed in Temperature control stirrer, are stirred evenly, whipping temp is
110-130 DEG C, obtain mixed material A;
(2) thermoplastic elastomer (TPE) 20-40 parts is added in the mixed material A made from step (1), stirring to thermoplastic elastomer (TPE) is melted
Change uniformly, whipping temp is 140-160 DEG C, obtains mixed material B;
(3) tackifying resin 40-55 parts is added in the mixed material B made from step (2), stirs evenly, whipping temp 180-
200 DEG C to get melt pressure sensitive gluing agent.